Tibial high-density polyethylene wear in conforming tibiofemoral prostheses



Download PDF

Abstract

We have studied 27 tibial prostheses retrieved from knee replacements after 1 to 9 years. In 22 the femoral components were of cobalt-chrome, in five polyacetal. The design of the components gave a nominal contact area of 320 mm2 on each condyle. The tibial component was of high-density polyethylene (HDP) at least 6 mm thick, and not heat-treated. In the metal/HDP prostheses the average wear rate was 0.025 mm/year. The relative wear on the medial and lateral sides was related to the leg axis. None of the retrieved prostheses showed any severe disruption of their surface. The polyacetal/HDP prostheses showed similar wear with a statistically insignificant trend towards slower penetration. We conclude that the rate of wear of HDP in a conforming tibiofemoral bearing with a fixed tibial component at least 6 mm thick and not heat-treated is slow enough to be safe in clinical practice.

For access options please click here