WEAR OF RETRIEVED CERAMIC TOTAL KNEE PROSTHESIS IN CLINICAL USE FOR 23 YEARS



Abstract

According to the knee simulator test results in 1970s, the total decrease in thickness of UHMWPE tibial tray in combination with ceramic femoral component [F-Comp] was less than one tenth as that of the combination with metal [1]. These advantages led to development of total knee prosthesis [TKP] with alumina ceramics. In this study, we report the wear surface observation, the clinical wear and the oxidation of the retrieved TKP used clinically for 23 years, comparing with a metal TKP.

The retrieved TKP was implanted in 1979, and retrieved on January 9th in 2002. This TKP consisted of an alumina ceramic F-Comp and a UHMWPE tray combined with a alumina ceramic tibial component. Observations of the surface of alumina F-Comp and UHMWPE tray were carried out using SEM. Shape of UHMWPE tray was determined three-dimensionally. Comparing the result with original shape based on the product’s plan, liner wear and volumetric wear were calculated. Oxidation index was determined by Fourier transform infrared spectrophotometry.

Alumina F-Comp did not have any scratch on the surface by seeing with naked eye. UHMWPE tray had deformation and scratches obviously. The liner wear rate was 37 micrometer/year and volumetric wear rate was 18.8 mm3/year. The oxidation indexes were 0.6 in the unworn area, 1.2 in the worn area and 0.2 in the inner area.

SEM observations of the F-Comp demonstrated no scratch or pit. In contrast, many scratches were clearly observed on the UHMWPE tray. However, higher magnification observations did not demonstrate severe wear, which was shown on the wear analysis of a metallic F-Comp. Oxidation degradation is a problem to solve. However, the low wear rate and mild wear pattern demonstrate that ceramic F-Comp reduced UHMWPE wear.

The abstracts were prepared by Nico Verdoschot. Correspondence should be addressed to him at Orthopaedic Research Laboratory, Universitair Medisch Centrum, Orthopaedie / CSS1, Huispost 800, Postbus 9101, 6500 HB Nijmegen, Th. Craanenlaan 7, 6525 GH Nijmegen, The Netherlands.