RETRIEVAL ANALYSIS OF SQUEAKING ALUMINA CERAMIC-ON-CERAMIC BEARINGS.



Abstract

Squeaking is a rare complication of hard-on-hard hip bearings. Occasionally the noise is troublesome enough to warrant revision surgery. The purpose of this study is to contribute to the understanding of the mechanism(s) underlying squeaking.

We analyzed 10 alumina ceramic-on-ceramic bearings from squeaking hips collected at revision surgery. The reason for revision was given as squeaking (6 cases) or squeaking and pain (4 cases). Six of the 10 patients were male, average patient age was 48. Bearings were retrieved after an average of 23 months in service (11 to 61 months). There were 4 different designs of acetabular component from 2 different manufacturers. Nine have an elevated metal rim which is proud of the ceramic and one does not. Two bearings were 36mm in diameter, 6 were 32mm and 2 were 28mm.

All 10 bearings showed evidence of edge loading wear. Mean dimensions of the wear patch were 37mm by 12mm on the acetabular component and 32mm by 13mm on the femoral heads. Wear dimension was not related to bearing diameter. Seven of the 10 implants also had evidence of impingement of the femoral neck against the elevated metallic rim or the ceramic insert or both. There was no chipping or fracture of any of the ceramic components.

Squeaking is a recently recognized complication of hard on hard bearing surface. This retrieval study is the first of its kind, to our knowledge attempting to unravel the mechanism of this undesirable complication. Although impingement seems to be present in majority of cases, the latter does not seem to be necessary. Edge loading wear was the common factor in all cases and this may prove to be a critical mechanism.