TYPE-I COLLAGEN MEMBRANE AS A SCAFFOLD FOR TENDON REPAIR: AN IN VITRO AND IN VIVO STUDY.



Abstract

Aims: A new type I collagen membrane developed for use as a tendon graft was tested in vitro and in vivo.

Methods: The membrane (Opocrin, Italy) is obtained from type-I collagen harvested from equine Achilles tendon and is composed of collagen I fibres oriented in a single direction. It is isotropic, resorbable, hygroscopic and non immunogenic acellular membrane.

Primary human fibroblasts were seeded on collagen I membranes with aligned fibres (# 40133) with and randomly arranged fibres (# 40153). Cell proliferation was evaluated at 4, 8 and 12 days by spectrophotometry. Membrane sections were studied by immunohistochemistry and by confocal microscope on day 12 of culture.

The middle third of the patellar tendon was lesioned bilaterally in 10 adult male New Zealand White rabbits and repaired on the right side by a graft (# 40133). The contralateral tendon was left untreated and served as control. Animals were euthanized 1 or 6 months after surgery and the tendon grafts subjected to histological examination.

Results: The in vitro study demonstrated cell viability and proliferation already on day 4 from membrane seeding.

Cells were homogeneously distributed, with a more marked orientation along the main membrane axis in batch 40133 than in 40153. The in vivo study showed that cell orientation and differentiation in the scaffold with aligned fibres was satisfactory, with decreased cellularity, good integration with the surrounding tissue and crimp formation. Inflammatory reaction or excessive implant neovascularization were never observed.

Conclusion: The new type I collagen membrane exhibited a behaviour similar to other tendon or ligament scaffolds. Fibre orientation in the membrane with aligned fibres allowed to obtain a quick and well-oriented cell growth. The membrane appears to be suitable for application in tendon and ligament repair and substitution.