SEVEN TO TEN YEAR FOLLOW-UP OF HIGHLY CROSS-LINKED POLYETHYLENE LINERS IN TOTAL HIP ARTHROPLASTY

Abstract

Highly cross-linked polyethylene (HXLPE) is one of the most widely utilized bearing surfaces for total hip arthroplasty (THA). The first patients to receive XLPE will be 10 years post-op as of December 31, 2008. The purpose of this study is to report the long-term clinical and radiographic outcomes of patients implanted with HXLPE.

A group of 247 primary total hip replacements (224 patients) using HXLPE liners (Longevity or Durasul, Zimmer Inc.) with 22, 26, 28, or 32mm femoral heads were implanted between 1999 and 2001. Clinical evaluation measures included the Harris hip, EQ-5D, SF-36 functional scores, and UCLA activity scores. In addition to plain radiograph assessment, the computerized Martell method was used to measure head penetration over time. A matched group of 241 primary total hip replacements (201 patients) with the same head sizes using conventional polyethylene (PE) with a minimum of 7 years follow-up was used as a Martell method control group. The steady state penetration rate was defined as the slope of the linear regression line of the plot of head penetration from the 1 year film to each subsequent film to discount the early bedding-in process. A student’s t-test was used to compare wear rates between head sizes in each group, and a repeated-measures mixed model ANOVA was used to compare the groups for the 28mm head size.

There were no osteolytic lesions around the cup or stem, and no revisions were performed for polyethylene wear or liner fracture. Clinical outcome scores were averaged: Harris Hip 88.1±11.97, EQ-5D 74.0±27.0, SF-36 physical activity scores 53.3±8.4, SF-36 mental score 46.9±11.1, and UCLA activity 6.4±2.1. The steady state wear of the conventional polyethylene patients increased with time for both 26 and 28mm head sizes (0.144 and 0.127mm/year, respectively). No significant difference was found between the head sizes coupled with conventional polyethylene (p=0.14). Femoral head penetration in the highly cross-linked polyethylene did not increase over time after the first year. The steady state wear rates of HXLPE liners with 28mm or 32mm femoral heads were not significantly different than a slope of zero (p=0.54 for both head sizes).

Clinical follow-up results are typical of a primary THR patient population, and the radiographic results are excellent with no signs of peri-prosthetic osteolysis. Patients with PE show wear rates that are significantly different than zero indicating significant wear of the material. Conversely, patients with HXLPE display no measureable wear at 7–9 years as the wear rates were within the error detection of the Martell method. This long-term clinical and radiographic follow-up study for this new bearing material shows excellent clinical outcomes with very low in vivo wear.