Abstract
Formation of micro-cracks occurs in bone due to daily activities. Through a mechanism of self-repair, these micro-cracks are detected, and the damaged areas are restored, avoiding further propagation. The Scissors Model suggests that the osteocyte processes that cross the micro-cracks break as consequence of the cyclic displacements of the micro-crack faces, due to fatigue, and this triggers the remodelling processes. A fresh bovine tibia bone was cut in sections oriented 20° from the transversal direction. The cortical bone was sliced using a circular saw and shaped to the dimensions: 20 × 10 × 1 (mm) and the surfaces were polished. µCT images were obtained from all the samples (μCT 40, Scanco Medical, Brüttisellen, Switzerland). From the DICOM files, the geometries were reconstructed and meshed using tetrahedrons, in ICEM CFD. The Elasticity Modulus (E) was determined in Bonemat, by applying an empirical relationship Elasticity-Density from the literature. The parts were then imported into ANSYS APDL to simulate micro-crack propagation in bone. This model will be validated with further experimental work where the micro-crack will be initiated in the prepared samples and propagated due to fatigue loading, and the osteocyte processes will be visualized in the Scanning Electron Microscope (SEM). This investigation aims to study how cyclic loading in bones and failure of osteocyte processes can trigger target the mechanism of bone remodelling. The resulting model can later contribute for the investigation of treatments for bone diseases such as osteoporosis and the response of bone to the presence of orthopaedic implants.