Abstract
In 2011, approximately 1.6 million total hip arthroplasties (THAs) were conducted in 27 of the 34 member countries in the Organization for Economic Cooperation and Development (OECD) However, approximately 10–15% of patients still require revision surgery every year. Therefore, new technologies are required to increase the life-spam of the prosthesis from the current 10–15 years to at least 20–30 years. Our strategy focuses on surface modification of the bearing materials with a hydrophilic coating to improve their wear behaviour. These coatings are biocompatible, with high swelling capacity and antifouling properties, mimicking the properties of natural cartilage, i.e. wear resistance with permanent hydrated layer that prevents prosthesis damage. Clear beneficial advantages of this coating have been demonstrated in different conditions and different materials, such as UHMWPE, PEEK, CrCo, Stainless steel, ZTA and Alumina. Using routine tribological experiments, the wear for UHMWPE substrate was decreased by 75% against alumina, ZTA and stainless steel. For PEEK-CFR substrate coated, the amount of material lost against ZTA and CrCo was at least 40% lower. Further experiments on hip simulator adding abrasive particles (1-micron sized aluminium particles) during 3 million cycles, on a total of 6 million, showed a wear decreased of around 55% compared to uncoated UHMWPE and XLPE. In conclusion, CIDETEC‘s coating technology is versatile and can be adapted to protect and improve the tribological properties of different types of surfaces used for prosthesis, even in abrasive conditions.