Abstract
The enthesis is a specialised zonal tissue interface between tendon and bone, essential for adequate force transmission and composed by four distinct zones (tendon, fibrocartilage, mineralized fibrocartilage and bone). After injury, the native structure is often not re-established and a mechanically weaker fibrovascular scar is formed. Traditionally used monotherapies have failed to be effective, posing the need for multi-cargo localized delivery vehicles. We hypothesize that multilayer collagen-based scaffolds can serve as delivery vehicles for specific bioactive molecules with tenogenic, chondrogenic and osteogenic potential to enhance the functional regeneration of the enthesis. Three-layer scaffolds composed by a tendon-like layer of collagen type I, a cartilage-like layer of collagen type II and a bone-like layer of collagen type I and hydroxyapatite were fabricated by an iterative layering freeze-drying technique. The scaffolds were cross-linked with varying concentration of 4-arm polyethylene glycol (4s-PEG) and the biological and mechanical properties were assessed. Each layer was functionalized with platelet-derived growth factor, insulin growth factor, heparan sulfate or bone morphogenetic protein 7 and their tenogenic, chondrogenic and osteogenic potential on bone-marrow derived stem cells was investigated in vitro. Scaffolds cross-linked with 1 mM 4s-PEG showed 60% free amines reduction respect to non-cross-linked scaffolds, were stable in collagenase over 24 hours and had a compression modulus of 30 kPa. The bioactive molecules had a sustained release profile (approximately 50 ng/mL) over 5 days as a function of cross-linking. Preliminary in vitro studies confirmed the chondrogenic potential of heparin sulfate and insulin growth factor by the increase of proteoglycans.