Abstract
This study reports the ten-year outcomes of a three-arm, multicentre randomised controlled trial comparing Cobalt-Chrome (CoCr) and Oxidised Zirconium (OxZr) femoral heads with ultra-high molecular weight polyethylene (UHMWPE) versus highly cross-linked polyethylene (XLPE) liners in total hip arthroplasty (THA).
Patients undergoing THA from four institutions were prospectively randomised into three groups. Group A received a CoCr femoral head and XLPE liner; Group B received an OxZr femoral head and XLPE liner; and Group C received an OxZr femoral head and UHMWPE liner. The outcomes of 262 study patients were analysed at ten years follow-up.
At ten years, increased linear wear rates were recorded in group C compared to group A (0.133 ± 0.21 mm/yr vs 0.031 ± 0.07 mm/yr respectively, p<0.001) and group B (0.133 ± 0.21 mm/yr vs 0.022 ± 0.05 mm/yr respectively, p<0.001). Patients in group C had increased risk of osteolysis and aseptic loosening requiring revision surgery compared with group A (7/133 vs 0/133 respectively, p=0.007) and group B (7/133 vs 0/135 respectively, p=0.007). There was a non- significant trend towards increased liner wear rates in group A compared to group B (0.031 ± 0.07 mm/yr vs 0.022 ± 0.05 mm/yr respectively, p=0.128). All three groups were statistically comparable preoperatively and at ten years follow-up from a clinical score perspective.
The use of UHMWPE was associated with progressively increased annual liner wear rates. At ten years follow-up, this translated to an increased incidence of osteolysis and aseptic loosening requiring revision, compared with XLPE. Femoral heads composed of OxZr were associated with a non-significant trend towards reduced wear rates compared to CoCr, but this did not translate to any differences in osteolysis, functional outcomes, or revision surgery between the two treatments groups.