Abstract
Introduction
In specific conditions, infection may lead to bone loss and is difficult to treat1. Current clinical approaches rely on the introduction of antibiotics. While these may be effective, there are concerns regarding the rise of antimicrobial resistance. There is therefore interest in the development of antimicrobial bone graft substitutes for dental and trauma surgery.
Aim & Objectives
The incorporation of zinc into biomaterials has been shown to confer broad spectrum antimicrobial activity, but this has not yet been applied to the development of a commercial bone graft substitute. The aim of this research was therefore to prepare and characterise a series of zinc-substituted nanoscale hydroxyapatite (nHA) materials, including evaluation of antimicrobial activity.
Method
Zinc (Zn) substituted nHA materials were prepared (0, 5, 10, 15 & 20 mol.% Zn) using a wet chemical precipitation method with a rapid mixing(2). The reaction was carried out using zinc hydroxide at pH 10. The suspension formed was washed and dried into both powder & paste forms. The resultant powders were characterized using transmission electron microscopy (TEM) and X-ray diffraction (XRD). The antimicrobial activity was evaluated against Staphylococcus aureus (S8650 strain - isolated from an osteomyelitis case), by two techniques. The Miles and Misra method was applied to determine the number of colony-forming units (CFUs) in bacterial suspensions incubated with pastes. Secondly, a biofilm initialization method was used to evaluate the capacity of the materials to prevent biofilm formation. One-way analysis of variance (ANOVA) was used for the statistical analysis and results with p-value < 0.05 were considered statistically significant.
Results
XRD indicated the formation of pure hydroxyapatite with up to 10 mol.% Zn without any side products. However, when Zn was increased to 15 & 20 mol %, zinc oxide (ZnO) peaks were detected. The TEM showed nanoscale needle-like particles when Zn was increased compared to nHA particles. Regarding the antibacterial activity, ZnHA pastes at all concentrations caused a significant reduction in bacterial CFUs in a dose-dependent manner (50, 100 & 200 mg). Additionally, even the lowest zinc substitution (5 mol.%) significantly reduced biofilm formation.
Conclusion
The results demonstrated a novel method to produce a Zn-substituted nHA that showed antimicrobial activity against a pathogen isolated from a bone infection.