Abstract
Two types of ceramic materials currently used in total hip replacements are third generation hot isostatic pressed (HIPed) alumina ceramic (commercially known as BIOLOX®forte, CeramTec) and an alumina matrix composite material consisting of 75% alumina, 24% zirconia, and 1% mixed oxides (BIOLOX®delta, CeramTec). The aim of this study is to compare BIOLOX delta femoral heads to BIOLOX forte femoral heads revised within 2 years in vivo.
Ceramic bearings revised at one center from 1998 to 2010 were collected (61 bearings). BIOLOX delta heads (n=11) revised between 1–33 months were compared to BIOLOX forte femoral heads with less than 24 months in vivo (n=20). The surface topography of the femoral heads was measured using a chromatically encoded confocal measurement machine (Artificial Hip Profiler, RedLux Ltd.).
The median time to revision for BIOLOX delta femoral heads was 12 months, compared to 13 months for BIOLOX forte femoral heads. Sixteen out of 20 BIOLOX forte femoral heads and 6 out of 11 BIOLOX delta femoral heads had edge loading wear. The average volumetric wear rate for BIOLOX forte was 0.96 mm3/yr (median 0.13 mm3/yr), and 0.06 mm3/yr (median 0.01 mm3/yr) for BIOLOX delta (p=0.03). There was no significant difference (p>0.05) in age, gender, time to revision or femoral head diameter between the two groups.
Early results suggest less volumetric wear with BIOLOX delta femoral heads in comparison to BIOLOX forte femoral heads.