UHMWPE WEAR USING THE MALLORY HEAD CEMENTLESS TOTAL HIP PROSTHESIS. A LONG TERM CLINICAL FOLLOW UP STUDY

European Federation of National Associations of Orthopaedics and Traumatology (EFORT) - 12th Congress



Abstract

INTRODUCTION

Cementless Total Hip Replacement surgery is a well established procedure for relative young patients with severe hip disease. Excellent long term clinical results have been published on the performance of the femoral component. With growing clinical experience, our concern focused on excessive wear of the Ultra High Molecular Weight Polyethylene (UHMWPE) ringloc liner of the Mallory Head cementless Total Hip Prosthesis. After its introduction in our clinic in 1997, this implant is still in use without any modification. We were concerned that due to premature liner wear, the performance of this implant would not be compliant with the international guideline on implant survival (NICE guidelines: at 10 year follow up, 90% of all implants should still be in situ). Our objective was to establish the amount of liner wear in our first 200 MH implants.

METHODS

Our first 200 patients consecutively treated with Mallory Head prostheses were followed up to obtain a recent digital image. Follow up was complete for 181 (90.5%) of our 200 patients. Ten had died and nine were not able or willing to come for follow up. The mean duration of follow up was 8.3 years (range: 8–13). The 181 recent digital images were classified as either excessive wear or no excessive wear by two independent orthopedic surgeons. Next, liner wear was measured in the 2D frontal plane using PolyWare Pro/3D Digital Version Rev 5.1 software (Draftware Developers, Conway, USA). A threshold for excessive liner wear was set at 0.2mm/year, according to literature.

RESULTS

Using software for measuring PE wear, 46.7% of all patients had excessive UHMWPE wear (> 0.2mm/yr). There was no relation between the amount of wear and BMI, gender, component size or the acetabular inclination angle. Thirteen patients (6.5%) were revised. Nine of these revisions were for excessive liner wear or aseptic loosening (4.5%). For now, our series of cementless Mallory Head prostheses is compliant with the NICE guideline on implant survival. However, with the measured amount of wear we expect to see a significant increase in the number of revisions for liner wear in the near future.

DISCUSSION

Our clinical observation of premature UHMWPE wear proved correct. The measured amount of UHMWPE wear is consistent with the few other studies published on this subject. Although we present a retrospective study, limiting the strength of our results, we have included a large group of patients with acceptable loss to follow up. It is unclear if the observed wear will lead to a sharp increase in the number of revisions within the next few years. Possibly, future revisions will be complicated by loss of acetabular bone stock following the pathofysiological reaction to wear particles. Our results can probably be generalised for any district hospital.