LOCAL TISSUE REACTION IN TOTAL HIP ARTHROPLASTY WITH TITANIUM MODULAR NECK

European Orthopaedic Research Society (EORS) 2015, Annual Conference, 2–4 September 2015. Part 2.



Abstract

Modular femoral stems for total hip arthroplasty (THA) were introduced to allow additional options for surgeons in controlling leg lengths, offset, and implant stability. This option is widely used in Region Emilia Romagna, Italy, where the study was conducted, having a modular neck stem nearly 35% of primary THA in 2013. Great majority of modular neck is made of Titanium alloy.

The study was designed as a retrospective descriptive case series of 67 hips in patients who underwent revision of a THA. All had a Titanium modular neck. In 44 cases revision was due to breakage of the neck, in the remaining 23 it was due to different reasons unrelated to modular neck such as bone fracture, breakage of a ceramic component, cup loosening.

Mean follow up was 3.5 yrs. For all patients excised capsule and surrounding tissue were graded for presence of necrosis, inflammatory exudate, lymphocytes, and wear particles using light microscopy of routine paraffin sections stained with hematoxylin and eosin. The retrieved modular neck-body and head-neck junctions were examined for evidence of fretting and corrosion. For some patient dosage of circulating Titanium was obtained. Approval was obtained from institutional review board.

It resulted that a variable amount of wear was observed in the first group of patients, with no evidence of lymphocytic reaction, but with variable notes of necrosis. Broken necks showed different patterns of damage, with different degree of corrosion, beside the fatigue fracture. In the second group wear was less evident or absent and negativity of lymphocyte reaction was substantially confirmed. Circulating Titanium ions were one order of magnitude higher in first group (mean 35 micrograms /litre).

It can be concluded that fracture of Titanium modular necks occurs progressively, wear does not induce lymphocytic reaction and circulating ions increase.

Level of Evidence

III retrospective, comparative study