As compared to magnesium (Mg) and iron (Fe), solid zinc (Zn)-based absorbable implants show better degradation rates. An ideal bone substitute should provide sufficient mechanical support, but pure Zn itself is not strong enough for load-bearing medical applications. Modern processing techniques, like additive manufacturing (AM), can improve mechanical strength of Zn. To better mimic the in vivo situation in the human body, we evaluated the degradation behavior of porous Zn implants in vitro under dynamic conditions. Our study applied selective laser melting (SLM) to build topographically ordered absorbable Zn implants with superior mechanical properties. Specimens were fabricated from pure Zn powder using SLM and diamond unit cell topological design. In vitro degradation was performed under both static and dynamic conditions in a custom-built set-up under cell culture conditions (37 °C, 20% O2 and 5% CO2) for up to 28 days. Mechanical properties of the porous structures were determined according to ISO 13314: 2011 at different immersion time points. Modified ISO 10993 standards were used to evaluate biocompatibility through direct cell seeding and indirect extract-based cytotoxicity tests (MTS assay, Promega) against identically designed porous titanium (Ti-6Al-4V) specimens as reference material. Twenty-four hours after cell seeding, its efficacy was evaluated by Live-Dead staining (Abcam) and further analyzed using dual channel fluorescent optical imaging (FOI) and subsequent flow cytometric quantification. Porous Zn implants were successfully produced by means of SLM with a yield strength and Young's modulus in the range of 3.9–9.6 MPa and 265–570 MPa, respectively. Dynamic flow significantly increased the degradation rate of AM porous Zn after 28 days. Results from Zn extracts were similar to Ti-6Al-4V with >95% of cellular activity at all tested time points, confirming level 0 cytotoxicity (i.e., This study clearly shows the great potential of AM porous Zn as a bone substituting material. Moreover, we demonstrate that complex topological design permits control of mechanical properties and degradation behavior.

Bioabsorbable metals hold a lot of potential as orthopaedic implant materials. Three metal families are currently being investigated: iron (Fe), magnesium (Mg) and zinc (Zn). Currently, however, biodegradation of such implants is poorly predictable. We thus used Direct Metal Printing to additively manufacture porous implants of a standardized bone-mimetic design and evaluated their mechanical properties and degradation behaviour, respectively, under in vivo-like conditions.

Atomized powder was manufactured to porous implants of repetitive diamond unit cells, using a ProX DMP 320 (Layerwise, Belgium) or a custom-modified ReaLizer SLM50 metal printer. Degradation behaviour was characterized under static and dynamic conditions in a custom-built bioreactor system (37ºC, 5% CO₂ and 20% O₂) for up of 28 days. Implants were characterized by micro-CT before and after in vivo-like degradation. Mechanical characterization (according to ISO 13314: 2011) was performed on an Instron machine (10kN load cell) at different immersion times in simulated body fluid (r-SBF). Morphology and composition of degradation products were analysed (SEM, JSM-IT100, JEOL). Topographically identical titanium (Ti-6Al-4V, Ti64) specimen served as reference.

Micro-CT analyses confirmed average strut sizes (420 ± 4 μm), and porosity (64%), to be close to design values. After 28 days of in vivo-like degradation, scaffolds were macroscopically covered by degradation products in an alloy-specific manner. Weight loss after cleaning also varied alloy-specifically, as did the change in pH value of the r-SBF. Corrosion time-dependent changes in Young's moduli from 1200 to 800 MPa for Mg, 1000 to 700 MPa for Zn and 48-8 MPa for iron were statistically significant.

In summary, DMP allows to accurately control interconnectivity and topology of implants from all three families and micro-structured design holds potential to optimize their degradation speed. This first systematic report sheds light into how design influences degradation behaviour under in vivo-like conditions to help developing new standards for future medical device evaluation.

The ideal bone substituting biomaterials should possess bone-mimicking mechanical properties; have of porous interconnected structure, and adequate biodegradation behaviour to enable full recovery of bony defects. Direct metal printed porous scaffolds hold potential to satisfy all these requirements and were additively manufactured (AM) from atomized WE43 magnesium alloy powder with grain sizes between 20 and 60 μm. Their micro-structure, mechanical properties, degradation behavior and biocompatibility was then evaluated in vitro. Firstly, post-processing values nicely followed design parameters. Next, Young's moduli were similar to that of trabecular bone (i.e., E = 700–800 MPa) even after 28 days of simulated in vivo-like corrosion by in vitro immersion. Also, a relatively moderate hydrogen evolution, corresponding to a calculated 19.2% of scaffold mass loss, was in good agreement with 20.7% volume reduction as derived from reconstructed μCT images. Finally, only moderate cytotoxicity (i.e., level 0, <25%), even after extensive ISO 10993-conform testing for 72 h using MG-63 cells, was determined using WE43 extracts (2 way ANOVA, post-hoc Tukey's multiple comparisons test; α = 0.05). Cytotoxicity was further evaluated by direct live-dead staining assays, revealing a higher cell death in static culture. However, intimate cell-metal contact was observed by SEM. In summary, while pure WE43 may not yet be an ideal surface for cell adhesion, this novel AM process allows for adjusting biodegradation through topological design. Our approach holds tremendous potential to develop functional and biodegradable implants for orthopaedic applications.