Orthopaedic Proceedings
Vol. 99-B, Issue SUPP_2 | Pages 45 - 45
1 Jan 2017
Manjubala I Ganesan P Narendrakumar U Madhan B
Full Access

Current strategy for orthopedic tissue engineering mainly focusses on the regeneration of the damaged tissue using cell-seeded three-dimensional scaffolds. Biocompatible scaffolds with controllable degradation and suitable mechanical property are required to support new tissue in-growth and regeneration [1]. Porous composite scaffolds made from organic and inorganic materials are highly preferred, which can mimic the natural bone in their composition as well can enhance tissue repair [2]. Scaffolds with optimum mechanical strength in both dry and wet state are more suitable for in vivo orthopedic application. Biphasic calcium phosphate (BCP), a biocompatible ceramic and carboxymethyl cellulose (CMC), a semi-natural polymer are used in the study to prepare composite scaffolds. Citric acid is used as a crosslinking agent for the polymer to improve its stability [3]. Stability, mechanical property in dry and wet conditions and cytocompatibility of the scaffolds were investigated.

Cellulose-BCP (BC25) and crosslinked cellulose-BCP (BC25CA) scaffolds are fabricated by freeze-drying method. The stability of the scaffolds was assessed in phosphate buffered saline (PBS) and compressive modulus was measured in dry and wet condition. Cytocompatibility was assessed by culturing pre-osteoblast cells at a density of 2.5×104 on crosslinked scaffold and cell proliferation was measured by performing MTT assay on day 4 and 7.

Crosslinked scaffold was more stable than non-crosslinked scaffold in aqueous environment as the latter disintegrated within few hours in the solution. Non-crosslinked scaffold showed higher compressive modulus of 116.3±14.8 kPa in dry condition but is reduced to 1.2±0.7 kPa in hydrated state. Though the crosslinked scaffold shows low compressive modulus of 37.67±6.7 kPa in dry state, it exhibited appreciable compressive moduli of 17.15±1.3 kPa in hydrated state. Thus, the crosslinking of the scaffolds improved the stability as well as the mechanical strength in wet condition. Cytocompatibility was assessed by culturing pre-osteoblast cells and from the MTT assay, it is shown that the cells are proliferating on the crosslinked scaffolds with time which indicates that the scaffolds are non-toxic and cytocompatible. Stability and optimum mechanical property for scaffold in aqueous environment are highly crucial for in vivo hard tissue regeneration.

This study demonstrated the preparation of crosslinked scaffolds which exhibited good stability and mechanical strength in wet condition along with a porous architecture, controlled degradability and cytocompatibility, hence, crosslinked cellulose-BCP scaffold can be used for orthopedic application.


Orthopaedic Proceedings
Vol. 99-B, Issue SUPP_1 | Pages 104 - 104
1 Jan 2017
Manjubala I Basu P Narendrakumar U
Full Access

Bone grafting utilises tissue harvesting from second anatomic location of same patient (autograft) or from a human donor (allograft) to treat bone defects. Limited availability of bone grafts, donor site morbidity and risk of disease transmission led to an alternative strategy for bone grafting as synthetic materials that can promote bone regeneration. Engineered bone grafts are biocompatible and possess sufficient mechanical strength to support fractured bone. Polymer scaffolds lack mechanical stability whereas ceramic scaffolds are stiffer resulting in loosening of implants. Combining polymer and ceramic to form scaffolds can enhance the physical and mechanical properties and can be used for bone tissue engineering. We hypothesised that the nucleation of hydroxyapatite in carboxymethyl cellulose (CMC) matrix would improve scaffold properties physically and mechanically; thus, demonstrating CMC based biomimetic process to synthesise novel CMC/ HA scaffolds with suitable physical, mechanical and biological properties for bone tissue engineering.

CMC/ HA scaffolds were synthesized by in situmethod at room temperature (RT) and 60°C and are labelled as CHRT and CH60 respectively, keeping the molar ratio of Ca/P as constant ∼1.6. The nucleation of hydroxyapatite (HA) from calcium chloride (CaCl2) and sodium dihydrogen phosphate (NaH2PO4) was initiated inside carboxymethyl cellulose (CMC). CaCl2solution was introduced gently in aqueous solution of CMC, thereafter; NaH2PO4solution was added dropwise and the mixture was stirred vigorously, kept overnight for aging at RT to obtain milky white slurry. The slurry was washed with distilled water to neutralize, cast into moulds and dried in hot air oven for 72 h to obtain scaffolds. Scanning electron microscopy (SEM) was performed to determine the surface topography of the scaffolds. Mechanical properties were tested with Universal Testing Machine (UTM) and cytotoxicity was performed by MTT assay using fibroblast cells (NIH 3T3).

SEM images shows that HA aggregates like beads and knitted orderly over CMC backbone. There is an increase in HA agglomerates and decrease in bead size with increase in synthesis temperature from RT to 60°C. Scaffolds synthesized at 60°C show enhanced mechanical properties. Compressive strength of CHRT and CH60 are 0.68 MPa and 0.9 MPa respectively and compressive moduli of CHRT and CH60 are 33 MPa and 69 MPa respectively. MTT assay confirmed proliferation of fibroblast cells, hence; proved the non-toxic nature of the scaffolds. MTT assay reveals the cell viability (cell exoskeleton) on the scaffolds after 24 h incubation.

In this study, CMC/ HA scaffolds were synthesised by in situmethod at RT and 60°C. Enhanced mechanical properties and cytocompatibility reveal the potentiality of the scaffolds for bone tissue engineering purposes.