The aim of this study was to assess the functional gain achieved following hip resurfacing arthroplasty (HRA). A total of 28 patients (23 male, five female; mean age, 56 years (25 to 73)) awaiting Birmingham HRA volunteered for this prospective gait study, with an age-matched control group of 26 healthy adults (16 male, ten female; mean age, 56 years (33 to 84)). The Oxford Hip Score (OHS) and gait analysis using an instrumented treadmill were used preoperatively and more than two years postoperatively to measure the functional change attributable to the intervention.Aims
Patients and Methods
Aims. Metal-on-metal hip resurfacing (MoM-HR) has seen decreased usage due to safety and longevity concerns. Joint registries have highlighted the risks in females, smaller hips, and hip dysplasia. This study aimed to identify if reported risk factors are linked to revision in a long-term follow-up of MoM-HR performed by a non-designer surgeon. Methods. A retrospective review of consecutive MoM hip arthroplasties (MoM-HRAs) using
Aims. We investigated whether blood metal ion levels could effectively
identify patients with bilateral
Hip resurfacing remains a potentially valuable surgical procedure for appropriately-selected patients with optimised implant choices. However, concern regarding high early failure rates continues to undermine confidence in use. A large contributor to failure is adverse local tissue reactions around metal-on-metal (MoM) bearing surfaces. Such phenomena have been well-explored around MoM total hip arthroplasties, but comparable data in equivalent hip resurfacing procedures is lacking. In order to define genetic predisposition, we performed a case-control study investigating the role of human leucocyte antigen (HLA) genotype in the development of pseudotumours around MoM hip resurfacings. A matched case-control study was performed using the prospectively-collected database at the host institution. In all, 16 MoM hip resurfacing 'cases' were identified as having symptomatic periprosthetic pseudotumours on preoperative metal artefact reduction sequence (MARS) MRI, and were subsequently histologically confirmed as high-grade aseptic lymphocyte-dominated vasculitis-associated lesions (ALVALs) at revision surgery. ‘Controls’ were matched by implant type in the absence of evidence of pseudotumour. Blood samples from all cases and controls were collected prospectively for high resolution genetic a nalysis targeting 11 separate HLA loci. Statistical significance was set at 0.10 a priori to determine the association between HLA genotype and pseudotumour formation, given the small sample size.Aims
Methods
The aims of the study were to report for a cohort aged younger than 40 years: 1) indications for HRA; 2) patient-reported outcomes in terms of the modified Harris Hip Score (HHS); 3) dislocation rate; and 4) revision rate. This retrospective analysis identified 267 hips from 224 patients who underwent an hip resurfacing arthroplasty (HRA) from a single fellowship-trained surgeon using the direct lateral approach between 2007 and 2019. Inclusion criteria was minimum two-year follow-up, and age younger than 40 years. Patients were followed using a prospectively maintained institutional database.Aims
Methods
To establish the survivorship, function, and metal ion levels in an unselected series of metal-on-metal hip resurfacing arthroplasties (HRAs) performed by a non-designer surgeon. We reviewed 105 consecutive HRAs in 83 patients, performed by a single surgeon, at a mean follow-up of 14.9 years (9.3 to 19.1). The cohort included 45 male and 38 female patients, with a mean age of 49.5 years (SD 12.5)Aims
Methods
Modern metal-on-metal (MoM) hip resurfacing arthroplasty (HRA), while achieving good results with well-orientated, well-designed components in ideal patients, is contraindicated in women, men with head size under 50 mm, or metal hypersensitivity. These patients currently have no access to the benefits of HRA. Highly crosslinked polyethylene (XLPE) has demonstrated clinical success in total hip arthroplasty (THA) and, when used in HRA, potentially reduces metal ion-related sequelae. We report the early performance of HRA using a direct-to-bone cementless mono-bloc XLPE component coupled with a cobalt-chrome femoral head, in the patient group for whom HRA is currently contraindicated. This is a cross-sectional, observational assessment of 88 consecutive metal-on-XLPE HRAs performed in 84 patients between 2015 and 2018 in three centres (three surgeons, including the designer surgeon). Mean follow-up is 1.6 years (0.7 to 3.9). Mean age at operation was 56 years (Objectives
Methods
We investigated the reliability of the cobalt-chromium (CoCr) synovial joint fluid ratio (JFR) in identifying the presence of a severe aseptic lymphocyte-dominated vasculitis-associated lesion (ALVAL) response and/or suboptimal taper performance (SOTP) following metal-on-metal (MoM) hip arthroplasty. We then examined the possibility that the CoCr JFR may influence the serum partitioning of Co and Cr. For part A, we included all revision surgeries carried out at our unit with the relevant data, including volumetric wear analysis, joint fluid (JF) Co and Cr concentrations, and ALVAL grade (n = 315). Receiver operating characteristic curves were constructed to assess the reliability of the CoCr JFR in identifying severe ALVAL and/or SOTP. For part B, we included only patients with unilateral prostheses who had given matched serum and whole blood samples for Co and Cr analysis (n = 155). Multiple regression was used to examine the influence of JF concentrations on the serum partitioning of Co and Cr in the blood.Objectives
Methods
The high revision rates of the DePuy Articular Surface Replacement (ASR) and the DePuy ASR XL (the total hip arthroplasty (THA) version) have led to questions over the viability of metal-on-metal (MoM) hip joints. Some designs of MoM hip joint do, however, have reasonable mid-term performance when implanted in appropriate patients. Investigations into the reasons for implant failure are important to offer help with the choice of implants and direction for future implant designs. One way to assess the performance of explanted hip prostheses is to measure the wear (in terms of material loss) on the joint surfaces. In this study, a coordinate measuring machine (CMM) was used to measure the wear on five failed cementless Biomet Magnum/ReCap/ Taperloc large head MoM THAs, along with one Biomet ReCap resurfacing joint. Surface roughness measurements were also taken. The reason for revision of these implants was pain and/or adverse reaction to metal debris (ARMD) and/or elevated blood metal ion levels.Objectives
Methods
We have encountered patients who developed large joint fluid collections with massive elevations in chromium (Cr) and cobalt (Co) concentrations following metal-on-metal (MoM) hip arthroplasties. In some cases, retrieval analysis determined that these ion concentrations could not be explained simply by the wear rates of the components. We hypothesized that these effects may be associated with aseptic lymphocyte-dominated vasculitis-associated lesion (ALVAL). We examined the influence of the ALVAL grade on synovial fluid Co and Cr concentrations following adjustment for patient and device variables, including volumetric wear rates. Initially restricting the analysis to include only patients with one MoM hip resurfacing device, we performed multiple regression analyses of prospectively collected data. We then repeated the same statistical approach using results from a larger cohort with different MoM designs, including total hip arthroplasties.Objectives
Patients and Methods
This review examines the future of total hip arthroplasty, aiming to avoid past mistakes
The June 2012 Hip &
Pelvis Roundup360 looks at: whether metal-on-metal is really such a disaster; resurfacings with unexplained pain; large heads and high ion levels; hip arthroscopy for FAI; the inaccuracy of clinical tests for impingement; arthroscopic lengthening of iliopsoas; the OA hip; the injured hamstring – football’s most common injury; an algorithm for hip fracture surgery; and sparing piriformis at THR.
Pseudotumours (abnormal peri-prosthetic soft-tissue reactions)
following metal-on-metal hip resurfacing arthroplasty (MoMHRA) have
been associated with elevated metal ion levels, suggesting that
excessive wear may occur due to edge-loading of these MoM implants.
This study aimed to quantify The duration and magnitude of edge-loading Objectives
Methods
An ongoing prospective study to investigate failing metal-on-metal
hip prostheses was commenced at our centre in 2008. We report on
the results of the analysis of the first consecutive 126 failed
mated total hip prostheses from a single manufacturer. Analysis was carried out using highly accurate coordinate measuring
to calculate volumetric and linear rates of the articular bearing
surfaces and also the surfaces of the taper junctions. The relationship
between taper wear rates and a number of variables, including bearing
diameter and orientation of the acetabular component, was investigated.Objectives
Methods
The aims of this piece of work were to: 1) record the background
concentrations of blood chromium (Cr) and cobalt (Co) concentrations
in a large group of subjects; 2) to compare blood/serum Cr and Co
concentrations with retrieved metal-on-metal (MoM) hip resurfacings;
3) to examine the distribution of Co and Cr in the serum and whole
blood of patients with MoM hip arthroplasties; and 4) to further
understand the partitioning of metal ions between the serum and
whole blood fractions. A total of 3042 blood samples donated to the local transfusion
centre were analysed to record Co and Cr concentrations. Also, 91
hip resurfacing devices from patients who had given pre-revision
blood/serum samples for metal ion analysis underwent volumetric
wear assessment using a coordinate measuring machine. Linear regression analysis
was carried out and receiver operating characteristic curves were
constructed to assess the reliability of metal ions to identify
abnormally wearing implants. The relationship between serum and
whole blood concentrations of Cr and Co in 1048 patients was analysed
using Bland-Altman charts. This relationship was further investigated
in an Objectives
Methods