A total of 219 hips in 192 patients aged between 18 and 65 years were randomised to 28-mm metal-on-metal uncemented total hip replacements (THRs, 107 hips) or hybrid hip resurfacing (HR, 112 hips). At a mean follow-up of eight years (6.6 to 9.3) there was no significant difference between the THR and HR groups regarding rate of revision (4.0% (4 of 99) vs 5.8% (6 of 104), p = 0.569) or re-operation rates without revision (5.1% (5 of 99) vs 2.9% (3 of 104), p = 0.428). In the THR group one recurrent dislocation, two late deep infections and one peri-prosthetic fracture required revision, whereas in the HR group five patients underwent revision for femoral head loosening and one for adverse reaction to metal debris. The mean University of California, Los Angeles activity scores were significantly higher in HR (7.5 (sd 1.7) vs 6.9 (sd 1.7), p = 0.035), but similar mean Western Ontario and McMaster Universities Osteoarthritis Index scores were obtained (5.8 (sd 9.5) in HR vs 5.1 (sd 8.9) in THR, p = 0.615) at the last follow-up. Osteolysis was found in 30 of 81 THR patients (37.4%), mostly in the proximal femur, compared with two of 83 HR patients (2.4%) (p < 0.001). At five years the mean metal ion levels were < 2.5 μg/l for cobalt and chromium in both groups; only titanium was significantly higher in the HR group (p = 0.001). Although revision rates and functional scores were similar in both groups at mid-term, long-term survival analysis is necessary to determine whether one procedure is more advantageous than the other.

Cite this article: Bone Joint J 2013;95-B:1464–73.

We have updated our previous randomised controlled trial comparing release of chromium (Cr) and cobalt (Co) ions and included levels of titanium (Ti) ions. We have compared the findings from 28 mm metal-on-metal total hip replacement, performed using titanium CLS/Spotorno femoral components and titanium AlloFit acetabular components with Metasul bearings, with Durom hip resurfacing using a Metasul articulation or bearing and a titanium plasma-sprayed coating for fixation of the acetabular component.

Although significantly higher blood ion levels of Cr and Co were observed at three months in the resurfaced group than in total hip replacement, no significant difference was found at two years post-operatively for Cr, 1.58 μg/L and 1.62 μg/L respectively (p = 0.819) and for Co, 0.67 μg/L and 0.94 μg/L respectively (p = 0.207). A steady state was reached at one year in the resurfaced group and after three months in the total hip replacement group. Interestingly, Ti, which is not part of the bearing surfaces with its release resulting from metal corrosion, had significantly elevated ion levels after implantation in both groups. The hip resurfacing group had significantly higher Ti levels than the total hip replacement group for all periods of follow-up. At two years the mean blood levels of Ti ions were 1.87 μg/L in hip resurfacing and and 1.30 μg/L in total hip replacement (p = 0.001).

The study confirms even with different bearing diameters and clearances, hip replacement and 28 mm metal-on-metal total hip replacement produced similar Cr and Co metal ion levels in this randomised controlled trial study design, but apart from wear on bearing surfaces, passive corrosion of exposed metallic surfaces is a factor which influences ion concentrations. Ti plasma spray coating the acetabular components for hip resurfacing produces significantly higher release of Ti than Ti grit-blasted surfaces in total hip replacement.