Bone & Joint Research
Vol. 5, Issue 9 | Pages 370 - 378
1 Sep 2016
Munir S Oliver RA Zicat B Walter WL Walter WK Walsh WR

Objectives

This study aimed to characterise and qualitatively grade the severity of the corrosion particles released into the hip joint following taper corrosion.

Methods

The 26 cases examined were CoC/ABG Modular (n = 13) and ASR/SROM (n = 13). Blood serum metal ion levels were collected before and after revision surgery. The haematoxylin and eosin tissue sections were graded on the presence of fibrin exudates, necrosis, inflammatory cells and corrosion products. The corrosion products were identified based on visible observation and graded on abundance. Two independent observers blinded to the clinical patient findings scored all cases. Elemental analysis was performed on corrosion products within tissue sections. X-Ray diffraction was used to identify crystalline structures present in taper debris.


Orthopaedic Proceedings
Vol. 105-B, Issue SUPP_11 | Pages 27 - 27
7 Jun 2023
Hothi H Henckel J Di Laura A Schlueter-Brust K Hart A
Full Access

3D printing is rapidly being adopted by manufacturers to produce orthopaedic implants. There is a risk however of structural defects which may impact mechanical integrity. There are also no established standards to guide the design of bone-facing porous structures, meaning that manufacturers may employ different approaches to this. Characterisation of these variables in final-production implants will help understanding of the impact of these on their clinical performance. We analysed 12 unused, final-production custom-made 3D printed acetabular cups that had been produced by 6 orthopaedic manufacturers. We performed high resolution micro-CT imaging of each cup to characterise the morphometric features of the porous layers: (1) the level of porosity, (2) pore size, (3) thickness of porous struts and (4) the depth of the porous layers. We then examined the internal cup structures to identify the presence of any defects and to characterise: (1) their total number, (2) volume, (3) sphericity, (4) size and (5) location. There was a variability between designs in the level of porosity (34% to 85%), pore size (0.74 to 1.87mm), strut thickness (0.28 to 0.65mm), and porous layer depth (0.57 to 11.51mm). One manufacturer printed different porous structures between the cup body and flanges; another manufacturer printed two differing porous regions within the cup body. 5 cups contained a median (range) of 90 (58–101) defects. The median defect volume was 5.17 (1.05–17.33) mm3. The median defect sphericity and size were 0.47 (0.19–0.65) and 0.64 (0.27–8.82) mm respectively. The defects were predominantly located adjacent to screw holes, within flanges and at the transition between the flange and main cup body; these were between 0.17 and 4.66mm from the cup surfaces. There is a wide variability between manufacturers in the porous titanium structures they 3D print. The size, shape and location of the structural defects identified are such that there may be an increased risk of crack initiation from them, potentially leading to a fracture. Regulators, surgeons, and manufacturers should be aware of this variability in final print quality


The Bone & Joint Journal
Vol. 99-B, Issue 10 | Pages 1304 - 1312
1 Oct 2017
Langton DJ Sidaginamale RP Joyce TJ Meek RD Bowsher JG Deehan D Nargol AVF Holland JP

Aims

We sought to determine whether cobalt-chromium alloy (CoCr) femoral stem tapers (trunnions) wear more than titanium (Ti) alloy stem tapers (trunnions) when used in a large diameter (LD) metal-on-metal (MoM) hip arthroplasty system.

Patients and Methods

We performed explant analysis using validated methodology to determine the volumetric material loss at the taper surfaces of explanted LD CoCr MoM hip arthroplasties used with either a Ti alloy (n = 28) or CoCr femoral stem (n = 21). Only 12/14 taper constructs with a rough male taper surface and a nominal included angle close to 5.666° were included. Multiple regression modelling was undertaken using taper angle, taper roughness, bearing diameter (horizontal lever arm) as independent variables. Material loss was mapped using a coordinate measuring machine, profilometry and scanning electron microscopy.


The Bone & Joint Journal
Vol. 99-B, Issue 6 | Pages 724 - 731
1 Jun 2017
Mei-Dan O Jewell D Garabekyan T Brockwell J Young DA McBryde CW O’Hara JN

Aims

The aim of this study was to evaluate the long-term clinical and radiographic outcomes of the Birmingham Interlocking Pelvic Osteotomy (BIPO).

Patients and Methods

In this prospective study, we report the mid- to long-term clinical outcomes of the first 100 consecutive patients (116 hips; 88 in women, 28 in men) undergoing BIPO, reflecting the surgeon’s learning curve. Failure was defined as conversion to hip arthroplasty. The mean age at operation was 31 years (7 to 57). Three patients (three hips) were lost to follow-up.