Total knee arthroplasty is one of the most common surgeries. About 92% of all implanted knee endorposthesis in 2020 were manufactured from uncoated CoCrMo articulating on ultra-high-molecular-weight polyethylene. All articluations generate wear particles and subsequent emission of metal ions due to the mechanical loading. These wear particles cause diverse negative reactions in the surrounding tissues and can lead to implant loosening. Coating technologies might offer the possibility to reduce this wear. Therefore, we investigated the applicability of tetrahedral amorphous carbon (ta-C) coating on CoCrMo alloy. Polished specimens made of CoCrMo wrought alloy according to ISO 5832-12 were coated with ta-C coatings with different layer structure using pulsed laser deposition (PLD). This process allows the deposition of ta-C coatings with low internal stress using an additional relaxation laser. Surface quality and mechanical properties of the coating were characterised using optical surface measurements (NanoFocus μsurf expert, NanoFocus AG) and a nanoindentation tester NHT. 3. (Anton Paar GmbH). Scratch tests were performed on Micro Scratch Tester MST. 3. (Anton Paar TriTec SA) to define the coating adhesion. Pin-on-plate tribological tests, with a polyethylene ball sliding on the ta-C-coated plate under a defined load according to ISO 14243-1 were performed using a linear tribometer (Anton Paar GmbH) to evaluate the tribological and wear properties. The ta-C coatings showed a mean roughness Ra of 5-20 nm and a hardness up to 60 GPa (n=3). The adhesion of the ta-C coatings (n=3) was comparable to the commercial coatings like TiN and TiNbN. The pin-on-plate tests showed an improvement of tribological properties in comparison with the polished uncoated CoCrMo specimens (n=3). The ta-C coatings applied by DLP technology show increased hardness compared to the base material and sufficient adhesion. Further research will be needed to investigate the optimal coating strategy for implant coating

An increasing elderly population means joint replacement surgery numbers are projected to increase, with associated complications such as periprosthetic joint infections (PJI) also rising. PJI are particularly challenging due to antimicrobial resistant biofilm development on implant surfaces and surrounding tissues, with treatment typically involving invasive surgeries and systemic antibiotic delivery. Consequently, functionalisation of implant surfaces to prevent biofilm formation is a major research focus. This study characterises clinically relevant antimicrobials including gentamicin, clindamycin, daptomycin, vancomycin and caspofungin within a silica-based, biodegradable sol-gel coating for prosthetic devices. Antimicrobial activity of the coatings against clinically relevant microorganisms was assessed via disc diffusion assays, broth microdilution culture methods and the MBEC assay used to determine anti-biofilm activity. Human and bovine cells were cultured in presence of antimicrobial sol-gel to determine cytotoxicity using Alamar blue and antibiotic release was measured by LC-MS. Biodegradability in physiological conditions was assayed by FT-IR, ICP-MS and measuring mass change. Effect of degradation products on osteogenesis were studied by culturing mesenchymal stem cells in the presence of media in which sol-gel samples had been immersed. Antimicrobial-loaded coatings showed strong activity against a wide range of clinically relevant bacterial and fungal pathogens with no loss of activity from antibiotic alone. The sol-gel coating demonstrated controlled release of antimicrobials and initial sol-gel coatings showed no loss of viability on MSCs with gentamicin containing coatings. Current work is underway investigating cytotoxicity of sol-gel compositions against MG-63 cells and primary osteoblasts. This research forms part of an extended study into a promising antimicrobial delivery strategy to prevent PJI. The implant coating has potential to advance PJI infection prevention, reducing future burden upon healthcare costs and patient wellbeing

Failure of osseointegration and periprosthetic joint infection (PJI) are the two main reasons of implant failure after total joint replacement (TJR). Nanofiber (NF) implant surface coating represents an alternative local drug eluting device that improves osseointegration and decreases the risk of PJI. The purpose of this study was to investigate the therapeutic efficacies of erythromycin (EM)-loaded coaxial PLGA/PCL-PVA NF coating in a rat S. aureus-infected tibia model. NF coatings with 100mg and 1000mg EM were prepared. NF without EM was included as positive control. 56 Sprague Dawley rats were divided into 4 groups. A titanium pin (1.0-mm x 8 mm) was placed into the tibia through the intercondylar notch. S. aureus (SA) was introduced by both direct injection of 10 μl broth (1 × 10. 4. CFU) into the medullary cavity and single dip of Ti pins into a similar solution prior to insertion. Rats were sacrificed at 8 and 16 weeks after surgery. The outcome measurements include μCT based quantitative osteolysis evaluation and hard tissue histology. Results: EM-NF coating (EM100 and EM1000) reduced osteolysis at 8 and 16 weeks, compared to EM0 and negative control. The effective infection control by EM-NFs was further confirmed by hard tissue section analysis. The Bone implant contact (BIC) and bone area fraction Occupancy (BAFO) within 200 µm of the surface of the pins were used to evaluate the osseointegration and new bone formation around the implants. At 16 weeks, the bone implant contact (BIC) of EM 100 (35.08%) was higher than that of negative control (3.43%) and EM0 (0%). The bone area fraction occupancy within 200 µm (BAFO) of EM100 (0.63 mm2) was higher than that of negative control (0.390 mm2) and EM0 (0.0 mm. 2. ). The BAFO of EM100 was also higher than that of EM1000 (0.3mm. 2. ). There was much less osteolysis observed with EM100 and EM1000 NF coatings at 16 weeks, as compared to EM0 positive control, p=0.08 and p=0.1, respectively. Osseointegration and periprosthetic bone formation was enhanced by EM-NFs, especially EM100. Data from this pilot study is promising for improving implant surface fabrication strategies

Infection of implanted medical devices (biomaterials), like titanium orthopaedic implants, can have disastrous consequences, including removal of the device. These so-called biomaterial-associated infections (BAI) are mainly caused by Staphylococcus aureus and Staphylococcus epidermidis. To prevent biofilm formation using a non-antibiotic based strategy, we aimed to develop a novel permanently fixed antimicrobial coating for titanium devices based on stable immobilized quaternary ammonium compounds (QACs). Medical grade titanium implants were dip-coated in subsequent solutions of hyperbranched polymer, polyethyleneimine and 10 mM sodium iodide, and ethanol. The QAC-coating was characterized using water contact angle measurements, scanning electron microscopy, FTIR, AFM and XPS. The antimicrobial activity of the coating was evaluated against S. aureus strain JAR060131 and S. epidermidis strain ATCC 12228 using the JIS Z 2801:2000 surface microbicidal assay. Lastly, we assessed the in vivo antimicrobial activity in a mouse subcutaneous implant infection model with S. aureus administered locally on the QAC-coated implants prior to implantation to mimic contamination during surgery. Detailed material characterization of the titanium samples showed the presence of a homogenous and stable coating layer at the titanium surface. Moreover, the coating successfully killed S. aureus and S. epidermidis in vitro. The QAC-coating strongly reduced S. aureus colonization of the implant surface as well as of the surrounding tissue, with no apparent macroscopic signs of toxicity or inflammation in the peri-implant tissue at 1 and 4 days after implantation. An antimicrobial coating with stable quaternary ammonium compounds on titanium has been developed which holds promise to prevent BAI. Non-antibiotic-based antimicrobial coatings have great significance in guiding the design of novel antimicrobial coatings in the present, post-antibiotic era. Acknowledgements: This research was financially supported by the Health∼Holland/LSH-TKI call 2021–2022, project 25687, NACQAC: ‘Novel antimicrobial coatings with stable non-antibiotic Quaternary Ammonium Compounds and photosensitizer technology'

Device-associated bacterial infections are a major and costly clinical challenge. This project aimed to develop a smart new biomaterial for implants that helps to protect against infection and inflammation, promote bone growth, and is biodegradable. Gallium (Ga) doped strontium-phosphate was coated on pure Magnesium (Mg) through a chemical conversion process. Mg was distributed in a graduated manner throughout the strontium-phosphate coating GaSrPO4, with a compact structure and a Ga-rich surface. We tested this sample for its biocompatibility, effects on bone remodeling and antibacterial activities including Staphylococcus aureus, S. epidermidis and E. coli - key strains causing infection and early failure of the surgical implantations in orthopaedics and trauma. Ga was distributed in a gradient way throughout the entire strontium-phosphate coating with a compact structure and a gallium-rich surface. The GaSrPO4 coating protected the underlying Mg from substantial degradation in minimal essential media at physiological conditions over 9 days. The liberated Ga ions from the coatings upon Mg specimens inhibited the growth of bacterial tested. The Ga dopants showed minimal interferences with the SrPO4 based coating, which boosted osteoblasts and undermined osteoclasts in in vitro co-cultures model. The results evidenced this new material may be further translated to preclinical trial in large animal model and towards clinical trial. Acknowledgements: Authors are grateful to the financial support from the Australian Research Council through the Linkage Scheme (ARC LP150100343). The authors acknowledge the facilities, and the scientific and technical assistance of the RMIT University and John Curtin School of Medical Research, Australian National University

Musculoskeletal disorders is one of most important health problems human population is facing includes. Approximately 310 thousand of hip protheses have been used in 45 years and older patients in total according to the recent studies have been done. [1, 2]. Many factors, including poor osseointegration or relaxation of the implant due to stress, limit the life of the load-bearing implants [3]. To overcome these difficulties and to protect metal implants inside the body, the surfaces of the implants were coated with silver ion doped hydroxyapatite/bioglass. In this study, silver doped hydroxyapatite ceramic powder and 6P57 bioglass were synthesized. Two different coating suspensions, 100% bioglass and 70% Ag-HAp / 30% bioglass, were prepared in methyl alcohol with a solid content of 1% by weight. Two layers were coated on the external fixator nails by using electrospray method with the bioglass and Ag-Hap/Bioglass suspensions respectively. The coated implants were cut with an equal surface area and kept in human blood plasma for different time. The scanning electron microscopy (SEM, Zeiss Supra 50VP and Zeiss Evo 50EP) and stereo microscope (Zeiss Axiocam Stemi 2000-C) were used to characterize microstructure and thickness of coated surface. Energy dispersive X-ray Spectroscopy was used characterized of chemical composition of coating. Changing of pH value of plasma was measured by pH meter (Hanna HI83414). In addition, the ICP method was used to determine the elements contained in the plasma fluid after dissolution. As a result of this study, physical and chemical changes occurring on the coating surface in different time periods are presented in detail

Intraneural electrodes can be harnessed to control neural prosthetic devices in human amputees. However, in chronic implants we witness a gradual loss of device functionality and electrode isolation due to a nonspecific inflammatory response to the implanted material, called foreign body reaction (FBR). FBR may eventually lead to a fibrous encapsulation of the electrode surface. Poly(ethylene glycol) (PEG) is one of the most common low-fouling materials used to coat and protect electrode surfaces. Yet, PEG can easily undergo encapsulation and oxidative damage in long-term in vivo applications. Poly(sulfobetaine methacrylate) - poly(SBMA) - zwitterionic hydrogels may represent more promising alternatives to minimize the FBR due to their ultra-low fouling features. Here, we tested and compared the poly(SBMA) zwitterionic hydrogel coating with the PEG coating in reducing adhesion and activation of pro-inflammatory and pro-fibrotic cells to polyimide surfaces, which are early hallmarks of FBR. We aimed to coat polyimide surfaces with a hydrogel thin film and analysed the release of a model drug from the hydrogel. We performed hydrogel synthesis, mechanical characterization and biocompatibility analysis. Cell adhesion, viability and morphology of human myofibroblasts cultured on PEG- and hydrogel-coated surfaces were evaluated through confocal microscopy-based high-content analysis (HCA). Reduced activation of pro-inflammatory human macrophages cultured on hydrogels was assessed as well as the hydrogel drug release profile. Because of its high hydration, biocompatibility, low stiffness and ultra-low fouling characteristics the hydrogel enabled lower adhesion and activation of pro-inflammatory and pro-fibrotic cells vs. polystyrene controls, and showed a long-term release of the anti-fibrotic drug Everolimus. Furthermore, a polyimide surface was successfully coated with a hydrogel thin film. Our soft zwitterionic hydrogel could outperform PEG as more suitable coating material of neural electrodes for mitigating the FBR. Such poly(SBMA)-based biomaterial could also be envisioned as long-term delivery system for a sustained release of anti-inflammatory and anti-fibrotic drugs in vivo

Orthopaedic and trauma implant related infection remains one of the major complications that negatively impact clinical outcome and significantly increase healthcare expenditure. Hydroxyapatite has been used for many years to increase implant osseointegration. Silver has been introduced into hydroxyapatite as an antimicrobial coating for orthopedic implants. This surface coatings can both increase tissue compatibility and prevent implant-related infections. We examined infection markers and blood silver values, liver and kidney function tests of 30 patients with of three groups of orthopedic implants, external fixators, intramedullary nails and hip replacements, coated with Ag + ion doped CaP based ceramic powder to determine safety and effectiveness of this dual-function coating. During 1 year follow-up, the pin sites were observed at the external fixator group, and wound areas for the proximal femoral nail and hip arthroplasty group at regular intervals. In addition, liver and kidney function tests, infection markers and blood silver values were checked in patients. In the external fixator group, only 4 out of 91 pin sites (%4.39) were infected. The wound areas healed without any problem in patients with proximal femoral nails and hip arthroplasty. There was no side effect suggesting silver toxicity such as systemic toxic side effect or argyria in any patient and blood silver level did not increase. Compared to similar patient groups in the literature, much lower infection rates were obtained (p = 0.001), and implant osseointegration was good. In patients with chronic infection, the implants were applied acutely after removing the primary implant and with simple debridement. Unlike other silver coating methods, silver was trapped in hydroxyapatite crystals in the ionic form, which is released from the coating during the process of osseointegration, thus, the silver was released into the systemic circulation gradually that showed antibacterial activity locally. We conclude that the use of orthopedic implants with a silver ion added calcium phosphate-based special coating is a safe method to prevent the implant-related infection. This work was supported by TUBİTAK Project Number 315S101

Objectives. An experimental rabbit model was used to test the null hypothesis, that there is no difference in new bone formation around uncoated titanium discs compared with coated titanium discs when implanted into the muscles of rabbits. Methods. A total of three titanium discs with different surface and coating (1, porous coating; 2, porous coating + Bonemaster (Biomet); and 3, porous coating + plasma-sprayed hydroxyapatite) were implanted in 12 female rabbits. Six animals were killed after six weeks and the remaining six were killed after 12 weeks. The implants with surrounding tissues were embedded in methyl methacrylate and grinded sections were stained with Masson-Goldners trichrome and examined by light microscopy of coded sections. Results. Small amounts of bone were observed scattered along the surface of five of the 12 implants coated with porous titanium, and around one out of 12 porous coated surfaces with Bonemaster. No bone formation could be detected around porous coated implants with plasma-sprayed hydroxyapatite. Conclusion. Porous titanium coating is to some degree osteoinductive in muscles

Uncemented implants combining antimicrobial properties with osteoconductivity would be highly desirable in revision surgery due to periprosthetic joint infection (PJI). Silver coatings convey antibacterial properties, however, at the cost of toxicity towards osteoblasts. On the other hand, topological modifications such as increased surface roughness or porosity support osseointregation but simultaneously lead to enhanced bacterial colonization. In this study, we investigated the antibacterial and osteoconductive properties of silver-coated porous titanium (Ti) alloys manufactured by electron beam melting, rendering a macrostructure that mimics trabecular bone. Trabecular implants with silver coating (TR-Ag) or without coating (TR) were compared to grit-blasted Ti6Al4V (GB) and glass cover slips as internal controls. Physicochemical characterization was performed by X-ray diffraction (XRD) and energy dispersive X-rays (EDX) together with morphological characterization through electron scanning microscopy (SEM). Bacterial adherence after incubation of samples with Staphylococcus (S.) aureus and S. epidermidis strains harvested from PJI patients was quantitatively assessed by viable count after detachment of adherent bacteria by collagenase/dispase treatment. Primary human osteoblasts (hOB) were used to investigate the osteoconductive potential by lactate dehydrogenase (LDH) and alkaline phosphatase (ALP) activity. Cell morphology was investigated by fluorescence microscopy after staining with carboxifluorescein diacetate succinimidyl ester (CFDA-SE) and 4′,6-diamidino-2-phenylindole (DAPI). The trabecular implants depicted a porosity of 70% with pore sizes of 600µm. The amount of silver analyzed by EDX accounted for 35%wt in TR-Ag but nil in TR. Silver-coated TR-Ag implants had 24% lower S. aureus viable counts compared to non-coated TR analogues, and 9% lower compared to GB controls. Despite trabecular implants, both with and without silver, had higher viable counts than GB, the viable count of S. epidermidis was 42% lower on TR-Ag compared to TR. The percentage of viable hOB, measured by LDH and normalized to controls and area at 1 day, was lower on both TR-Ag (18%) and on TR (13%) when compared with GB (89%). However, after 1 week, cell proliferation increased more markedly on trabecular implants, with a 5-fold increase on TR-Ag, a 3.4-fold increase on TR, and a 1.7-fold increase on GB. Furthermore, after 2 weeks of hOB culture, proliferation increased 20-fold on TR-Ag, 29-fold on TR, and 3.9-fold for GB, compared to 1 day. The osteoconductive potential measured by ALP illustrated slightly higher values for TR-Ag compared to TR at 1 day and 2 weeks, however below those of GB samples. Cell morphology assessed by microscopy showed abundant growth of osteoblast-like cells confined to the pores of TR-Ag and TR. Overall, our findings indicate that the silver coating of trabecular titanium exerts limited cytotoxic effects on osteoblasts and confers antimicrobial effects on two PJI-relevant bacterial strains. We conclude that improving material design by mimicking the porosity and architecture of cancellous bone can enhance osteoconductivity while the deposition of silver confers potent antimicrobial properties

Preventing infections in joint replacements is a major ongoing challenge, with limited effective clinical technologies currently available for uncemented knee and hip prostheses. This research aims to develop a coating for titanium implants, consisting of a supported lipid bilayer (SLB) encapsulating an antimicrobial agent. The SLB will be robustly tethered to the titanium using self-assembled monolayers (SAMs) of octadecylphosphonic acid (ODPA). The chosen antimicrobial is Novobiocin, a coumarin-derived antibiotic known to be effective against resistant strains of Staphylococcus aureus. ODPA SAMs were deposited on TiO. 2. -coated quartz crystal microbalance (QCM) sensors using two environmentally friendly non-polar solvents (anisole and cyclopentyl methyl ether, CPME), two concentrations of ODPA (0.5mM and 1mM) and two processing temperatures (21°C and 60°C). QCM, water contact angle measurements, X-ray photoelectron spectroscopy (XPS), atomic force microscopy (AFM) and temperature-programmed desorption mass spectrometry (TPD-MS) were used to characterise the ODPA SAM. A SLB with encapsulated Novobiocin was subsequently developed on the surface of the ODPA SAM using fluorescent lipids and a solvent assisted method. The prototype implant surface was tested for antimicrobial activity against S. aureus. A well-ordered, uniform ODPA SAM was rapidly formed using 0.5 mM ODPA in CPME at 21°C during 10 min, as confirmed by high Sauerbrey mass (≍285-290 ng/cm. 2. ), high atomic percentage phosphorus (detected using XPS) and high water contact angles (117.6±2.5°). QCM measurements combined with fluorescence microscopy provided evidence of complete planar lipid bilayer formation on the titanium surface using a solvent assisted method. Incorporation of Novobiocin into the SLB resulted in reduced attachment and viability of S. aureus. Key parameters were established for the rapid, robust and uniform formation of an ODPA SAM on titanium (solvent, temperature and concentration). This allowed the successful formation of an antimicrobial SLB, which demonstrated potential for reducing attachment and viability of pathogens associated with joint replacement infections

Invasive intraneural electrodes implanted in peripheral nerves are neural prosthetic devices that are exploied to control advanced neural-interfaced prostheses in human amputees. One of the main issues to be faced in chronic implants is represented by the gradual loss of functionality of such intraneural interfaces due to an electrical impedance increase caused by the progressive formation of a fibrotic capsule around the electrodes, which is originally due to a nonspecific inflammatory response called foreign body reaction (FBR). In this in vitro work, we tested the biocompatibility and ultra-low fouling features of the synthetic coating - poly(ethylene glycol) (PEG) - compared to the organic polymer - zwitterionic sulfated poly(sulfobetaine methacrylate) (SBMA) hydrogel - to prevent or reduce the first steps of the FBR: plasma protein adsorption and cell adhesion to the interface. Synthesis and characterization of the SBMA hydrogel was done. Preliminary biocompatibility analysis of the zwitterionic hydrogel, using hydrogel-conditioned medium, showed no cytotoxicity at all vs. control. We seeded GFP-labelled human myofibroblasts on PEG- and SBMA hydrogel-coated polyimide surfaces and evaluated their adhesion and cell viability at different time-points. Because of the high hydration, low stiffness reflecting the one of neural tissue, and ultra-low fouling characteristics of the SBMA hydrogel, this polymer showed lower myofibroblast adhesion and different cell morphology compared to adhesion controls, thereby representing a better coating than PEG for potentially mitigating the FBR. We conclude that soft SBMA hydrogels could outperform PEG coatings in vitro as more suitable dressings of intraneural electrodes. Furthermore, such SBMA-based antifouling materials can be envisioned as long-term diffusion-based delivery systems for controlled release of anti-inflammatory and anti-fibrotic drugs in vivo

Background. External fixation is a method of osteosynthesis currently required in traumatology and orthopaedic surgery. Pin tract infection is a common problem in clinical practice. Infection occurs after a bacterial colonisation of the pin due to its contact with skin and local environment. To prevent such local contamination, one way to handle this issue is to create a specific coating using method which could be applied in the medical field. In this work we develop a surface coating for external fixator pins based on photocatalytic TiOα properties, producing a bactericidal effect with sufficient mechanical strength to be compatible with surgical use. Method. The morphology and structure of the sol-gel coating layers were characterised using, respectively, scanning electron microscopy and X-ray diffraction. Resistance properties of the coating were investigated by mechanical testing. Photo-degradation of acid orange 7 in aqueous solution was used as a probe, to assess the photo-catalytic activity of titanium dioxide layers under UV irradiation. The bactericidal effect induced by the process was evaluated against 2 strains: a Staphylococcus aureus and a multiresistant Staphylococcus epidermidis. Results. The coated pins showed good mechanical strength and efficient antibacterial effect after 1 hour of UV irradiation. Conclusion. Our study allowed to develop an antibacterial coating for stainless steel commonly used in surgical practice. The process using photoactive TiO2 exposed to UV irradiation is actually well known and applied in many disinfection fields, and exhibited efficiency against the two main bactericidal strains involved in pin tract infections. Mechanical tests confirmed the coating's ability to resist to important stresses. Moreover, this kind of coating created by sol-gel dip-coating techniques is not expensive and quite easy to do. As a consequence, we can hope that this new option would treat preventively pin tract infection, even if there is an important optimisation task to be done in order to amplify bactericidal properties. Level of evidence. II

The success of long-term transcutaneous implants depends on dermal attachment to prevent downgrowth of the epithelium and infection. Hydroxyapatite (HA) coatings and fibronectin (Fn) have independently been shown to regulate fibroblast activity and improve attachment. In an attempt to enhance this phenomenon we adsorbed Fn onto HA-coated substrates. Our study was designed to test the hypothesis that adsorption of Fn onto HA produces a surface that will increase the attachment of dermal fibroblasts better than HA alone or titanium alloy controls. . Iodinated Fn was used to investigate the durability of the protein coating and a bioassay using human dermal fibroblasts was performed to assess the effects of the coating on cell attachment. Cell attachment data were compared with those for HA alone and titanium alloy controls at one, four and 24 hours. Protein attachment peaked within one hour of incubation and the maximum binding efficiency was achieved with an initial droplet of 1000 ng. We showed that after 24 hours one-fifth of the initial Fn coating remained on the substrates, and this resulted in a significant, three-, four-, and sevenfold increase in dermal fibroblast attachment strength compared to uncoated controls at one, four and 24 hours, respectively

Prosthetic joint infections (PJI) occur infrequently, but they represent the most devastating complication with high morbidity and substantial cost. Staphylococcus aureus are the most common infecting agents associated with acute PJI, and also appear in some cases of delayed PJI. 1. S. aureus biofilm development can be divided in two stages: adhesion and proliferation. 2. To avoid PJI bacterial adhesion has to be decreased. Hybrid organo-inorganic sol-gel coatings are proposed as a promising biomaterial improvement. 3. One of these compounds is a mixture of two organopolisiloxanes: 3-methacryloxypropyltrimethoxysilane (MAPTMS) and tetramethylorthosilicate (TMOS). The aim of this work was to evaluate bacterial adhesion on MAPTMS-TMOS coating compared to titanium parts made by powder metallurgy. MAPTMS-TMOS sol-gel coating was produced using a molar ratio of 1:2 (MAPTMS:TMOS) and dispersed in ethanol. The sol-gel was deposited by dip-coating on titanium parts made by powder metallurgy followed by a thermal treatment at 120 ºC for 30 minutes. 4. Titanium parts without sol-gel coating were used as control. S. aureus 15981 strain adherence study was performed using the protocol described by Kinnari et al. 5. with 90 min incubation. After incubation, the samples were stained with LIVE/DEAD BacLight Bacterial Viability Kit. Proportion of total adhered, live and dead bacteria was calculated and studied by using ImageJ software. The experiments were performed in triplicate. The statistical data were analyzed by pairwise comparisons using the nonparametric Mann-Whitney test with a level of statistical significance of p<0.05. Values are cited and represented as medians. S. aureus 15981 adherence was 942-fold lower on MAPTMS-TMOS coating than on uncoated titanium. According with our results, MAPTMS-TMOS sol-gel coating is a promising antiadherent surface for S. aureus. More studies are necessary in order to evaluate this property with other species and strains

Development of antibacterial surfaces or coatings to prevent bacterial adhesion and hence colonization of implants and biofilm formation is an attractive option, in order to reduce the tremendous impact of implant-related infections associated with modern surgery. To overcome the lack of in vivo and clinical models, able to evaluate the performance of anti-adhesive coatings, we designed an in vitro experimental setting that allows to quantitatively evaluate the ability of a coating to reduce bacterial adhesion on a given surface; this model may efficiently serve as a surrogate endpoint to validate anti-adhesive medical devices and compounds. Here we report the results the evaluation of the anti-adhesive properties of a patented, fast-resorbable hydrogel coating, (“Defensive Antibacterial Coating”, DAC). Sterile sandblasted titanium discs of approximately 5cm. 2. surface area were used as substrates for bacterial adhesion. The gel was prepared as follows: syringes prefilled with 300 mg of DAC powder (Novagenit Srl) were reconstituted with 5 ml of sterile water to obtain a hydrogel with a DAC concentration of 6%. Two experiments were conducted. In the first, 200 mg of hydrogel were homogenously spread on the surface of titanium disc, with the spreading device provided by the manufacturer. Both coated and uncoated substrates (controls) were overlaid with a standardized inoculum (10. 8. CFU/ml) of a wild methicillin-resistant Staphylococcus aureus strain, previously isolated from a peri-prosthetic joint infection, for 15, 30, 60 and 120 minutes. Afterwards, non-adherent bacteria were removed by rinsing with sterile saline. The remaining adhered cells were seeded on agar plates for CFU count. In the second experiment, the discs were first inoculated with bacterial cells followed by a treatment with the hydrogel and bacterial count as described above. Ten discs were used for each condition and each time interval (total 160 discs). The adhesion density of S. aureus on titanium discs pre-treated with DAC was significantly lower than that observed on untreated controls at each time point. In particular, the average number of adherent bacteria at 15, 30, 60 and 120 minutes of incubation, was respectively reduced by 86.8%, 80.4%, 74.6% and 66.7%, compared to controls (p<0.001). DAC treatment of discs with previously adhered S. aureus reduced bacterial adhesion, at 15, 30, 60 and 120 minutes of incubation, by, respectively, 84.0% (p<0.05), 72.8%, 72.3% and 64.3% (p<0.001), compared to untreated controls. Our results shows that DAC, “Defensive Antibacterial Coating”, has anti-adhesive properties that allow to reduce bacterial adhesion on a sanded titanium surface by more than 80%, even in the presence of remarkably high bacterial loads (10. 8. CFU/ml), of multi-resistant bacteria (MRSA) and even in the case of previous contamination. Providing anti-adhesive properties to a surface with a fast-resorbable coating may be a safe option to protect inorganic and organic surfaces and biomaterials. Those observation could be the pre-requisite for its in vivo application

Summary Statement. An Implant Disposable Antibacterial Coating (i-DAC®) is described, consisting of a fully resorbable, biocompatible hydrogel, able to release antibacterial and antibiofilm agents. Direct application of the hydrogel on implants prevented infection occurrence in an in vitro model of peri-prosthetic infection. Introduction. Biofilm-related infections are among the main reasons for failure of joint prosthesis with high associated social and economical costs. Bacterial adhesion and subsequent biofilm formation have been shown to develop early after biomaterials implant into the human body, when a “race to the surface” takes place between the host's cells and the colonizing bacteria eventually present at the surgical site. Providing an antibacterial/antibiofilm coating of the implant may then play a strategic role in preventing biofilm related infections. Here we report the results of a series of in vitro and in vivo studies, partially performed under the European 7th Framework Programme (Implant Disposable Antibiotic Coating, IDAC, collaborative research project # 277988), concerning a fully resorbable, biocompatible antibacterial hydrogel coating (DAC®, Novagenit, Italy). The patented hydrogel, a co-polimer comprising of hyaluronic acid and a polylactic acid, has been designed to be mixed with various antibacterial agents and applied directly on the implant at the time of surgery, being fully resorbed within few days. Patients & Methods. The tested hydrogel (DAC®, Novagenit, Italy) is a derivative of a low molecular weight hyaluronan, grafted with poly-D, L-lactic acid and provided in powder form. At the point of care, the powder is hydrated with the antibiotic or antibiofilm solution, thus generating the final compound to be applied onto the implant surface. In vitro studies were conducted using DAC® coating on different biomaterials, including titanium, chrome-cobalt and polyethylene discs. The release of different antibacterial agents, including vancomycin, ciprofloxacin, meropenem, gentamycin, amikacin, tobramycin, clindamycin, doxycyclin, linezolid, NAsalycilate and N-acetylcisteine, adequately mixed with the hydrogel, has been tested by means of gas chromatography and microbiological methods. In vivo studies were then performed on 35 rabbits divided in 7 groups. Animals were implanted with an intramedullary titanium rod in their femur, with a known inoculum of methicillin-resistant Staph. aureus and vancomycin-loaded DAC® at different concentrations (2% and 5%) and compared with controls. Results. Regardless of the tested material, in vitro studies showed the ability of the hydrogel to be loaded and to sustain the release of the following antibacterial/antibiofilm compounds for up to 96 hours: vancomycin, ciprofloxacin, meropenem, gentamycin, amikacin, tobramycin, clindamycin, doxycyclin, linezolid, NAsalycilate, N-acetylcisteine. In vivo studies showed a bacterial load reduction ranging from 94% to 99.9% using vancomycin-loaded DAC®, compared to controls. Discussion/Conclusion. DAC®, a fast-resorbable antibacterial coating, showed the ability to be loaded with various antibacterial compounds and the ability to provide a highly significant reduction of bacterial colonization of implanted biomaterials in an animal model, opening a new pathway to local prevention and treatment of biofilm-/implant-related infections

We inserted two hydroxyapatite (HA)-coated implants with crystallinities of either 50% (HA-50%) or 75% (HA-75%) bilaterally into the medial femoral condyles of the knees of 16 dogs. The implants were allocated to two groups with implantation periods of 16 and 32 weeks. They were weight-bearing and subjected to controlled micromovement of 250 μm during each gait cycle. After 16 weeks, mechanical fixation of the HA-50% implants was increased threefold as compared with the HA-75% implants. After 32 weeks there was no difference between HA-50% and HA-75%. Fixation of HA-75% increased from 16 to 32 weeks whereas that of HA-50% was unchanged. HA-50% implants had 100% more bone ingrowth than HA-75% implants after 16 weeks. More HA coating was removed on HA-50% implants compared with HA-75% implants after both 16 and 32 weeks. No further loss of the HA coating was shown from 16 to 32 weeks. Our study suggests that the crystallinity of the HA coating is an important factor in its bioactivity and resorption during weight-bearing conditions. Our findings suggest two phases of coating resorption, an initial rapid loss, followed by a slow loss. Resorbed HA coating was partly replaced by bone ingrowth, suggesting that implant fixation will be durable

Infection remains among the first reasons for failure of joint prosthesis. Currently, the golden standard for treating prosthetic joint infections (PJIs) is two-stage revision. However, two-stage procedures have been reported to be associated with higher costs and possible higher morbidity and mortality, compared to one-stage. Furthermore, recent studies showed the ability of a fast-resorbable, antibacterial-loaded hydrogel coating to reduce surgical site infections after joint replacement, by preventing bacterial colonization of implants. Aim of this study was then to compare the infection recurrence rate after a one-stage, cemenless exchange, performed with an antibacterial coated implant versus a standardized two-stage revision procedure. In this two-center prospective study, 22 patients, candidate to revision surgery for PJI, were enrolled to undergo a one-stage revision surgery with cementless implants, coated intra-operatively with a fast-resorbable, antibiotic-loaded hyaluronan and poly-D,L-lactide based hydrogel coating (“Defensive Antibacterial Coating”, DAC, Novagenit, Italy). DAC was reconstructed according to manufacturer indications and loaded with Vancomycin or Vancomycin + Meropenem, according to cultural examinations, and directly spread onto the implant before insertion. This prospective cohort was compared with a retrospective series of 22 consecutive patients, matched for age, sex, host type, site of surgery, that underwent a two stage procedure, using a preformed, antibiotic-loaded spacer (Tecres, Italy) and a cementless implant. The second surgery, for definitive implant placing, was performed only after CRP normalization and no clinical sign of infection. Clinical, laboratory and radiographic evaluation were performed at 3, 6 and 12 months, and every 6 months thereafter. Infection recurrence was defined by the presence of a sinus tract communicating with the joint, or at least two among the following criteria: clinical signs of infections; elevated CRP and ESR; elevated synovial fluid WBC count; elevated synovial fluid leukocyte esterase; a positive cultural examination from synovial fluid; radiographic signs of stem loosening. The two groups did not differ significantly for age, sex, host type and site of surgery (18 knees and 4 hips, respectively). The DAC hydrogel was loaded intra-operatively, according to cultural examination, with vancomycin (14 patients) or vancomycin and meropenem (8 cases). At a mean follow-up of 20.2 ± 6.3 months, 2 patients (9.1%) in the DAC group showed an infection recurrence, compared to 3 patients (13.6%) in the two-stage group. No adverse events associated with the use of DAC or radiographic loosening of the stem were observed at the latest follow-up months. This is the first report on one-stage cementless revision surgery for PJI, performed with a fast-resorbable antibacterial hydrogel coating. Our data, although in a limited series of patients and at a relatively short follow-up, show similar infection recurrence rate after one-stage exchange with cementless, coated implants, compared to two-stage revision. These findings warrant further studies in the possible applications of antibacterial coating technologies to treat implant-related infections

We have studied the beneficial effects of a hydroxyapatite (HA) coating on the prevention of the migration of wear debris along the implant-bone interface. We implanted a loaded HA-coated implant and a non-coated grit-blasted titanium alloy (Ti) implant in each distal femoral condyle of eight Labrador dogs. The test implant was surrounded by a gap communicating with the joint space and allowing access of joint fluid to the implant-bone interface. We injected polyethylene (PE) particles into the right knee three weeks after surgery and repeated this weekly for the following five weeks. The left knee received sham injections. The animals were killed eight weeks after surgery. Specimens from the implant-bone interface were examined under plain and polarised light. Only a few particles were found around HA-coated implants, but around Ti implants there was a large amount of particles. HA-coated implants had approximately 35% bone ingrowth, whereas Ti implants had virtually no bone ingrowth and were surrounded by a fibrous membrane. Our findings suggest that HA coating of implants is able to inhibit peri-implant migration of PE particles by creating a seal of tightly-bonded bone on the surface of the implant