The creep and wear behaviour of highly cross-linked polyethylene and standard polyethylene liners were examined in a prospective, double-blind randomised, controlled trial using radiostereometric analysis. We randomised 54 patients to receive hip replacements with either highly cross-linked polyethylene or standard liners and determined the three-dimensional penetration of the liners over three years. After three years the mean total penetration was 0.35 mm (SD 0.14) for the highly cross-linked polyethylene group and 0.45 mm (SD 0.19) for the standard group. The difference was statistically significant (p = 0.0184). From the pattern of penetration it was possible to discriminate creep from wear. Most (95%) of the creep occurred within six months of implantation and nearly all within the first year. There was no difference in the mean degree of creep between the two types of polyethylene (highly cross-linked polyethylene 0.26 mm, SD 0.17; standard 0.27 mm, SD 0.2; p = 0.83). There was, however, a significant difference (p = 0.012) in the mean wear rate (highly cross-linked polyethylene 0.03 mm/yr, SD 0.06; standard 0.07 mm/yr, SD 0.05). Creep and wear occurred in significantly different directions (p = 0.01); creep was predominantly proximal whereas wear was anterior, proximal and medial. We conclude that penetration in the first six months is creep-dominated, but after one year virtually all penetration is due to wear. Highly cross-linked polyethylene has a 60% lower rate of wear than standard polyethylene and therefore will probably perform better in the long term

Oxidized zirconium (Oxinium) and highly cross-linked polyethylene (HXLPE) were developed with the purpose of minimizing wear, and subsequent osteolysis, in Total Hip Arthroplasty (THA). However, few articles have been published on long-term results of Oxinium on highly cross-linked polyethylene. The purpose of this investigation is to report minimum 10-year HXLPE wear rates and the clinical outcome of patients in this group and compare this population to a control group of cobalt chrome and ceramic. One hundred forty THAs were performed for 123 patients using an Oxinium head with an HXLPE liner. Ninety-seven had 10 years of clinical follow-up (avg. 14.5). Harris Hip Scores (HHS) were collected preoperatively and at the most recent follow-up. Radiographs of 85 hips were available for a minimum 10-year follow-up (avg. 14.5) and used to calculate wear using PolyWare software. Control groups of cobalt chrome and ceramic articulation on HXLPE with a minimum 10-year follow-up were studied. Clinical follow-up of the Oxinium group showed a statistical improvement compared to preoperative and was similar to the control group of patients. Radiographic evaluation found the linear and volumetric wear rates for the Oxinium group of 0.03 mm/year (range 0.00–0.08) and 3.46 mm. 3. /year (range 1.0 to 15.0) respectively. There was no statistically significant difference in linear or volumetric wear rate between the groups (P-value 0.92 and 0.55 respectively). None of these patients underwent revision of their hip for any reason. Oxinium on highly cross-linked polyethylene has performed exceptionally with wear rates comparable to those of cobalt chrome or ceramic on HXLPE

Aims. Limited implant survival due to aseptic cup loosening is most commonly responsible for revision total hip arthroplasty (THA). Advances in implant designs and materials have been crucial in addressing those challenges. Vitamin E-infused highly cross-linked polyethylene (VEPE) promises strong wear resistance, high oxidative stability, and superior mechanical strength. Although VEPE monoblock cups have shown good mid-term performance and excellent wear patterns, long-term results remain unclear. This study evaluated migration and wear patterns and clinical and radiological outcomes at a minimum of ten years’ follow-up. Methods. This prospective observational study investigated 101 cases of primary THA over a mean duration of 129 months (120 to 149). At last follow-up, 57 cases with complete clinical and radiological outcomes were evaluated. In all cases, the acetabular component comprised an uncemented titanium particle-coated VEPE monoblock cup. Patients were assessed clinically and radiologically using the Harris Hip Score, visual analogue scale (pain and satisfaction), and an anteroposterior radiograph. Cup migration and polyethylene wear were measured using Einzel-Bild-Röntgen-Analyze software. All complications and associated treatments were documented until final follow-up. Results. Clinical assessment showed persistent major improvement in all scores. On radiological assessment, only one case showed a lucent line (without symptoms). At last follow-up, wear and migration were below the critical thresholds. No cup-related revisions were needed, indicating an outstanding survival rate of 100%. Conclusion. Isoelastic VEPE cups offer high success rates and may prevent osteolysis, aseptic loosening, and the need for revision surgeries in the long term. However, longer follow-up is needed to validate our findings and confirm the advantages offered by this cup. Cite this article: Bone Jt Open 2024;5(10):825–831

Aims. Highly cross-linked polyethylene (HXLPE) has greatly improved the durability of total hip arthroplasty (THA) in young patients because of its improved wear characteristics. Few studies have followed this population into the second decade, and therefore the purpose of this investigation was to evaluate the clinical outcome for THA patients 50 years of age and younger at a minimum of 15 years postoperatively. The second purpose was to evaluate the radiological findings secondary to wear or mechanical failure of the implant. Methods. Between October 1999 and December 2005, 105 THAs were performed in 95 patients (53 female, 42 male) aged 50 years and younger (mean 42 years (20 to 50)). There were 87 patients (96 hips) that were followed for a minimum of 15 years (mean 17.3 years (15 to 21)) for analysis. Posterior approach was used with cementless fixation with a median head size of 28 mm. HXLPE was the acetabular bearing for all hips. Radiographs were evaluated for polyethylene wear, radiolucent lines, and osteolysis. Results. Clinical outcomes showed significant improvement of mean Harris Hip Scores from 52.8 (SD 13.5) preoperatively to 94.8 (SD 7.6) postoperatively. One hip was revised for recurrent instability, and there were no infections. No hips were revised for mechanical loosening or osteolysis. Mean polyethylene linear wear was 0.04 mm/year and volumetric wear was 6.22 mm. 3. /year, with no significant differences between head size or material. Osteolysis was not present in any of the hips. Conclusion. The use of HXLPE in THA for patients aged 50 years and younger has performed exceptionally well without evidence of significant wear causing mechanical loosening or necessitating revision. The radiolucent lines of the acetabular component must be followed to determine the prognostic significance. This investigation represents the longest clinical follow-up of a large, consecutive cohort of patients aged 50 years or younger with THA using HXLPE. This long-term analysis found negligible polyethylene wear, no incidence of aseptic loosening, and excellent clinical outcomes at and beyond 15 years of follow-up. Cite this article: Bone Joint J 2021;103-B(7 Supple B):78–83

Aims. Radiostereometric analysis (RSA) is the most accurate radiological method to measure in vivo wear of highly cross-linked polyethylene (XLPE) acetabular components. We have previously reported very low wear rates for a sequentially irradiated and annealed X3 XLPE liner (Stryker Orthopaedics, USA) when used in conjunction with a 32 mm femoral heads at ten-year follow-up. Only two studies have reported the long-term wear rate of X3 liners used in conjunction with larger heads using plain radiographs which have poor sensitivity. The aim of this study was to measure the ten-year wear of thin X3 XLPE liners against larger 36 or 40 mm articulations with RSA. Methods. We prospectively reviewed 19 patients who underwent primary cementless THA with the XLPE acetabular liner (X3) and a 36 or 40 mm femoral head with a resultant liner thickness of at least 5.8 mm. RSA radiographs at one week, six months, and one, two, five, and ten years postoperatively and femoral head penetration within the acetabular component were measured with UmRSA software. Of the initial 19 patients, 12 were available at the ten-year time point. Results. The median proximal, 2D, and 3D wear rates calculated between one and ten years were all less than 0.005 mm/year, with no patient recording a proximal wear rate of more than 0.021 mm/year. Importantly, there was no increase in the wear rate between five and ten years. Conclusion. The very low wear rate of X3 XLPE liners with larger articulations remains encouraging for the future clinical performance of this material. Cite this article: Bone Jt Open 2023;4(11):839–845

Aims. We aimed to evaluate the long-term outcome of highly cross-linked polyethylene (HXLPE) cemented acetabular components and assess whether any radiolucent lines (RLLs) which arose were progressive. Methods. We retrospectively reviewed 170 patients who underwent 187 total hip arthroplasties at two hospitals with a minimum follow-up of ten years. All interventions were performed using the same combination of HXLPE cemented acetabular components with femoral stems made of titanium alloy. Kaplan-Meier survival analysis was performed for the primary endpoint of acetabular component revision surgery for any reason and secondary endpoint of the appearance of RLLs. RLLs that had appeared once were observed over time. We statistically assessed potential relationships between RLLs and a number of factors, including the technique of femoral head autografting and the Japanese Orthopaedic Association score. Results. The mean follow-up period was 13.0 years (10.0 to 16.3). Femoral head autografting was performed on 135 hips (72.2%). One acetabular component was retrieved because of deep infection. No revision was performed for the aseptic acetabular loosening. The Kaplan-Meier survival curve for the primary and secondary endpoints were 98.2% (95% confidence interval (CI) 88.6% to 99.8%) and 79.3% (95% CI 72.8% to 84.6%), respectively. RLLs were detected in 38 hips (21.2%), at a mean of 1.7 years (1 month to 6 years) postoperatively. None of the RLLs were progressive, and the presence of RLLs did not show a significant association with the survival and clinical score. RLLs were more frequently observed in hips without femoral head autografts than in those with autografts. Conclusion. The use of HXLPE cemented acetabular components in total hip arthroplasty demonstrated excellent clinical outcomes after ten years, and no RLLs were progressive, and their presence did not affect the outcome. Femoral head autografting did not negatively impact the acetabular component survival or the appearance of RLLs. Cite this article: Bone Joint J 2021;103-B(10):1604–1610

Aims. The aim of this study was to evaluate the performance of first-generation annealed highly cross-linked polyethylene (HXLPE) in cementless total hip arthroplasty (THA). Methods. We retrospectively evaluated 29 patients (35 hips) who underwent THA between December 2000 and February 2002. The survival rate was estimated using the Kaplan-Meier method. Hip joint function was evaluated using the Japanese Orthopaedic Association (JOA) score. Two-dimensional polyethylene wear was estimated using Martell’s Hip Analysis Suite. We calculated the wear rates between years 1 and 5, 5 and 10, 10 and 15, and 15 and final follow-up. Results. The mean follow-up period was 19.1 years (SD 0.6; 17.3 to 20.1). The 19-year overall survival rate with the end point of all-cause revision was 97.0% (95% confidence interval (CI) 91 to 100). The mean JOA score improved from 43.2 (SD 10.6; 30 to 76) before surgery to 90.2 (SD 6.4; 76 to 98) at the final follow-up (p < 0.001). There was no osteolysis or loosening of the acetabular or femoral components. The overall steady-state wear rate was 0.013 mm/year (SD 0.012). There was no hip with a steady-state wear rate of > 0.1 mm/year. There was no significant difference in wear rates for each period. We found no significant correlation between the wear rate and age, body weight, BMI, or cup inclination. Conclusion. First-generation annealed HXLPE shows excellent wear resistance and no acceleration of wear for approximately 20 years, with low all-cause revision rates. Cite this article: Bone Joint J 2022;104-B(2):200–205

Aims. The objective of this five-year prospective, blinded, randomised controlled trial (RCT) was to compare femoral head penetration into a vitamin E diffused highly cross-linked polyethylene (HXLPE) liner with penetration into a medium cross-linked polyethylene control liner using radiostereometric analysis. . Patients and Methods. Patients scheduled for total hip arthroplasty (THA) were randomised to receive either the study E1 (32 patients) or the control ArComXL polyethylene (35 patients). The median age (range) of the overall cohort was 66 years (40 to 76). Results. The five-year median (interquartile range) proximal femoral head penetration into the E1 was -0.05 mm (-0.13 to -0.02) and 0.07 mm (-0.03 to 0.16) for ArComXL. At three and five years, the penetration was significantly greater in the ArComXL group compared with the E1 group (p = 0.029 and p = 0.019, respectively). All patient-reported outcomes (PROs) improved significantly from the pre-operative interval compared with those at one year, and remained favourable at five years. There were no differences between the two groups at any interval. Conclusion. The five-year results showed that E1 polyethylene does not wear more than the control, ArComXL. This is the longest-term RCT comparing the wear performance and clinical outcome of vitamin E diffused HXLPE with a previous generation of medium cross-linked polyethylene. Cite this article: Bone Joint J 2017;99-B:577–84.

Highly cross-linked polyethylene (HXLPE) has decreased wear and revision rates in total hip replacement (THR) at a long-term. However, the effect of HXLPE manufacturing characteristics on femoral head penetration has not been clearly defined yet. We report this single-institution study to investigate the clinical and radiological results of different HXLPE liners in THR. In this retrospective cohort analysis of our prospective database, we identified 904 THRs performed between 2000 and 2013. Seven different HXLPE liner types were assessed: remelted (3), annealed (2), sequentially annealed (1) and vitamin E-infused (1). The linear femoral head penetration rate was measured at six weeks, one year, and annually thereafter, using the Roman Software v1.70 package. Thirty hips were revised for the following reasons: aseptic loosening (11), dislocation (12), periprosthetic femoral fracture (6), and infection (1). No hip was revised for wear or osteolysis. 741 THRs were evaluated for a mean follow-up of 15 years (range, 10 to 20). The mean total penetration 15 years after THR was 0.17 mm in the sequentially annealed, and 0.16 mm in the vitamin E-infused groups, whereas it was 0.26 mm in the melted 95 kGy, 0.27 mm in the melted 5 Mrad and 0.25 mm in the melted 100 kGy groups (p=0.001). From one to 15 years after surgery, the mean wear was 0.206 mm in cups with an acetabular inclination greater than 50º and 0.105 mm in those placed between 35º and 50º (p<0.001). Although HXLPE characteristics can result in a different wear performance in patients undergoing THR at a mean follow-up of 15 years, the clinical results are excellent. The position of the acetabular component can influence on the femoral head penetration of modern HXLPEs. Nevertheless, these patients should continue to be monitored to detect future problems

Aims. Several short- and mid-term studies have shown minimal liner wear of highly cross-linked polyethylene (HXLPE) in total hip arthroplasty (THA), but the safety of using thinner HXLPE liners to maximize femoral head size remains uncertain. The objective of this study was to analyze clinical survival and radiological wear rates of patients with HXLPE liners, a 36 mm femoral head, and a small acetabular component with a minimum of ten years’ follow-up. Methods. We retrospectively identified 55 patients who underwent primary THA performed at a single centre, using HXLPE liners with 36 mm cobalt-chrome heads in acetabular components with an outer diameter of 52 mm or smaller. Patient demographic details, implant details, death, and all-cause revisions were recorded. Cox regression and Kaplan-Meier survival was used to determine all-cause and liner-specific revision. Of these 55 patients, 22 had a minimum radiological follow-up of seven years and were assessed radiologically for linear and volumetric wear. Results. Overall survival rate for all-cause revision was 94.5% (95% confidence interval (CI) 81.7% to 97.2%) at a mean follow-up of 12.8 years (10.9 to 18.7). Three patients were revised, none for liner wear, fracture, or dissociation. A total of 22 patients were included in the radiological analysis (mean follow-up 9.9 years (7.5 to 13.7)). Mean linear liner wear was 0.085 mm (95% CI -0.086 to 0.257) and the volumetric wear rate was 11.097 mm. 3. /year (95% CI -6.5 to 28.7). Conclusion. Using HXLPE liners with 36 mm heads in 52 mm acetabular components or smaller is safe, with excellent survival and low rates of linear and volumetric wear at medium-term follow-up. Patients did not require revision surgery for liner complications such as fracture, dissociation, or wear. Our results suggest that the advantages of using larger heads outweigh the potential risks of using thin HXLPE liners. Cite this article: Bone Joint J 2023;105-B(1):29–34

Polyethylene wear debris can cause osteolysis and the failure of total hip arthroplasty. We present the five-year wear rates of a highly cross-linked polyethylene (X3) bearing surface when used in conjunction with a 36 mm ceramic femoral head. This was a prospective study of a cohort of 100 THAs in 93 patients. Pain and activity scores were measured pre- and post-operatively. Femoral head penetration was measured at two months, one year, two years and at five years using validated edge-detecting software (PolyWare Auto). At a mean of 5.08 years (3.93 to 6.01), 85 hips in 78 patients were available for study. The mean age of these patients was 59.08 years (42 to 73, the mean age of males (n = 34) was 59.15 years, and females (n = 44) was 59.02 years). All patients had significant improvement in their functional scores (p < 0.001). The steady state two-dimensional linear wear rate was 0.109 mm/year. The steady state volumetric wear rate was 29.61 mm. 3. /year. No significant correlation was found between rate of wear and age (p = 0.34), acetabular component size (p = 0.12) or clinical score (p = 0.74). Our study shows low steady state wear rates at five years in X3 highly cross-linked polyethylene in conjunction with a 36 mm ceramic femoral head. The linear wear rate was almost identical to the osteolysis threshold of 0.1 mm/year recommended in the literature. Cite this article: Bone Joint J 2015;97-B:1470–4

Aims. The purpose of this study was to compare the long-term results of primary total hip arthroplasty (THA) in young patients using either a conventional (CPE) or a highly cross-linked (HXLPE) polyethylene liner in terms of functional outcome, incidence of osteolysis, radiological wear and rate of revision. Methods. We included all patients between the ages of 45 and 65 years who, between January 2000 and December 2001, had undergone a primary THA for osteoarthritis at our hospital using a CPE or HXLPE acetabular liner and a 28 mm cobalt-chrome femoral head. . From a total of 160 patients, 158 (177 hips) were available for review (CPE 89; XLPE 88). The mean age, body mass index (BMI) and follow-up in each group were: CPE: 56.8 years (46 to 65); 30.7 kg/m. 2. (19 to 58); 13.2 years (2.1 to 14.7) and HXLPE: 55.6 years (45 to 65); BMI: 30 kg/m. 2. (18 to 51); 13.1 years (5.7 to 14.4). Results. The mean Harris hip score (HHS) at final follow-up was 89.3 for the CPE group and 90.9 for the HXLPE group (p = 0.078). Osteolysis was present around 15 acetabular (17%) and 16 femoral (18%) components in the CPE hips compared with none (0%) in the HXLPE hips. The mean radiological linear wear of the CPE liners was 0.11 mm/year compared with 0.035 mm/year for the HXLPE liners (p = 0.006). The cumulative implant survival, with revision for polyethylene wear as the endpoint, was 86% (95% confidence interval 78 to 94) in the CPE group and 100% in the HXLPE group at 13 years (numbers at risk at 13 years - CPE: 65, XLPE: 61). Discussion. This study shows that HXLPE liners are associated with significantly less osteolysis and a lower rate of revision THA than CPE liners at long-term follow-up. Take home message: The findings of this study highlight the clinical benefits of using HXLPE liners in THA and support the routine use of the material in order to improve implant longevity and to decrease the number of patients needing revision for aseptic osteolysis. . Cite this article: Bone Joint J 2016;98-B:28–32

We report on an innovative surface grafting to highly crosslinked (HXLPE) bearing for THA using a biocompatible-phospholipid-polymer poly (2-methacryloyloxyethyl phosphorylcholine) (PMPC). Such hydrophilic surfaces mimic articular cartilage and are hypothesized to improve lubrication and thereby reduce friction and wear. We performed in vitro testing of wear and friction of ceramic-on-polyethylene THRs with the PMPC treatment, and compared them with untreated controls. Highly cross-linked UHMWPE bearings, gamma-ray-irradiated at different levels with and without vitamin E (HXL Vit. E: 125 kGy, HXL: 75 kGy, respectively) were divided so half were PMPC treated (n=3 for all four groups). All were paired with identical 40 mm diameter zirconia-toughened-alumina ceramic heads. Testing was carried-out on an AMTI hip simulator for 10 million simulated walking cycles with standard lubricant and conditions (ISO-14242-1). Wear was measured gravimetrically at 21 intervals, and so was frictional torque with a previously described and tested methodology. PMPC treatment produced a statistically significant 71% in wear reduction of HXL poly (1.70±1.36 mg/Mc for PMPC vs. 5.86±0.402 mg/Mc for controls, p=0.013). A similar significant wear reduction was found for PMPC treated HXL with Vit. E liners (0.736±0.750 mg/Mc, vs. 2.14±0.269 mg/Mc, p=0.035). The improvements were associated with 12% and 5% reductions in friction of the HXL and Vit. E HXL respectively (statistically significant p=0.003, and marginal p=0.116, one tailed). These results were an important step in the quest for lower wearing, thin and strong UHMWPE liners for larger diameter femoral heads with the potential benefit of longevity and less risk of dislocation after surgery

Introduction

THA for patient's 50 years and younger is a procedure at high risk for complications and failure because of the high level of activity of this population. Highly cross linked polyethylene (HXLPE) has greatly improved the durability of the implant because of the improved wear characteristics. Few studies have followed this population into the second decade and therefore the purpose of this investigation was to evaluate the clinical outcome for the patients 5o years of age and younger at a minimum of 15 years. The second purpose was to evaluate the radiographic findings secondary to wear or mechanical failure of the implant.

Aims

The most frequent indication for revision surgery in total hip arthroplasty (THA) is aseptic loosening. Aseptic loosening is associated with polyethylene liner wear, and wear may be reduced by using vitamin E-doped liners. The primary objective of this study was to compare proximal femoral head penetration into the liner between a) two cross-linked polyethylene (XLPE) liners (vitamin E-doped (vE-PE)) versus standard XLPE liners, and b) two modular femoral head diameters (32 mm and 36 mm).

Two Durasul highly crosslinked polyethylene liners were exchanged during revision surgery four and five years after implantation, respectively. The retrieved liners were evaluated macroscopically and surface analysis was performed using optical and electron microscopy. A sample of each liner was used to determine the oxidation of the material by Fourier transform infrared spectroscopy. Samples of the capsule were examined histologically.

The annual wear rate was found to be 0.010 and 0.015 mm/year, respectively. Surface analysis showed very little loss of material caused by wear. Histological evaluation revealed a continuous neosynovial lining with single multinucleated foreign-body giant cells. Our findings showed no unexpected patterns of wear on the articulating surfaces up to five years after implantation and no obvious failure of material.

The primary purpose of the current study was to evaluate and compare the wear properties of vitamin E-doped, highly-crosslinked PE (VEPE) and one formulation of moderately cross-linked and mechanically-annealed ultra-high molecular weight PE (ModXLPE) in patients five years after primary THA. We also sought to understand whether polyethylene wear is associated with radiographic evidence of bone resorption or with deterioration in patient-reported outcome measures (PROMs).

A total of 221 patients from four international centers were recruited into a prospective RSA and clinical outcomes study. Seventy percent (76%) of patients received VEPE (vs. ModXLPE) liners, and 36% received ceramic (vs. metal) femoral heads. PROMs and radiographs were collected preoperatively and at one, two, and five years postoperatively. In addition, RSA radiographs were collected to measure PE wear.

We observed similar bedding in through the one-year interval and wear through the two-year interval between the two liner types. However, there was significantly more femoral head penetration in the ModXLPE cohort compared to the VEPE cohort at the five-year follow-up (p<0.001). The only variables independently predictive of increased wear were ModXLPE (vs VEPE) liner type (β=0.22, p=0.010) and metal (vs. ceramic) femoral head type (β=0.21, p=0.013). There was no association between increased wear and radiolucency development (p=0.866) or PROMs. No patients were found to have evidence of osteolysis.

At five-years postoperatively, patients treated with VEPE (vs. ModXLPE) and ceramic (vs. metal) femoral heads demonstrated decreased wear. At the longest follow-up (five years postoperatively), the wear rates for both liner groups were very low and have not led to any osteolysis or implant failures via aseptic loosening.

Between 1999 and 2001, 90 patients underwent total hip replacement using the same uncemented acetabular and femoral components with a 28 mm metallic femoral head but with prospective randomisation of the acetabular liner to either Durasul highly cross-linked polyethylene or nitrogen-sterilised Sulene polyethylene. We assessed 83 patients at a minimum follow-up of ten years. Linear penetration of the femoral head was estimated at six weeks, six and 12 months and annually thereafter, using the Dorr method, given the non-spherical shape of the acetabular component.

There was no loosening of any component; only one hip in the Sulene group showed proximal femoral osteolysis. The mean penetration of the femoral head at six weeks was 0.08 mm (0.02 to 0.15) for the Durasul group and 0.16 mm (0.05 to 0.28) for the Sulene group (p = 0.001). The mean yearly linear penetration was 64.8% lower for the Durasul group at 0.05 mm/year (sd 0.035) for the Sulene group and 0.02 mm/year (sd 0.016) for the Durasul (p < 0.001). Mean linear femoral head penetration at ten years was 61% less in the Durasul than Sulene group. Highly cross-linked polyethylene gives excellent results at ten years.

Cite this article: Bone Joint J 2013;95-B:326–32.

Aims. A significant reduction in wear at five and ten years was previously reported when comparing Durasul highly cross-linked polyethylene with nitrogen-sterilized Sulene polyethylene in total hip arthroplasty (THA). We investigated whether the improvement observed at the earlier follow-up continued, resulting in decreased osteolysis and revision surgery rates over the second decade. Methods. Between January 1999 and December 2001, 90 patients underwent surgery using the same acetabular and femoral components with a 28 mm metallic femoral head and either a Durasul or Sulene liner. A total of 66 hips of this prospective randomized study were available for a minimum follow-up of 20 years. The linear femoral head penetration rate was measured at six weeks, one year, and annually thereafter, using the Dorr method on digitized radiographs with a software package. Results. In the Durasul group, no patients underwent revision due to loosening or showed radiological evidence of osteolysis. In the Sulene group, four patients (four hips) were revised due to femoral component loosening. The 20-year cumulative failure incidence in the presence of the competing event of death for revision surgery was 4.5% (95% confidence interval (CI) 0.8 to 13.6) in the Durasul group, and 8.9% (95% CI 2.8 to 19.5) in the Sulene group. The mean wear one year after surgery was 0.09 mm (SD 0.007) in the Durasul group and 0.24 (SD 0.015) in the Sulene group (p < 0.001). From one to 20 years after surgery, the mean total penetration was 0.32 mm (SD 0.045) in the Durasul group and 1.07 mm (SD 0.13) in the Sulene group (p < 0.001). Mean femoral head penetration at 20 years was approximately 70.0% less in the Durasul group than the Sulene group. Conclusion. The significant reduction in femoral head penetration obtained with the Durasul compared with Sulene in uncemented THA resulted in lower osteolysis and revision rates after 20 years. Cite this article: Bone Joint J 2022;104-B(9):1032–1038

Aims. Contemporary outcomes of primary total hip arthroplasties (THAs) with highly cross-linked polyethylene (HXLPE) liners in patients with inflammatory arthritis have not been well studied. This study examined the implant survivorship, complications, radiological results, and clinical outcomes of THA in patients with inflammatory arthritis. Methods. We identified 418 hips (350 patients) with a primary diagnosis of inflammatory arthritis who underwent primary THA with HXLPE liners from January 2000 to December 2017. Of these hips, 68% had rheumatoid arthritis (n = 286), 13% ankylosing spondylitis (n = 53), 7% juvenile rheumatoid arthritis (n = 29), 6% psoriatic arthritis (n = 24), 5% systemic lupus erythematosus (n = 23), and 1% scleroderma (n = 3). Mean age was 58 years (SD 14.8), 66.3% were female (n = 277), and mean BMI was 29 kg/m. 2. (SD 7). Uncemented femoral components were used in 77% of cases (n = 320). Uncemented acetabular components were used in all patients. Competing risk analysis was used accounting for death. Mean follow-up was 4.5 years (2 to 18). Results. The ten-year cumulative incidence of any revision was 3%, and was highest in psoriatic arthritis patients (16%). The most common indications for the 15 revisions were dislocations (n = 8) and periprosthetic joint infections (PJI; n = 4, all on disease-modifying antirheumatic drugs (DMARDs)). The ten-year cumulative incidence of reoperation was 6.1%, with the most common indications being wound infections (six cases, four on DMARDs) and postoperative periprosthetic femur fractures (two cases, both uncemented femoral components). The ten-year cumulative incidence of complications not requiring reoperation was 13.1%, with the most common being intraoperative periprosthetic femur fracture (15 cases, 14 uncemented femoral components; p = 0.13). Radiological evidence of early femoral component subsidence was observed in six cases (all uncemented). Only one femoral component ultimately developed aseptic loosening. Harris Hip Scores substantially improved (p < 0.001). Conclusion. Contemporary primary THAs with HXLPE in patients with inflammatory arthritis had excellent survivorship and good functional outcomes regardless of fixation method. Dislocation, PJI, and periprosthetic fracture were the most common complications in this cohort with inflammatory arthritis. Cite this article: Bone Joint J 2023;105-B(7):768–774