We present minimum 20 year results of a randomized, prospective double blinded trial (RCT) of cross-linked versus conventional polyethylene (PE), using a computer assisted method of PE wear measurement. After Ethics Committee approval, 122 patients were enrolled into an RCT comparing Enduron (non cross-linked PE) and highly cross-linked Marathon PE (DePuy, Leeds, UK). Other than the PE liners, identical components were used, a Duraloc 300 metal shell with one screw, a 28mm CoCr femoral head and a cemented Charnley Elite femoral stem. All patients were followed with anteroposterior (A∼P) and lateral radiographs at 3 days, 6 weeks, 3 months, 6 months, 1, 2, 3, 4, 5, 10 and 20 years. PE wear was measured with PolyMig, which has a phantom validated accuracy of ± 0.09mm. At minimum 20 year follow-up, 47 patients had died, 5 of which had been revised prior to their death. Another 32 patients were revised and alive, leaving 43 patients unrevised and alive (15 Enduron, 28 Marathon). No patients were lost to follow-up, but 2 were not able to be radiographed (dementia), leaving 41 patients (15 Enduron, 26 Marathon) available for PE wear measurement. After the bedding-in period, Enduron liners had a wear rate of 0.182 mm/year, and Marathon liners had a wear rate of 0.028 mm/year. At 20 years follow-up, 37 patients had required revision. Patients with conventional PE had three times the revision rate (28/37) of those who received XLPE (9/37). This is the longest term RCT showing substantially improved clinical and radiological results when XLPE is used as the bearing surface

Ceramic bearing fracture is a rare complication following implantation using modern day ceramic bearing materials. Revision bearing options in such cases is debated, with the choice between ceramic-on-ceramic and ceramic-on-polyethylene bearings. Revision to a hard on soft bearing raises concerns about potential catastrophic wear secondary to a third-body reaction caused by the fractured ceramic particles. Data was collected retrospectively from the NJR, electronic patient records, revision database and picture archiving and communication system. Templating software was used to determine linear wear between first post-operative radiograph and the latest available follow up. Univariate analysis was used to examine patient demographics and the wear rates for revision of ceramic bearing fractures to ceramic on polyethylene components. The intra and inter-rater reliability of wear measurements was calculated. There were twelve patients identified as meeting the inclusion criteria. The average age at revision was 62 years (54–72). There were 6 liner and 6 head fractures revised to delta ceramic heads and cross-linked polyethylene acetabular components. The most frequently used head size was 32mm. At mean follow up of 3.8 years (0.5 6.1 years), median 4.4 years, linear wear rate was calculated at 0.08± 0.06 mm/year. Both intra-rater and inter-rater reliability was excellent with ICC scores of 0.99 at all timepoints. Revision to ceramic on polyethylene (CoP) bearings following ceramic fracture does not cause early catastrophic wear at early follow up. It appears safe to use this hard on soft bearing combination, given that wear rates are comparable to what is expected in a primary hip replacement setting. Longer follow up is required to establish if this trend persists

Introduction. In 2010, a widely used metal-on-metal hip implant was voluntarily recalled from the market by the manufacturer. Our lab performed detailed retrieval analysis of 548 of the explanted devices and 165 periprosthetic tissue specimens. We reported a high degree of variability in the multiple measurements that we performed on the components, including volumetric wear. Other studies using semi-quantitative tissue grading methods to describe the histology of the periprosthetic tissues from metal-on-metal hips have looked for relationships between component wear and histological features. Grammatopoulos et al found higher ALVAL scores in 45 hip resurfacing patients with pseudotumors compared to 11 without pseudotumors and a moderately positive correlation between wear and the histological rankings for tissue necrosis and lymphocytic response. We examined correlations between the component wear measurements from retrieval analysis and the tissue features in this large group of one metal-on-metal hip design. Materials and Methods. Tissues were processed routinely into paraffin sections, stained with H&E and characterized with light microscopic semi-quantitative scores for ALVAL features and for the number of macrophages and lymphocytes, extent of metal debris and the estimated percentage of necrosis per slide. Spearman correlation analysis was conducted to evaluate any correlations between retrieval wear measurements and histological findings. Results. The median combined cup and ball wear volume was 17.5mm3 in these 165 cases. The median tissue ALVAL score was 5.5 out of 10. Component total wear volume was not predictive of the ALVAL score (P = 0.09, R = −0.007) or the number of lymphocytes (P= 0.170, R= −0.077) but there was a positive correlation between wear volume and the ranking for macrophages in the tissues (P< 0.001, R=0.215). No other correlations were found for component wear. The median time to revision was 4.84 years. There was a negative correlation between tissue inflammation ranking (P=0.002, R=−0.183) and for lymphocyte ranking and time to revision (P=0.003, R=−0.173). There was a positive correlation between time to revision and the macrophage ranking (P=0.005, R=0.166). Conclusion. From this large-scale retrieval analysis of one design of metal-on-metal total hip, a high degree of variability was observed over the multiple analyses performed, including volumetric wear and tissue features. This likely reflects our previous observation that no single particular failure mechanism was predominant in this large cohort. Funded by DePuy Synthes Companies of Johnson & Johnson

Aims

Several short- and mid-term studies have shown minimal liner wear of highly cross-linked polyethylene (HXLPE) in total hip arthroplasty (THA), but the safety of using thinner HXLPE liners to maximize femoral head size remains uncertain. The objective of this study was to analyze clinical survival and radiological wear rates of patients with HXLPE liners, a 36 mm femoral head, and a small acetabular component with a minimum of ten years’ follow-up.

Aims

Limited implant survival due to aseptic cup loosening is most commonly responsible for revision total hip arthroplasty (THA). Advances in implant designs and materials have been crucial in addressing those challenges. Vitamin E-infused highly cross-linked polyethylene (VEPE) promises strong wear resistance, high oxidative stability, and superior mechanical strength. Although VEPE monoblock cups have shown good mid-term performance and excellent wear patterns, long-term results remain unclear. This study evaluated migration and wear patterns and clinical and radiological outcomes at a minimum of ten years’ follow-up.

Objectives. The accuracy and precision of two new methods of model-based radiostereometric analysis (RSA) were hypothesised to be superior to a plain radiograph method in the assessment of polyethylene (PE) wear. Methods. A phantom device was constructed to simulate three-dimensional (3D) PE wear. Images were obtained consecutively for each simulated wear position for each modality. Three commercially available packages were evaluated: model-based RSA using laser-scanned cup models (MB-RSA), model-based RSA using computer-generated elementary geometrical shape models (EGS-RSA), and PolyWare. Precision (95% repeatability limits) and accuracy (Root Mean Square Errors) for two-dimensional (2D) and 3D wear measurements were assessed. Results. The precision for 2D wear measures was 0.078 mm, 0.102 mm, and 0.076 mm for EGS-RSA, MB-RSA, and PolyWare, respectively. For the 3D wear measures the precision was 0.185 mm, 0.189 mm, and 0.244 mm for EGS-RSA, MB-RSA, and PolyWare respectively. Repeatability was similar for all methods within the same dimension, when compared between 2D and 3D (all p > 0.28). For the 2D RSA methods, accuracy was below 0.055 mm and at least 0.335 mm for PolyWare. For 3D measurements, accuracy was 0.1 mm, 0.2 mm, and 0.3 mm for EGS-RSA, MB-RSA and PolyWare respectively. PolyWare was less accurate compared with RSA methods (p = 0.036). No difference was observed between the RSA methods (p = 0.10). Conclusions. For all methods, precision and accuracy were better in 2D, with RSA methods being superior in accuracy. Although less accurate and precise, 3D RSA defines the clinically relevant wear pattern (multidirectional). PolyWare is a good and low-cost alternative to RSA, despite being less accurate and requiring a larger sample size

Aims

The aim of this study was to evaluate the performance of first-generation annealed highly cross-linked polyethylene (HXLPE) in cementless total hip arthroplasty (THA).

Aims

Acetabular edge-loading was a cause of increased wear rates in metal-on-metal hip arthroplasties, ultimately contributing to their failure. Although such wear patterns have been regularly reported in retrieval analyses, this study aimed to determine their in vivo location and investigate their relationship with acetabular component positioning.

Objectives

Previous studies have suggested that metal-on-metal (MoM) Pinnacle (DePuy Synthes, Warsaw, Indiana) hip arthroplasties implanted after 2006 exhibit higher failure rates. This was attributed to the production of implants with reduced diametrical clearances between their bearing surfaces, which, it was speculated, were outside manufacturing tolerances. This study aimed to better understand the performance of Pinnacle Systems manufactured before and after this event.

Objectives

We investigated the reliability of the cobalt-chromium (CoCr) synovial joint fluid ratio (JFR) in identifying the presence of a severe aseptic lymphocyte-dominated vasculitis-associated lesion (ALVAL) response and/or suboptimal taper performance (SOTP) following metal-on-metal (MoM) hip arthroplasty. We then examined the possibility that the CoCr JFR may influence the serum partitioning of Co and Cr.

Objectives

The high revision rates of the DePuy Articular Surface Replacement (ASR) and the DePuy ASR XL (the total hip arthroplasty (THA) version) have led to questions over the viability of metal-on-metal (MoM) hip joints. Some designs of MoM hip joint do, however, have reasonable mid-term performance when implanted in appropriate patients. Investigations into the reasons for implant failure are important to offer help with the choice of implants and direction for future implant designs. One way to assess the performance of explanted hip prostheses is to measure the wear (in terms of material loss) on the joint surfaces.

Aims

We sought to determine whether cobalt-chromium alloy (CoCr) femoral stem tapers (trunnions) wear more than titanium (Ti) alloy stem tapers (trunnions) when used in a large diameter (LD) metal-on-metal (MoM) hip arthroplasty system.

Objectives. The determination of the volumetric polyethylene wear on explanted material requires complicated equipment, which is not available in many research institutions. Our aim in this study was to present and validate a method that only requires a set of polyetheretherketone balls and a laboratory balance to determine wear. Methods. The insert to be measured was placed on a balance, and a ball of the appropriate diameter was inserted. The cavity remaining between the ball and insert caused by wear was filled with contrast medium and the weight of the contrast medium was recorded. The volume was calculated from the known density of the liquid. The precision, inter- and intraobserver reliability, were determined by four investigators on four days using nine inserts with specified wear (0.094 ml to 1.626 ml), and the intra-class correlation coefficient was calculated. The feasibility of using this method in routine clinical practice and the time required for measurement were tested on 84 explanted inserts by one investigator. Results. In order to get the mean for all investigators and determinations, the deviation between the measured and specified wear was -0.08 ml . (sd. 0.12; -0.21 to 0.11). The interobserver reliability was 0.989 ml (95% confidence interval (CI) 0.964 to 0.997) and the intraobserver reliability was 0.941 for observer 1 (95% CI 0.846 to 0.985), 0.983 for observer 2 (95% CI 0.956 to 0.995), 0.939 for observer 3 (95% CI 0.855 to 0.984), and 0.934 for observer 4 (95% CI 0.790 to 0.984). The mean time required to examine the samples was two minutes . (sd. 2; 1 to 5). Conclusion. The method presented here was shown to be sufficiently precise for many settings and is a cost-effective and quick method of determining the volumetric wear of explanted acetabular components. However, the measurement of wear for scientific purposes will probably continue to involve more accurate and dedicated laboratory equipment. Cite this article: Bone Joint Res 2017;6:530–534

Aims

Our aim in this study was to describe a continuing review of 11 total hip arthroplasties using 22.225 mm Alumina ceramic femoral heads on a Charnley flanged femoral component, articulating against a silane crosslinked polyethylene.

Aims

This paper describes the methodology, validation and reliability of a new computer-assisted method which uses models of the patient’s bones and the components to measure their migration and polyethylene wear from radiographs after total hip arthroplasty (THA).

Polyethylene wear debris can cause osteolysis and the failure of total hip arthroplasty. We present the five-year wear rates of a highly cross-linked polyethylene (X3) bearing surface when used in conjunction with a 36 mm ceramic femoral head.

This was a prospective study of a cohort of 100 THAs in 93 patients. Pain and activity scores were measured pre- and post-operatively. Femoral head penetration was measured at two months, one year, two years and at five years using validated edge-detecting software (PolyWare Auto).

At a mean of 5.08 years (3.93 to 6.01), 85 hips in 78 patients were available for study. The mean age of these patients was 59.08 years (42 to 73, the mean age of males (n = 34) was 59.15 years, and females (n = 44) was 59.02 years). All patients had significant improvement in their functional scores (p < 0.001). The steady state two-dimensional linear wear rate was 0.109 mm/year. The steady state volumetric wear rate was 29.61 mm³/year. No significant correlation was found between rate of wear and age (p = 0.34), acetabular component size (p = 0.12) or clinical score (p = 0.74).

Our study shows low steady state wear rates at five years in X3 highly cross-linked polyethylene in conjunction with a 36 mm ceramic femoral head. The linear wear rate was almost identical to the osteolysis threshold of 0.1 mm/year recommended in the literature.

Cite this article: Bone Joint J 2015;97-B:1470–4.

Aims

The objective of this five-year prospective, blinded, randomised controlled trial (RCT) was to compare femoral head penetration into a vitamin E diffused highly cross-linked polyethylene (HXLPE) liner with penetration into a medium cross-linked polyethylene control liner using radiostereometric analysis.

Objectives

High failure rates of metal-on-metal hip arthroplasty implants have highlighted the need for more careful introduction and monitoring of new implants and for the evaluation of the safety of medical devices. The National Joint Registry and other regulatory services are unable to detect failing implants at an early enough stage. We aimed to identify validated surrogate markers of long-term outcome in patients undergoing primary total hip arthroplasty (THA).

Aims

The purpose of this study was to compare the long-term results of primary total hip arthroplasty (THA) in young patients using either a conventional (CPE) or a highly cross-linked (HXLPE) polyethylene liner in terms of functional outcome, incidence of osteolysis, radiological wear and rate of revision.

We report the five-year outcome of a randomised controlled trial which used radiostereometric analysis (RSA) to assess the influence of surface oxidised zirconium (OxZr, Oxinium) on polyethylene wear in vivo.

A total of 120 patients, 85 women and 35 men with a mean age of 70 years (59 to 80) who were scheduled for primary cemented total hip arthroplasty were randomly allocated to four study groups. Patients were blinded to their group assignment and received either a conventional polyethylene (CPE) or a highly cross-linked (HXL) acetabular component of identical design. On the femoral side patients received a 28 mm head made of either cobalt-chromium (CoCr) or OxZr.

The proximal head penetration (wear) was measured with repeated RSA examinations over five years. Clinical outcome was measured using the Harris hip score.

There was no difference in polyethylene wear between the two head materials when used with either of the two types of acetabular component (p = 0.3 to 0.6). When comparing the two types of polyethylene there was a significant difference in favour of HXLPE, regardless of the head material used (p < 0.001).

In conclusion, we found no advantage of OxZr over CoCr in terms of polyethylene wear after five years of follow-up. Our findings do not support laboratory results which have shown a reduced rate of wear with OxZr. They do however add to the evidence on the better resistance to wear of HXLPE over CPE.

Cite this article: Bone Joint J 2015;97-B:1463–9.