Purpose of the Study. This study aims at investigating the effect of application time of bone cement on the cement-bone interface strength in two types of commercially available bone cements, Cement-A and Cement-B. Materials and methods. Cement-A and Cement-B were applied to cancellous bone specimens at two different times; 2 and 4 minutes (min). The bone specimens were formulated from bovine bone. Specimens were loaded to failure and the force at which the cement-bone interface failed was recorded. The shear strength of the cement-bone interface was calculated by dividing the force at failure by the cross-sectional surface area of the cement-bone interface. Results. The mean (± standard deviation) and median (inter-quartile range) shear strength of the cement-bone interface was 2.79 ± 1.29 MPa and 2.29 (2.34) MPa for Cement-A applied at 2 min; 1.35 ± 0.89 MPa and 1.35 (1.74) MPa for Cement-A applied at 4 min; 2.93 ± 1.21 MPa and 3.01 (2.61) MPa for Cement-B applied at 2 min; and 3.00 ± 1.11 MPa and 2.92 (1.61) MPa for Cement-B applied at 4 min. Compared to all other groups, the cement-bone interface strength was significantly lower when Cement-A was applied to the bone specimens at 4 min (p < 0.05). There was no significant difference in the cement-bone interface strength when Cement-B was applied to bone at 2 and at 4 min. Conclusions. Under these testing conditions, the cement-bone interface strength did not seem to be affected by the time of application of Cement-B to bone. However, it was significantly lower when Cement-A was applied to bone at 4 min

Introduction. Antibiotic-impregnated bone cement (AIBC) has been used for decades to treat and prevent post-operative infections in joint arthroplasty. Local delivery of antibiotics may theoretically have a bactericidal effect, however evidence supporting this is controversial and literature suggests its prophylactic use in primary total knee arthroplasty (TKA) is seldom justified. With evolving standards of care, historical data is no longer relevant in addressing the efficacy of AIBC in the contemporary TKA. The purpose of this study was to evaluate outcomes following primary TKA using AIBC and regular non-AIBC by comparing rates of surgical site infection (SSI) and prosthetic joint infection (PJI). Methods. A retrospective review was conducted of all cemented primary TKA procedures from a large institutional database between January 1, 2015 and December 31st, 2016. This identified 6,073 cases, n=2,613 in which AIBC was used and n=3,460 cases using bone cement without antibiotics. Patients were stratified into low risk and high-risk groups based on age (>65 years), BMI (>40), and Charlson Comorbidity Index (CCI; >3). Medical records were reviewed for diagnoses of SSI (skin and superficial wound infections) and PJI (deep joint infections requiring surgery) over a 2-year postoperative period. Univariate analysis and multivariate regression models were used to ascertain the effects of cement type, patient factors (age, gender, BMI, CCI), operative time, and length of stay on infection rates. Additionally, mixed models (adjusted for gender, age, race, BMI, and CCI) were built to account for surgeon variability. Results. The use of AIBC and risk group distributions were equal across the study period and no collinearity was found between the study variables. The SSI rate was 3.0% and the PJI rate was 0.8% in the total study population. Univariate analysis showed there was no significant difference in SSI rates with AIBC compared to non-AIBC (3.3% vs. 2.8%, p=0.278) or in PJI rates (1.0% vs. 0.7%, p=0.203). Multivariate logistic regression analysis adjusted for patient factors, operative time, and length of stay showed no significant difference in SSI rates with a procedure using AIBC compared to non-AIBC (OR=0.90; 95% CI, 0.66–1.23; p=0.515) and no significant difference in PJI rates (OR=1.01; 95% CI, 0.55–1.84; p=0.984). Mixed models also showed no difference in PJI rates with AIBC use after adjusting for surgeon variability as well as patient factors (gender, race, age, BMI, and CCI). Discussion. Prophylactic use of AIBC in primary TKA is not without consequence when considering the significant increase in cost and its potential side effects, namely organism specific antibiotic resistance and mechanical loosening. This study shows that even when adjusted for patient factors, procedure-related factors, and length of stay, there is no clinically significant decrease in infection rates with the use of AIBC in primary TKAs

Aims. The main objective of this study is to analyze the penetration of bone cement in four different full cementation techniques of the tibial tray. Methods. In order to determine the best tibial tray cementation technique, we applied cement to 40 cryopreserved donor tibiae by four different techniques: 1) double-layer cementation of the tibial component and tibial bone with bone restrictor; 2) metallic cementation of the tibial component without bone restrictor; 3) bone cementation of the tibia with bone restrictor; and 4) superficial bone cementation of the tibia and metallic keel cementation of the tibial component without bone restrictor. We performed CT exams of all 40 subjects, and measured cement layer thickness at both levels of the resected surface of the epiphysis and the endomedular metaphyseal level. Results. At the epiphyseal level, Technique 2 gave the greatest depth compared to the other investigated techniques. At the endomedular metaphyseal level, Technique 1 showed greater cement penetration than the other techniques. Conclusion. The best metaphyseal cementation technique of the tibial component is bone cementation with cement restrictor. Additionally, if full tibial component cementation is to be done, the cement volume used should be about 40 g of cement, and not the usual 20 g. Cite this article: Bone Joint Res 2021;10(8):467–473

Aims. Antibiotic-loaded bone cements (ALBCs) may offer early protection against the formation of bacterial biofilm after joint arthroplasty. Use in hip arthroplasty is widely accepted, but there is a lack of evidence in total knee arthroplasty (TKA). The objective of this study was to evaluate the use of ALBC in a large population of TKA patients. Materials and Methods. Data from the National Joint Registry (NJR) of England and Wales were obtained for all primary cemented TKAs between March 2003 and July 2016. Patient, implant, and surgical variables were analyzed. Cox proportional hazards models were used to assess the influence of ALBC on risk of revision. Body mass index (BMI) data were available in a subset of patients. Results. Of 731 214 TKAs, 15 295 (2.1%) were implanted with plain cement and 715 919 (97.9%) with ALBC. There were 13 391 revisions; 2391 were performed for infection. After adjusting for other variables, ALBC had a significantly lower risk of revision for any cause (hazard ratio (HR) 0.85, 95% confidence interval (CI) 0.77 to 0.93; p < 0.001). ALBC was associated with a lower risk of revision for all aseptic causes (HR 0.85, 95% CI 0.77 to 0.95; p < 0.001) and revisions for infection (HR 0.84, 95% CI 0.67 to 1.01; p = 0.06). The results were similar when BMI was added into the model, and in a subanalysis where surgeons using only ALBC over the entire study period were excluded. Prosthesis survival at ten years for TKAs implanted with ALBC was 96.3% (95% CI 96.3 to 96.4) compared with 95.5% (95% CI 95.0 to 95.9) in those implanted with plain cement. On a population level, where 100 000 TKAs are performed annually, this difference represents 870 fewer revisions at ten years in the ALBC group. Conclusion. After adjusting for a range of variables, ALBC was associated with a significantly lower risk of revision in this registry-based study of an entire nation of primary cemented knee arthroplasties. Using ALBC does not appear to increase midterm implant failure rates. Cite this article: Bone Joint J 2019;101-B:1331–1347

Introduction. The role of porosity in the longevity of polymethylmethacrylate (PMMA) bone cement mantles remains unclear, although porosity reduction is probably desirable. It is not known whether pore patterns, pore distribution or pore morphology contribute to failure, since it is difficult to assess these features with traditional techniques. We used a novel microtomographic technique to quantitatively and qualitatively assess porosity in PMMA cements of differing viscosities to establish whether pore distribution can be effectively assessed and to document any differences in porosity (in both quantity, distribution and morphology). Each cement was also examined with and without the addition of vacuum, since this is thought to reduce porosity. Methods and materials. Four PMMA bone cements of different viscosities (three of the same brand and the fourth chosen due to its popularity) were prepared and moulded according to established protocols (ASTM F451-99a), with and without the addition of vacuum. 25 samples per group (200 total) were prepared and densities for each sample calculated using Archimedes' principle. Four samples per group (total 32) were randomly selected for further analysis. These samples underwent micro-computer tomography (micro-CT) at a magnification of 20× and slice thickness of 13.67μm and reconstructed images were analysed with in-house developed software to measure pore size and volume. Results were analysed and compared with the two-sample T-test assuming significance at P<0.05. Qualitative assessment of pore character and distribution was made using three dimensional (3D) reconstruction. Results. Densities and mean total pore volume showed an overall reduction in porosity with vacuum. Mean pore volume (MPV) was not significantly different between samples due to the huge range of pore sizes. Qualitative assessment revealed a striking, distinctive pore distribution between cements with an asymmetric distribution in the high viscosity group. Pore size was also qualitatively distinct between cement types and groups with and without vacuum. Conclusion. Micro-CT allows detailed in vitro quantitative and qualitative assessment of porosity in PMMA cement. Pore volume, architecture and volumetric distribution differ in cements of differing viscosity and with or without the application of vacuum. This effect is marked enough to allow distinction between cements based on their micro-CT appearances. Further study using this technique in combination with other methods (such as quantitative analysis of 3D pore distribution) may shed light on the failure mechanisms in PMMA cement mantles, particularly with regard to the role of pore orientation, distribution and size

Aims. A novel enhanced cement fixation (EF) tibial implant with deeper cement pockets and a more roughened bonding surface was released to market for an existing total knee arthroplasty (TKA) system.This randomized controlled trial assessed fixation of the both the EF (ATTUNE S+) and standard (Std; ATTUNE S) using radiostereometric analysis. Methods. Overall, 50 subjects were randomized (21 EF-TKA and 23 Std-TKA in the final analysis), and had follow-up visits at six weeks, and six, 12, and 24 months to assess migration of the tibial component. Low viscosity bone cement with tobramycin was used in a standardized fashion for all subjects. Patient-reported outcome measure data was captured at preoperative and all postoperative visits. Results. The patient cohort mean age was 66 years (SD seven years), 59% were female, and the mean BMI was 32 kg/m. 2. (SD 6 kg/m. 2. ). Mean two-year subsidence of the EF-TKA was 0.056 mm (95% confidence interval (CI) 0.025 to 0.086) versus 0.006 mm (95% CI -0.029 to 0.040) for the Std-TKA, and the two-year maximum total point motion (MTPM) was 0.285 mm (95% upper confidence limit (UCL) ≤ 0.363) versus 0.346 mm (95% UCL ≤ 0.432), respectively, for a mean difference of -0.061 mm (95% CI -0.196 to 0.074). Inducible displacement also did not differ between groups. The MTPMs between 12 and 24 months for each group was below the published threshold of 0.2 mm for predicting early aseptic loosening (p < 0.001 and p = 0.001, respectively). Conclusion. Both the enhanced fixation and the standard tibial implant design showed fixation with a predicted low risk of long-term aseptic loosening. Cite this article: Bone Jt Open 2024;5(1):20–27

Aims

Aseptic loosening is the most common cause of failure following cemented total knee arthroplasty (TKA), and has been linked to poor cementation technique. We aimed to develop a consensus on the optimal technique for component cementation in TKA.

Aims. We propose a state-of-the-art temporary spacer, consisting of a cobalt-chrome (CoCr) femoral component and a gentamicin-eluting ultra-high molecular weight polyethylene (UHMWPE) tibial insert, which can provide therapeutic delivery of gentamicin, while retaining excellent mechanical properties. The proposed implant is designed to replace conventional spacers made from bone cement. Methods. Gentamicin-loaded UHMWPE was prepared using phase-separated compression moulding, and its drug elution kinetics, antibacterial, mechanical, and wear properties were compared with those of conventional gentamicin-loaded bone cement. Results. Gentamicin-loaded UHMWPE tibial components not only eradicated planktonic Staphylococcus aureus, but also prevented colonization of both femoral and tibial components. The proposed spacer possesses far superior mechanical and wear properties when compared with conventional bone cement spacers. Conclusion. The proposed gentamicin-eluting UHMWPE spacer can provide antibacterial efficacy comparable with currently used bone cement spacers, while overcoming their drawbacks. The novel spacer proposed here has the potential to drastically reduce complications associated with currently used bone cement spacers and substantially improve patients’ quality of life during the treatment. Cite this article: Bone Joint J 2020;102-B(6 Supple A):151–157

Introduction. Infection remains as one of the major challenges of total joint surgery. One-stage irrigation, debridement and reimplantation, or two-stage revision surgery with a temporary implantation of antibiotic eluting bone cement spacer followed by reimplantation are two methods often used to treat infected patients with mixed outcomes. Like bone cement, ultra-high molecular weight polyethylene (UHMWPE) can also be used as a carrier for antibiotics. Recently, we demonstrated that vancomycin and rifampin can be delivered from UHMWPE implants at therapeutic levels to eradicate Staphylococcus aureus biofilm in a lupine animal model. There are regulatory challenges in translating these types of combination devices to clinical use. Last year, at this meeting, we presented the preliminary pre-clinical testing for a temporary UHMWPE spacer containing gentamicin sulfate as a first step towards clinical use. Since then, we carried out a survey among the Knee Society membership about their preference for spacer use in two-stage revision surgery and found that 43% prefer to use a CoCr femoral component on an all-poly cemented tibial insert, 22% prefer bone cement spacers molded in the OR, 20% prefer static bone cement spacers, and 14% prefer pre-formed bone cement spacers. We modified our implant design based on the majority's preference for a total knee system, rather than bone cement spacers, in the temporary two-stage approach. In this study, we explored the effect of gentamicin sulfate (GS) elution from UHMWPE/GS tibial inserts on bacterial colonization on CoCr surfaces. Methods. We characterized the gentamicin sulfate (GS) particles with scanning electron microscopy (SEM). We molded UHMWPE/GS powder blends and characterized the morphology using SEM and Energy Dispersive X-Ray Spectroscopy (EDS). We submerged samples of molded UHMWPE/GS in buffered phosphate solution (PBS) at 37°C and quantified the extent of GS elution into PBS with a method described by Gubernator et al. using o-phthaladehyde (OPA) [1]. Under basic conditions, OPA reacts with primary amino groups to form fluorescent complexes. Since gentamicin is the only source of such amino acids in our elution samples, the number of fluorescent complexes formed is directly proportional to the amount of gentamicin in the sample. Using this method, we could quantify gentamicin elution by measuring sample fluorescence post OPA-reaction. We used a plate reader to excite the fluorescent complexes formed in the OPA reaction and measured the resulting emission at wavelengths of 340 nm and 455 nm, respectively. We also quantified the effect of the standard cleaning protocol (heated sonication in alkaline water and alcohol) used to clean UHMWPE implants on subsequent GS elution from UHMWPE/GS samples using the OPA method. We used agar diffusion tests to characterize antibacterial properties of UHMWPE/GS samples after cleaning. For these tests, we collected eluents collected from UHMWPE/GS and gentamicin-impregnated bone cement (BC/GS) following 1, 2, 3, and 4 weeks of elution, and tested against S. aureus (ATCC 12600). We used the “daughter cells” method developed by Bechert et al. to assess anticolonizing properties of UHMWPE/GS [2,3]. We also characterized the colonization of bacteria on CoCr surfaces in the presence of GS eluting from UHMWPE/GS test samples. For this we modified a Pin-on-Disc (PoD) wear tester: An UHMWPE/GS pin and UHMWPE pin (control) articulated against an implant-finish CoCr disc with Tryptic Soy Broth containing S. Aureus as the lubricant. After 18 hrs, we rinsed the articular surfaces of the pin and disc and stamped them onto Agar gel to transfer any adherent bacteria. We incubated the Agar plate overnight such that adherent bacteria proliferated and became visible. Results. SEM characterized the GS particles as hollow spheres (Fig 1a). These formed small groups of agglomerated domains at the virgin resin boundaries of UHMWPE after molding (Fig 1b). Sulfur signature from the EDS analysis identified the agglomerated domains as GS particles (Fig 2). Elution of GS started with an initial burst and was followed by steady elution up to 12 weeks (Fig 3). Cleaning reduced the initial burst GS elution; and the elution remained unchanged after 2 days (Fig 4). The agar diffusion test showed simmilar inhibition zones for the eluents collected from UHMWPE/GS and BC/GS, suggesting that these samples yield similar antibacterial activity against S. aureus (Fig 5). UHMWPE/GS demonstrated pronounced anticolonizing properties, effectively mitigating the proliferation of S. aureus “daughter” cells. Anticolonizing activity of Palacos R+G was not significantly different when compared with UHMWPE/GS. The PoD test showed little-to-no colonization of CoCr surfaces in the presence of UHMWPE/GS pins, indicative of excellent antibacterial properties of UHMWPE/GS against S. aureus. Conclusion. SEM and EDS has allowed us to visualize domains of gentamicin sulfate particles in UHMWPE. Our OPA method has greater precision than traditional agar-well diffusion methods of measuring gentamicin concentration and showed that gentamicin sulfate-loaded UHMWPE elutes at the same rate as Palacos R+G. Pin-on-disc experiments and the daughter cell method both confirmed that these two materials have similar anticolonization abilities. We also found that using the standard cleaning protocol for UHMWPE orthopedic implants decreased the burst of gentamicin eluting from UHMWPE, but after 2 days, it had no effect compared to uncleaned UHMWPE/GS. Finally, we found that UHMWPE/GS can reduce the colonization of bacteria on CoCr. UHMWPE/GS continues to be a promising material for treating PJI. For figures, tables, or references, please contact authors directly

Aims. To establish our early clinical results of a new total knee arthroplasty (TKA) tibial component introduced in 2013 and compare it to other designs in use at our hospital during the same period. Methods. This is a retrospective study of 166 (154 patients) consecutive cemented, fixed bearing, posterior-stabilized (PS) TKAs (ATTUNE) at one hospital performed by five surgeons. These were compared with a reference cohort of 511 knees (470 patients) of other designs (seven manufacturers) performed at the same hospital by the same surgeons. There were no significant differences in age, sex, BMI, or follow-up times between the two cohorts. The primary outcome was revision performed or pending. Results. In total, 19 (11.5%) ATTUNE study TKAs have been revised at a mean 30.3 months (SD 15), and loosening of the tibial component was seen in 17 of these (90%). Revision is pending in 12 (7%) knees. There was no difference between the 31 knees revised or with revision pending and the remaining 135 study knees in terms of patient characteristics, type of bone cement (p = 0.988), or individual surgeon (p = 0.550). In the reference cohort, there were significantly fewer knees revised (n = 13, 2.6%) and with revision pending (n = 8, 1.5%) (both p < 0.001), and only two had loosening of the tibial component as the reason for revision. Conclusion. This new TKA design had an unexpectedly high early rate of revision compared with our reference cohort of TKAs. Debonding of the tibial component was the most common reason for failure. Additional longer-term follow-up studies of this specific component and techniques for implantation are warranted. The version of the ATTUNE tibial component implanted in this study has undergone modifications by the manufacturer. Cite this article: Bone Joint J 2021;103-B(6 Supple A):137–144

Introduction. Periprosthetic infection (PJI) after primary total knee arthroplasty (TKA) remains a challenging issue affecting 1–2% of cases. Locally delivered prophylactic antibiotics, including tobramycin or gentamicin mixed in polymethylmethacrylate (PMMA) bone cement and vancomycin powder, are increasingly used despite a lack of high quality evidence for either practice. In this study, we report the antibiotic susceptibility of organisms recovered in culture from patients with acute prosthetic joint infection after primary TKA to gentamicin, tobramycin and vancomycin. Methods. Using a retrospective database of all primary TKA performed at a single institution between January, 1 2014 and July 1, 2018, we identified 18 cases of acute PJI after primary TKA, as defined by the Musculoskeletal Infection Society 2011 guidelines as less than 3 months from symptoms or index surgery to presentation. The use of antibiotic bone cement during the index procedure and time to surgical management of the infection were recorded. Fluid cultures and tissue cultures were obtained intraoperatively at the time of revision. The organisms from positive cultures underwent MIC testing to gentamicin, tobramycin and vancomycin using a gradient diffusion method (ETEST). MIC breakpoints for susceptibility were based on Clinical and Laboratory Standards Institute definitions. Results. 18 cases of PJI after TKA were identified, including 4 polymicrobial infections (22.2%) (Table 1). Average time to revision for infection was 38 days (range: 6–84 days). 34.8% of bacterial isolates were resistant to gentamicin, 39.1% were resistant to tobramycin and 17.4% were resistant to vancomycin. Of the 8 bacterial isolates resistant to gentamicin, 7 (87.5%) were susceptible tobramycin. Of the 9 bacterial isolates resistant to tobramycin, (88.9%) were susceptible to vancomycin. One bacterial isolate, a Fusobacterium nucleatum from a polymicrobial infection was resistant to gentamicin, tobramycin and vancomycin. Conclusion. Over one third of bacteria causing acute PJI after primary TKA were resistant to the aminoglycosides pre-mixed in commercially available bone cements. All but one of the bacteria resistant to gentamicin and tobramycin were susceptible to vancomycin. The addition of vancomycin to bone cement or as powder in the surgical field has the potential to expand antibiotic coverage to include most organisms responsible for acute PJI after TKA. For figures, tables, or references, please contact authors directly

Infection remains as one of the major challenges of total joint surgery. One-stage irrigation, debridement and reimplantation or two-stage revision surgery with a temporary implantation of antibiotic eluting bone cement spacer followed by reimplantation are two methods often used to treat infected patients with mixed outcomes. Like bone cement, ultra-high molecular weight polyethylene (UHMWPE) can also be used as a carrier for antibiotics. Recently, we demonstrated that vancomycin and rifampin can be successfully delivered from UHMWPE implants at therapeutic levels to eradicate Staphylococcus aureus biofilm in a lupine animal model. There are regulatory challenges in translating these types of combination devices in to clinical use. One approach is to follow a stepwise strategy, with the first step of seeking clearance for a temporary UHMWPE spacer containing gentamicin sulfate. In this study, we explored the effect of gentamicin sulfate (GS) content in UHMWPE on GS elution rate and antimicrobial activity against methicillin-sensitive S. aureus(MSSA). We also assessed the effect of spacer fabrication on the activity of gentamicin sulfate. We prepared and consolidated UHMWPE/GS blends in varying concentrations. After consolidation, we fabricated test samples with surface area (350mm2) to volume (300mm3) ratio of 1.2 for elution in 1.5ml phosphate buffered saline at body temperature for up to six months and quantified eluted GS content using liquid chromatography – mass spectrometry (LCMS). We assessed the antibacterial activity of the obtained samples in vitro against various concentrations of MSSA (103–106 CFU/ml). Furthermore, we quantified the probability of bacterial colonization of UHMWPE impregnated with GS compared to GS containing bone cement. We assessed any detectable changes in activity of eluted GS caused by spacer fabrication by screening m/z peaks of GS isomers in mass spectra obtained from LC-MS. Gentamicin sulfate activity was not compromised by the elevated temperature and pressure used during spacer fabrication. Elution rate of GS increased with increasing GS content in the blends studied. At comparable elution rates, the GS-loaded UHMWPE was either equivalent or better in terms of antibacterial and anticolonization properties when compared with gentamicin containing bone cement. GS-impregnated UHMWPE is a promising material for temporary spacers

Introduction. Periprosthetic joint infection (PJI) remains the main cause of failure in primary and revision total knee arthroplasties (TKAs). Local delivery of antibiotics, mainly antibiotic-loaded bone cement (ALBC), is commonly employed to prevent PJI. Over the past decade, tantalum and porous titanium have been successfully utilized as metaphyseal fixation devices to address bone loss and improve biologic fixation during revision TKA. However, no study has examined the antimicrobial properties compared to bone cement. The purpose of this study was to compare the ability of tantalum, 3D porous titanium, antibiotic-loaded bone cement (ALBC) and smooth titanium alloy (STA) to inhibit Staphylococci bacterial agents in an in vitro medium environment, based on the evaluation of the zone of inhibition (ZOI) and the antibacterial activity duration. Our study hypothesis was that we will found no significant difference between groups to inhibit Methicillin-Sensitive or Methicillin-Resistant Staphylococcus aureus (MSSA/MRSA) agents. Methods. Thirty beads made of 3 different materials (tantalum/ 3D porous titanium/ STA) were bathed during 1hour inside of a solution made of 1g vancomycin with 20-mL of sterile water for injection (bath concentration: 50 mg/mL). Ten 1cm. 3. cylinders were also created mixing standard surgical cement with 1g of Vancomycin in standardized sterile molds (ALBC beads). Finally, thirty beads made of tantalum/ 3D porous titanium/ STA were bathed in phosphate buffered saline solution to act as a control group. Cylinders were then placed on agar plates inoculated with MSSA and MRSA. Inhibition zone diameters were measured each day and cylinders were transferred onto a new inoculated plate. Inhibition zones were measured with a manual Vernier caliper and with automated software. The mean inhibition zones between groups were compared using the Wilcoxon Test. Results. The inter-class coefficient correlation values indicated an optimal intra-observer and inter-observer reproducibility for ZOI measurement (ICC 0.96 and ICC 0.98). For MSSA and MRSA, no inhibitory effect was found in the control group and antibiotic-loaded STA beads exhibited a short inhibitory effect until day 2. For MSSA, both tantalum and 3D porous titanium beads exhibited larger inhibition zones than cement beads (all p<0.01) each day until day 7 for tantalum and until day 3 for 3D porous titanium. After 6 days, ALBC presented larger inhibition zone than the 3D porous titanium, but no difference was found with tantalum. For MRSA, both tantalum and 3D porous titanium beads had significantly larger inhibition zones than ALBC each day until day 6 for tantalum (all p<0.01) and until day 3 for 3D porous titanium (all p<0.04). ALBC presented larger inhibition zone than tantalum and 3D porous titanium from day 7 to 9 (all p<0.04). Conclusion. Our results demonstrate that porous metal implants can deliver local antibiotics over slightly varying time frames based on our in vitro analysis. Antibiotic-impregnated tantalum and 3D porous titanium constructs exhibited superior antimicrobial properties when compared to STA. Future goals include impregnating porous metals with antibiotics for intraoperative use during revision TKA. For figures, tables, or references, please contact authors directly

Aims. The aim of this study was to compare the ability of tantalum, 3D porous titanium, antibiotic-loaded bone cement, and smooth titanium alloy to inhibit staphylococci in an in vitro environment, based on the evaluation of the zone of inhibition (ZOI). The hypothesis was that there would be no significant difference in the inhibition of methicillin-sensitive or methicillin-resistant Staphylococcus aureus (MSSA/MRSA) between the two groups. Methods. A total of 30 beads made of three different materials (tantalum/3D porous titanium and smooth titanium alloy) were bathed for one hour in a solution of 1 g vancomycin in 20 ml of sterile water for injection (bath concentration: 50 mg/mL). Ten 1 cm. 3. cylinders of antibiotic-loaded cement were also created by mixing standard surgical cement with 1 g of vancomycin in standardized sterile moulds. The cylinders were then placed on agar plates inoculated with MSSA and MRSA. The ZOIs were measured each day and the cylinders were transferred onto a new inoculated plate. Results. For MSSA and MRSA, no inhibitory effect was found in the control group, and antibiotic-loaded smooth titanium alloy beads showed a short inhibitory effect until day 2. For MSSA, both tantalum and 3D porous titanium beads showed significantly larger mean ZOIs than cement beads (all p < 0.01) each day until day 7 for tantalum and until day 3 for 3D porous titanium. After six days, antibiotic-loaded cement had significantly larger mean ZOIs than the 3D porous titanium (p = 0.027), but no significant difference was found with tantalum (p = 0.082). For MRSA, both tantalum and 3D porous titanium beads had significantly larger mean ZOIs than antibiotic-loaded cement each day until day 6 for tantalum (all p < 0.01) and until day 3 for 3D porous titanium (all p < 0.04). Antibiotic-loaded cement had significantly larger mean ZOIs than tantalum and 3D porous titanium from day 7 to 9 (all p < 0.042). Conclusion. These results show that porous metal implants can deliver local antibiotics over slightly varying time frames based on in vitro analysis. Cite this article: Bone Joint J 2020;102-B(6 Supple A):158–162

Aims. Although bone cement is the primary mode of fixation in total knee arthroplasty (TKA), cementless fixation is gaining interest as it has the potential of achieving lasting biological fixation. By 3D printing an implant, highly porous structures can be manufactured, promoting osseointegration into the implant to prevent aseptic loosening. This study compares the migration of cementless, 3D-printed TKA to cemented TKA of a similar design up to two years of follow-up using radiostereometric analysis (RSA) known for its ability to predict aseptic loosening. Methods. A total of 72 patients were randomized to either cementless 3D-printed or a cemented cruciate retaining TKA. RSA and clinical scores were evaluated at baseline and postoperatively at three, 12, and 24 months. A mixed model was used to analyze the repeated measurements. Results. The mean maximum total point motion (MTPM) at three, 12, and 24 months was 0.33 mm (95% confidence interval (CI) 0.25 to 0.42), 0.42 mm (95% CI 0.33 to 0.51), and 0.47 mm (95% CI 0.38 to 0.57) respectively in the cemented group, versus 0.52 mm (95% CI 0.43 to 0.63), 0.62 mm (95% CI 0.52 to 0.73), and 0.64 mm (95% CI 0.53 to 0.75) in the cementless group (p = 0.003). However, using three months as baseline, no difference in mean migration between groups was found (p = 0.497). Three implants in the cemented group showed a > 0.2 mm increase in MTPM between one and two years of follow-up. In the cementless group, one implant was revised due to pain and progressive migration, and one patient had a liner-exchange due to a deep infection. Conclusion. The cementless TKA migrated more than the cemented TKA in the first two-year period. This difference was mainly due to a higher initial migration of the cementless TKA in the first three postoperative months after which stabilization was observed in all but one malaligned and early revised TKA. Whether the biological fixation of the cementless implants will result in an increased long-term survivorship requires a longer follow-up. Cite this article: Bone Joint J 2020;102-B(8):1016–1024

Aims. The aims of this study were to compare the mean duration of antibiotic release and the mean zone of inhibition between vancomycin-loaded porous tantalum cylinders and antibiotic-loaded bone cement at intervals, and to evaluate potential intrinsic antimicrobial properties of tantalum in an in vitro medium environment against methicillin-sensitive Staphylococcus aureus (MSSA). Materials and Methods. Ten porous tantalum cylinders and ten cylinders of cement were used. The tantalum cylinders were impregnated with vancomycin, which was also added during preparation of the cylinders of cement. The cylinders were then placed on agar plates inoculated with MSSA. The diameter of the inhibition zone was measured each day, and the cylinders were transferred to a new inoculated plate. Inhibition zones were measured with a Vernier caliper and using an automated computed evaluation, and the intra- and interobserver reproducibility were measured. The mean inhibition zones between the two groups were compared with Wilcoxon’s test. Results. MSSA was inhibited for 12 days by the tantalum cylinders and for nine days by the cement cylinders. At day one, the mean zone of inhibition was 28.6 mm for the tantalum and 19.8 mm for the cement group (p < 0.001). At day ten, the mean zone of inhibition was 3.8 mm for the tantalum and 0 mm for the cement group (p < 0.001). The porous tantalum cylinders soaked only with phosphate buffered solution showed no zone of inhibition. Conclusion. Compared with cement, tantalum could release antibiotics for longer. Further studies should assess the advantages of using antibiotic-loaded porous tantalum implants at revision arthroplasty. Cite this article: Bone Joint J 2019;101-B:848–851

Aims

Micromotion of the polyethylene (PE) inlay may contribute to backside PE wear in addition to articulate wear of total knee arthroplasty (TKA). Using radiostereometric analysis (RSA) with tantalum beads in the PE inlay, we evaluated PE micromotion and its relationship to PE wear.

Aims

Unicompartmental knee arthroplasty (UKA) is the preferred treatment for anterior medial knee osteoarthritis (OA) owing to the rapid postoperative recovery. However, the risk factors for UKA failure remain controversial.

Aims

Periprosthetic joint infection (PJI) is a challenging complication of any arthroplasty procedure. We reviewed our use of static antibiotic-loaded cement spacers (ABLCSs) for staged management of PJI where segmental bone loss, ligamentous instability, or soft-tissue defects necessitate a static construct. We reviewed factors contributing to their failure and techniques to avoid these complications when using ABLCSs in this context.

Aims

This multicentre retrospective observational study’s aims were to investigate whether there are differences in the occurrence of radiolucent lines (RLLs) following total knee arthroplasty (TKA) between the conventional Attune baseplate and its successor, the novel Attune S+, independent from other potentially influencing factors; and whether tibial baseplate design and presence of RLLs are associated with differing risk of revision.