Problems associated with allograft are well known. The addition of hydroxyapatite (HA) to allograft has various mechanical advantages, especially within revision arthroplasty. The mixing of bone and HA results in mechanical properties different from the individual parts. However, at present the changes in material properties the mix have not been fully investigated and the optimum mixing ratio not characterized. A compressive uniaxial chamber was used to investigate the change in mechanical properties occurring with the addition of HA in varying proportions to morcellised bone graft (MBG). Materials and methods. MBG was prepared using femoral heads donated from patients undergoing total hip replacement surgery using a bone mill in a standard manner. Non porous HA (npHA) was prepared using a precipitation method of Calcium Carbonate and Orthophosphoric acid. The porous HA, (pHA) is a 60% macroporosity HA commercially prepared. Chamber. The uniaxial compression chamber was a 30mm diameter, steel chamber. Holes were drilled to allow fluid drainage. Loads were applied using a 10 kN load cell. Specimens were prepared in the volumetric proportions pure HA, pure MBG, 2:1, 1:1, 1:2 ratio of MBG to HA. The samples were subjected to compressive forces of incrementally increasing loads of up to 2 KN for 60 cycles. The sample was then allowed to creep under a stress of 2 kN. MBG was also tested up to forces of 7 kN. The mechanical parameters that were examined were the stiffness of the sample at the 60th cycle, (Ec60), and creep. Statistical analysis. The different bone: HA mixes were compared by Mann Whitney U tests. The parameters analysed were the Ec60 and creep for the different mixes. All samples were also compared to MBG compacted with higher forces. Results. Apparent stiffness. The Ec60 of the MBG increased with increasing axial stress. The Ec60 of the different proportions of MBG and both npHA and pHA lay between the values of the MBG and HA individually and were significantly different from one another (p<0.05). MBG:npHA were significantly stiffer than the comparative mixes of MBG:pHA. (p<0.05). Creep rate. With increasing axial stress the creep rate for pure MBG decreased up to a precycling stress of 4 MPa. Subsequent increases in stress had no significant effect. Pure npHA and all of the mixes of MBG:npHA demonstrated significantly less creep than the comparable mixes of MBG:pHA (p=0.01). Applicability of results. The increase in apparent stiffness associated with an increase in the volume fraction of HA is accompanied by a concomitant decrease in the creep rate. Comparison of the mechanical response of the MBG at the high precycling stresses (4 - 7 MPa) to the mechanical response of the MBG:HA mixes at 3 MPa demonstrated an overlap in the mechanical response of the pure MBG at high stress and both the MBG:npHA and MBG: pHA mixes. Conclusions. Greater proportions of HA in the mix led to improvement in the mechanical response without the need for increased force of impaction. These improvements can be quantified by using a uniaxial compression test. The results raise the interesting possibility of tailoring bone graft mixtures to specific patient requirements dependent upon their weight and the quality of their bone stock

Biphasic calcium phosphate (BCP) with a characteristic needle-shaped submicron surface topography (MagnetOs) has attracted much attention due to its unique bone-forming ability which is essential for repairing critical-size bone defects such as those found in the posterolateral spine. Previous in vitro and ex-vivo data performed by van Dijk LA and Yuan H demonstrated that these specific surface characteristics drive a favorable response from the innate immune system. This study aimed to evaluate and compare the in vivo performance of three commercially-available synthetic bone grafts, (1) i-FACTOR Putty. ®. , (2) OssDsign. ®. Catalyst Putty and (3) FIBERGRAFT. ®. BG Matrix, with that of a novel synthetic bone graft in a clinically-relevant instrumented sheep posterolateral lumbar spine fusion (PLF) model. The novel synthetic bone graft comprised of BCP granules with a needle-shaped submicron surface topography (MagnetOs) embedded in a highly porous and fibrillar collagen matrix (MagnetOs Flex Matrix). Four synthetic bone grafts were implanted as standalone in an instrumented sheep PLF model for 12 weeks (n=3 bilateral levels per group; levels L2/3 & L4/5), after which spinal fusion was determined by manual palpation, radiograph and µCT imaging (based on the Lenke scale), range-of-motion mechanical testing, and histological and histomorphological evaluation. Radiographic fusion assessment determined bilateral robust bone bridging (Lenke scale A) in 3/3 levels for MagnetOs Flex Matrix compared to 1/3 for all other groups. For µCT, bilateral fusion (Lenke scale A) was found in 2/3 levels for MagnetOs Flex Matrix, compared to 0/3 for i-FACTOR Putty. ®. , 1/3 for OssDsign. ®. Catalyst Putty and 0/3 for FIBERGRAFT. ®. BG Matrix. Fusion assessment for MagnetOs Flex Matrix was further substantiated by histology which revealed significant graft resorption complemented by abundant bone tissue and continuous bony bridging between vertebral transverse processes resulting in bilateral spinal fusion in 3/3 implants. These results show that MagnetOs Flex Matrix achieved better fusion rates compared to three commercially-available synthetic bone grafts when used as a standalone in a clinically-relevant instrumented sheep PLF model

Bone defects require implantable graft substitutes, especially porous and biodegradable biomaterial for tissue regeneration. The aim of this study was to fabricate and assess a 3D-printed biodegradable hydroxyapatite/calcium carbonate scaffold for bone regeneration. Materials and methods:. A 3D-printed biodegradable biomaterial containing calcium phosphate and aragonite (calcium carbonate) was fabricated using a Bioplotter. The physicochemical properties of the material were characterised. The materials were assessed in vitro for cytotoxicity and ostegenic potential and in vivo in rat intercondylar Φ3mm bone defect model for 3 months and Φ5mm of mini pig femoral bone defects for 6 months. The results showed that the materials contained hydroxyapatite and calcium carbonate, with the compression strength of 2.49± 0.2 MPa, pore size of 300.00 ± 41mm, and porosity of 40.±3%. The hydroxyapatite/aragonite was not cytotoxic and it promoted osteogenic differentiation of human umbilical cord matrix mesenchymal stem cells in vitro. After implantation, the bone defects were healed in the treatment group whereas the defect of controlled group with gelatin sponge implantation remained non-union. hydroxyapatite/aragonite fully integrated with host bone tissue and bridged the defects in 2 months, and significant biodegradation was followed by host new bone formation. After implantation into Φ5mm femoral defects in mini pigs hydroxyapatite/aragonite were completed degraded in 6 months and fully replaced by host bone formation, which matched the healing and degradation of porcine allogenic bone graft. In conclusion, hydroxyapatite/aragonite is a suitable new scaffold for bone regeneration. The calcium carbonate in the materials may have played an important role in osteogenesis and material biodegradation

Cervical and lumbar spine fusion procedures are increasing every year. Nonetheless, these procedures are associated with high infection rates, resulting in additional cost burden. The conundrum of achieving efficient spinal fusions with minimum complications requires an ideal bone graft with osteoconductive, osteoinductive, osteogenic and structural characteristics. Synthetic bone graft substitutes with or without autograft, allograft or synthetic bone substitutes have been commonly used for fusion procedures. We carried out a meta-analysis of comparative studies and prospective case series (n = 29) with cervical and lumbar fusion procedures using synthetic bone graft substitutes, autograft or allograft and other biologics. Synthetic bone graft substitutes analysed included HA (Hydroxyapatite), β-TPC (Tri Calcium Phosphate), β-TSC (Tri Calcium Sulfate), PMMA (Polymethylmetacrylate), Surgibone, BOP (Biocompatible Osteoconductive Polymer). The analysis revealed suboptimal evidence for the efficacy and safety of synthetic products used in spinal fusion procedures. Further studies are needed to determine beneficial effects of synthetic substitutes. However, the infection rate could be highly decreased with surface and composition modification of widely used polyether ether ketone (PEEK) implants. Laser modification of surface characteristics and collagen fleeces with micro and nano pore structures can prove to be excellent surface for increased osteoblasts cell proliferation and vitality

Pseudoarthrosis after spinal fusion is an important complication leading to revision spine surgeries. Iliac Crest Bone Graft is considered the gold standard, but with limited availability and associated co-morbidities, spine surgeons often utilize alternative bone grafts. Determine the non-inferiority of a novel submicron-sized needle-shaped surface biphasic calcium phosphate (BCP<µm) as compared to autograft in instrumented posterolateral spinal fusion. Adult patients indicated for instrumented posterolateral spinal fusion of one to six levels from T10-S2 were enrolled at five participating centers. After instrumentation and preparation of the bone bed, the randomized allocation side of the graft type was disclosed. One side was grafted with 10cc of autograft per level containing a minimum of 50% iliac crest bone. The other side was grafted with 10cc of BCP<µm granules standalone (without autograft or bone marrow aspirate). In total, 71 levels were treated. Prospective follow-up included adverse events, Oswestry Disability Index (ODI), and a fine-cut Computerized Tomography (CT) at one year. Fusion was systematically scored as fused or not fused per level per side by two spine surgeons blinded for the procedure. The first fifty patients enrolled are included in this analysis (mean age: 57 years; 60% female and 40% male). The diagnoses included deformity (56%), structural instability (28%), and instability from decompression (20%). The fusion rate determined by CT for BCP<μm was 76.1%, which compared favorably to the autograft fusion rate of 43.7%. Statistical analysis through binomial modeling showed that the odds of fusion of BCP<μm was 2.54 times higher than that of autograft. 14% of patients experienced a procedure or possible device-related severe adverse event and there were four reoperations. Oswestry Disability Index (ODI) score decreased from a mean of 46.0 (±15.0) to a mean of 31.7 (±16.9), and 52.4% of patients improved with at least 15-point decrease. This data, aiming to determine non-inferiority of standalone BCP<μm as compared to autograft for posterior spinal fusions, is promising. Ongoing studies to increase the power of the statistics with more patients are forthcoming

Impaction allograft is an established method of securing initial stability of an implant in arthroplasty. Subsequent bone integration can be prolonged, and the volume of allograft may not be maintained. Intermittent administration of parathyroid hormone has an anabolic effect on bone and may therefore improve integration of an implant. Using a canine implant model we tested the hypothesis that administration of parathyroid hormone may improve osseointegration of implants surrounded by bone graft. In 20 dogs a cylindrical porous-coated titanium alloy implant was inserted into normal cancellous bone in the proximal humerus and surrounded by a circumferential gap of 2.5 mm. Morsellised allograft was impacted around the implant. Half of the animals were given daily injections of human parathyroid hormone (1–34) 5 μg/kg for four weeks and half received control injections. The two groups were compared by mechanical testing and histomorphometry. We observed a significant increase in new bone formation within the bone graft in the parathyroid hormone group. There were no significant differences in the volume of allograft, bone-implant contact or in the mechanical parameters. These findings suggest that parathyroid hormone improves new bone formation in impacted morsellised allograft around an implant and retains the graft volume without significant resorption. Fixation of the implant was neither improved nor compromised at the final follow-up of four weeks

The role of bone-graft extenders in impaction revision surgery is becoming increasingly important. Tricalcium phosphate and hydroxyapatite have been shown to be both biocompatible and osteoconductive, yet many surgeons remain reluctant to use them. The difficulty in handling bone-graft extenders can be partly alleviated by using porous particles and adding clotted blood. In an in vitro model we measured the cohesive properties of various impaction graft mixes. Several factors were evaluated including the use of pure bone graft compared with mixes with extender, washing the bone and the addition of clotted blood. Our findings showed that pure allograft bone particles had significantly higher cohesion than when mixed with extender (p < 0.001). Washing had no effect on cohesion. The addition of clotted blood significantly increased the cohesion of both pure bone (p < 0.019) and mixes with pure bone and with porous graft extender (p < 0.044)

The complications of impaction bone grafting in revision hip replacement includes fracture of the femur and subsidence of the prosthesis. In this in vitro study we aimed to investigate whether the use of vibration, combined with a perforated tamp during the compaction of morsellised allograft would reduce peak loads and hoop strains in the femur as a surrogate marker of the risk of fracture and whether it would also improve graft compaction and prosthetic stability. We found that the peak loads and hoop strains transmitted to the femoral cortex during graft compaction and subsidence of the stem in subsequent mechanical testing were reduced. This innovative technique has the potential to reduce the risk of intra-operative fracture and to improve graft compaction and therefore prosthetic stability

Autologous bone grafting is a standard procedure for the clinical repair of skeletal defects, and good results have been obtained. Autologous vascularized bone grafting is currently the procedure of choice because of high osteogenic potential and resistance against reabsorption. Disadvantages of this procedure include limited availability of donor sites, clinical difficulty in handling, and a failure rate exceeding 10%. Allografts are often used for massive bone loss, but since only the marginal portion is newly vascularized after the implantation non healing fractures are often reported, along with a graft reabsorption. To overcome these problems, some studies in literature tried to conjugate bone graft and vascular supply, with encouraging results. On the other side, several studies in literature reported the ability of bone marrow derived cells to promote neo-vascularization. In fact, bone marrow contains not only hematopoietic stem cells (HSCs) and MSCs as a source for regenerating tissues but also accessory cells that support angiogenesis and vasculogenesis by producing several growth factors. In this scenario a new procedure was developed, consisting in an allogenic bone graft transplantation in a critical size defect in rabbit radius, plus a deviation at its inside of the median artery and vein with a supplement of autologous bone marrow concentrate on a collagen scaffold. Twenty-four New Zealand male white rabbits (2500–3000 g) were divided into 2 groups, each consisting of 12 animals. Surgeries were performed as follow:. −. Group 1 (#12): allogenic bone graft (left radius) / allogenic bone graft + vascular pedicle + autologous bone marrow concentrate (right radius). −. Group 2 (#12): sham operated (left radius)/ allogenic bone graft + vascular pedicle (right radius). For each group, 3 experimental time: 8, 4 and 2 weeks (4 animals for each time). The bone used as graft was previously collected from an uncorrelated study. An in vitro evaluation of bone marrow concentrate was performed in all cases, and at the time of sacrifice histological and histomorphometrical assessment were performed with immunohistochemical assays for VEGF, CD31 e CD146 to highlight the presence of vessels and endothelial cells. Micro-CT Analysis with quantitative bone evaluation was performed in all cases. The bone marrow concentrate showed a marked capability to differentiate into osteogenic, chondrogenic and agipogenic lineages. No complications such as infection or intolerance to the procedure were reported. The bone grafts showed only a partial integration, mainly at the extremities in the group with vascular and bone marrow concentrate supplement, with a good and healthy residual bone. immunohistochemistry showed an interesting higher VEGF expression in the same group. Micro CT analysis showed a higher remodeling activities in the groups treated with vascular supplement, with an area of integration at the extremities increasing with the extension of the sacrifice time. The present study suggests that the vascular and marrow cells supplement may positively influence the neoangiogenesis and the neovascularization of the homologous bone graft. A longer time of follow up and improvement of the surgical technique are required to validate the procedure

Porous collagen-glycosaminoglycan (Col/GAG) scaffolds have previously been used clinically as regeneration templates for peripheral nerves and skin. [1]. For defects involving even minimal load-bearing applications however, these scaffolds do not possess the required stiffness. Calcium phosphates (CaPs) are often used as bone-graft substitutes due to their biocompatibility and direct bone-bonding ability. While CaPs have sufficient stiffness for bone-defect applications, unlike Col/GAG they lack elasticity and are very brittle. Combining these two materials produces a composite with enhanced material properties and chemical similarity to natural bone. The addition of CaP nanocrystallites into the Col/GAG matrix produces a 3-dimensional structure that maintains its structural integrity even when wet. In this study, the in vivo performance of mineralised Col/GAG composites was evaluated by implantation into a six-week ovine bone-defect model. Four different materials were implanted; Col/GAG alone, Col/GAG with octacalcium phosphate, Col/GAG with hydroxyapatite and Col/GAG with brushite. Implants with a diameter of 9mm and length of 9mm, were placed bilaterally into the distal femoral condyle of the hind legs of thirteen sheep. This site was selected due to the large volume of load-bearing cancellous bone. Cancellous autograft was harvested from the tibial tuberosity and placed in the defect sites of two sheep as a positive control. All animals were sacrificed after 6 weeks and tissue containing the implants was prepared for histological evaluation. Image analysis of Von Kossa stained sections showed that all mineralised Col/GAG implants had significantly more bone in the implant site than unmineralised Col/GAG but were not significantly different between CaPs. Interestingly, new bone formation often followed the structure of the porous material struts which acted as a template. The defect containing the autograft contained the greatest amount of new bone. Conclusions. The inclusion of mineral substantially improves the osteoconductivity of Col/GAG. No significant difference between the different calcium phosphates was seen. Whilst these materials did not stimulate bone formation to the same extent as autograft, many bone graft procedures are carried out with allograft which performs less favourably

Abstract

The use of impacted, morsellised bone grafts has become popular in revision total hip arthroplasty (THA). The initial stability of the reconstruction and the effectiveness of any subsequent process of revitalisation and incorporation will depend on the mechanical integrity of the graft. Our aim in this study was to document the time-dependent mechanical properties of the morsellised graft. This information is useful in clinical application of the graft, in studies of migration of the implant and in the design of the joint. We used 16 specimens of impacted, morsellised cancellous bone from the sternum of goats to assess the mechanical properties by confined compression creep tests. Consideration of the graft material as a porous, permeable solid, filled with fluid, allowed determination of the compressive modulus of the matrix, and its permeability to fluid flow. In all specimens the compression tests showed large, irreversible deformations, caused by flow-independent creep behaviour as a result of rolling and sliding of the bone chips. The mean permeability was 8.82 *10. −12. m. 4. /Ns (SD 43%), and the compressive modulus was 38.7 MPa (SD 34%). No correlation was found between the apparent density and the permeability or between the apparent density and the compressive modulus. The irreversible deformations in the graft could be captured by a creep law, for which the parameters were quantified. We conclude that in clinical use the graft is bound to be subject to permanent deformation after operation. The permeability of the material is relatively high compared with, for example, human cartilage. The confined compression modulus is relatively low compared with cancellous bone of the same apparent density. Designs of prostheses used in revision surgery must accommodate the viscoelastic and permanent deformations in the graft without causing loosening at the interface

The properties of impacted morsellised bone graft (MBG) in revision total knee arthroplasty (TKA) were studied in 12 horses. The left hind metatarsophalangeal joint was replaced by a human TKA. The horses were then randomly divided into graft and control groups. In the graft group, a unicondylar, lateral uncontained defect was created in the third metatarsal bone and reconstructed using autologous MBG before cementing the TKA. In the control group, a cemented TKA was implanted without the bone resection and grafting procedure. After four to eight months, the animals were killed and a biomechanical loading test was performed with a cyclic load equivalent to the horse’s body-weight to study mechanical stability. After removal of the prosthesis, the distal third metatarsal bone was studied radiologically, histologically and by quantitative and micro CT. Biomechanical testing showed that the differences in deformation between the graft and the control condyles were not significant for either elastic or time-dependent deformations. The differences in bone mineral density (BMD) between the graft and the control condyles were not significant. The BMD of the MBG was significantly lower than that in the other regions in the same limb. Micro CT showed a significant difference in the degree of anisotropy between the graft and host bone, even although the structure of the area of the MBG had trabecular orientation in the direction of the axial load. Histological analysis revealed that all the grafts were revascularised and completely incorporated into a new trabecular structure with few or no remnants of graft. Our study provides a basis for the clinical application of this technique with MBG in revision TKA

We investigated the antibiotic concentration in fresh-frozen femoral head allografts harvested from two groups of living donors. Ten samples were collected from patients with osteoarthritis of the hip and ten from those with a fracture of the neck of the femur scheduled for primary arthroplasty. Cefazolin (1 g) was administered as a pre-operative prophylactic antibiotic. After storage at −80°C for two weeks the pattern of release of cefazolin from morsellised femoral heads was evaluated by an in vitro broth elution assay using high-performance liquid chromatography. The bioactivity of the bone was further determined with an agar disc diffusion and standardised tube dilution bioassay. The results indicated that the fresh-frozen femoral heads contained cefazolin. The morsellised bone released cefazolin for up to four days. The concentration of cefazolin was significantly higher in the heads from patients with osteoarthritis of the hip than in those with a fracture. Also, in bioassays the bone showed inhibitory effects against bacteria.

We concluded that allografts of morsellised bone from the femoral head harvested from patients undergoing arthroplasty of the hip contained cefazolin, which had been administered pre-operatively and they exhibited inhibitory effects against bacteria in vitro.

In vitro femoral studies have demonstrated the addition of hydroxyapatite (HA), to morcellised bone graft (MBG) decreases femoral prosthesis subsidence. However, with an increased risk of femoral fracture during the impaction of a MBG:HA mixture, possibly due to greater force transmission to the femoral cortex via the HA. The aim was to compare the hoop strains and subsidence of a 1:1 mixture of MBG:HA with pure bone allograft during impaction and subsequent endurance testing in a revision hip arthroplasty model. Materials and methods Large Sawbone femurs were prepared to represent a femur with bone loss (Sawbones, Sweden). 12 uniaxial strain gauges were attached to each femur at 0, 90, 180 and 270 degrees, at distal, midshaft, proximal points to measure hoop strain. Impaction grafting was performed using X-Change 2 instruments and an Instron servohydaulic machine for 2 distal impactions and 4 proximal impactions for 60 impactions each. Study groups. The study consisted of four experimental groups: 1)Pure MBG, force of 1.98 kN 2)Pure MBG, force 3.63kN. 3)1:1 mixture of MBG: porous HA (pHA), 4)1:1 mixture MBG: non porous HA (npHA). 6 samples of each group were performed. Endurance testing. The potted femur was loaded in a manner representing the walking cycle (1.98kN) at 1 Hz for 50 000 cycles. The displacement of the femoral head during loading was measured by two displacement transducers (LVDT) were mounted on aluminum brackets to measure vertical displacement and rotation. Statistical analysis. Statistical analysis was performed using a Mann – Whitney U test for total subsidence and prosthesis cyclical movement at 6 hours between the control MBG1.98 and the other experimental groups. Subsequent analysis compared pHA and npHA mixes with and HA to MBG3. 65kN. Level of significance was taken at p<0.05. Results. Distal strain gauges:. All experimental groups had a significantly greater distal hoop strain than MBG1.98 kN (p=0.004). Middle strain gauges:. No significant differences between the HA groups and MBG1.98. MBG3.65 was significantly greater (p=0.02). Top strain gauges:. No significant differences, p=0.9. Endurance testing There was a non significant trend towards decreased subsidence in the HA groups compared to the bone groups. (p=0.7) but significantly less cyclical subsidence between HA groups and MBG 1.98 (p=0.02). No difference between the MBG 3.65 kN and HA groups for the cyclical subsidence. Statistically significant difference in cyclical rotation between both the MBG1.98 and the pHA (p=0.02) and npHA(p=0.02) and the bone 3.65 and pHA and npHA groups(p=0.04). Conclusion. The addition of HA to MBG decreases total and cyclical subsidence. There were significantly greater hoop strains in the distal and midshaft strain gauges with greater impaction force and in the distal gauges with the use of HA. Endurance testing demonstrated a significant decrease in cyclical motion and cyclical rotational stability of the prosthesis with a trend to a decrease in total subsidence during endurance testing with HA groups. The addition of HA might have longer term benefits in terms of prosthesis stability and subsequent graft healing but caution is needed during impaction

In impaction grafting of contained bone defects after revision joint arthroplasty the graft behaves as a friable aggregate and its resistance to complex forces depends on grading, normal load and compaction. Bone mills in current use produce a distribution of particle sizes more uniform than is desirable for maximising resistance to shear stresses.

We have performed experiments in vitro using morsellised allograft bone from the femoral head which have shown that its mechanical properties improve with increasing normal load and with increasing shear strains (strain hardening). The mechanical strength also increases with increasing compaction energy, and with the addition of bioglass particles to make good the deficiency in small and very small fragments. Donor femoral heads may be milled while frozen without affecting the profile of the particle size. Osteoporotic femoral heads provide a similar grading of sizes, although fewer particles are obtained from each specimen. Our findings have implications for current practice and for the future development of materials and techniques.

This study investigates the use of porous biphasic ceramics as graft extenders in impaction grafting of the femur during revision hip surgery.

Impaction grafting of the femur was performed in four groups of sheep. Group one received pure allograft, group two 50% allograft and 50% BoneSave, group three 50% allograft and 50% BoneSave type 2 and group four 10% allograft and 90% BoneSave as the graft material. Function was assessed using an index of pre- and post-operative peak vertical ground reaction force ratios. Changes in bone mineral density were measured by dual energy X ray absorptiometry (DEXA) scanning. Loosening and subsidence were assessed radiographically and by histological examination of the explanted specimens.

There was no statistically significant difference between the four groups after 18 months of unrestricted functional loading for all outcome measures.

Various approaches have been implemented to enhance bone regeneration, including the utilization of autologous platelet-rich plasma and bone morphogenetic protein-2. The objective of this study was to evaluate the impact of Marburg Bone Bank-derived bone grafts in conjunction with platelet-rich plasma (PRP), recombinant human bone morphogenetic protein-2 (rhBMP-2), and zoledronic acid (ZA) on osteogenesis within rabbit bone defects. Methodology. Bone defects (5mm in diameter) were created in the femurs of 96 male rabbits. The animals were allocated into five groups: (1) bone graft + PRP (BG + PRP), (2) bone graft + 5μg rhBMP-2 (BG + rhBMP-2), (3) bone graft + 5μg ZA (BG + ZA), (4) bone graft + 10μg rhBMP-2 + 5μg ZA (BG + rhBMP-2 + ZA), and (5) bone graft (BG). Marburg Bone Bank-processed human femoral head allografts were utilized for bone grafting. The rabbits were euthanized at 14-, 30-, and 60-days post-surgery, and their femurs underwent histopathological and histomorphometric assessments. Results. Histomorphometric analysis revealed significantly enhanced de novo osteogenesis within the bone allografts in the BG + PRP and BG + rhBMP-2 groups compared to the BG, BG + ZA, and BG + rhBMP-2 + ZA groups at 14 and 30 days (p < 0.05). However, on day 60, the BG + rhBMP-2 group exhibited elevated osteoclastic activity (early resorption). The local co-administration of ZA with thermally treated grafts impeded both bone graft resorption and new bone formation within the bone defect across all time points. The addition of ZA to BG + rhBMP-2 resulted in diminished osteogenic activity compared to the BG + rhBMP-2 group (p < 0.000). Conclusion. The study findings indicated that the combination of PRP and rhBMP-2 with Marburg bone grafts facilitates early-stage osteogenesis in bone defect healing. Incorporating ZA into the thermally treated bone graft hinders both graft resorption and de novo bone formation

To design slow resorption patient-specific bone graft whose properties of bone regeneration are increased by its geometry and composition and to assess it in in-vitro and in-vivo models. A graft composed by hydroxyapatite (HA) and β-TCP was designed as a cylinder with 3D gyroid porosities and 7 mm medullary space based on swine's anatomy. It was produced using a stereolithography 3D-printing machine (V6000, Prodways). Sterile bone grafts impregnated with or without a 10µg/mL porcine BMP-2 (pBMP-2) solution were implanted into porcine femurs in a bone loss model. Bone defect was bi-weekly evaluated by X-ray during 3 months. After sacrifice, microscanner and non-decalcified histology analysis were conducted on biopsies. Finally, osteoblasts were cultured inside the bone graft or in monolayer underneath the bone graft. Cell viability, proliferation, and gene expression were assessed after 7 and 14 days of cell culture (n=3 patients). 3D scaffolds were successfully manufactured with a composition of 80% HA and 20% β-TCP ±5% with indentation compressive strength of 4.14 MPa and bending strength of 11.8MPa. In vivo study showed that bone regeneration was highly improved in presence of pBMP-2. Micro-CT shows a filling of the gyroid sinuses of the implant (Figure 1). In vitro, the presence of BMP2 did not influence the viability of the osteoblasts and the mortality remained below 3%. After 7 days, the presence of BMP2 in the scaffold significantly increased by 85 and 65% the COL1A1 expression and by 8 and 33-fold the TNAP expression by osteoblasts in the monolayer or in the scaffold, respectively. This BMP2 effect was transient in monolayer and did not modify gene expression at day 14. BMP2-impregnated bone graft is a promising patient-personalized 3D-printed solution for bone defect regeneration, by promoting neighboring host cells recruitment and solid new bone formation. For any figures and tables, please contact the authors directly

Our objective was to conduct a systematic review and meta-analysis, comparing differences in clinical outcomes between either autologous or synthetic bone grafts in the operative management of tibial plateau fractures: a traumatic pattern of injury, associated with poor long-term functional prognosis. A structured search of MEDLINE, EMBASE, The Bone & Joint and CENTRAL databases from inception until 07/28/2021 was performed. Randomised, controlled, clinical trials that compared autologous and synthetic bone grafts in tibial plateau fractures were included. Preclinical studies, clinical studies in paediatric patients, pathological fractures, fracture non-union or chondral defects were excluded. Outcome data was assessed using the Risk of Bias 2 (ROB2) framework and synthesised in random-effect meta-analysis. Preferred Reported Items for Systematic Review and Meta-Analysis guidance was followed throughout. Six comparable studies involving 352 patients were identified from 3,078 records. Following ROB2 assessment, five studies (337 patients) were eligible for meta-analysis. Within these studies, more complex tibia plateau fracture patterns (Schatzker IV-VI) were predominant. Primary outcomes showed non-significant reductions in articular depression at immediate postoperative (mean difference −0.45mm, p=0.25, 95% confidence interval (95%CI): −1.21-0.31mm, I. 2. =0%) and long-term (>6 months, standard mean difference −0.56, p=0.09, 95%CI: −1.20-0.08, I. 2. =73%) follow-up in synthetic bone grafts. Secondary outcomes included mechanical alignment, limb functionality, defect site pain, occurrence of surgical site infections, secondary surgery, perioperative blood loss, and duration of surgery. Blood loss was lower (90.08ml, p<0.001, 95%CI: 41.49-138.67ml, I. 2. =0%) and surgery was shorter (16.17minutes, p=0.04, 95%CI: 0.39-31.94minutes, I. 2. =63%) in synthetic treatment groups. All other secondary measures were statistically comparable. Our findings supersede previous literature, demonstrating that synthetic bone grafts are non-inferior to autologous bone grafts, despite their perceived disadvantages (e.g. being biologically inert). In conclusion, surgeons should consider synthetic bone grafts when optimising peri-operative patient morbidity, particularly in complex tibial plateau fractures, where this work is most applicable