The number of total knee arthroplasties continues to increase annually with over 90,000 total knee replacements performed in the United Kingdom in 2018. Multiple national bodies including the British Association for Surgery of the Knee (BASK) and the British Orthopaedic Association collaborated in July 2019 to produce best practice guidance for knee arthroplasty surgery. This study aims to review practice in a regional healthcare trust against these guidelines. Fifty total knee replacement operation notes were reviewed between January and February 2020 from 11 different consultant orthopaedic surgeons. Documents were assessed against 17 criteria recommended by the BASK guidance. Personnel names and grades were generally well documented. Tourniquet time and pressure were documented in over 98% of operation notes however, protection from spirit burns was not documented at all. Trialling and soft tissue balancing was well recorded in 100% and 96% of operation notes respectively. Areas lacking in documentation included methods utilised to optimise cementation technique and removal of cement debris. Protection of key knee structures was documented in only 56% of operation notes clearly. Prior to closure, final assessment of mechanism integrity, collateral ligament was not documented at all and final ROM after implantation of components was recorded 34% of the time. Subsequently authors have created a universal operation note template, uploaded onto the patient electronic notes, which prompts surgeons to complete documentation of the relevant criteria advocated by BASK. In conclusion, detailed and systematic documentation is vital to prevent adverse events and reduce the risk of litigation. By producing detailed operative templates this risk can be mitigated

We performed 83 consecutive cemented revision total hip arthroplasties in 77 patients between 1977 and 1983 using improved cementing techniques. One patient (two hips) was lost to follow-up. The remaining 76 patients (81 hips) had an average age at revision of 63.7 years (23 to 89). At the final follow-up 18 hips (22%) had had a reoperation, two (2.5%) for sepsis, three (4%) for dislocation and 13 (16%) for aseptic loosening. The incidence of rerevision for aseptic femoral loosening was 5.4% and for aseptic acetabular loosening 16%. These results confirm that cemented femoral revision is a durable option in revision hip surgery when improved cementing techniques are used, but that cemented acetabular revision is unsatisfactory

We examined the roles of methylmethacrylate (MMA) monomer and cementing technique in the formation, and haemodynamic outcome, of pulmonary fat emboli. The preparation of the femoral canal and the cementing technique were studied in four groups of adult dogs as follows: control (no preparation); lavage; cement pressurisation; and cement pressurisation after lavage. We measured the intramedullary pressure, pulmonary artery pressure (PAP), pulmonary capillary wedge pressure and bilateral femoral vein levels of triglyceride, cholesterol and MMA monomer at rest and after reaming, lavage, and cementing. Femoral vein triglyceride and cholesterol levels did not vary significantly from resting levels despite significant elevations in intramedullary pressure with reaming, lavage and cementing (p = 0.001). PAP was seen to rise significantly with reaming (p = 0.0038), lavage (p = 0.0031), cementing (p = 0.0024) and cementing after lavage (p = 0.0028) while the pulmonary capillary wedge pressure remained unchanged. MMA monomer was detected in femoral vein samples when cement pressurisation was used. Intramedullary lavage before cementing had no significant effect on the MMA level. Haemodynamic evidence of pulmonary embolism was noted with reaming and intramedullary canal preparation, irrespective of the presence of MMA monomer. We found no relationship between MMA monomer level and intramedullary pressure, PAP or pulmonary capillary wedge pressure. Our findings suggest that the presence of MMA monomer in femoral venous blood has no effect on the formation of fat emboli or their pulmonary haemodynamic outcome during cemented hip arthroplasty

Background. Aseptic loosening of cemented femoral stems results from migration of wear particles along the bone-cement interface, producing a foreign body reaction. After cement insertion, blood back pressure can disrupt the bone-cement interface, enabling this spread of wear particles. Our study investigates whether altering timing and speed of stem insertion can reduce this risk. Methods. We inserted mock “C-Stem” femoral components (De Puy-Synthes), using Smartset HV cement (De Puy-Synthes) into artificial femora, fitted with proximal and distal pressure transducers. Cement insertion began two, three or four minutes after mixing. Cement pressures were then allowed to settle for one minute and the stems were then inserted over durations of 25, 60 or 90 seconds. Results. Quicker insertion led to high peak pressures; however insertion over 90 seconds at 4 and 5 minutes achieved more sustained pressures above blood back pressure. Slower insertion particularly improved proximal pressurisation. Furthermore when the stem was inserted over 90 seconds at 5 minutes then the cement pressures remained high after full insertion of the stem. Conclusions. Commonly, femoral stems are inserted rapidly. Our study demonstrates that by inserting the femoral stem more slowly, cement pressure can be maintained above blood back pressure for longer. We believe that after slower stem insertion, the higher cement viscosity enables the surgeon to maintain cement pressure, via the stem, sufficient to resist blood back pressure without inadvertently over inserting the stem. This safe and simple modification of cementing technique generates higher and more sustained cement pressures. Level of evidence. 3. Disclosures. Depuy-Synthes kindly provided the equipment used in the study. None of the authors received any payment or other benefits

A complete cement mantle is important for the longevity of a total hip replacement. In the minimally-invasive direct anterior approach used at the Innsbruck University hospital, the femoral component has to be inserted into the femoral canal by an angulated movement. In a cadaver study, the quality and the extent of the cement mantle surrounding 13 Exeter femoral components implanted straight through a standard anterolateral transgluteal approach were compared with those of 13 similar femoral components implanted in an angulated fashion through a direct anterior approach. A third-generation cementing technique was used. The inner and outer contours of the cement mantles was traced from CT scans and the thickness and cross-sectional area determined. In no case was the cement mantle incomplete. The total mean thickness of the cement mantle was 3.62 mm (95% confidence interval 3.59 to 3.65). The mean thickness in the group using the minimally-invasive approach was 0.16 mm less than that in the anterolateral group. The distribution of the thickness was similar in the two groups. The mean thickness was less on the anteromedial and anterolateral aspect than on the posterior aspect of the femur. There is no evidence that the angulated introduction of Exeter femoral components in the direct anterior approach in cadavers compromises the quality, extent or thickness of the cement mantle

The ‘cement reaction’ is a recognised cardio-respiratory response to methylmethacrylate bone cement, characterised by hypotension, reduced cardiac output, and on occasion fatal circulatory collapse. It is seen in 0.5-1% of cemented hip arthroplasties during the insertion and pressurisation of cement into the femur, and is believed to be secondary to marrow thromboembolism, the vasodilatory effect of methylmethacrylate, or a combination of the two. A number of steps, within the operating surgeon's control, can be undertaken to reduce the risk of the ‘cement reaction’ occurring. An e-mail based questionnaire was sent to all trainees and consultants in the West of Scotland containing eight questions relating to cementing technique when performing hemiarthroplasty of the hip. The questions related to measures to reduce the potential for ‘cement reaction’, e.g.: whether or not they routinely use a cement restrictor. Seventy-two complete replies were received. For five of the eight measures, the surgeons routinely employed the suggested practices. For the remaining three, the consensus opinion was contrary to the suggested practice for reduction of the risk of ‘cement reaction’. These were with respect to the surgical approach employed, whether or not to attempt to remove all cancellous bone from the proximal femur, and the use, or not, of a venting tube during cement insertion. In all three cases, the difference was statistically significant on chi-squared testing. The cohort of surgeons questioned routinely employ more than half of the methods suggested to reduce the potential for ‘cement reaction’ in hemiarthroplasty of the hip. Further surveys of why they do, or do not, undertake certain practices during cementing would help improve awareness of ‘cement reaction’, and perhaps reduce the incidence of this potentially fatal phenomenon

Fatigue fractures which originate at stress-concentrating voids located at the implant-cement interface are a potential cause of septic loosening of cemented femoral components. Heating of the component to 44°C is known to reduce the porosity of the cement-prosthesis interface. The temperature of the cement-bone interface was recorded intra-operatively as 32.3°C. A simulated femoral model was devised to study the effect of heating of the component on the implant-cement interface. Heating of the implant and vacuum mixing have a synergistic effect on the porosity of the implant-cement interface, and heating also reverses the gradients of microhardness in the mantle. Heating of the implant also reduces porosity at the interface depending on the temperature. A minimum difference in temperature between the implant and the bone of 3°C was required to produce this effect. The optimal difference was 7°C, representing a balance between maximal reduction of porosity and an increased risk of thermal injury. Using contemporary cementing techniques, heating the implant to 40°C is recommended to produce an optimum effect

We have compared the interface morphology at the stem-cement interface of standard Charnley stems with a satin finish (Ra = 0.75 μm) with identical stems which had been grit-blasted over their proximal third (Ra = 5.3 μm) to promote a proximal bond. The stems were cemented into cadaver femora using conventional contemporary cementing techniques. After transverse sectioning, we determined the percentage of the perimeter of the stem which had a gap at the interface. There were substantial gaps (mean 31.4 ± 17.1%) at the stem-cement interface in the grit-blasted region. This fraction was significantly (paired t-test, p = 0.0054) higher than that found around the contralateral satin-finished stems (mean 7.7 ± 11.7%). Although studies of isolated metal-cement interfaces have shown that the bond strength can increase with surface roughness it cannot be assumed that this effect will be observed under clinical conditions

The outcome of a cemented hip arthroplasty is partly dependent on the type of cement which is used. The production of an interface gap between the stem and the cement mantle as a result of shrinkage of the cement, may be a factor involved. Palacos R, Palacos LV (both with gentamicin), CMW 1, CMW 2, CMW Endurance (CMWE) and Simplex were prepared under vacuum and allowed to cure overnight in similar cylinders. The next day this volume was determined by the displacement of water. Shrinkage varied between 3.82% and 7.08% with CMWE having the lowest and Palacos LV the highest. This could be a factor to consider when choosing a cement for a shape-closed stem.

The aim of our study was to investigate whether placing of the femoral component of a hip resurfacing in valgus protected against spontaneous fracture of the femoral neck.

We performed a hip resurfacing in 20 pairs of embalmed femora. The femoral component was implanted at the natural neck-shaft angle in the left femur and with a 10° valgus angle on the right. The bone mineral density of each femur was measured and CT was performed. Each femur was evaluated in a materials testing machine using increasing cyclical loads.

In specimens with good bone quality, the 10° valgus placement of the femoral component had a protective effect against fractures of the femoral neck. An adverse effect was detected in osteoporotic specimens.

When resurfacing the hip a valgus position of the femoral component should be achieved in order to prevent fracture of the femoral neck. Patient selection remains absolutely imperative. In borderline cases, measurement of bone mineral density may be indicated.

The role of vacuum mixing on the reduction of porosity and on the clinical performance of cemented total hip replacements remains uncertain. We have used paired femoral constructs prepared with either hand-mixed or vacuum-mixed cement in a cadaver model which simulated intra-operative conditions during cementing of the femoral component. After the cement had cured, the distribution of its porosity was determined, as was the strength of the cement-stem and cement-bone interfaces.

The overall fraction of the pore area was similar for both hand-mixed and vacuum-mixed cement (hand 6%; vacuum 5.7%; paired t-test, p = 0.187). The linear pore fractions at the interfaces were also similar for the two techniques. The pore number-density was much higher for the hand-mixed cement (paired t-test, p = 0.0013). The strength of the cement-stem interface was greater with the hand-mixed cement (paired t-test, p = 0.0005), while the strength of the cement-bone interface was not affected by the conditions of mixing (paired t-test, p = 0.275). The reduction in porosity with vacuum mixing did not affect the porosity of the mantle, but the distribution of the porosity can be affected by the technique of mixing used.

This study explored the relationship between the initial stability of the femoral component and penetration of cement into the graft bed following impaction allografting.

Impaction allografting was carried out in human cadaveric femurs. In one group the cement was pressurised conventionally but in the other it was not pressurised. Migration and micromotion of the implant were measured under simulated walking loads. The specimens were then cross-sectioned and penetration of the cement measured.

Around the distal half of the implant we found approximately 70% and 40% of contact of the cement with the endosteum in the pressure and no-pressure groups, respectively. The distal migration/micromotion, and valgus/varus migration were significantly higher in the no-pressure group than in that subjected to pressure. These motion components correlated negatively with the mean area of cement and its contact with the endosteum.

The presence of cement at the endosteum appears to play an important role in the initial stability of the implant following impaction allografting.

We have investigated the role of the penetration of saline on the shear strength of the cement-stem interface for stems inserted at room temperature and those preheated to 37°C using a variety of commercial bone cements. Immersion in saline for two weeks at 37°C reduced interfacial strength by 56% to 88% after insertion at room temperature and by 28% to 49% after preheating of the stem. The reduction in porosity as a result of preheating ranged from 71% to 100%. Increased porosity correlated with a reduction in shear strength after immersion in saline (r = 0.839, p < 0.01) indicating that interfacial porosity may act as a fluid conduit.

The Capital Hip implant was a Charnley-based system which included a flanged and a roundback stem, both of which were available in stainless steel and titanium. The system was withdrawn from the market because of its inferior performance. However, all four of the designs did not produce poor rates of survival. Using a simulated-based, finite-element analysis, we have analysed the Capital Hip system. Our aim was to investigate whether our simulation was able to detect differences which could account for the varying survival between the Capital Hip designs, thereby further validating the simulation.

We created finite-element models of reconstructions with the flanged and roundback Capital Hips. A loading history was applied representing normal walking and stair-climbing, while we monitored the formation of fatigue cracks in the cement.

Corresponding to the clinical findings, our simulation was able to detect the negative effects of the titanium material and the flanged design in the Capital Hip system. Although improvements could be made by including the effect of the roughness of the surface of the stem, our study increased the value of the model as a predictive tool for determining failure of an implant.

Normal function of the patellofemoral joint is maintained by a complex interaction between soft tissues and articular surfaces. No quantitative data have been found on the relative contributions of these structures to patellar stability. Eight knees were studied using a materials testing machine to displace the patella 10 mm laterally and medially and measure the force required. Patellar stability was tested from 0° to 90° knee flexion with the quadriceps tensed to 175 N. Four conditions were examined: intact, vastus medialis obliquus relaxed, flat lateral condyle, and ruptured medial retinaculae. Abnormal trochlear geometry reduced the lateral stability by 70% at 30° flexion, while relaxation of vastus medialis obliquus caused a 30% reduction. Ruptured medial retinaculae had the largest effect at 0° flexion with 49% reduction. There was no effect on medial stability. There is a complex interaction between these structures, with their contributions to loss of lateral patellar stability varying with knee flexion.

Post-mortem retrieval of canine, cemented femoral components was analysed to assess the performance of these implants in the dog as a model for human total hip replacement (THR). Mechanical testing and radiological analysis were performed to determine the stability of the implant and the quality of the cement. Thirty-eight implants from 29 dogs were retrieved after time intervals ranging from 0.67 to 11.67 years. The incidence of aseptic loosening was 63.2%, much higher than in human patients (6% in post-mortem studies). Failure of the femoral implants began with debonding at the cement-metal interface, similar to that in implants in man. The incidence of aseptic loosening was much lower in bilateral than in unilateral implants. Significant differences were observed for three different designs of implant. While the dog remains the animal model of choice for THR, results from this study provide insight into interspecies differences in the performance of implants. For example, the performance of THR in dogs should be compared with that in young rather than in elderly human patients.