Aims. To report our experience with trunnion corrosion following metal-on-polyethylene total hip arthroplasty, in particular to report the spectrum of presentation and determine the mean time to presentation. Patients and Methods. We report the presenting symptoms and signs, intraoperative findings, and early results and complications of operative treatment in nine patients with a mean age of 74 years (60 to 86). The onset of symptoms was at a mean of seven years (3 to 18) after index surgery. Results. Patients presented with a variety of symptoms including pain, limp and rash. The preoperative mean serum cobalt level was 7.1 ppb (2.2 to 12.8) and mean serum chromium level was 2.2 ppb (0.5 to 5.2). Metal artifact reduction sequence (MARS) MRI showed fluid collection and possible pseudotumour formation in five hips, fluid collection in two hips, and synovitis/debris in one hip, with no MRI in one patient. Acetabular revision was performed in three patients, six patients underwent liner and head exchange only. The postoperative metal levels decreased in all patients: mean cobalt 0.5 ppb (0 to 1.8) and mean chromium 0.9 ppb (0 to 2.6) at a mean of five months (3 to 8) postoperatively. Seven patients had good pain relief and no complications at one year. There were two major complications requiring reoperation: acute infection at six weeks, for which the patient required two-stage reimplantation; and recurrent dislocation, for which the patient was revised to a dual mobility component. Conclusion. Trunnion corrosion in metal-on-polyethylene THA has a range of presenting symptoms, and may present later than previously described. A high index of suspicion is warranted, and serum cobalt and chromium levels are recommended for diagnosis. Patients should be counselled about possible postoperative complications. Cite this article: Bone Joint J 2018;100-B:898–902

Aims. To present a surgically relevant update of trunnionosis. . Materials and Methods. Systematic review performed April 2017. Results. Trunnionosis accounts for approximately 2% of the revision total hip arthroplasty (THA) burden. Thinner (reduced flexural rigidity) and shorter trunnions (reduced contact area at the taper junction) may contribute to mechanically assisted corrosion, exacerbated by high offset implants. The contribution of large heads and mixed metallurgy is discussed. Conclusion. Identifying causative risk factors is challenging due to the multifactorial nature of this problem. Cite this article: Bone Joint J 2018;100-B(1 Supple A):44–9

Modular femoral stems offer surgeons great flexibility in biomechanical configuration during total hip replacement (THR) however introduce a taper-trunnion articulation known to be a source of additional wear debris through crevice, fretting and galvanic corrosion with mixed material combinations. This study aimed to investigate the influence of the trunnion bearing surface combination on the revision rate following primary total hip replacement (THR). All patients who underwent THR using an Exeter V40 cemented stainless steel stem and monobloc cemented polyethylene acetabular component (uncemented cups excluded to standardise the acetabular bearing surface and fixation) between January 2003 and December 2019 were extracted from the National Joint Registry for England, Wales, Northern Ireland, and the Isle of Man. The primary exposure was the head substrate used corresponding to the trunnion bearing. Time-to-event was determined by duration of implantation from primary surgery to revision with cases censored at death or end of available follow-up. Multivariable Cox proportional hazard models were used to identify predictors of all cause revision, adjusted for age, sex, American Association of Anaesthesiologists (ASA) grade, body mass index, surgical indication (osteoarthritis or other), and femoral head size. 229,870 THR were identified (66% female, mean age 73.4 years (SD 9.1) with the majority (91%) performed for osteoarthritis of which 4,598 were revised. Mean time from primary to revision or censoring was 6.8 years (SD 4.0). Multivariable modelling showed CoCr/SS trunnions were associated with a significantly higher risk of revision (hazard ratio (HR) 1.31 (95%CI 1.15 to 1.48, p<0.0001) as compared to SS/SS (reference). Both Alumina/SS (HR 0.74 (0.65 to 0.84), p<0.0001) and Zirconia/SS (HR 0.61 (0.49 to 0.74), p<0.0001) were associated with a significantly lower risk of revision. Ceramic heads on an Exeter stem were associated with significantly improved survivorship compared to metal heads in primary THR. CoCr/SS trunnion articulations had the poorest survivorship which may be contributed to by trunnionosis

Trunnion corrosion in metal-on-polyethylene THA is poorly understood, with multifactorial etiology, and the patients present with “hip pain”. We analysed the presenting symptoms and signs, intraoperative findings and the early results and complications of operative treatment. One surgeon treated 9 patients (6 male, 3 female), mean age 74 years, with the onset of symptoms at a mean of 7 years (range 3–18) after index surgery. The taper size was 12/14 in seven, 14/16 in one, and 6 degree in one hip. The preoperative mean cobalt level was 7.1 ppb (range, 2.2–12.8) and mean chromium level was 2.2 ppb (range, 0.5–5.2). MARS MRI showed fluid collection and pseudotumor in 5, fluid collection only in two, and synovitis/debris in one hip. In one patient, there was no preoperative MRI. There were a myriad of clinical presentations: thigh rash alone in one; diffuse leg pain and hip rash in one; acute pseudo-sepsis in one; iliopsoas tendinitis and diffuse rash in one; trochanteric bursitis in one; groin pain only in one; thigh-buttock pain in two; and diffuse hip pain and limp in one patient. Intraoperatively, 6 patients had liner and ceramic (or oxidized zirconium) head exchange only. Three patients had concurrent acetabular revision: one for broken locking mechanism; one because liner was unavailable, and one had acetabular loosening. The postoperative metal levels decreased in all patients: mean cobalt 0.5 ppb (range, 0–1.8) and mean chromium 0.9 ppb (range, 0–2.6). Seven patients had good pain relief and no complications. There were two major complications requiring reoperation: acute infection at 6 weeks and patient required 2-stage reimplantation; and second patient had recurrent dislocation and was revised to a dual mobility component. Trunnion corrosion in metal-on-polyethylene THA has several clinical presentations, including local skin rash, iliopsoas tendinitis, and other limb dysfunction. There should be a high index of suspicion and serum cobalt/chromium levels are recommended for diagnosis. The patients should be counseled about possible postoperative complications

Fracture of contemporary femoral stems is a rare occurrence. Earlier THR stems failed due to design issues or post manufacturing heat treatments that weakened the core metal. Our group identified and analyzed 4 contemporary fractured femoral stems after revision surgery in which electrochemical welds contributed to the failure.

All four stems were proximally porous coated titanium alloy components. All failures occurred in the neck region post revision surgery in an acetabular cup exchange. All were men and obese. The fractures occurred at an average of 3.6 years post THR redo (range, 1.0–6.5 years) and 8.3 years post index surgery (range, 5.5–12.0 years). To demonstrate the effect of electrocautery on retained femoral stems following revision surgery, we applied intermittent electrosurgical currents at three intensities (30, 60, 90 watts) to the polished neck surface of a titanium alloy stem under dry conditions.

At all power settings, visible discoloration and damage to the polished neck surface was observed. The localized patterns and altered metal surface features exhibited were like the electrosurgically-induced damage priorly reported.

The neck regions of all components studied displayed extensive mechanical and/or electrocautery damage in the area of fracture initiation. The use of mechanical instruments and electrocautery was documented to remove tissues in all 4 cases.

The combination of mechanical and electrocautery damage to the femoral neck and stem served as an initiation point and stress riser for subsequent fractures. The electrocautery and mechanical damage across the fracture site observed occurred iatrogenically during revision surgery. The notch effect, particularly in titanium alloys, due to mechanical and/or electrocautery damage, further reduced the fatigue strength at the fractured femoral necks. While electrocautery and mechanical dissection is often required during revision THA, these failures highlight the need for caution during this step of the procedure in cases where the femoral stem is retained.

Adverse reaction to wear and corrosion debris is a cause for concern in total hip arthroplasty (THA). Modular junctions are a potential source of such wear products and are associated with secondary pseudotumour formation.

We present a consecutive series of 17 patients treated at our unit for this complication following metal-on-highly cross-linked polyethylene (MoP) THA. We emphasise the risk of misdiagnosis as infection, and present the aggregate laboratory results and pathological findings in this series.

The clinical presentation was pain, swelling or instability. Solid, cystic and mixed soft-tissue lesions were noted on imaging and confirmed intra-operatively. Corrosion at the head–neck junction was noted in all cases. No bacteria were isolated on multiple pre- and intra-operative samples yet the mean erythrocyte sedimentation rate was 49 (9 to 100) and C-reactive protein 32 (0.6 to 106) and stromal polymorphonuclear cell counts were noted in nine cases.

Adverse soft–tissue reactions can occur in MoP THA owing to corrosion products released from the head–neck junction. The diagnosis should be carefully considered when investigating pain after THA. This may avoid the misdiagnosis of periprosthetic infection with an unidentified organism and mitigate the unnecessary management of these cases with complete single- or two-stage exchange.

Cite this article: Bone Joint J 2015;97-B:1024–1030.

Aims

We present a case series of ten metal-on-polyethylene total hip arthroplasties (MoP THAs) with delayed dislocation associated with unrecognised adverse local tissue reaction due to corrosion at the trunnion and pseudotumour formation.

Aims. The aim of this study was to compare the design of the generic OptiStem XTR femoral stem with the established Exeter femoral stem. Materials and Methods. We obtained five boxed, as manufactured, implants of both designs at random (ten in total). Two examiners were blinded to the implant design and independently measured the mass, volume, trunnion surface topography, trunnion roughness, trunnion cone angle, Caput-Collum-Diaphyseal (CCD) angle, femoral offset, stem length, neck length, and the width and roughness of the polished stem shaft using peer-reviewed methods. We then compared the stems using these parameters. Results. We found that the OptiStems were lighter (p < 0.001), had a rougher trunnion surface (p <  0.001) with a greater spacing and depth of the machined threads (p < 0.001), had greater trunnion cone angles (p = 0.007), and a smaller radius at the top of the trunnion (p = 0.007). There was no difference in stem volume (p = 0.643), CCD angle (p = 0.788), offset (p = 0.993), neck length (p = 0.344), stem length (p = 0.808), shaft width (p = 0.058 to 0.720) or roughness of the polished surface (p = 0.536). Conclusion. This preliminary investigation found that whilst there were similarities between the two designs, the generic OptiStem is different to the branded Exeter design. Cite this article: Bone Joint J 2017;99-B:310–16

Several implants have a proven track record of durability and function in patients over many years. As manufacturers' patents expire it is understandable that cheaper generic copies would be considered. There is currently no established, independent method of determining design equivalence between generic and branded orthopaedic implants. We acquired 10 boxed, as manufactured components consisting of the generic OptiStem XTR model (n=5) and branded Exeter (n=5) femoral stems. Two examiners were blinded to the implant design and independently measured the mass, volume, trunnion surface topography, roughness, trunnion cone angle, CCD angle and femoral offset using peer-reviewed methods. We then compared the stems using these parameters. We found that the OptiStems (1) were lighter (p<0.001) (2) had a rougher trunnion surface (p<0.001) with a greater spacing and depth of the machined threads (p<0.001), (3) had greater trunnion cone angles (p=0.007) and (4) a smaller radius at the top of the trunnion (p=0.007). There was no difference for stem volume (p=0.643), CCD angle (p=0.788) or offset (p=0.993). This study is the first independent investigation of the equivalence of a generic orthopaedic implant to its branded design. We found a clear difference in trunnion roughness, trunnion cone angle and radius, and implant mass when comparing the two generic and branded stem designs. All implants require standard regulatory processes to be followed. It does not appear feasible that generic implants can be manufactured to predictability guarantee the same performance as generic drugs. We found a number of physical differences between the generic and branded implants. Whilst both designs are likely to work in clinical practice, they are different

Introduction. Trunnion wear has been reported as a cause for failure of modern total hip replacement implants. While there are several reports on the prevalence of trunnion corrosion with specific stem designs, little is known about the prevalence of this problem across other femoral stem designs. The purpose of this study is to review three commonly used uncemented femoral stems and to correlate any established risk factors with rates of revision. Methods. We reviewed all patients followed prospectively over a 15-year period (March 2000 to September 2015) who underwent total hip arthroplasty with one of three modern uncemented femoral stem designs. All of the stems were made of titanium (Ti. 6. Al. 4. V alloy) with a 12/14 taper design. We included only metal (cobalt chromium) on highly cross-linked polyethylene articulations. We evaluated age, gender, body mass index (BMI), femoral head size, head length, neck angle and offset as potential risk factors for all cause revision and revision excluding infection by univariate analysis. We performed a logistic regression analysis with odds ratios (OR) for each parameter for both all cause revision as well as with infection excluded. We used a p value of <0.05 as a level of significance. Results. A total of 2095 patients were included during the study period and had a minimum three-year follow-up. There were no differences in age, gender, or BMI across the three femoral component groups. There were no cases of trunnion wear or corrosion (with or without an associated adverse local tissue reaction) requiring revision identified across all three stem groups. Univariate logistic regression analysis demonstrated that head size was associated with increased risk of both all cause revision and revision excluding infection. Age, BMI, gender, offset and neck angle did not have significant association to all cause revision or to revisions excluding infection (p>0.05). Multivariate logistic regression controlling for age and BMI demonstrated that a femoral head size less than 32mm was associated with increased likelihood of all cause revision rates (OR 4.60 (95%CI 1.8, 11.8)) and revision excluding infection (OR 4.94 (95%CI 1.7, 14.41). Conclusions. None of the patients who received one of the three modern uncemented femoral stem designs in this cohort demonstrated trunnion wear or corrosion requiring revision for adverse local soft tissue reactions. We recognize that low-levels of corrosion might exist in this cohort and therefore continued follow-up of these patients is required. For any tables or figures, please contact the authors directly

Objectives. The use of ceramic femoral heads in total hip arthroplasty (THA) has increased due to their proven low bearing wear characteristics. Ceramic femoral heads are also thought to reduce wear and corrosion at the head-stem junction with titanium (Ti) stems when compared with metal heads. We sought to evaluate taper damage of ceramic compared with metal heads when paired with cobalt chromium (CoCr) alloy stems in a single stem design. Methods. This retrieval study involved 48 total hip arthroplasties (THAs) with CoCr V40 trunnions paired with either CoCr (n = 21) or ceramic (n = 27) heads. The taper junction of all hips was evaluated for fretting/corrosion damage and volumetric material loss using a roundness-measuring machine. We used linear regression analysis to investigate taper damage differences after adjusting for potential confounding variables. Results. We measured median taper material loss rates of 0.210 mm. 3. /year (0.030 to 0.448) for the metal head group and 0.084 mm. 3. /year (0.059 to 0.108) for the ceramic group. The difference was not significant (p = 0.58). Moreover, no significant correlation between material loss and implant or patient factors (p > 0.05) was found. Conclusions. Metal heads did not increase taper damage on CoCr trunnions compared with ceramic heads from the same hip design. The amount of material released at the taper junctions was very low when compared with available data regarding CoCr/Ti coupling in metal-on-metal bearings. Cite this article: A. Di Laura, H. Hothi, J. Henckel, I. Swiatkowska, M. H. L. Liow, Y-M. Kwon, J. A. Skinner, A. J. Hart. Retrieval analysis of metal and ceramic femoral heads on a single CoCr stem design. Bone Joint Res 2017;6:–350. DOI: 10.1302/2046-3758.65.BJR-2016-0325.R1

The purpose was to determine the lifetime risk of re-operation due to specific complications related to dual mobility using re-operation as a competing risk, excluding loosening, periprosthetic fracture, and infection. 1503 mono-block dual mobility total hip arthroplasty (DM-THAs). Defining the re-operation when anesthesia (for dislocation) and revision when the implant changed. Surgery (801 for primary, 702 for revision with 201 for recurrent dislocation and 501 for loosening) performed between 1990 and 2020 in average 81-year-old (range 50–102) patients, with 522 living patients at 10 years follow-up. During the first month, outer dislocation (60 cases; 4%) was the cause re-operation (1% among primary and 6 % among revisions). Twenty-four intra-prosthetic dislocations (IPD) were an iatrogenic consequence of a failed closed reduction (reduction maneuver dissociating the inner head) with 1.6% revision. Between 1 month and 1 year, 22 new outer dislocations, while 25 of the 60 “first month” dislocations had recurrent dislocation. Fifteen other IPDs as iatrogenic consequences were observed. At one year, the cumulative revision was 3% (49 of 82 dislocations). Between 1- 10-year FU, 132 other dislocations, and 45 other revisions for dislocations were observed. Corrosion was another cause of revision (37 cases): between the cobalt-chromium shell and the femoral neck (23 hips), or 14 crevice corrosion between the trunnion and the metal head (trunnion damage). In summary, at 10-year: dislocation first cause of re-operation (214 anesthesia, 14%), while among 131 revisions (8.9 %) the 55 iatrogenic intra-prosthetic dislocations were the first revision cause before 39 recurrent dislocations and 37 corrosions. The 522 patients followed ten years or more had a 15% risk revision due to DM specific complications during their lifetime and 10% more risk associated with loosening (6%), periprosthetic fracture (2%) and infection (2%)

Aims. We have previously demonstrated raised cobalt and chromium levels in patients with larger diameter femoral heads, following metal-on-polyethylene uncemented total hip arthroplasty. Further data have been collected, to see whether these associations have altered with time and to determine the long-term implications for these patients and our practice. Methods. Patients from our previous study who underwent Trident-Accolade primary total hip arthroplasties using a metal-on-polyethylene bearing in 2009 were reviewed. Patients were invited to have their cobalt and chromium levels retested, and were provided an Oxford Hip Score. Serum ion levels were then compared between groups (28 mm, 36 mm, and 40 mm heads) and over time. Results. Metal ion levels were repeated in 33 patients. When comparing the results of serum metal ion levels over time, regardless of head size, there was a significant increase in both cobalt and chromium levels (p < 0.001). Two patients with larger head sizes had undergone revision arthroplasty with evidence of trunnion damage at surgery. Two patients within the 40 mm subgroup had metal ion levels above the MHRA (Medicines and Healthcare Products Regulatory Agency) threshold for detailed investigation. The increase in cobalt and chromium, when comparing the 36 mm and 40 mm groups with those of the 28 mm group, was not significant (36 mm vs 28 mm; p = 0.092/p = 0.191; 40 mm vs 28 mm; p = 0.200/p = 0.091, respectively). There was no difference, between femoral head sizes, when comparing outcome as measured by the Oxford Hip Score. Conclusion. This study shows an increase in cobalt and chromium levels over time for all modular femoral head sizes in patients with metal-on-polyethylene bearings, with two patients demonstrating ion levels above the MHRA threshold for failure, and a further two patients requiring revision surgery. These results may have clinical implications regarding longer term follow-up of patients and future implant choice, particularly among younger patients. Cite this article: Bone Joint J 2020;102-B(7):832–837

A: - determine the incidence of intraoperative periprosthetic femoral fracture (PFF). B: - determine the incidence of, and the reoperation rate for postoperative PFF. When using either CC or PTS femoral components. Retrospective review of a consecutive series of 11,018 THAs over a ten-year period. All PFFs were identified using regional radiograph archiving and electronic care systems. Of the 11,018 THAs 4,952 were CC and 6,066 were PTS. Between groups, age, sex, and BMI did not differ. A: - 55 (0.5%) had an intraoperative PFF. 44 CC and 11 PTS (p<0.001). 3 patients in each group had a femoral shaft fracture, remaining fractures were either the calcar (20 CC and 2 group) or the greater trochanter (11 CC and 6 PTS). B: - 91(0.8%) sustained a postoperative PFF. Of those 15 were managed conservatively, 15 were revised and 61 (80.3%) had an ORIF. The CC group had both a lower overall rate of postoperative PFFs (0.7% (36/4,952) vs 0.9% (55/6,066); p = 0.341), and a lower rate of return to theatre (0.4% (22/4,952) vs 0.9% (54/6,066); p = 0.005). 1.3% of male PTS (36/2,674) had a reoperation compared to 0.3% of male CC (7/2,121) (p<0.001). With regard to stem fracture there were none in the Corail group and 5 in the Exeter group. Of these 2 were sub trunnion and 3 were basal neck. A: - There were significantly more intraoperative PFFs with CC 44 (0.8%) than PTS 11 (0.2%). However, the majority of fractures were either of the calcar or greater trochanter with no impact on early recovery or one year Oxford scores. B: - Male PTS were five times more likely to have a reoperation for postoperative PFF. Females had the same incidence of reoperation with either component type. There were 5 stem fractures in the Exeter group and none in the Corail. These results represent robust estimates, which are likely to be more accurate than revision only studies typically generated from registry data

The practice of removing a well-fixed cementless femoral component is associated with high morbidity. Ceramic bearing couples are low wearing and their use minimises the risk of subsequent further revision due to the production of wear debris. A total of 165 revision hip replacements were performed, in which a polyethylene-lined acetabular component was revised to a new acetabular component with a ceramic liner, while retaining the well-fixed femoral component. A titanium sleeve was placed over the used femoral trunnion, to which a ceramic head was added. There were 100 alumina and 65 Delta bearing couples inserted. . The mean Harris hip score improved significantly from 71.3 (9.0 to 100.0) pre-operatively to 91.0 (41.0 to 100.0) at a mean follow up of 4.8 years (2.1 to 12.5) (p < 0.001). No patients reported squeaking of the hip. There were two fractures of the ceramic head, both in alumina bearings. No liners were seen to fracture. No fractures were observed in components made of Delta ceramic. At 8.3 years post-operatively the survival with any cause of failure as the endpoint was 96.6% (95% confidence interval (CI) 85.7 to 99.3) for the acetabular component and 94.0% (95% CI 82.1 to 98.4) for the femoral component. The technique of revising the acetabular component in the presence of a well-fixed femoral component with a ceramic head placed on a titanium sleeve over the used trunnion is a useful adjunct in revision hip practice. The use of Delta ceramic is recommended. Cite this article: Bone Joint J 2013;95-B:333–8

Aims. Fretting and corrosion at the modular head/neck junction, known as trunnionosis, in total hip arthroplasty (THA) is a cause of adverse reaction to metal debris (ARMD). We describe the outcome of revision of metal-on-polyethylene (MoP) THA for ARMD due to trunnionosis with emphasis on the risk of major complications. Patients and Methods. A total of 36 patients with a MoP THA who underwent revision for ARMD due to trunnionosis were identified. Three were excluded as their revision had been to another metal head. The remaining 33 were revised to a ceramic head with a titanium sleeve. We describe the presentation, revision findings, and risk of complications in these patients. Results. The patients presented with pain, swelling, stiffness, or instability and an inflammatory mass was confirmed radiologically. Macroscopic material deposition on the trunnion was seen in all patients, associated with ARMD. Following revision, six (18.2%) dislocated, requiring further revision in four. Three (9.1%) developed a deep infection and six (18.2%) had significant persistent pain without an obvious cause. One developed a femoral artery thrombosis after excision of an iliofemoral pseudotumor, requiring a thrombectomy. Conclusion. The risk of serious complications following revision MoP THA for ARMD associated with trunnionosis is high. In the presence of extensive tissue damage, a constrained liner or dual mobility construct is recommended in these patients. Cite this article: Bone Joint J 2018;100-B:720–4

Objectives. Modular junctions are ubiquitous in contemporary hip arthroplasty. The head-trunnion junction is implicated in the failure of large diameter metal-on-metal (MoM) hips which are the currently the topic of one the largest legal actions in the history of orthopaedics (estimated costs are stated to exceed $4 billion). Several factors are known to influence the strength of these press-fit modular connections. However, the influence of different head sizes has not previously been investigated. The aim of the study was to establish whether the choice of head size influences the initial strength of the trunnion-head connection. Materials and Methods. Ti-6Al-4V trunnions (n = 60) and two different sizes of cobalt-chromium (Co-Cr) heads (28 mm and 36 mm; 30 of each size) were used in the study. Three different levels of assembly force were considered: 4 kN; 5 kN; and 6 kN (n = 10 each). The strength of the press-fit connection was subsequently evaluated by measuring the pull-off force required to break the connection. The statistical differences in pull-off force were examined using a Kruskal–Wallis test and two-sample Mann–Whitney U test. Finite element and analytical models were developed to understand the reasons for the experimentally observed differences. Results. 36 mm diameter heads had significantly lower pull-off forces than 28 mm heads when impacted at 4 kN and 5 kN (p < 0.001; p < 0.001), but not at 6 kN (p = 0.21). Mean pull-off forces at 4 kN and 5 kN impaction forces were approximately 20% larger for 28 mm heads compared with 36 mm heads. Finite element and analytical models demonstrate that the differences in pull-off strength can be explained by differences in structural rigidity and the resulting interface pressures. Conclusion. This is the first study to show that 36 mm Co-Cr heads have up to 20% lower pull-off connection strength compared with 28 mm heads for equivalent assembly forces. This effect is likely to play a role in the high failure rates of large diameter MoM hips. Cite this article: A. R. MacLeod, N. P. T. Sullivan, M. R. Whitehouse, H. S. Gill. Large-diameter total hip arthroplasty modular heads require greater assembly forces for initial stability. Bone Joint Res 2016;5:338–346. DOI: 10.1302/2046-3758.58.BJR-2016-0044.R1

Aims. Surgeons have commonly used modular femoral heads and stems from different manufacturers, although this is not recommended by orthopaedic companies due to the different manufacturing processes. We compared the rate of corrosion and rate of wear at the trunnion/head taper junction in two groups of retrieved hips; those with mixed manufacturers (MM) and those from the same manufacturer (SM). . Materials and Methods. We identified 151 retrieved hips with large-diameter cobalt-chromium heads; 51 of two designs that had been paired with stems from different manufacturers (MM) and 100 of seven designs paired with stems from the same manufacturer (SM). We determined the severity of corrosion with the Goldberg corrosion score and the volume of material loss at the head/stem junction. We used multivariable statistical analysis to determine if there was a significant difference between the two groups. . Results. We found no significant difference in the corrosion scores of the two groups. The median rate of material loss at the head/stem junction for the MM and SM groups were 0.39 mm. 3. /year (0.00 to 4.73) and 0.46 mm. 3. /year (0.00 to 6.71) respectively; this difference was not significant after controlling for confounding factors (p = 0.06). . Conclusion. The use of stems with heads of another manufacturer does not appear to affect the amount of metal lost from the surfaces between these two components at total hip arthroplasty. Other surgical, implant and patient factors should be considered when determining the mechanisms of failure of large diameter metal-on-metal hip arthroplasties. Cite this article: Bone Joint J 2016;98-B:917–24

Introduction. Dual-mobility bearings increase the stable range of motion of total hip arthroplasty (THA) but are limited by the mechanical effects of a large diameter metal on polyethylene bearing which may cause high rates of wear from the surfaces of the polyethylene bearing and the head-stem taper. Improved polyethylene (PE) has reduced concern over bearing wear but the effects on the taper junction are unknown. We aimed to better understand the effect of dual mobility bearings on fretting-corrosion damage to the taper junction by comparison to standard bearings. Materials and Methods. We collected and analysed retrieved hips of one design with either dual mobility (n= 39) or standard bearings (n=30). The bearing size in the dual mobility group was 42mm whereas in the standard bearing group it had a median of 36mm. Stem trunnions had V40 tapers. Time of implantation and body mass index were comparable between the two groups. Fretting and corrosion at the stem trunnions was quantified by: 1) visual scoring and 2) surface profilometry. Results. Corrosion and fretting of the head-stem taper junction was lower in the dual mobility group when compared to the standard group as measured by both visual scoring (p=0.0002) and surface profilometry to measure material loss (p<0.0001). We did not see black debris, characteristic of severe corrosion processes, at the male surfaces in the dual mobility group. Discussion. In this study, visual damage at the male taper surfaces of dual mobility systems was less that that occurring at the male taper surfaces of standard articulating systems, measurements of wear rates were in agreements with the macroscopic evaluation. Conclusions. The frictional torque on the head-stem taper junction may be reduced with the use of a dual-mobility system when compared to a standard bearing system

Dislocation remains among the most common complications of, and reasons for, revision of both primary and revision total hip replacements (THR). Hence, there is great interest in maximising stability to prevent this complication. Head size has been recognised to have a strong influence on the risk of dislocation post-operatively. As femoral head size increases, stability is augmented, secondary to an increase in impingement-free range of movement. Larger head sizes also greatly increase the ‘jump distance’ required for the head to dislocate in an appropriately positioned cup. Level-one studies support the use of larger diameter heads as they decrease the risk of dislocation following primary and revision THR. Highly cross-linked polyethylene has allowed us to increase femoral head size, without a marked increase in wear. However, the thin polyethylene liners necessary to accommodate larger heads may increase the risk of liner fracture and larger heads have also been implicated in causing soft-tissue impingement resulting in groin pain. Larger diameter heads also impart larger forces on the femoral trunnion, which may contribute to corrosion, metal release, and adverse local tissue reactions. Alternative large bearings including large ceramic heads and dual mobility bearings may mitigate some of these risks, and several of these devices have been used with clinical success. Cite this article: Bone Joint J 2014;96-B(11 Suppl A):23–6