Meniscus has many important functions in the knee joint such as load bearing, shock absorption, joint stability, joint lubrication and proprioception. In the recent years, meniscus injuries have been the focus of orthopaedic surgeons and musculoskeletal tissue engineering applications because of its avascular nature. In this study, we aimed to compare the regeneration capacities of two composite scaffolds in a New Zealand Rabbit meniscal defect model. The first scaffold consists Poly-Lactic Acid (PLA) + chitosan + loofah and the second PLA + Hydroxyapatite (HAp) + loofah. In order to produce these scaffolds; 4% chitosan, 4% PLA and 4% HAp solutions were seperately prepared. The loofah pieces were saturated with these solutions and vacuum-dried for 14 days and sterilized with ethylene oxide. There were several characterizations performed such as Fourier Transform Infrared Spectroscopy (FTIR) for the investigation of chemical structure, Scanning Electron Microscopy (SEM) for morphological analysis, thermogravimetric differential thermal analysis (TGA/DTA) for thermal properties, mechanical compression and swelling ratio analysis. Moreover, in order to investigate biocompatibility of the scaffolds, WST-1 colorimetric assay at days 3, 7, 10, 14 and 21 was conducted. After these biocompatibility analysis, a 1.5-mm cylindrical defect was created in the avascular portion of the anterior horn of the medial meniscus in 14 New Zealand rabbits (2.5–3 kg weight) which were randomly grouped in two. The scaffolds were implanted at the defect site with the help of a freshly prepared fibrin glue. 8 weeks after the operation, the rabbits were sacrificed and their tissues were kept for further mechanical, radiological and histological analysis. In conclusion, we succeeded to produce a new meniscus scaffold. The proliferation ability of PLA + chitosan + loofah scaffold is higher than PLA + HAp + loofah scaffold. However, there was no statistically significant difference among them.
Bone fractures are highly observed clinical situation in orthopaedic treatments. In some cases, there might be non-union problems. Therefore, recent studies have focused on tissue engineering applications as alternative methods to replace surgical procedures. Various biopolymer based scaffolds are produced using different fabrication techniques for bone tissue engineering applications. In this study, hydroxyapatite (HAp) and loofah containing carboxymethyl chitosan (CMC) scaffolds were prepared. In this regard, first 4 ml of CMC solution, 0.02 g of hydroxyapatite (HAP) and 0.06 g of poly (ethylene glycol) diglycidyl ether (PEGDE) were mixed in an ultrasonic bath until the HAp powders were suspended. Next, 0.04 g of loofah was added to the suspension and with the help of PEGDE as the cross-linking agent, then, the mixture was allowed to cross-link at 40oC overnight. Finally, the three-dimensional, porous and sponge-like scaffolds were obtained after lyophilization (TELSTAR - LyoQuest −85) at 0.1 mbar and −25°C for 2 days. Morphologies, chemical structures and thermal properties of the scaffolds were characterized by scanning electron microscopy (SEM), Fourier Transform infrared spectroscopy (FT-IR) and thermogravimetric differential thermal analysis (TGA/DTA), respectively. In addition, swelling behavior and mechanical properties of the scaffolds under compression loading were determined. In order to investigate biocompatibility of the scaffolds, WST-1 colorimetric assay at days 0, 1, 3, 5 and 7 was conducted by using human dermal fibroblast. Also, histological and morphological analysis were performed for cell attachment at day 7. In conclusion, the produced scaffolds showed no cytotoxic effect. Therefore, they can be considered as a candidate scaffold for bone tissue regeneration. Further studies will be performed by using bone marrow and periosteum derived mesenchymal stem cells with these scaffolds.
