Methods and Materials

Two groups of 8 skeletally mature female sheep were anaesthetized before aspiration of bone marrow from the iliac crest. For both groups, mononuclear cells were isolated, and injected into a perfusion bioreactor (Millenium Biologix AG, Switzerland). Scaffold granules Ø∼900–1500 μm, ∼88% porosity) in group 1, consisted of hydroxyapatite (HA, 70%) with -tricalcium-phosphate (−TCP, 30%) (Danish Technological Institute, Denmark). The granules were coated with poly-lactic acid (PLA) 12%, in order to increase the mechanical strength of the material (Phusis, France). Scaffold granules Ø∼900–1400 μm, 80% porosity) in group 2 consisted of pure HA/-TCP (Fin Ceramica, Italy). For both groups, cells were incubated in the bioreactor for 2 weeks. Fresh culture medium supplemented with dexamethasone and ascorbic-acid was added every third or fourth day.

Porous titanium alloy implants with diameter=length=10mm (Biomet, USA) were inserted bilaterally in each of the distal femurs of the sheep; thus 4 implants in each sheep. The concentric gap (2 mm) surrounding the implant was filled with 1) BAG (autogenous), 2) granules, 3) granules+bone marrow aspirate (BMA, autologous) or 4) allograft. The sheep were euthanized after 6 weeks. Distal femurs were removed and implant-bone samples were divided in two parts. The superficial part was used for mechanical testing and micro-CT scanning, and the profound part for histomorphometry. Push-out tests were performed on an 858 Bionix MTS hydraulic materials testing machine. Shear mechanical properties between implant and newly generated bone were calculated to assess implant fixation. Results were assessed by One-way ANOVA. P-values less than 0.05 were considered significant.