Orthopaedic Proceedings
Vol. 98-B, Issue SUPP_11 | Pages 8 - 8
1 Jun 2016
Cook R Bolland B Tilley S Latham J
Full Access

Using a femoral head from one manufacturer on the stem of another manufacturer poses the risk that the taper interface between the components do not contact correctly and the performance of the joint will be impaired. The cohorts in this study are a combination of modular Birmingham Hip Resurfacing (BHR) and Adept femoral heads on CPT stems. The study reviews the geometry of the taper interfaces to establish if the taper clearance angles was outside of the normal range for other taper interfaces. In addition the rates of material loss from the bearings and taper and a ranking of the stem damage were reviewed to determine if the levels of loss were above that seen for other similar joints.

The material loss analysis demonstrated that the rates or levels of loss from the bearings, taper and stem are no different to levels published for manufacturer matched joints and in many cases are lower. The results demonstrate that the taper clearance angles for the mixed manufacturer joints (BHR-CPT: 0.067 to −0.116, Adept-CPT: 0.101 to −0.056) were within the range of other studies and manufacturer matched clearances (0.134 to −0.149).

Using components from different manufacturers has not in this instance increased the level of material loss from the joints, when compared to other similar manufacturer matched joints.


The Bone & Joint Journal
Vol. 97-B, Issue 4 | Pages 463 - 472
1 Apr 2015
Panagiotidou A Meswania J Osman K Bolland B Latham J Skinner J Haddad FS Hart A Blunn G

The aim of this study was to assess the effect of frictional torque and bending moment on fretting corrosion at the taper interface of a modular femoral component and to investigate whether different combinations of material also had an effect. The combinations we examined were 1) cobalt–chromium (CoCr) heads on CoCr stems 2) CoCr heads on titanium alloy (Ti) stems and 3) ceramic heads on CoCr stems.

In test 1 increasing torque was imposed by offsetting the stem in the anteroposterior plane in increments of 0 mm, 4 mm, 6 mm and 8 mm when the torque generated was equivalent to 0 Nm, 9 Nm, 14 Nm and 18 Nm.

In test 2 we investigated the effect of increasing the bending moment by offsetting the application of axial load from the midline in the mediolateral plane. Increments of offset equivalent to head + 0 mm, head + 7 mm and head + 14 mm were used.

Significantly higher currents and amplitudes were seen with increasing torque for all combinations of material. However, Ti stems showed the highest corrosion currents. Increased bending moments associated with using larger offset heads produced more corrosion: Ti stems generally performed worse than CoCr stems. Using ceramic heads did not prevent corrosion, but reduced it significantly in all loading configurations.

Cite this article: Bone Joint J 2015;97-B:463–72.