Multispecies biofilms are associated with difficult periprosthetic joint infections (PJI), particularly if they have different antibiotic sensitivities. We aimed to determine if we could generate and kill a multispecies biofilm consisting of a Gram negative and Gram positive pathogen To establish whether we could co-culture mixed species biofilms various combinations of Aim
Methods
C Three strains of Aim
Method
Daptomycin has a unique mechanism of action against Gram-positive bacteria. Daptomycin is only bactericidal in the presence of calcium ions. [1] Kanellakopoulou et al [2] investigated elution of daptomycin from calcium sulfate. The results indicated above MIC elution concentrations out to 28 days. Experience reports that the ability for calcium sulfate to set hard when combined with daptomycin can be problematic.[3] This study aimed to investigate the combination of daptomycin with a synthetic recrystallised form of calcium sulfate and investigate zone of inhibition (ZOI) testing against susceptible organisms. 6mm hemispherical beads, were prepared using a commercially available calcium sulfate hemihydrate powder (CSH) – CaSO4 ·1/2H2O. [4] In order to combine daptomycin [5] with the CSH and enable it to set hard, 7mls of saline solution was added to 20g CSH powder and mixed for 80 seconds to initiate the setting reaction. Then 1g of daptomycin powder was added and mixed for a further 30 seconds. The resultant paste was applied to a bead mat and allowed to set. Tryptone soya agar plates were seeded with 0.2ml of a 10e6 – 10e8 cfu/ml suspension of the relevant organism. The plates were incubated at 33 °C ± 2 °C for 30 minutes. The plates were then removed from the incubator and the beads placed on the surface. The plates were then incubated at 33 °C ± 2 °C for 24 hours before examination for the absence of growth as seen by a clear zone around the test sample. Triplicate samples were tested against Staphylococcus epidermidis, Staphylococcus aureus, MRSA, VRE Enterococcus faecium and Propionibacterium acnes. Repeat tests were carried out for beads that had been stored at 37 °C for 21 days to simulate in-vivo conditions. Setting times for the CSH/daptomycin beads were approximately 20 minutes. ZOIs indicating efficacy were seen for all samples both ‘fresh’ and ‘incubated’ with MRSA and Propionibacterium acnes having the largest ZOIs at 31–33mm. A mixing protocol was established to enable set beads to be formed with daptomycin loaded calcium sulfate. As assessed by ZOI testing, the eluted antibiotic maintained efficacy against susceptible pathogens. Results obtained in-vitro may not be indicative of in-vivo performance.