Unicompartmental knee replacement (UKR) is a conservative option for degenerative disease, with mobile (Oxford UKR) and fixed bearing (Physica ZUK) the most commonly used devices. The primary reasons for revising UKRs include disease progression (36.9%), loosening (31.7%), and pain (7.5%). Loosening typically occurs due to osteolysis caused by wear particles from the polyethylene (PE) inserts. There is limited published literature which has quantified volumetric material loss from the PE inserts of cemented fixed-bearing UKRs. This study aimed to quantify bearing wear and backside deformation of these PE components. At our national retrieval centre, we measured changes volumetric bearing wear and backside deformation of 31 explanted fixed-bearing Physica ZUK UKR PE inserts using a peer-reviewed methodology based on coordinate measuring machine analysis. These explants had been revised for any indication [Females (19) and Males (12)]. The location of the wear scars was identified and mapped. We compared the volumetric wear from the bearing surface with contemporary total knee replacement (TKR) inserts.Objectives
Design and Methods
Several studies have reported elevated blood cobalt (Co) and chromium (Cr) concentrations in patients with total knee replacements (TKRs). Up to 44% of tissue samples taken from patients with failed TKRs exhibit histological evidence of metal sensitivity/ALVAL. In simulated conditions, metal particles contribute approximately 12% of total wear debris in TKR. We carried out this investigation to determine the source and quantity of metal release in TKRs. We analysed 225 explanted fixed-bearing TKRs (Attune, Genesis II, NexGen, PFC, and Vanguard) revised for any indication. These were analysed using peer-reviewed [coordinate measuring machine (CMM)] methodology to measure the volumetric wear of the polyethylene (PE) bearing surfaces and trays. The trays were analysed using 2D profilometry (surface roughness-Ra) and light microscopy. Histological and blood metal ion concentration analyses were performed in a sub-sample of patients.Objectives
Design and Methods
We identified an unusual pattern of backside deformation on polyethylene (PE) inserts of contemporary total knee replacements (TKRs). The PE backside's margins were inferiorly deformed in TKRs with NexGen central-locking trays. This backside deformation was significantly associated with tray debonding. Furthermore, recent studies have shown high rate of tray debonding in PS NexGen TKRs. Subsequently, a field safety notice was issued regarding the performance of this particular device combination and the Option tray has been withdrawn from use. Therefore, we hypothesised that the backside deformation of PS inserts may be greater than that of CR inserts. At our national implant retrieval centre, we used peer-reviewed techniques to analyse changes in the bearing wear rate and backside surface deformation of NexGen PE inserts using coordinate measuring machines [N=84 (CR-43 and PS-41) TKRs with non-augmented-trays]. Multiple regression was used to determine which variable had the greatest influence on backside deformation. The amount of cement cover on trays was quantified as a %of the total surface using Image-J software.Objectives
Design and Methods
At our national explant retrieval unit, we identified an unusual pattern of backside-deformation on polyethylene (PE) inserts of contemporary total-knee-replacements (TKRs). The PE backside's margins were inferiorly deformed in TKRs with central-locking trays. We reported that this backside-deformation appeared to be linked to tray debonding. Moreover, recent studies have shown high-rate of tray debonding in PS NexGen TKRs. Therefore, we hypothesised that backside deformation on PS inserts may be more than on CR inserts. We used peer-reviewed techniques to analyse changes in the bearing (wear rate) and backside surfaces (deformation) of PE inserts using coordinate measuring machines [N=61 NexGen (CR-39 and PS-22) TKRs with non-augmented-trays]. Multiple regression was used to determine which variable had the greatest influence on backside-deformation. The amount of cement cover on trays was quantified as a %of the total surface using Image-J software.Abstract
Introduction
Methodology
Several studies have reported significant cobalt(Co) and chromium(Cr) elevations in the blood of patients with total-knee-replacements (TKRs), and histological signs of metal sensitivity have been reported in up to 44% of patients undergoing revision of their TKRs. We carried out this investigation to determine the source and quantity of metal release in TKRs. We identified all TKRs with polished CoCr trays (N=59) [Vanguard=29, Attune=4 and PFC=26]. These were analysed using peer-reviewed [coordinate-measuring-machine (CMM)] methodology to measure the volumetric wear of the polyethylene (PE) bearing surfaces and trays. The trays were analysed using 2D-profilometry (surface roughness-Ra) and 4D-microscopy. Histological and blood metal ion concentration analyses were performed.Abstract
Introduction
Methodology
Cobalt chrome alloy is commonly used in joint replacement surgery. However, it is recognised that some patients develop lymphocyte mediated delayed type hypersensitivity (DTH) responses to this material, which may result in extensive bone and soft tissue destruction.
A total of 606 DNA samples, from 397 males and 209 female patients, were typed. This included 176 from patients with failed prostheses, and 430 from asymptomatic patients at a mean of >10 years follow up. C-index and ROC(t) scores suggested a high degree of discrimination, whilst the IBS indicated good calibration and further backed up the indication of high discriminatory ability. At ten years, the weighted mean survival probability error was < 4%. At present, there are no tests in widespread clinical use which use a patient's genetic profile to guide implant selection or inform post-operative management. The algorithm described herein may address this issue and we suggest that the application may not be restricted to the field of MoM hip arthroplasty.
We aimed to identify genes associated with the development of ALVAL at relatively low levels of wear. At our unit all patients undergoing revision of a MoM hip prosthesis have periprosthetic tissue samples graded for ALVAL. Explants undergo volumetric wear testing of the bearing and taper surfaces. We identified patients with moderate/severe ALVAL who had been exposed to lower than the median wear rate of all recorded patients who had developed ALVAL (<3mm3/year). This was termed the “ALVAL” group. We then identified all patients whose tissues had shown no signs of ALVAL. The patients in the two groups were sent buccal DNA collection kits. DNA was examined using next generation sequencing. Alleleic frequencies in the two groups were compared using Fisher's test and compared to a background UK population group (n=8514). We then conducted binary logistic regression with patient age, sex, primary source of debris (taper/bearing) and HLA genotype as the predictors. With the hypothesis that a cobalt/albumin metalloprotein acts as the epitope, we used validated binding prediction software to determine the relative affinities of the binding grooves created by different DQA1/DQB1 genetic combinations for albumin derived peptides. Given the protection that male sex and younger age appears to confer against ALVAL, we hypothesized that testosterone peptides may compete for these binding sites.Introduction
Methods
Some reports have suggested that debris generated from the head neck taper junction is more destructive than equivalent doses from metal bearing surfaces. Part 1. We examined the relationship between the source (taper/bearing) and volume of metal debris on Cr and Co concentrations in corresponding blood and hip synovial fluid samples and the observed agglomerated particle sizes in excised tissues using regression analysis of prospectively collected data at a single revision unit. Part 2. We investigated variables most strongly associated with macroscopic soft tissue injury as documented at revision surgery using ordinal logistic regression. Independent variables included source and volume of CoCr exposure, Cr and Co joint fluid concentrations, joint fluid grade, ALVAL (Aseptic Lymphocytic Vasculitis Associated Lesion) grade, presence of vascular hyalinisation, agglomerated particle size, implant type, patient sex and age.Background
Methods
Historical studies have reported incidences of taper corrosion in retrieved MoP hips of 20–50%. These studies relied on visual assessments, rather than using modern analytical techniques. The Northern Retrieval Registry was initiated to routinely analyse all retrieved hips. The volumetric wear rates of retrieved Exeter head tapers were measured using a coordinate measuring machine using validated methods and compared to the available results obtained from an ongoing study of failed MoM prostheses. Power analysis suggested that we would need at least fifty Exeter head tapers to provide significant results. Non-parametric tests were used to assess differences. We have previously identified head diameter/offset/taper angle and taper surface roughness as variables associated with taper wear. The effect of bearing material combination remains unquantified. These design variables were entered into a multiple regression model following log normalisation of taper wear.Introduction
Patients/Materials and Methods
In this study, we aimed to investigate the effect of the topography of the female taper surface on taper wear. We measured volumetric material loss at the female taper surface of the first consecutive 36mm MoM hips received at our centre. The MoM hips were from a single manufacturer and possessed matching: head size (36mm); taper geometry (5.65 degree 12 14 tapers); and metallurgy (cobalt chrome female taper mated with a titanium stem). Volume loss was measured with a coordinate measuring machine using validated methods. Surface roughness was measured using a Surftest SJ400. There were 111 head tapers available for analysis. The majority had been revised secondary to ARMD, and a minority for loosening. The mean duration of implantation was 56 months. Volumetric wear values were log normalised in order to construct a multiple regression model to investigate the interaction of head offset, the head taper angle and the Rp value of the female taper surface. Rp is a roughness parameter, which is a measure of the peaks above the plateau of a surface.Introduction
Patients/Materials & Methods
Previous studies have suggested that the modular junction of metal on metal (MoM) total hip replacements (THR) is an important source of metallic debris. We carried out a prospective study using custom techniques to analyse one of the largest collections of failed contemporary MoM devices in the world. All explants from patients who had suffered adverse reactions to metal debris (ARMD) were included in this study. These explants included: 82 36mm THRs, and 147 resurfacing head THRs and 140 resurfacing arthroplasties from several manufactures. Volumetric wear analysis of the bearing surfaces and taper junctions was carried out using a coordinate measuring machine. The relationships between total metallic loss and metal ion concentrations and the macroscopic and histological tissue appearance of THR patients were compared to those in resurfacing patients. Mann Whitney test for non-parametric data was used to assess significant differences between groups.Background
Methods
We have previously described the relationship between wear rates of MOM components and soft tissue necrosis. In this study we investigated the link between wear rates, metal ion concentrations and osteolysis. All unilateral patients who underwent revision of hip resurfacings at our centre were included. Retrieved components were analysed using a coordinate measuring machine to determine total volumetric material loss and rates of wear. Given the accuracy of the wear calculations (which we have previously published), wear rates were considered “abnormal” if ≥3mm3/yr. ROC curves were constructed to determine a Co concentration which would be clinically useful to detect abnormal wear. During revision, the presence/absence of osteolysis was documented.Background
Methods
Total hip prostheses which use a ceramic head within a metal liner are a relatively recent innovation. As such, survivorship rates from independent centres alongside explant analysis are rare. The early clinical experience with this novel ceramic-on-metal (CoM) bearing couple is reported alongside explant analysis of failed devices. All CoM hips implanted between 2008 and 2009 at a single hospital by a single surgeon were reviewed. Radiographs were analysed using EBRA software to determine acetabular cup inclination and anteversion angles. Blood metal ion concentrations were measured using inductively coupled plasma mass spectroscopy (ICPMS). Explants were measured for bearing surface and taper wear using a high precision co-ordinate measuring machine (Mitutoyo Legex 322, manufacturer's claimed accuracy 0.8µm). The roughness of the articulating surfaces of heads and liners was measured with a non-contact profilometer (ZYGO NewView 5000, 1nm resolution).Introduction
Methods and materials
A detailed clinical examination and investigations are required to evaluate the cause of persisting groin pain following a metal on metal (MoM) hip replacement. Adverse reaction to metallic debris (ARMD) is an emerging problem with MoM hip replacements. It is an umbrella term encompassing metallosis, pseudo-tumors and aseptic lymphocytic vasculitis associated lesions (ALVAL). The role of imaging in the diagnosis of this complex problem is still unclear. A study was undertaken to evaluate the efficacy of ultrasound in diagnosis of ARMD following a MoM hip replacement. The study group included 35 patients with a clinical and histological diagnosis of ARMD, who had a preoperative ultrasound. All ultrasound procedures were performed on the anterior and lateral aspects of the painful hip with a high frequency probe of 9–13 MHz (Sonoline Antares – Siemens).INTRODUCTION
METHODS
The failure and subsequent withdrawal of the ASR device in both its resurfacing and THR form has been well documented. The National Joint Registry report of 2010 quoted figures of 12–13% failure at five years. Adverse reaction to metal debris (ARMD) is a poorly understood condition and patients developing severe metal reactions may go unrecognised for sometime. In 2004 a single surgeons prospective study of the ASR bearing surface was undertaken. We present the ARMD failure rates of the ASR resurfacing and ASR THR systems. The diagnosis of ARMD was made by the senior author and was based on clinical history, examination, ultrasound findings, metal ion analysis of blood and joint fluid, operative findings and histopathological analysis of tissues retrieved at revision. Mean follow up was 52 months (24–81) and 70 patients were beyond 6 years of the procedure at the time of writing. Kaplan Meier survival analysis was carried out firstly with joints designated “failure” if the patient had undergone revision surgery or if the patient had been listed. A second survival analysis was carried out with a failure defined as a serum cobalt > 7µg/L. Full explant analysis was carried out for retrieved prostheses.Background
Patients and Methods
Adverse reaction to metal debris (ARMD) is an increasingly recognised complication of metal-on-metal hip arthroplasty. A previous study described poor results following revision and recommended early intervention1. We determined the outcome of revision for ARMD and present the largest case series to date. Between 2005 and 2010, 98 patients (101 hips) underwent revision for ARMD. The diagnosis of ARMD was based on clinical history, examination, appearance at revision and histology. Patients were reviewed at 3, 6 and 12 months and annually thereafter. Patient satisfaction, Harris hip scores (HHS) and metal ions were analysed.Introduction
Methods
Metal-on-metal hip resurfacing prostheses are a relatively recent intervention for relieving the symptoms of common musculoskeletal diseases such as osteoarthritis. While some short term clinical studies have offered positive results, in a minority of cases there is a recognised issue of femoral fracture, which commonly occurs in the first few months following the operation. This problem has been explained by a surgeon's learning curve and notching of the femur but, to date, studies of explanted early fracture components have been limited. Tribological analysis was carried out on fourteen retrieved femoral components of which twelve were revised after femoral fracture and two for avascular necrosis (AVN). Eight samples were Durom (Zimmer, Indiana, USA) devices and six were Articular Surface Replacements (ASR, DePuy, Leeds, United Kingdom). One AVN retrieval was a Durom, the other an ASR. The mean time to fracture was 3.4 months. The AVNs were retrieved after 16 months (Durom) and 38 months (ASR). Volumetric wear rates were determined using a Mitutoyo Legex 322 co-ordinate measuring machine (scanning accuracy within 1 micron) and a bespoke computer program. The method was validated against gravimetric calculations for volumetric wear using a sample femoral head that was artificially worn in vitro. At 5mm3, 10mm3, and 15mm3 of material removal, the method was accurate to within 0.5mm3. Surface roughness data was collected using a Zygo NewView500 interferometer (resolution 1nm). Mean wear rates of 17.74mm3/year were measured from the fracture components. Wear rates for the AVN retrievals were 0.43mm3/year and 3.45mm3/year. Mean roughness values of the fracture retrievals (PV = 0.754, RMS = 0.027) were similar to the AVNs (PV = 0.621, RMS = 0.030), though the AVNs had been in vivo for significantly longer. Theoretical lubrication calculations were carried out which found that in both AVN retrievals and in seven of the twelve cases of femoral fracture the roughening was sufficient to change the lubrication regime from fluid film to mixed. Three of these surfaces were bordering on the boundary lubrication regime. The results show that even before the femoral fracture, wear rates and roughness values were high and the implants were performing poorly.
We conducted independent wear analysis of retrieved metal on metal (MoM) hip components from around the world. All patients with resurfaced hips who developed adverse reactions to metal debris (ARMD) were found to have increased wear of the bearing surfaces. This was untrue in patients with large diameter (?36mm) MoM total hip replacements. This led us to search for other factors leading to ARMD. MoM THR explants retrieved from 78 patients suffering ARMD underwent full volumetric wear analysis of bearing surface and taper-junctions using coordinate measuring machine. Scanning electron microscopy (SEM) used to characterise material composition of specific areas.Introduction
Methods
Total hip prostheses which use a ceramic head within a metal liner are a relatively recent introduction. As such, survivorship rates from independent centres alongside explant analysis are rare. The early experience with this novel ceramic-on-metal (CoM) bearing couple is reported. All CoM hips implanted between 2008 and 2009 at a single hospital by a single surgeon were reviewed. Radiographs were analysed using EBRA software to determine acetabular cup inclination and anteversion angles. Blood metal ion concentrations were measured using inductively coupled plasma mass spectroscopy (ICPMS). Explants were measured for bearing surface and taper wear using a high precision co-ordinate measuring machine. The roughness of the articulating surfaces was measured with a non-contact profilometer.Introduction
Methods and Materials
The worldwide withdrawal of the DePuy Articular Surface Replacement (ASR) device in both its resurfacing and total hip replacement (THR) form on 26 August 2010, after 93,000 were implanted worldwide, has had major implications. The 2010 National Joint Registry for England and Wales quoted figures of 12-13% failure at five years; however these figures may be an underestimate. In 2004 a single surgeon prospective study of the ASR bearing surface was undertaken. Presented are the Adverse Reaction to Metal Debris (ARMD) failure rates of the ASR resurfacing and ASR THR systems. The diagnosis of ARMD was made by the senior author and was based on clinical history, examination, ultrasound findings, metal ion analysis of blood and joint fluid, operative findings and histopathological analysis of tissues retrieved at revision. Acetabular cup position in vivo was determined using EBRA software. Mean follow up was 52 months (24-81) and 70 patients were beyond 6 years of the procedure at the time of writing. Kaplan Meier survival analysis was carried out firstly with joints designated ‘failure’ if the patient had undergone revision surgery or if the patient had been listed for revision. A second survival analysis was carried out with a failure defined as a serum cobalt concentration > 7microgrammes/L (MHRA guideline from MDA-2010-069). Full explant analysis was carried out for retrieved prostheses.Background
Patients and methods