McNamara I Ong M Rayment A Brooks R Prevost T Best S Rushton N
Full Access

Problems associated with allograft are well known. The addition of hydroxyapatite (HA) to allograft has various mechanical advantages, especially within revision arthroplasty. The mixing of bone and HA results in mechanical properties different from the individual parts. However, at present the changes in material properties the mix have not been fully investigated and the optimum mixing ratio not characterized. A compressive uniaxial chamber was used to investigate the change in mechanical properties occurring with the addition of HA in varying proportions to morcellised bone graft (MBG).

Materials and methods

MBG was prepared using femoral heads donated from patients undergoing total hip replacement surgery using a bone mill in a standard manner. Non porous HA (npHA) was prepared using a precipitation method of Calcium Carbonate and Orthophosphoric acid. The porous HA, (pHA) is a 60% macroporosity HA commercially prepared.

Chamber

The uniaxial compression chamber was a 30mm diameter, steel chamber. Holes were drilled to allow fluid drainage. Loads were applied using a 10 kN load cell. Specimens were prepared in the volumetric proportions pure HA, pure MBG, 2:1, 1:1, 1:2 ratio of MBG to HA. The samples were subjected to compressive forces of incrementally increasing loads of up to 2 KN for 60 cycles. The sample was then allowed to creep under a stress of 2 kN. MBG was also tested up to forces of 7 kN. The mechanical parameters that were examined were the stiffness of the sample at the 60th cycle, (Ec60), and creep