Orthopaedic Proceedings
Vol. 99-B, Issue SUPP_6 | Pages 18 - 18
1 Mar 2017
Stratton-Powell A Tipper J Williams S Redmond A Brockett C
Full Access

Introduction

Total ankle replacement (TAR) is less successful than other joint replacements with a 77% survivorship at 10 years. Predominant indications for revision include: Insert dislocation, soft tissue impingement and pain/stiffness. Insert edge-loading may be both a product and cause of these indications and was reported to affect 22% of patients with the, now withdrawn from market, Ankle Evolutive System (AES) TAR (Transysteme, Nimes, France). Compressive forces up to seven times body weight over a relatively small contact area (∼6.0 to 9.2 cm2), in combination with multi-directional motion potentially causes significant polyethylene wear and deformation in mobile-bearing TAR designs. Direct methods of measuring component volume (e.g. pycnometer) use Archimedes' principle but cannot identify spatial changes in volume or form indicative of wear/deformation. Quantitative methods for surface analysis bridge this limitation and may advance methods for analysing the edge loading phenomena in TAR.

Aim

Determine the frequency of edge loading in a cohort of explanted total ankle replacements and compare the quantitative surface characteristics using a novel explant analysis method.


Orthopaedic Proceedings
Vol. 98-B, Issue SUPP_16 | Pages 44 - 44
1 Oct 2016
Stratton-Powell A Tipper JL Williams SD Redmond A Brockett CL
Full Access

Total ankle replacement (TAR) has a mean survivorship of 77% at 10 years which is poor compared to other types of joint arthroplasty. Osteolysis and aseptic loosening are commonly cited TAR failure modes, the mechanisms of which are unknown. Retrieval analyses of TAR devices may reveal mechanisms of failure similar or dissimilar to other joint replacements. This study investigated whether TAR explants exhibit similar damage modes to those recognised in other total joint replacements.

22 Ankle Evolution System TARs (Transystème, Nimes, France) were implanted and retrieved by the same surgeon. Mean implantation time was 7.8 yrs (5.3 to 12.1 range). Pain and/or loosening were the indications for revision. Macro photography, an Alicona Infinite microscope and the Hood/Wasielewski scale were used to classify damage modes on the polyethylene insert. Scanning electron microscopy with energy dispersive X-ray spectroscopy was used to determine the composition of third body debris and to image the fixation surface of the tibial components.

Mean damage score was 185.4 (± 40.0 SD). Damage modes common to total knee replacements were identified on both the superior and inferior insert surfaces, these included: burnishing, scratching, pitting and abrasion. Titanium particles, hydroxyapatite fragments and bone debris were embedded in the insert surfaces. Fixation surface delamination was identified by the ongrowth of tissue between the cobalt chromium substrate and titanium alloy coating.

Damage modes indicative of high levels of wear and deformation were evident. Pitting caused by third body debris was abundant and suggested fixation surface wear and failure.