Despite many claims of good wear properties following total knee replacement (TKR) with an oxidised zirconium (OxZr) femoral component, there are conflicting clinical results. We hypothesised that there would be no difference in either the mid-term clinical and radiological outcomes or the characteristics of the polyethylene wear particles (weight, size and shape) in patients using an OxZr or cobalt-chrome (CoCr) femoral component. In all 331 patients underwent bilateral TKR, receiving an OxZr femoral component in one knee and a CoCr femoral component in the other. The mean follow-up was 7.5 years (6 to 8). Following aspiration, polyethylene wear particles were analysed using thermogravimetric methods and scanning electron microscopy. At the most recent follow-up, the mean Knee Society score, Western Ontario and McMaster Universities Osteoarthritis Index score, range of movement and satisfaction score were not significantly different in the two groups. The mean weight, size, aspect ratio and roundness of the aspirated wear particles were similar for each femoral component. Survivorship of the femoral, tibial and patellar components was 100% in both groups. In the absence of evidence of an advantage in the medium term we cannot justify the additional expense of an OxZr femoral component.

Aims. The aims of this study were to evaluate wear on the surface of cobalt-chromium (CoCr) femoral components used in total knee arthroplasty (TKA) and compare the wear of these components with that of ceramic femoral components. Methods. Optical profilometry was used to evaluate surface roughness and to examine the features created by the wear process in a knee wear simulator. We developed a method of measuring surface changes on five CoCr femoral components and quantifying the loss of material from the articular surface during the wear process. We also examined the articular surface of three ceramic femoral components from a previous test for evidence of surface damage, and compared it with that of CoCr components. Results. We found that the surface roughness of CoCr components rapidly increased during the first 1,000 wear cycles, then reached a steady state, but material loss from the surface continued at a rate of 1,778,000 μm. 3. per million cycles as carbides were removed from its matrix. These carbides formed third-body wear particles, leading to the formation of new scratches even as older scratches were worn away. In contrast, no scratching, loss of material, or other surface damage, when evaluated with one nanometer resolution, was found on the surface of the ceramic components after a 15 M wear cycle test. Conclusion. This study showed wear and loss of CoCr material from scratching and microabrasive wear in TKA. The material loss from the surface continued in a linear relationship with increasing cycles. We also found the absence of scratching and roughening of ceramic femoral components in simulated wear, suggesting an advantage in wear rate and avoiding metal sensitivity. This may have implications in the management of persistent pain after TKA. Cite this article: Bone Joint J 2021;103-B(6 Supple A):94–101

Aims

We propose a state-of-the-art temporary spacer, consisting of a cobalt-chrome (CoCr) femoral component and a gentamicin-eluting ultra-high molecular weight polyethylene (UHMWPE) tibial insert, which can provide therapeutic delivery of gentamicin, while retaining excellent mechanical properties. The proposed implant is designed to replace conventional spacers made from bone cement.

Aims

We sought to establish whether an oxidised zirconium (OxZr) femoral component causes less loss of polyethylene volume than a cobalt alloy (CoCr) femoral component in total knee arthroplasty.