Aims

Osteopetrosis (OP) is a rare hereditary disease that causes reduced bone resorption and increased bone density as a result of osteoclastic function defect. Our aim is to review the difficulties, mid-term follow-up results, and literature encountered during the treatment of OP.

We compared the outcome of closed intramedullary nailing with minimally invasive plate osteosynthesis using a percutaneous locked compression plate in patients with a distal metaphyseal fracture in a prospective study.

A total of 85 patients were randomised to operative stabilisation either by a closed intramedullary nail (44) or by minimally invasive osteosynthesis with a compression plate (41). Pre-operative variables included the patients’ age and the side and pattern of the fracture. Peri-operative variables were the operating time and the radiation time. Postoperative variables were wound problems, the time to union of the fracture, the functional American Orthopaedic Foot and Ankle surgery score and removal of hardware.

We found no significant difference in the pre-operative variables or in the time to union in the two groups. However, the mean radiation time and operating time were significantly longer in the locked compression plate group (3.0 vs 2.12 minutes, p < 0.001, and 97.9 vs 81.2 minutes, p < 0.001, respectively). After one year, all the fractures had united. Patients who had intramedullary nailing had a higher mean pain score, but better function, alignment and total American Orthopaedic Foot and Ankle surgery scores, although the differences were not statistically significant (p = 0.234, p = 0.157, p = 0.897, p = 0.177 respectively). Three (6.8%) patients in the intramedullary nailing group and six (14.6%) in the locked compression plate group showed delayed wound healing, and 37 (84.1%) in the former group and 38 (92.7%) in the latter group expressed a wish to have the implant removed.

We conclude that both closed intramedullary nailing and a percutaneous locked compression plate can be used safely to treat Orthopaedic Trauma Association type-43A distal metaphyseal fractures of the tibia. However, closed intramedullary nailing has the advantage of a shorter operating and radiation time and easier removal of the implant. We therefore prefer closed intramedullary nailing for patients with these fractures.

The augmentation of fixation with bone cement is increasingly being used in the treatment of severe osteoporotic fractures. We investigated the influence of bone quality on the mechanics of augmentation of plate fixation in a distal femoral fracture model (AO 33 A3 type). Eight osteoporotic and eight non-osteoporotic femoral models were randomly assigned to either an augmented or a non-augmented group. Fixation was performed using a locking compression plate. In the augmented group additionally 1 ml of bone cement was injected into the screw hole before insertion of the screw. Biomechanical testing was performed in axial sinusoidal loading. Augmentation significantly reduced the cut-out distance in the osteoporotic models by about 67% (non-augmented mean 0.30 mm (sd 0.08) vs augmented 0.13 mm (sd 0.06); p = 0.017). There was no statistical reduction in this distance following augmentation in the non-osteoporotic models (non-augmented mean 0.15 mm (sd 0.02) vs augmented 0.15 mm (sd 0.07); p = 0.915). In the osteoporotic models, augmentation significantly increased stability (p = 0.017).

Cite this article: Bone Joint J 2013;95-B:1406–9.

Filling the empty holes in peri-articular locking plates may improve the fatigue strength of the fixation. The purpose of this in vitro study was to investigate the effect of plugging the unused holes on the fatigue life of peri-articular distal femoral plates used to fix a comminuted supracondylar fracture model.

A locking/compression plate was applied to 33 synthetic femurs and then a 6 cm metaphyseal defect was created (AO Type 33-A3). The specimens were then divided into three groups: unplugged, plugged with locking screw only and fully plugged holes. They were then tested using a stepwise or run-out fatigue protocol, each applying cyclic physiological multiaxial loads.

All specimens in the stepwise group failed at the 770 N load level. The mean number of cycles to failure for the stepwise specimen was 25 500 cycles (sd 1500), 28 800 cycles (sd 6300), and 26 400 cycles (sd 2300) cycles for the unplugged, screw only and fully plugged configurations, respectively (p = 0.16). The mean number of cycles to failure for the run-out specimens was 42 800 cycles (sd 10 700), 36 000 cycles (sd 7200), and 36 600 cycles (sd 10 000) for the unplugged, screw only and fully plugged configurations, respectively (p = 0.50). There were also no differences in axial or torsional stiffness between the constructs. The failures were through the screw holes at the level of comminution.

In conclusion, filling the empty combination locking/compression holes in peri-articular distal femur locking plates at the level of supracondylar comminution does not increase the fatigue life of the fixation in a comminuted supracondylar femoral fracture model (AO 33-A3) with a 6 cm gap.

We investigated the static and cyclical strength of parallel and angulated locking plate screws using rigid polyurethane foam (0.32 g/cm³) and bovine cancellous bone blocks. Custom-made stainless steel plates with two conically threaded screw holes with different angulations (parallel, 10° and 20° divergent) and 5 mm self-tapping locking screws underwent pull-out and cyclical pull and bending tests. The bovine cancellous blocks were only subjected to static pull-out testing. We also performed finite element analysis for the static pull-out test of the parallel and 20° configurations. In both the foam model and the bovine cancellous bone we found the significantly highest pull-out force for the parallel constructs. In the finite element analysis there was a 47% more damage in the 20° divergent constructs than in the parallel configuration. Under cyclical loading, the mean number of cycles to failure was significantly higher for the parallel group, followed by the 10° and 20° divergent configurations.

In our laboratory setting we clearly showed the biomechanical disadvantage of a diverging locking screw angle under static and cyclical loading.

We identified 11 women with a mean age of 74 years (65 to 81) who sustained comminuted distal radial and ulnar fractures and were treated by volar plating and slight shortening of the radius combined with a primary Sauvé-Kapandji procedure.

At a mean of 46 months (16 to 58), union of distal radial fractures and arthrodesis of the distal radioulnar joint was seen in all patients. The mean shortening of the radius was 12 mm (5 to 18) compared to the contralateral side. Flexion and extension of the wrist was a mean of 54° and 50°, respectively, and the mean pronation and supination of the forearm was 82° and 86°, respectively. The final mean disabilities of the arm, shoulder and hand score was 26 points. According to the Green and O’Brien rating system, eight patients had an excellent, two a good and one a fair result.

The good clinical and radiological results, and the minor complications without the need for further operations related to late ulnar-sided wrist pain, justify this procedure in the elderly patient.