This study reports on ceramic-on-metal (CoM) bearings in total hip replacement. Whole blood metal ion levels were measured. The median increase in chromium and cobalt at 12 months was 0.08 μg/1 and 0.22 μg/1, respectively, in CoM bearings. Comparable values for metal-on-metal (MoM) were 0.48 μg/1 and 0.32 μg/1. The chromium levels were significantly lower in CoM than in MoM bearings (p = 0.02). The cobalt levels were lower, but the difference was not significant. Examination of two explanted ceramic heads revealed areas of thin metal transfer. CoM bearings (one explanted head and acetabular component, one explanted head and new acetabular component, and three new heads and acetabular components) were tested in a hip joint simulator. The explanted head and acetabular component had higher bedding-in. However, after one million cycles all the wear rates were the same and an order of magnitude less than that reported for MoM bearings. There were four outliers in each clinical group, primarily related to component malposition

Aims

A significant reduction in wear at five and ten years was previously reported when comparing Durasul highly cross-linked polyethylene with nitrogen-sterilized Sulene polyethylene in total hip arthroplasty (THA). We investigated whether the improvement observed at the earlier follow-up continued, resulting in decreased osteolysis and revision surgery rates over the second decade.

Aims

Head-taper corrosion is a cause of failure in total hip arthroplasty (THA). Recent reports have described an increasing number of V40 taper failures with adverse local tissue reaction (ALTR). However, the real incidence of V40 taper damage and its cause remain unknown. The aim of this study was to evaluate the long-term incidence of ALTR in a consecutive series of THAs using a V40 taper and identify potentially related factors.

Aims

The aim of this study was to evaluate the performance of first-generation annealed highly cross-linked polyethylene (HXLPE) in cementless total hip arthroplasty (THA).

Aims

Arthroplasty skills need to be acquired safely during training, yet operative experience is increasingly hard to acquire by trainees. Virtual reality (VR) training using headsets and motion-tracked controllers can simulate complex open procedures in a fully immersive operating theatre. The present study aimed to determine if trainees trained using VR perform better than those using conventional preparation for performing total hip arthroplasty (THA).

Aims

Vitamin E-diffused, highly crosslinked polyethylene (VEPE) and porous titanium-coated (PTC) shells were introduced in total hip arthroplasty (THA) to reduce the risk of aseptic loosening. The purpose of this study was: 1) to compare the wear properties of VEPE to moderately crosslinked polyethylene; 2) to assess the stability of PTC shells; and 3) to report their clinical outcomes at seven years.

Aims

This study reports the mid-term results of total hip arthroplasty (THA) performed using a monoblock acetabular component with a large-diameter head (LDH) ceramic-on-ceramic (CoC) bearing.

Aims

The purpose of this study was to compare two different types of metal-on-metal (MoM) bearing for total hip arthroplasty (THA): one with a large femoral head (38 mm to 52 mm) and the other with a conventional femoral head (28 mm or 32 mm). We compared clinical outcome, blood metal ion levels, and the incidence of pseudotumour in the two groups.

Aims

There are limited published data detailing the volumetric material loss from tapers of conventional metal-on-polyethylene (MoP) total hip arthroplasties (THAs). Our aim was to address this by comparing the taper wear rates measured in an explanted cohort of the widely used Exeter THA with those measured in a group of metal-on-metal (MoM) THAs.

We reviewed the literature on the currently available choices of bearing surface in total hip replacement (THR). We present a detailed description of the properties of articulating surfaces review the understanding of the advantages and disadvantages of existing bearing couples. Recent technological developments in the field of polyethylene and ceramics have altered the risk of fracture and the rate of wear, although the use of metal-on-metal bearings has largely fallen out of favour, owing to concerns about reactions to metal debris. As expected, all bearing surface combinations have advantages and disadvantages. A patient-based approach is recommended, balancing the risks of different options against an individual’s functional demands.

Cite this article: Bone Joint J 2014;96-B:147–56.

Oxidised zirconium (OxZi) has been developed as an alternative bearing surface for femoral heads in total hip arthroplasty (THA). This study has investigated polyethylene wear, functional outcomes and complications, comparing OxZi and cobalt–chrome (CoCr) as part of a three-arm, multicentre randomised controlled trial. Patients undergoing THA from four institutions were prospectively randomised into three groups. Group A received a CoCr femoral head and highly cross-linked polyethylene (XLPE) liner; Group B received an OxZi femoral head and XLPE liner; Group C received an OxZi femoral head and ultra-high molecular weight polyethylene (UHMWPE) liner. At five years, 368 patients had no statistically significant differences in short-form-36 (p = 0.176 mental, p = 0.756 physical), Western Ontario and McMaster Universities Osteoarthritis Index (p = 0.847), pain scores (p = 0.458) or complications. The mean rate of linear wear was 0.028 mm/year (standard deviation (sd) 0.010) for Group A, 0.023 mm/year (sd 0.010) for Group B, and 0.09 mm/year (sd 0.045) for Group C. Penetration was significantly higher in the UHMWPE liner group compared with both XLPE liner groups (p < 0.001) but no significant difference was noted between CoCr and OxZi when articulating with XLPE (p = 0.153). In this, the largest randomised study of this bearing surface, it appears that using a XLPE acetabular liner is more important in reducing THA component wear than the choice of femoral head bearing, at mid-term follow-up. There is a non-significant trend towards lower wear, coupling OxZi rather than CoCr with XLPE but long-term analysis is required to see if this observation changes with time and becomes significant.

Cite this article: Bone Joint J 2015;97-B:883–9.

In a double-blinded randomised controlled trial, 83 patients with primary osteoarthritis of the hip received either a ceramic-on-metal (CoM) or metal-on-metal (MoM) total hip replacement (THR). The implants differed only in the bearing surfaces used. The serum levels of cobalt and chromium and functional outcome scores were compared pre-operatively and at six and 12 months post-operatively.

Data were available for 41 CoM and 36 MoM THRs (four patients were lost to follow-up, two received incorrect implants). The baseline characteristics of both cohorts were similar. Femoral head size measured 36 mm in all but two patients who had 28 mm heads. The mean serum cobalt and chromium levels increased in both groups, with no difference noted between groups at six months (cobalt p = 0.67, chromium p = 0.87) and 12 months (cobalt p = 0.76, chromium p = 0.76) post-operatively. Similarly, the mean Oxford hip scores, Western Ontario and McMaster Universities Osteoarthritis index and University of California, Los Angeles activity scores showed comparable improvement at 12 months.

Our findings indicate that CoM and MoM couplings are associated with an equivalent increase in serum cobalt and chromium levels, and comparable functional outcome scores at six and 12-months follow-up.

We report the five-year outcome of a randomised controlled trial which used radiostereometric analysis (RSA) to assess the influence of surface oxidised zirconium (OxZr, Oxinium) on polyethylene wear in vivo.

A total of 120 patients, 85 women and 35 men with a mean age of 70 years (59 to 80) who were scheduled for primary cemented total hip arthroplasty were randomly allocated to four study groups. Patients were blinded to their group assignment and received either a conventional polyethylene (CPE) or a highly cross-linked (HXL) acetabular component of identical design. On the femoral side patients received a 28 mm head made of either cobalt-chromium (CoCr) or OxZr.

The proximal head penetration (wear) was measured with repeated RSA examinations over five years. Clinical outcome was measured using the Harris hip score.

There was no difference in polyethylene wear between the two head materials when used with either of the two types of acetabular component (p = 0.3 to 0.6). When comparing the two types of polyethylene there was a significant difference in favour of HXLPE, regardless of the head material used (p < 0.001).

In conclusion, we found no advantage of OxZr over CoCr in terms of polyethylene wear after five years of follow-up. Our findings do not support laboratory results which have shown a reduced rate of wear with OxZr. They do however add to the evidence on the better resistance to wear of HXLPE over CPE.

Cite this article: Bone Joint J 2015;97-B:1463–9.

Aims

We wished to investigate the influence of metal debris exposure on the subsequent immune response and resulting soft-tissue injury following metal-on-metal (MoM) hip arthroplasty. Some reports have suggested that debris generated from the head-neck taper junction is more destructive than equivalent doses from metal bearing surfaces.

The Articular Surface Replacement (ASR) hip resurfacing arthroplasty has a failure rate of 12.0% at five years, compared with 4.3% for the Birmingham Hip Resurfacing (BHR). We analysed 66 ASR and 64 BHR explanted metal-on-metal hip replacements with the aim of understanding their mechanisms of failure. We measured the linear wear rates of the acetabular and femoral components and analysed the clinical cause of failure, pre-revision blood metal ion levels and orientation of the acetabular component.

There was no significant difference in metal ion levels (chromium, p = 0.82; cobalt, p = 0.40) or head wear rate (p = 0.14) between the two groups. The ASR had a significantly increased rate of wear of the acetabular component (p = 0.03) and a significantly increased occurrence of edge loading (p < 0.005), which can be attributed to differences in design between the ASR and BHR. The effects of differences in design on the in vivo wear rates are discussed: these may provide an explanation as to why the ASR is more sensitive to suboptimal positioning than the BHR.

Second-generation metal-on-metal bearings were introduced as a response to the considerable incidence of wear-induced failures associated with conventional replacements, especially in young patients. We present the results at ten years of a consecutive series of patients treated using a metal-on-metal hip resurfacing. A distinct feature of the bearings used in our series was that they had been subjected to double-heat treatments during the post-casting phase of their manufacture. In the past these bearings had not been subjected to thermal treatments, making this a unique metal-on-metal bearing which had not been used before in clinical practice.

We report the outcome of 184 consecutive hips (160 patients) treated using a hybrid-fixed metal-on-metal hip resurfacing during 1996. Patients were invited for a clinicoradiological follow-up at a minimum of ten years. The Oxford hip score and anteroposterior and lateral radiographs were obtained. The mean age at operation was 54 years (21 to 75). A series of 107 consecutive hips (99 patients) who received the same prosthesis, but subjected to a single thermal treatment after being cast, between March 1994 and December 1995, were used as a control group for comparison.

In the 1994 to 1995 group seven patients (seven hips) died from unrelated causes and there were four revisions (4%) for osteolysis and aseptic loosening. In the 1996 group nine patients died at a mean of 6.9 years after operation because of unrelated causes. There were 30 revisions (16%) at a mean of 7.3 years (1.2 to 10.9), one for infection at 1.2 years and 29 for osteolysis and aseptic loosening. Furthermore, in the latter group there were radiological signs of failure in 27 (24%) of the 111 surviving hips.

The magnitude of the problem of osteolysis and aseptic loosening in the 1996 cohort did not become obvious until five years after the operation. Our results indicate that double-heat treatments of metal-on-metal bearings can lead to an increased incidence of wear-induced osteolysis.

We studied 33 third generation, alumina ceramic-on-ceramic bearings retrieved from cementless total hip replacements after more than six months in situ. Wear volume was measured with a Roundtest machine, and acetabular orientation from the anteroposterior pelvic radiograph. The overall median early wear rate was 0.1 mm³/yr for the femoral heads, and 0.04 mm³/yr for the acetabular liners. We then excluded hips where the components had migrated. In this stable subgroup of 22 bearings, those with an acetabular anteversion of < 15° (seven femoral heads) had a median femoral head wear rate of 1.2 mm³/yr, compared with 0 mm³/yr for those with an anteversion of ≥15° (15 femoral heads, p < 0.001). Even under edge loading, wear volumes with ceramic-on-ceramic bearings are small in comparison to other bearing materials. Low acetabular anteversion is associated with greater wear.

The peri-prosthetic tissue response to wear debris is complex and influenced by various factors including the size, area and number of particles. We hypothesised that the ‘biologically active area’ of all metal wear particles may predict the type of peri-prosthetic tissue response.

Peri-prosthetic tissue was sampled from 21 patients undergoing revision of a small diameter metal-on-metal (MoM) total hip arthroplasty (THA) for aseptic loosening. An enzymatic protocol was used for tissue digestion and scanning electron microscope was used to characterise particles. Equivalent circle diameters and particle areas were calculated. Histomorphometric analyses were performed on all tissue specimens. Aspirates of synovial fluid were collected for analysis of the cytokine profile analysis, and compared with a control group of patients undergoing primary THA (n = 11) and revision of a failed ceramic-on-polyethylene arthroplasty (n = 6).

The overall distribution of the size and area of the particles in both lymphocyte and non-lymphocyte-dominated responses were similar; however, the subgroup with lymphocyte-dominated peri-prosthetic tissue responses had a significantly larger total number of particles.

14 cytokines (interleukin (IL)-1ß, IL-2, IL-4, IL-5, IL-6, IL-10, IL-13, IL-17, interferon (IFN)-γ, and IFN-gamma-inducible protein 10), chemokines (macrophage inflammatory protein (MIP)-1α and MIP-1ß), and growth factors (granulocyte macrophage colony stimulating factor (GM-CSF) and platelet derived growth factor) were detected at significantly higher levels in patients with metal wear debris compared with the control group.

Significantly higher levels for IL-1ß, IL-5, IL-10 and GM-CSF were found in the subgroup of tissues from failed MoM THAs with a lymphocyte-dominated peri-prosthetic response compared with those without this response.

These results suggest that the ‘biologically active area’ predicts the type of peri-prosthetic tissue response. The cytokines IL-1ß, IL-5, IL-10, and GM-CSF are associated with lymphocyte-dominated tissue responses from failed small-diameter MoM THA.

Cite this article: Bone Joint J 2015;97-B:917–23.

Large femoral heads have become popular in total hip replacement (THR) as a method of reducing the risk of dislocation. However, if large heads are used in ceramic-on-ceramic THR, the liner must be thinner, which may increase the risk of fracture. To compare the rates of ceramic fracture and dislocation between 28 mm and 32 mm ceramic heads, 120 hips in 109 patients (51 men and 58 women, mean age 49.2 years) were randomised to THR with either a 28 mm or a 32 mm ceramic articulation. A total of 57/60 hips assigned to the 28 mm group and 55/60 hips assigned to the 32 mm group were followed for at least five years. No ceramic component fractures occured in any patient in either group. There was one dislocation in the 32 mm group and none in the 28 mm group (p = 0.464). No hip had detectable wear, focal osteolysis or prosthetic loosening. In our small study the 32 mm ceramic articulation appeared to be safe in terms of ceramic liner fracture.

Cite this article: Bone Joint J 2014;96-B:1459–63.

Bioengineering reasons for increased wear and failure of metal-on-metal (MoM) bearings in hip prostheses have been described. Low wear occurs in MoM hips when the centre of the femoral head is concentric with the centre of the acetabular component and the implants are correctly positioned. Translational or rotational malpositioning of the components can lead to the contact-patch of the femoral component being displaced to the rim of the acetabular component, resulting in a ten- to 100-fold increase in wear and metal ion levels. This may cause adverse tissue reactions, loosening of components and failure of the prosthesis.