Modular dual-mobility (DM) articulations are increasingly used during total hip arthroplasty (THA). However, concerns remain regarding the metal liner modularity. This study aims to correlate metal artifact reduction sequence (MARS)-MRI abnormalities with serum metal ion levels in patients with DM articulations. A total of 45 patients (50 hips) with a modular DM articulation were included with mean follow-up of 3.7 years (SD 1.2). Enrolled patients with an asymptomatic, primary THA and DM articulation with over two years’ follow-up underwent MARS-MRI. Each patient had serum cobalt, chromium, and titanium levels drawn. Patient satisfaction, Oxford Hip Score, and Forgotten Joint Score-12 (FJS-12) were collected. Each MARS-MRI was independently reviewed by fellowship-trained musculoskeletal radiologists blinded to serum ion levels.Aims
Methods
Taper corrosion has been widely reported to be problematic for modular total hip arthroplasty implants. A simple and systematic method to evaluate taper damage with sufficient resolution is needed. We introduce a semiquantitative grading system for modular femoral tapers to characterize taper corrosion damage. After examining a unique collection of retrieved cobalt-chromium (CoCr) taper sleeves (n = 465) using the widely-used Goldberg system, we developed an expanded six-point visual grading system intended to characterize the severity, visible material loss, and absence of direct component contact due to corrosion. Female taper sleeve damage was evaluated by three blinded observers using the Goldberg scoring system and the expanded system. A subset (n = 85) was then re-evaluated following destructive cleaning, using both scoring systems. Material loss for this subset was quantified using metrology and correlated with both scoring systems.Aims
Methods
Head-taper corrosion is a cause of failure in total hip arthroplasty (THA). Recent reports have described an increasing number of V40 taper failures with adverse local tissue reaction (ALTR). However, the real incidence of V40 taper damage and its cause remain unknown. The aim of this study was to evaluate the long-term incidence of ALTR in a consecutive series of THAs using a V40 taper and identify potentially related factors. Between January 2006 and June 2007, a total of 121 patients underwent THA using either an uncemented (Accolade I, made of Ti12Mo6Zr2Fe; Stryker, USA) or a cemented (ABG II, made of cobalt-chrome-molybdenum (CoCrMo); Stryker) femoral component, both with a V40 taper (Stryker). Uncemented acetabular components (Trident; Stryker) with crosslinked polyethylene liners and CoCr femoral heads of 36 mm diameter were used in all patients. At a mean folllow-up of 10.8 years (SD 1.1), 94 patients (79%) were eligible for follow-up (six patients had already undergone a revision, 15 had died, and six were lost to follow-up). A total of 85 THAs in 80 patients (mean age 61 years (24 to 75); 47 (56%) were female) underwent clinical and radiological evaluation, including the measurement of whole blood levels of cobalt and chrome. Metal artifact reduction sequence MRI scans of the hip were performed in 71 patients.Aims
Methods
This study investigates head-neck taper corrosion with varying head size in a novel hip simulator instrumented to measure corrosion related electrical activity under torsional loads. In all, six 28 mm and six 36 mm titanium stem-cobalt chrome head pairs with polyethylene sockets were tested in a novel instrumented hip simulator. Samples were tested using simulated gait data with incremental increasing loads to determine corrosion onset load and electrochemical activity. Half of each head size group were then cycled with simulated gait and the other half with gait compression only. Damage was measured by area and maximum linear wear depth.Aims
Methods
Aims. This study aims to enhance understanding of clinical and radiological consequences and involved mechanisms that led to corrosion of the Precice Stryde (Stryde) intramedullary lengthening nail in the post market surveillance era of the device. Between 2018 and 2021 more than 2,000 Stryde nails have been implanted worldwide. However, the outcome of treatment with the Stryde system is insufficiently reported. Methods. This is a retrospective single-centre study analyzing outcome of 57 consecutive lengthening procedures performed with the Stryde nail at the authors’ institution from February 2019 until November 2020. Macro- and microscopic metallographic analysis of four retrieved nails was conducted. To investigate observed corrosion at telescoping junction, scanning electron microscopy (SEM) and energy dispersive x-ray spectroscopy (EDX) were performed. Results. Adjacent to the nail’s telescoping junction, osteolytic changes were observed in bi-planar radiographs of 20/57 segments (35%) after a mean of 9.5 months (95% confidence interval 7.2 to 11.9) after surgery. A total of 8/20 patients with osseous alterations (40%) reported rest and ambulation pain of the lengthened segment during consolidation. So far, 24 Stryde nails were retrieved and in 20 (83%) macroscopic corrosion was observed at the nail’s telescoping junction. Before implant removal 11/20 radiographs (55%) of lengthened segments with these 20 nails revealed osteolysis. Implant retrieval analysis by means of SEM showed pitting and
Aims. Dual mobility implants in total hip arthroplasty are designed to increase the functional head size, thus decreasing the potential for dislocation. Modular dual mobility (MDM) implants incorporate a metal liner (e.g. cobalt-chromium alloy) in a metal shell (e.g. titanium alloy), raising concern for mechanically assisted
Dual mobility (DM) implants have been shown to reduce the dislocation rate after total hip arthroplasty (THA), but there remain concerns about the use of cobalt chrome liners inserted into titanium shells. The aim of this study was to assess the clinical outcomes, metal ion levels, and periprosthetic femoral bone mineral density (BMD) at mid-term follow-up in young, active patients receiving a modular DM THA. This was a prospective study involving patients aged < 65 years, with a BMI of < 35 kg/m2, and University of California, Los Angeles activity score of > 6 who underwent primary THA with a modular cobalt chrome acetabular liner, highly cross-linked polyethylene mobile bearing, and a cementless titanium femoral stem. Patient-reported outcome measures, whole blood metal ion levels (μg/l), and periprosthetic femoral BMD were measured at baseline and at one, two, and five years postoperatively. The results two years postoperatively for this cohort have been previously reported.Aims
Methods
The aims of this study were to evaluate wear on the surface of cobalt-chromium (CoCr) femoral components used in total knee arthroplasty (TKA) and compare the wear of these components with that of ceramic femoral components. Optical profilometry was used to evaluate surface roughness and to examine the features created by the wear process in a knee wear simulator. We developed a method of measuring surface changes on five CoCr femoral components and quantifying the loss of material from the articular surface during the wear process. We also examined the articular surface of three ceramic femoral components from a previous test for evidence of surface damage, and compared it with that of CoCr components.Aims
Methods
The aim of this study was to develop a novel computational model for estimating head/stem taper mechanics during different simulated assembly conditions. Finite element models of generic cobalt-chromium (CoCr) heads on a titanium stem taper were developed and driven using dynamic assembly loads collected from clinicians. To verify contact mechanics at the taper interface, comparisons of deformed microgroove characteristics (height and width of microgrooves) were made between model estimates with those measured from five retrieved implants. Additionally, these models were used to assess the role of assembly technique—one-hit versus three-hits—on the taper interlock mechanical behaviour.Aims
Methods
We have previously demonstrated raised cobalt and chromium levels in patients with larger diameter femoral heads, following metal-on-polyethylene uncemented total hip arthroplasty. Further data have been collected, to see whether these associations have altered with time and to determine the long-term implications for these patients and our practice. Patients from our previous study who underwent Trident-Accolade primary total hip arthroplasties using a metal-on-polyethylene bearing in 2009 were reviewed. Patients were invited to have their cobalt and chromium levels retested, and were provided an Oxford Hip Score. Serum ion levels were then compared between groups (28 mm, 36 mm, and 40 mm heads) and over time.Aims
Methods
This combined clinical and in vitro study aimed to determine the incidence of liner malseating in modular dual mobility (MDM) constructs in primary total hip arthroplasties (THAs) from a large volume arthroplasty centre, and determine whether malseating increases the potential for fretting and corrosion at the modular metal interface in malseated MDM constructs using a simulated corrosion chamber. For the clinical arm of the study, observers independently reviewed postoperative radiographs of 551 primary THAs using MDM constructs from a single manufacturer over a three-year period, to identify the incidence of MDM liner-shell malseating. Multivariable logistic regression analysis was performed to identify risk factors including age, sex, body mass index (BMI), cup design, cup size, and the MDM case volume of the surgeon. For the in vitro arm, six pristine MDM implants with cobalt-chrome liners were tested in a simulated corrosion chamber. Three were well-seated and three were malseated with 6° of canting. The liner-shell couples underwent cyclic loading of increasing magnitudes. Fretting current was measured throughout testing and the onset of fretting load was determined by analyzing the increase in average current.Aims
Methods
This study aimed to determine if macrophages can attach and directly affect the oxide layers of 316L stainless steel, titanium alloy (Ti6Al4V), and cobalt-chromium-molybdenum alloy (CoCrMo) by releasing components of these alloys. Murine peritoneal macrophages were cultured and placed on stainless steel, CoCrMo, and Ti6Al4V discs into a 96-well plate. Cells were activated with interferon gamma and lipopolysaccharide. Macrophages on stainless steel discs produced significantly more nitric oxide (NO) compared to their control counterparts after eight to ten days and remained elevated for the duration of the experiment.Aims
Methods
In patients with a “dry” aspiration during the investigation of prosthetic joint infection (PJI), saline lavage is commonly used to obtain a sample for analysis. The aim of this study was to investigate prospectively the impact of saline lavage on synovial fluid analysis in revision arthroplasty. Patients undergoing revision hip (THA) or knee arthroplasty (TKA) for any septic or aseptic indication were enrolled. Intraoperatively, prior to arthrotomy, the maximum amount of fluid possible was aspirated to simulate a dry tap (pre-lavage) followed by the injection with 20 ml of normal saline and re-aspiration (post-lavage). Pre- and post-lavage synovial white blood cell (WBC) count, percent polymorphonuclear cells (%PMN), and cultures were compared.Aims
Methods
We evaluated a large database with mechanical failure of a single uncemented modular femoral component, used in revision hip arthroplasty, as the end point and compared them to a control group treated with the same implant. Patient- and implant-specific risk factors for implant failure were analyzed. All cases of a fractured uncemented modular revision femoral component from one manufacturer until April 2017 were identified and the total number of implants sold until April 2017 was used to calculate the fracture rate. The manufacturer provided data on patient demographics, time to failure, and implant details for all notified fractured devices. Patient- and implant-specific risk factors were evaluated using a logistic regression model with multiple imputations and compared to data from a previously published reference group, where no fractures had been observed. The results of a retrieval analysis of the fractured implants, performed by the manufacturer, were available for evaluation.Aims
Methods
Fretting and corrosion at the modular head/neck junction, known
as trunnionosis, in total hip arthroplasty (THA) is a cause of adverse
reaction to metal debris (ARMD). We describe the outcome of revision
of metal-on-polyethylene (MoP) THA for ARMD due to trunnionosis
with emphasis on the risk of major complications. A total of 36 patients with a MoP THA who underwent revision
for ARMD due to trunnionosis were identified. Three were excluded
as their revision had been to another metal head. The remaining
33 were revised to a ceramic head with a titanium sleeve. We describe
the presentation, revision findings, and risk of complications in
these patients.Aims
Patients and Methods
To present a surgically relevant update of trunnionosis. Systematic review performed April 2017.Aims
Materials and Methods
Many case reports and small studies have suggested that cobalt
ions are a potential cause of cardiac complications, specifically
cardiomyopathy, after metal-on-metal (MoM) total hip arthroplasty
(THA). The impact of metal ions on the incidence of cardiac disease
after MoM THA has not been evaluated in large studies. The aim of
this study was to compare the rate of onset of new cardiac symptoms
in patients who have undergone MoM THA with those who have undergone
metal-on-polyethylene (MoP) THA. Data were extracted from the Standard Analytics Files database
for patients who underwent MoM THA between 2005 and 2012. Bearing
surface was selected using International Classification of Diseases
ninth revision codes. Patients with a minimum five-year follow-up
were selected. An age and gender-matched cohort of patients who underwent
MoP THA served as a comparison group. New diagnoses of cardiac disease
were collected during the follow-up period. Comorbidities and demographics
were identified and routine descriptive statistics were used.Aims
Patients and Methods
We sought to determine whether cobalt-chromium alloy (CoCr) femoral
stem tapers (trunnions) wear more than titanium (Ti) alloy stem
tapers (trunnions) when used in a large diameter (LD) metal-on-metal
(MoM) hip arthroplasty system. We performed explant analysis using validated methodology to
determine the volumetric material loss at the taper surfaces of
explanted LD CoCr MoM hip arthroplasties used with either a Ti alloy
(n = 28) or CoCr femoral stem (n = 21). Only 12/14 taper constructs
with a rough male taper surface and a nominal included angle close
to 5.666° were included. Multiple regression modelling was undertaken
using taper angle, taper roughness, bearing diameter (horizontal
lever arm) as independent variables. Material loss was mapped using
a coordinate measuring machine, profilometry and scanning electron
microscopy.Aims
Patients and Methods