Aims. We aimed to investigate if the use of the largest possible cobalt-chromium head articulating with polyethylene acetabular inserts would increase the in vivo wear rate in total hip arthroplasty. Methods. In a single-blinded randomized controlled trial, 96 patients (43 females), at a median age of 63 years (interquartile range (IQR) 57 to 69), were allocated to receive either the largest possible modular femoral head (36 mm to 44 mm) in the thinnest possible insert or a standard 32 mm
Aims. Head-taper corrosion is a cause of failure in total hip arthroplasty (THA). Recent reports have described an increasing number of V40 taper failures with adverse local tissue reaction (ALTR). However, the real incidence of V40 taper damage and its cause remain unknown. The aim of this study was to evaluate the long-term incidence of ALTR in a consecutive series of THAs using a V40 taper and identify potentially related factors. Methods. Between January 2006 and June 2007, a total of 121 patients underwent THA using either an uncemented (Accolade I, made of Ti. 12. Mo. 6. Zr. 2. Fe; Stryker, USA) or a cemented (ABG II, made of cobalt-chrome-molybdenum (CoCrMo); Stryker) femoral component, both with a V40 taper (Stryker). Uncemented acetabular components (Trident; Stryker) with crosslinked polyethylene liners and CoCr femoral heads of 36 mm diameter were used in all patients. At a mean folllow-up of 10.8 years (SD 1.1), 94 patients (79%) were eligible for follow-up (six patients had already undergone a revision, 15 had died, and six were lost to follow-up). A total of 85 THAs in 80 patients (mean age 61 years (24 to 75); 47 (56%) were female) underwent clinical and radiological evaluation, including the measurement of whole blood levels of cobalt and chrome. Metal artifact reduction sequence MRI scans of the hip were performed in 71 patients. Results. A total of 20 ALTRs were identified on MRI, with an incidence of 26%. Patients with ALTR had significantly higher median Co levels compared with those without ALTR (2.96 μg/l (interquartile range (IQR) 1.35 to 4.98) vs 1.44 μg/l (IQR 0.79 to 2.5); p = 0.019). Radiological evidence of osteolysis was also significantly associated with ALTR (p = 0.014). Median Cr levels were not significantly higher in those with ALTR compared with those without one (0.97 μg/l (IQR 0.72 to 1.9) v 0.67 μg/l (IQR 0.5 to 1.19; p = 0.080). BMI, sex, age, type of femoral component,
Aims. This study investigates head-neck taper corrosion with varying
Aims. The primary outcome was investigating differences in wear, as measured by femoral head penetration, between cross-linked vitamin E-diffused polyethylene (vE-PE) and cross-linked polyethylene (XLPE) acetabular component liners and between 32 and 36 mm
Aims. The aim of this study was to evaluate fretting and corrosion in retrieved oxidized zirconium (OxZr; OXINIUM, Smith & Nephew, Memphis, Tennessee) femoral heads and compare the results with those from a matched cohort of cobalt-chromium (CoCr) femoral heads. Patients and Methods. A total of 28 OxZr femoral heads were retrieved during revision total hip arthroplasty (THA) and matched to 28 retrieved CoCr
Large femoral heads have been used with increasing
frequency over the last decade. The prime reason is likely the effect
of large
Aims. The most frequent indication for revision surgery in total hip arthroplasty (THA) is aseptic loosening. Aseptic loosening is associated with polyethylene liner wear, and wear may be reduced by using vitamin E-doped liners. The primary objective of this study was to compare proximal femoral head penetration into the liner between a) two cross-linked polyethylene (XLPE) liners (vitamin E-doped (vE-PE)) versus standard XLPE liners, and b) two modular femoral head diameters (32 mm and 36 mm). Methods. Patients scheduled for a THA were randomized to receive a vE-PE or XLPE liner with a 32 mm or 36 mm metal
Objectives. Modular junctions are ubiquitous in contemporary hip arthroplasty. The head-trunnion junction is implicated in the failure of large diameter metal-on-metal (MoM) hips which are the currently the topic of one the largest legal actions in the history of orthopaedics (estimated costs are stated to exceed $4 billion). Several factors are known to influence the strength of these press-fit modular connections. However, the influence of different
Objectives. Our primary aim was to describe migration of the Exeter stem with a 32 mm
Aims. Modular dual-mobility constructs reduce the risk of dislocation after revision total hip arthroplasty (THA). However, questions about metal ions from the cobalt-chromium (CoCr) liner persist, and are particularly germane to patients being revised for adverse local tissue reactions (ALTR) to metal. We determined the early- to mid-term serum Co and Cr levels after modular dual-mobility components were used in revision and complex primary THAs, and specifically included patients revised for ALTR. Patients and Methods. Serum Co and Cr levels were measured prospectively in 24 patients with a modular dual-mobility construct and a ceramic femoral head. Patients with CoCr
Although alumina has been used in orthopaedic surgery since the 1970s, the long-term clinical results of zirconia have not been well documented in vivo. We studied hips with these two different ceramics during the same period and with a minimum follow-up of ten years. Because the size of the alumina and zirconia
It has been suggested that the wear of ultra-high molecular weight polyethylene (UHMWPE) in total hip replacement is substantially reduced when the femoral head is ceramic rather than metal. However, studies of alumina and zirconia ceramic femoral heads on the penetration of an UHMWPE liner in vivo have given conflicting results. The purpose of this study was to examine the surface characteristics of 30 alumina and 24 zirconia ceramic femoral heads and to identify any phase transformation in the zirconia
We investigated the incidence of soft-tissue
lesions after small
We compared the incidence of pseudotumours after
large
We report two cases of surface deterioration of a zirconia ceramic femoral head associated with phase transformation after total hip arthroplasty. One
We compared a modular neck system with a non-modular system in a cementless anatomical total hip replacement (THR). Each group consisted of 74 hips with developmental hip dysplasia. Both groups had the same cementless acetabular component and the same articulation, which consisted of a conventional polyethylene liner and a 28 mm alumina
The vertical-centre-anterior margin (VCA) angle quantifies the anterior cover of the femoral head. However, when the femoral head is deformed it may be difficult to identify its centre. We have therefore created a new index, the anterior acetabular
Implantation of a large-diameter femoral head prosthesis with a metal-on-metal bearing surface reduces the risk of dislocation, increases the range of movement, minimises the risk of impingement and, in theory, results in little wear. Between February 2004 and March 2007 we implanted 100 consecutive total hip replacements with a metal-on-metal bearing and a large femoral head into 92 patients. There were 51 men and 41 women with a mean age of 50 years (18 to 70) at the time of surgery. Outcome was assessed using the Western Ontario McMaster University osteoarthritis index and the Harris hip score as well as the Devane activity score. These all improved significantly (p <
0.0001). At the last follow-up there were no cases of dislocation, no impingement, a good range of movement and no osteolysis, but seven revisions, two for infection and five for aseptic loosening. The probability of groin pain increased if the other acetabular component inclination exceeded 50° (p = 0.0007). At 4.8 years of follow-up, the projected survival of the Durom acetabular component, with revision for any reason, was 92.4% ( The design of the component made it difficult both to orientate and seat, which when combined with a poor porous coating, produced unpredictable fixation and a low survival at five years.
We have compared different types of intertrochanteric osteotomy for avascular of necrosis of the hip and evaluated their performance in the light of improving outcome after total hip arthroplasty (THA). During a period of 14 years we performed 63 flexion osteotomies (partly combined with varus or valgus displacement), 29 rotational osteotomies, 13 varus osteotomies, eight medialising osteotomies and two extension osteotomies. The mean period of follow-up for all 115 operations was 7.3 years (maximum 24.6). At follow-up, 27 of 29 patients with a rotational osteotomy had already undergone a THA, compared with 36 of 63 after flexion osteotomy. A high incidence of complications (55.2%) was seen early after rotational osteotomy, compared with 17.5% after flexion osteotomy. For all osteotomies there was a high correlation between the size of the necrotic area and the incidence of failure, which also correlated with the preoperative Ficat and Steinberg stages. Using Kaplan-Meier survivorship analysis, Sugioka’s rotational osteotomy showed a survival probability after five years of 0.26 (95% confidence interval 0.49 to 0.14), and after ten years of 0.15 (CI 0.36 to 0.06). The survival probability for flexion osteotomy was 0.70 (CI 0.83 to 0.59) after five years and 0.50 (CI 0.65 to 0.38) after ten years. The subgroup of flexion osteotomy with a necrotic sector of less than 180° achieved the best survival probability of 0.90 (CI 1.00 to 0.80) after five years and 0.61 (CI 0.84 to 0.45) after ten years. The indications for intertrochanteric osteotomy for avascular necrosis of the hip have to be addressed critically. Even flexion osteotomy in cases with small areas of necrosis provides only temporary benefit. Rotational osteotomy was associated with a high incidence of complications.
We describe three prostheses with cemented titanium-alloy stems and Al2O3 ceramic femoral heads which had to be revised after a mean period of implantation of 78 months. In each case, the neck of the prosthesis had been so severely worn that the profile was elliptical rather than circular. There was severe metallosis of the periprosthetic tissues. Metal particles isolated from the tissues were approximately one nanometre in size and the ratios of titanium, aluminium and vanadium in the particles were the same as in the original alloy. Histologically, the high concentration of metal particles masked the presence of high-density polyethylene (HDP) debris, but again particles about one nanometre in size were isolated from the tissues. The severe necrobiosis and necrosis noted were consistent with other reports of the presence of extensive wear particles in periprosthetic tissues. Wear is presumed to have occurred as a result of mismatch between the shape or size of the taper cone and the femoral head, or to changes in the geometry of loading due to migration of the cup. To facilitate early intervention, patients with this design of prosthesis should be monitored radiologically.