The augmentation of fixation with bone cement is increasingly being used in the treatment of severe osteoporotic fractures. We investigated the influence of bone quality on the mechanics of augmentation of plate fixation in a distal femoral fracture model (AO 33 A3 type). Eight osteoporotic and eight non-osteoporotic femoral models were randomly assigned to either an augmented or a non-augmented group. Fixation was performed using a locking compression plate. In the augmented group additionally 1 ml of bone cement was injected into the screw hole before insertion of the screw. Biomechanical testing was performed in axial sinusoidal loading. Augmentation significantly reduced the cut-out distance in the osteoporotic models by about 67% (non-augmented mean 0.30 mm (sd 0.08) vs augmented 0.13 mm (sd 0.06); p = 0.017). There was no statistical reduction in this distance following augmentation in the non-osteoporotic models (non-augmented mean 0.15 mm (sd 0.02) vs augmented 0.15 mm (sd 0.07); p = 0.915). In the osteoporotic models, augmentation significantly increased stability (p = 0.017).

Cite this article: Bone Joint J 2013;95-B:1406–9.

Filling the empty holes in peri-articular locking plates may improve the fatigue strength of the fixation. The purpose of this in vitro study was to investigate the effect of plugging the unused holes on the fatigue life of peri-articular distal femoral plates used to fix a comminuted supracondylar fracture model.

A locking/compression plate was applied to 33 synthetic femurs and then a 6 cm metaphyseal defect was created (AO Type 33-A3). The specimens were then divided into three groups: unplugged, plugged with locking screw only and fully plugged holes. They were then tested using a stepwise or run-out fatigue protocol, each applying cyclic physiological multiaxial loads.

All specimens in the stepwise group failed at the 770 N load level. The mean number of cycles to failure for the stepwise specimen was 25 500 cycles (sd 1500), 28 800 cycles (sd 6300), and 26 400 cycles (sd 2300) cycles for the unplugged, screw only and fully plugged configurations, respectively (p = 0.16). The mean number of cycles to failure for the run-out specimens was 42 800 cycles (sd 10 700), 36 000 cycles (sd 7200), and 36 600 cycles (sd 10 000) for the unplugged, screw only and fully plugged configurations, respectively (p = 0.50). There were also no differences in axial or torsional stiffness between the constructs. The failures were through the screw holes at the level of comminution.

In conclusion, filling the empty combination locking/compression holes in peri-articular distal femur locking plates at the level of supracondylar comminution does not increase the fatigue life of the fixation in a comminuted supracondylar femoral fracture model (AO 33-A3) with a 6 cm gap.