We report a long-term review of 60 acetabular components revised using impacted, morsellised bone allografts and a cemented polyethylene cup. The acetabular defects were cavitary (37) or combined (23). Follow-up was for a mean 11.8 years (10 to 15). Further revision was needed in five hips, two for septic and three for aseptic loosening. The overall survival rate at 11.8 years was 90%; excluding the septic cases it was 94%. Acetabular reconstruction with impacted morsellised cancellous grafts and cement gives satisfactory long-term results

The rotator cuff is often severely damaged in arthritis of the shoulder and there is no satisfactory technique for its repair. patients with a ruptured cuff and an eroded glenohumeral joint may have intractable pain, and standard methods of joint replacement are then inappropriate. A ball and socket prosthesis has been designed to replace the function of both the rotator cuff and the glenohumeral joint. Mechanical testing has shown that the scapular cup can be securely fixed. The outcome in 71 shoulders operated upon since 1973 is reported

We report the results of our continued review of 14 hip arthroplasties using alumina ceramic femoral heads with cross-linked polyethylene cups. There have been no complications and a very low rate of penetration. This was 0.02 mm per year after an initial ‘bedding-in’ period of two years. There has been no change in the mean rate between our earlier study at six years and the current results at 10 to 11 years. The use of these bearing surfaces appears to reduce the potential amount of polyethylene debris and may provide the next logical stage in the development of the Charnley low-friction arthroplasty

We examined 59 cemented high density polyethylene sockets removed at revision hip arthroplasty. Of these 19 showed areas of wear between the outside of the socket and the acetabular bone. This was associated with lack of acrylic cement in those areas and was also related to the depth of the wear on the articulating surface of the socket. It is suggested that, in some cases, changes at the bone-cement junction are secondary to socket loosening and abrasion against the bone of the acetabulum, rather than to particles migrating from the metal-polyethylene interface. It is therefore important that impingement of the neck of the femoral stem on the edge of the cup be avoided and that, when the socket is inserted, it is not in direct contact with the bone

We reviewed 120 consecutive primary total hip replacements in 109 patients in whom a Freeman uncemented metal-backed component had been used. Acetabular components were used with a Freeman neck-retaining stem in one of three configurations: cemented smooth stem, uncemented smooth stem or uncemented ridged stem. After a mean follow up of 72 months (62 to 113) there were nine cases of aseptic loosening; a survivorship at eight years of 83%. In addition, more than one-third of the remaining surviving cups showed loosening radiologically. The Freeman acetabular component demonstrated a characteristic pattern of loosening on radiographs. The high incidence of aseptic loosening can be explained by poor design and material failure

We used radiostereometric analysis to compare wear rates between uncemented porous sockets and cemented all-polyethylene sockets in a series of 102 hips randomised for either a Harris-Galante or a Charnley cup. Wear was evaluated in 95 hips at a mean of five years (2 to 7). All hips had a cemented, 22 mm head mono-bloc Charnley stem. The mean annual wear rate was 0.09 mm in the Charnley sockets and 0.10 mm in the Harris-Galante sockets, with no statistically significant differences in wear, migration or rotation. We conclude that, up to five years, the wear characteristics of the modular and porous Harris-Galante socket resemble that of the Charnley socket

We reviewed 261 patients with 320 Charnley low-friction arthroplasties who had a mean follow-up of 22 years 10 months (20 to 30). Of these, 93.9% considered the operation to be a success; 82.3% were free from pain and 11.6% had occasional discomfort. Satisfactory function was achieved in 59.6% and 62% had an excellent range of movement. The clinical results did not correlate well with the radiological appearance; radiologically loose components did not affect the clinical outcome. The main long-term problem was wear and loosening of the UHMWPE cup. Our findings suggest that the radiological appearance of the arthroplasty is a more reliable indication of the state of the arthroplasty than the clinical results

Four en-bloc resections for malignant tumours of the hip, the peri-acetabular region and the iliac wing were reconstructed using an irradiated hemipelvic allograft together with a total hip prosthesis. Technical aspects include the use of an anterior Enneking approach which excises the previous biopsy site, division and re-attachment of the iliac crest and fixation of the prosthesis using a modified acetabular cup and three polypropylene artificial ligaments to increase the stability of the joint. Weight-bearing was allowed at three months. The oncological and clinical results were satisfactory after a mean follow-up of 19 months, with walking distances of 500 metres to two kilometres without pain

We report the results of 24 acetabular reconstructions in which cemented polyethylene cups and tamped corticocancellous allografts were used for severe acetabular bone deficiency. Eleven hips had type-II (cavitary) bone deficiency and 13 had type-III (combined) defects. At a mean follow-up of 5.8 years, two components had migrated more than 5 mm and had accompanying radiolucent zones of more than 2 mm width. A radiolucency 5 mm wide was also seen in zone III of an acetabular implant which had not migrated. None of the patients had required revision because of loosening or infection

We implanted 203 smooth-stemmed femoral components before January 1988. The femoral component used was anatomically shaped, fluted and made of titanium. Thirty-two hips were revised due to mid-thigh pain, and the femoral implant was found to be loose in all. In the 157 patients with a two-year follow-up, the Merle d'Aubigne and pain scores for completely cementless arthroplasties were similar to those for hybrid prostheses (cemented acetabular cup and cementless femoral stem). Of the 145 cases with two-year radiographic follow-up, 59 had extensive radiolucencies and 22 were unstable. The five-year cumulative survival rate was 77%. Implantation of this stem should be restricted to patients in whom cement fixation is contra-indicated

We enrolled 98 patients (107 hips) with a mean age of 47 years (SD 8.6) into a prospective study of the Madreporic Lord THR; 34 hips had primary and 73 secondary osteoarthritis. After ten years, the survival rate using revision as the endpoint for failure was 70% (±9) for the cup and 98% (±0.3) for the stem. The combined clinical and radiological survival rates were 46% (±11) and 81% (±10), respectively. Osteoporosis due to stress-shielding was observed in the proximal femur. Hips with radiologically dense bone postoperatively showed the most pronounced bone loss. We recommend continued radiological follow-up of patients with this type of implant to allow revision to be performed before there is severe bony destruction of the pelvis

Osteolysis is due to particulate wear debris and is responsible for the long-term failure of total hip replacements. It has stimulated the development of alternative joint surfaces such as metal-on-metal or ceramic-on-ceramic implants. Since 1988 the second-generation metal-on-metal implant Metasul has been used in over 60 000 hips. Analysis of 118 retrieved specimens of the head or cup showed rates of wear of approximately 25 μm for the whole articulation per year in the first year, decreasing to about 5 μm per year after the third. Metal surfaces have a ‘self-polishing’ capacity. Scratches are worn out by further joint movement. Volumetric wear was decreased some 60-fold compared with that of metal-on-polyethylene implants, suggesting that second-generation metal-on-metal prostheses may considerably reduce osteolysis

Total hip replacement has been very successful in patients with painful, stiff hips associated with protrusio acetabuli, but the heat of polymerisation of methylmethacrylate cement may cause necrosis of the thin medial wall with consequent danger of migration of the cup. Since 1968 at Wrightington, thin slices of the head of the femur have been used as bone grafts to reinforce the acetabulum. We have reviewed 61 hips in 51 patients at an average of 4 years 3 months after operation. Grading for severity is discussed and the degree of physiological remodelling of the medial wall of the acetabulum after grafting assessed. There was an average of about 4 mm of remodelling, but this varied considerably; most took place within the first year. In no case was there relapse of the protrusio

Aims

The routine use of dual-mobility (DM) acetabular components in total hip arthroplasty (THA) may not be cost-effective, but an increasing number of patients undergoing THA have a coexisting spinal disorder, which increases the risk of postoperative instability, and these patients may benefit from DM articulations. This study seeks to examine the cost-effectiveness of DM components as an alternative to standard articulations in these patients.

We reviewed 80 patients (87 hips) who were older than 80 years of age at the time of cementless total hip arthroplasty. An Alloclassic SL stem had been implanted in all patients. A variety of cementless acetabular components was used. After a mean follow-up of 69.3 months (39.2 to 94.1) 48 hips in 43 patients were analysed clinically and radiologically. One patient had sustained a traumatic periprosthetic fracture of the femur with subsequent exchange of the stem 73 months after operation. Thirty-two patients (34 hips) had died and five patients (five hips) were unavailable for follow-up because of health reasons (four patients) or lack of co-operation (one patient). If the endpoint is defined as removal of the prosthesis because of aseptic loosening, the survival rate was 100% for the cup and stem after 78 months. The mean Harris hip score was 81.9 points. Radiolucent lines and osteolysis were seldom found

We have followed up for a period of seven to nine years 100 consecutive arthroplasties of the hip in which an entirely HA-coated implant had been used. The clinical results were excellent and bony incorporation was extensive in all components. No stem became loose or subsided but five cups were revised because of loosening after 3.8 to 5.5 years, having functioned painlessly and shown radiological ingrowth. Revision procedures because of excessive polyethylene wear have been performed on 18 hips and are planned for six more. Two eroded metal backings with worn-through polyethylene were exchanged; six hips showed metallosis without polyethylene wear-through. There were two cases of granulomatous cysts in the groin and 66 hips had osteolysis located periarticularly, in the greater trochanter or in the acetabulum

Polyethylene acetabular cups retrieved at revision surgery were measured by a shadowgraph technique to determine linear wear, and the values were compared with those obtained from radiographs. There was a close correlation between them, although the radiographic measurements slightly underestimated the true wear. Average linear wear rates for surface-replacement components were much greater than those for conventional prostheses with femoral heads up to 32 mm in diameter. Volumetric wear, calculated using a new formula, was found to be less than previously reported in vivo, and similar in magnitude to the results of experimental wear tests in vitro. The volumetric wear rates were greatest for the surface-replacement components and, for conventional components, were found to increase in a linear manner with component diameter

We made a semiquantitative study of the comparative histology of pseudomembranes from 12 loose cemented ceramic-ceramic and 18 metal-polyethylene total hip replacements. We found no significant difference in cellular reaction between the two groups, but there was a major difference in the origin of the particulate debris. In the metal-polyethylene group, polyethylene of articular origin was predominant, while in the ceramic-ceramic group the cellular reaction appeared to be a response to zirconia ceramic particles used to opacify cement used for fixation. Isolation and characterisation of the debris showed that the zirconia particles formed the greatest proportion (76%) in ceramic-ceramic hips, while alumina debris of articular origin formed only 12%. Our study has indicated that aseptic loosening of ceramic cups is not due to a response to debris generated at the articular interface, but to mechanical factors which lead to fragmentation of the cement

We implanted 300 uncoated cementless PM prostheses into 271 patients and followed 251 (92.6%) of them for four to seven years. By then 37 had already been revised for aseptic and three for septic loosening. The survival rate with implant failure as the endpoint was 88.8% for the cup and 85.3% for the stem after six years. There was a higher risk of implant loosening in congenital dysplasia, unilateral hip arthroplasty and obesity. The results of 225 unrevised hip replacements were assessed by questionnaire. Only 27.4% of the patients were completely free from pain and 17.9% had pain on walking any distance or at all times. The walking distance was for less than 30 minutes in 40%. Because of the poor results in comparison with other prostheses we do not recommend further use of the uncoated PM prosthesis