Between 1988 and 1998 we implanted 318 total hip replacements (THRs) in 287 patients using the Plasmacup (B. Braun Ltd, Sheffield, United Kingdom) and a conventional metal-on-polyethylene articulation. The main indications for THR were primary or secondary osteoarthritis.
At follow-up after a mean 11.6 years (7.6 to 18.4) 17 patients had died and 20 could not be traced leaving a final series of 280 THRs in 250 patients. There were 62 revisions (22.1%) in 59 patients. A total of 43 acetabular shells (15.4%) had been revised and 13 (4.6%) had undergone exchange of the liner. The most frequent indications for revision were osteolysis and aseptic loosening, followed by polyethylene wear. The mean Kaplan-Meier survival of the Plasmacup was 91% at ten years and 58% at 14 years. Osteolysis was found around 36 (17.1%) of the 211 surviving shells. The median annual rate of linear wear in the surviving shells was 0.12 mm/year and 0.25 mm/year in those which had been revised (p < 0.001). Polyethylene wear was a strong independent risk factor for osteolysis and aseptic loosening. The percentage of patients with osteolysis increased proportionately with each quintile of wear-rate.
There is a high late rate of failure of the Plasmacup. Patients with the combination of this prosthesis and bearing should be closely monitored after ten years.
This paper outlines the recent development of an exchange Travelling Fellowship scheme between the British and American Orthopaedic Research Societies.
Since the Oxford knee was first used unicompartmentally
in 1982, a small number of bearings have fractured. Of 14 retrieved
bearings, we examined ten samples with known durations
The survivorship of contemporary resurfacing arthroplasty of the hip using metal-on-metal bearings is better than that of first generation designs, but short-term failures still occur. The most common reasons for failure are fracture of the femoral neck, loosening of the component, osteonecrosis of the femoral head, reaction to metal debris and malpositioning of the component. In 2008 the Australian National Joint Registry reported an inverse relationship between the size of the head component and the risk of revision in resurfacing hip arthroplasty. Hips with a femoral component size of ≤ 44 mm have a fivefold increased risk of revision than those with femoral components of ≥ 55 mm irrespective of gender. We have reviewed the literature to explore this observation and to identify possible reasons including the design of the implant, loading of the femoral neck, the orientation of the component, the production of wear debris and the effects of metal ions, penetration of cement and vascularity of the femoral head. Our conclusion is that although multifactorial, the most important contributors to failure in resurfacing arthroplasty of the hip are likely to be the design and geometry of the component and the orientation of the acetabular component.
A total of 219 hips in 192 patients aged between
18 and 65 years were randomised to 28-mm metal-on-metal uncemented
total hip replacements (THRs, 107 hips) or hybrid hip resurfacing
(HR, 112 hips). At a mean follow-up of eight years (6.6 to 9.3)
there was no significant difference between the THR and HR groups
regarding rate of revision (4.0% (4 of 99)
Cite this article:
Antibiotic impregnated articulating spacers are used in two-stage revision total knee arthroplasty to deliver local antibiotic therapy while preserving function. We have observed infection control in greater than 95% of cases with functional outcomes approaching those seen in revision for aseptic loosening. Higher failure has been observed with methicillin resistant organisms.
Metallosis after shoulder replacement has not previously been described in the literature. We report a patient who developed extensive metallosis after implantation of an uncemented Nottingham shoulder replacement. He underwent a revision procedure.
Examination of the retrieved prosthesis showed that the titanium porous coating was separating from the humeral stem and becoming embedded in the ultra-high-molecular-weight polyethylene glenoid component, resulting in abrasive wear of the humeral component. There was metallosis despite exchange of the modular humeral head. Both components had to be exchanged to resolve the problem.
The original forged Müller straight stem (CoNiCr) has shown excellent ten- to 15-year results. We undertook a long-term survival analysis with special emphasis on radiological changes within a 20-year period of follow-up.
In all, 165 primary total hip replacements, undertaken between July 1984 and June 1987 were followed prospectively. Clinical follow-up included a standardised clinical examination, and radiological assessment was based on a standardised anteroposterior radiograph of the pelvis, which was studied for the presence of osteolysis, debonding and cortical atrophy.
Survival of the stem with revision for any reason was 81% (95% confidence interval (CI), 76 to 86) at 20 years and for aseptic loosening 87% (95% CI, 82 to 90). At the 20-year follow-up, 15 of the surviving 36 stems showed no radiological changes. Debonding (p = 0.005), osteolysis (p = 0.003) and linear polyethylene wear (p = 0.016) were associated with aseptic loosening, whereas cortical atrophy was not associated with failure (p = 0.008).
The 20-year results of the Müller straight stem are comparable to those of other successful cemented systems with similar follow-up. Radiological changes are frequently observed, but with a low incidence of progression, and rarely result in revision. Cortical atrophy appears to be an effect of ageing and not a sign of loosening of the femoral component.
We describe a cohort of patients with a high rate of mid-term failure following Kinemax Plus total knee replacement inserted between 1998 and 2001. This implant has been recorded as having a survival rate of 96% at ten years. However, in our series the survival rate was 75% at nine years. This was also significantly lower than that of subsequent consecutive series of PFC Sigma knee replacements performed by the same surgeon. No differences were found in the clinical and radiological parameters between the two groups. At revision the most striking finding was polyethylene wear. An independent analysis of the polyethylene components was therefore undertaken. Scanning electron microscopy revealed type 2 fusion defects in the ultra-high molecular weight polyethylene (UHMWPE), which indicated incomplete boundary fusion. Other abnormalities consistent with weak UHMWPE particle interface strength were present in both the explanted inserts and in unused inserts from the same period.
We consider that these type 2 fusion defects are the cause of the early failure of the Kinemax implants. This may represent a manufacturing defect resulting in a form of programmed polyethylene failure.
Following the recall of modular neck hip stems in July 2012, research into femoral modularity will intensify over the next few years. This review aims to provide surgeons with an up-to-date summary of the clinically relevant evidence. The development of femoral modularity, and a classification system, is described. The theoretical rationale for modularity is summarised and the clinical outcomes are explored. The review also examines the clinically relevant problems reported following the use of femoral stems with a modular neck.
Joint replacement registries in the United Kingdom and Australia have provided data on the failure rates of modular devices but cannot identify the mechanism of failure. This information is needed to determine whether modular neck femoral stems will be used in the future, and how we should monitor patients who already have them implanted.
Cite this article:
The debate whether to use cemented or uncemented components in primary total hip replacement (THR) has not yet been considered with reference to the cost implications to the National Health Service.
We obtained the number of cemented and uncemented components implanted in 2009 from the National Joint Registry for England and Wales. The cost of each component was established. The initial financial saving if all were cemented was then calculated. Subsequently the five-year rates of revision for each type of component were reviewed and the predicted number of revisions at five years for the actual components used was compared with the predicted number of revisions for a cemented THR. This was then multiplied by the mean cost of revision surgery to provide an indication of the savings over the first five years if all primary THRs were cemented.
The saving at primary THR was calculated to be £10 million with an additional saving during the first five years of between £5 million and £8.5 million. The use of cemented components in routine primary THR in the NHS as a whole can be justified on a financial level but we recognise individual patient factors must be considered when deciding which components to use.
Early failure associated with adverse reactions to metal debris is an emerging problem after hip resurfacing but the exact mechanism is unclear. We analysed our entire series of 660 metal-on-metal resurfacings (Articular Surface Replacement (ASR) and Birmingham Hip Resurfacing (BHR)) and large-bearing ASR total hip replacements, to establish associations with metal debris-related failures. Clinical and radiological outcomes, metal ion levels, explant studies and lymphocyte transformation tests were performed. A total of 17 patients (3.4%) were identified (all ASR bearings) with adverse reactions to metal debris, for which revision was required. This group had significantly smaller components, significantly higher acetabular component anteversion, and significantly higher whole concentrations of blood and joint chromium and cobalt ions than asymptomatic patients did (all p < 0.001). Post-revision lymphocyte transformation tests on this group showed no reactivity to chromium or cobalt ions. Explants from these revisions had greater surface wear than retrievals for uncomplicated fractures. The absence of adverse reactions to metal debris in patients with well-positioned implants usually implies high component wear.
Surgeons must consider implant design, expected component size and acetabular component positioning in order to reduce early failures when performing large-bearing metal-on-metal hip resurfacing and replacement.
This prospective study presents the ten-year (5 to 16) clinical and radiological results of 55 primary total hip replacements (THR) using a cementless modular femoral component (S-ROM). All patients had a significant anatomical abnormality which rendered the primary THR difficult.
The mean Harris hip score was 36 (12 to 72) pre-operatively, 83 (44 to 100) at five years, and 85 (45 to 99) at ten years. The Western Ontario and McMaster Universities osteoarthritis index (WOMAC) and short-form (SF)-12 scores were recorded from the year 2000. The mean SF-12 score at five years after surgery was 45.24 (22.74 to 56.58) for the physical component and 54.14 (29.20 to 66.61) for the mental component. By ten years the SF-12 scores were 42.86 (21.59 to 58.95) and 51.03 (33.78 to 61.40), respectively. The mean WOMAC score at five years post-operatively was 25 (0 to 59), and at ten years was 27 (2 to 70).
No femoral components were radiologically loose, although five had osteolysis in Gruen zone 1, three had osteolysis in zone 7, and two showed osteolysis in both zones 1 and 7. No osteolysis was observed around or distal to the prosthetic sleeve. No femoral components were revised, although three hips underwent an acetabular revision and two required a liner exchange. At a mean of ten years’ follow-up the S-ROM femoral component implanted for an anatomically difficult primary THR has excellent clinical and radiological results.
We determined the ten-year life expectancy of 5831 patients who had undergone 6653 elective primary total hip replacements at a regional orthopaedic centre between April 1993 and October 2004. Using hospital, general practitioner and the local health authority records, we recorded the dates of death for those who died following surgery.
The mean age at operation was 67 years (13 to 96) with a male:female ratio of 2:3. Of 1154 patients with a ten-year follow-up 340 (29.5%) had died a mean of 5.6 years (0 to 10) after surgery. Using Kaplan-Meier curves, the ten-year survival was 89% in patients under 65 years at surgery, 75% in patients aged between 65 and 74 years, and 51% in patients over 75.
The standardised mortality rates were considerably higher for patients under 45 years, 20% higher for those between 45 and 64 years, and steadily reduced in patients aged 65 and over.
The survival of cemented hip replacement derived from the Swedish Hip Arthroplasty Register Annual Report 2004 exceeds the life expectancy of patients over the age of 60 in our area, suggesting that cemented hip replacement is the procedure of choice in this population.
In a prospective study, 93 unselected consecutive uncemented hip arthroplasties were performed in 80 patients using the titanium-coated RM acetabular component and the CLS femoral component. The mean age of the patients at operation was 52 years (28 to 81). None were lost to follow-up. In the 23 patients who had died (26 hips) only one acetabular component had been revised. In the 57 living patients (67 hips), 13 such revisions had been performed. Of the 14 revisions, seven were for osteolysis, five for loosening and two for infection.
Survival analysis of this implant showed a total probability of survival of 83% (95% confidence interval 73 to 90), with all revisions as the endpoint, and a probability of 94% (95% confidence interval 87 to 98) with revision for aseptic loosening as the endpoint, indicating reliable long-term fixation of the titanium-coated RM acetabular component.
In a randomised study, 28 patients with a mean age of 62.2 years (32 to 81) with osteoarthritis or avascular necrosis of the hip received either a ceramic-on-ceramic or a metal-on-metal total hip replacement. Apart from the liners the acetabular and femoral components were made of Ti-Al-Nb alloy. The serum aluminium and cobalt levels were measured before, and at one year after surgery.
The 15 patients in the ceramic-on-ceramic group had a median pre-operative aluminium level of 1.3 μg/l (0.25 to 8.4) and a cobalt level below the detection limit. At one year the aluminium level was 1.1 μg/l (0.25 to 2.3) and the cobalt level was 0.4 μg/l (0.15 to 0.7). The 13 patients in the metal-on-metal group had a median pre-operative aluminium level of 1.9 μg/l (0.25 to 4.4) and a cobalt level below the detection limit. At one year the median aluminium level was 0.9 μg/l (0.25 to 3.9) whereas the cobalt level was 1.4 μg/l (0.5 to 10.5). This increase in the cobalt level at one year was significant (p < 0.001).
Our findings indicate that ceramic-on-ceramic bearings do not cause elevated levels of serum aluminium in the first post-operative year.
Despite excellent results, the use of cemented total hip replacement (THR) is declining. This retrospective cohort study records survival time to revision following primary cemented THR using the most common combination of components that accounted for almost a quarter of all cemented THRs, exploring risk factors independently associated with failure. All patients with osteoarthritis who had an Exeter V40/Contemporary THR (Stryker) implanted before 31 December 2010 and recorded in the National Joint Registry for England and Wales were included in the analysis. Cox’s proportional hazard models were used to analyse the extent to which risk of revision was related to patient, surgeon and implant covariates, with a significance threshold of p < 0.01. A total of 34 721 THRs were included in the study. The overall seven-year rate of revision for any reason was 1.70% (99% confidence interval (CI) 1.28 to 2.12). In the final adjusted model the risk of revision was significantly higher in THRs with the Contemporary hooded component (hazard ratio (HR) 1.88, p < 0.001) than with the flanged version, and in smaller head sizes (< 28 mm) compared with 28 mm diameter heads (HR 1.50, p = 0.005). The seven-year revision rate was 1.16% (99% CI 0.69 to 1.63) with a 28 mm diameter head and flanged component. The overall risk of revision was independent of age, gender, American Society of Anesthesiologists grade, body mass index, surgeon volume, surgical approach, brand of cement/presence of antibiotic, femoral head material (stainless steel/alumina) and stem taper size/offset. However, the risk of revision for dislocation was significantly higher with a ‘plus’ offset head (HR 2.05, p = 0.003) and a hooded acetabular component (HR 2.34, p < 0.001).
In summary, we found that there were significant differences in failure between different designs of acetabular component and sizes of femoral head after adjustment for a range of covariates.
We carried out a cross-sectional study with analysis of the demographic, clinical and laboratory characteristics of patients with metal-on-metal hip resurfacing, ceramic-on-ceramic and metal-on-polyethylene hip replacements. Our aim was to evaluate the relationship between metal-on-metal replacements, the levels of cobalt and chromium ions in whole blood and the absolute numbers of circulating lymphocytes. We recruited 164 patients (101 men and 63 women) with hip replacements, 106 with metal-on-metal hips and 58 with non-metal-on-metal hips, aged < 65 years, with a pre-operative diagnosis of osteoarthritis and no pre-existing immunological disorders.
Laboratory-defined T-cell lymphopenia was present in13 patients (15%) (CD8+ lymphopenia) and 11 patients (13%) (CD3+ lymphopenia) with unilateral metal-on-metal hips. There were significant differences in the absolute CD8+ lymphocyte subset counts for the metal-on-metal groups compared with each control group (p-values ranging between 0.024 and 0.046). Statistical modelling with analysis of covariance using age, gender, type of hip replacement, smoking and circulating metal ion levels, showed that circulating levels of metal ions, especially cobalt, explained the variation in absolute lymphocyte counts for almost all lymphocyte subsets.