In previous studies, we have demonstrated a fibrocartilaginous membrane around hydroxyapatite-coated implants subjected to micromovement in contrast to the fibrous connective tissue which predominates around similarly loaded titanium alloy implants. In the present study, in mature dogs, we investigated the effect of immobilising titanium (Ti)- or hydroxyapatite (HA)-coated implants already surrounded by a movement-induced fibrous membrane and compared the results with those of similar implants in which continuous micromovement was allowed to continue. The implants were inserted in the medial femoral condyles of 14 dogs and subjected to 150 microns movements during each gait cycle. After four weeks (when a fibrous membrane had developed), half the implants were immobilised to prevent further micromovement. The dogs were killed at 16 weeks and the results were evaluated by push-out tests and histological analysis. The continuously loaded Ti-coated implants were surrounded by a fibrous membrane, whereas bridges of new bone anchored the HA-coated implants. The immobilised implants were surrounded by bone irrespective of the type of coating. Push-out tests of the continuously loaded implants showed better fixation of those with HA coating (p < 0.001). The immobilised Ti-coated implants had four times stronger fixation than did continuously loaded Ti-coated implants (p < 0.01) but there was no equivalent difference between the two groups of HA-coated implants. The amount of bone ingrowth was greater into immobilised HA-coated implants than into immobilised Ti-coated implants (p < 0.01). Two-thirds of the HA coating had been resorbed after 16 weeks of implantation, but 25% of this resorbed HA had been replaced by bone.(ABSTRACT TRUNCATED AT 250 WORDS)

We report the histological findings in post-mortem specimens obtained ten days, 17 days and seven weeks after implantation of hydroxyapatite-coated femoral components of hip arthroplasties. There was early deposition of woven bone on the hydroxyapatite ceramic, identical to that deposited on surviving cancellous trabeculae. The space between these deposits became bridged from both sides by new trabeculae, and there was no evidence of an inflammatory reaction or of fibrous tissue formation. The use of an hydroxyapatite coating seems to allow early, sound, secondary fixation of implants

We report the outcomes of 20 patients (12 men, 8 women, 21 feet) with Charcot neuro-arthropathy who underwent correction of deformities of the ankle and hindfoot using retrograde intramedullary nail arthrodesis. The mean age of the patients was 62.6 years (46 to 83); their mean BMI was 32.7 (15 to 47) and their median American Society of Anaesthetists score was 3 (2 to 4). All presented with severe deformities and 15 had chronic ulceration. All were treated with reconstructive surgery and seven underwent simultaneous midfoot fusion using a bolt, locking plate or a combination of both. At a mean follow-up of 26 months (8 to 54), limb salvage was achieved in all patients and 12 patients (80%) with ulceration achieved healing and all but one patient regained independent mobilisation. There was failure of fixation with a broken nail requiring revision surgery in one patient. Migration of distal locking screws occurred only when standard screws had been used but not with hydroxyapatite-coated screws. The mean American Academy of Orthopaedic Surgeons Foot and Ankle (AAOS-FAO) score improved from 50.7 (17 to 88) to 65.2 (22 to 88), (p = 0.015). The mean Short Form (SF)-36 Health Survey Physical Component Score improved from 25.2 (16.4 to 42.8) to 29.8 (17.7 to 44.2), (p = 0.003) and the mean Euroqol EQ‑5D‑5L score improved from 0.63 (0.51 to 0.78) to 0.67 (0.57 to 0.84), (p = 0.012).

Single-stage correction of deformity using an intramedullary hindfoot arthrodesis nail is a good form of treatment for patients with severe Charcot hindfoot deformity, ulceration and instability provided a multidisciplinary care plan is delivered.

Cite this article: Bone Joint J 2015;97-B:76–82.

Aims. BoneMaster is a thin electrochemically applied hydroxyapatite (HA) coating for orthopaedic implants that is quickly resorbed during osseointegration. Early stabilization is a surrogacy marker of good survival of femoral stems. The hypothesis of this study was that a BoneMaster coating yields a fast early and lasting fixation of stems. Methods. A total of 53 patients were randomized to be treated using Bi-Metric cementless femoral stems with either only a porous titanium plasma-sprayed coating (P group) or a porous titanium plasma-sprayed coating with an additional BoneMaster coating (PBM group). The patients were examined with radiostereometry until five years after surgery. Results. At three months, the mean total translation (TT) was 0.95 mm (95% confidence interval (CI) 0.68 to 1.22) in the P group and 0.57 mm (95% CI 0.31 to 0.83) in the PBM group (p = 0.047). From two to five years, the TT increased by a mean of 0.14 mm (95% CI 0.03 to 0.25) more in the P group than in the PBM group (p = 0.021). In osteopenic patients (n = 20), the mean TT after three months was 1.61 mm (95% CI 1.03 to 2.20) in the P group and 0.73 mm (95% CI 0.25 to 1.21) in the PBM group (p = 0.023). After 60 months, the mean TT in osteopenic patients was 1.87 mm (95% CI 1.24 to 2.50) in the P group and 0.82 mm (95% CI 0.30 to 1.33) in the PBM group (p = 0.011). Conclusion. There was less early and midterm migration of cementless stems with BoneMaster coating compared with those with only a porous titanium plasma-sprayed coating. Although a BoneMaster coating seems to be important for stem fixation, especially in osteopenic patients, further research is warranted. Cite this article: Bone Joint J 2022;104-B(6):647–656

Implant-associated infection is a major source of morbidity in orthopaedic surgery. There has been extensive research into the development of materials that prevent biofilm formation, and hence, reduce the risk of infection. Silver nanoparticle technology is receiving much interest in the field of orthopaedics for its antimicrobial properties, and the results of studies to date are encouraging. Antimicrobial effects have been seen when silver nanoparticles are used in trauma implants, tumour prostheses, bone cement, and also when combined with hydroxyapatite coatings. Although there are promising results with in vitro and in vivo studies, the number of clinical studies remains small. Future studies will be required to explore further the possible side effects associated with silver nanoparticles, to ensure their use in an effective and biocompatible manner. Here we present a review of the current literature relating to the production of nanosilver for medical use, and its orthopaedic applications. Cite this article: Bone Joint J 2015; 97-B:582–9

This study describes 146 primary total knee replacements, either fully or partially coated with hydroxyapatite of which 74 knees in 68 patients were available for clinical and radiological assessment at a mean of 11.2 years (10 to 15). The global failure rate was 1.37% and survival rate with mechanical failure as the end-point was 98.14%. Radiological assessment indicated intimate contact between bone and the hydroxyapatite coating. Over time the hydroxyapatite coating appears to encourage filling of interface gaps remaining after surgery. Our results compare favourably with those of series describing cemented or porous-coated knee replacements, and suggest that fixation with hydroxyapatite is a reliable option in primary total knee replacement

Aims. The optimal method of tibial component fixation remains uncertain in total knee arthroplasty (TKA). Hydroxyapatite coatings have been applied to improve bone ingrowth in uncemented designs, but may only coat the directly accessible surface. As peri-apatite (PA) is solution deposited, this may increase the coverage of the implant surface and thereby fixation. We assessed the tibial component fixation of uncemented PA-coated TKAs versus cemented TKAs. Patients and Methods. Patients were randomised to PA-coated or cemented TKAs. In 60 patients (30 in each group), radiostereometric analysis of tibial component migration was evaluated as the primary outcome at baseline, three months post-operatively and at one, two and five years. A linear mixed-effects model was used to analyse the repeated measurements. Results. After five years of follow-up, one (cemented) component was revised due to ligament instability. Overall, uncemented PA-coated tibial components migrated significantly more (p = 0.003), with the mean maximum total point motion (MTPM) at five years being 0.62 mm (95% confidence intervals (CI) 0.49 to 0.76) for cemented tibial components and 0.97 mm (95% CI 0.81 to 1.15) for PA-coated tibial components in TKA. However, between three months and five years the cemented TKAs migrated significantly more (p = 0.02), displaying a MTPM of 0.27 mm (95% CI, 0.19 to 0.36) versus 0.13 mm (95% CI, 0.01 to 0.25) for PA-coated tibial components. One implant in each group was considered at risk for aseptic loosening due to continuous migration after five years of follow-up, albeit with different migration patterns for each group (i.e. higher initial migration but diminishing over time for the PA-coated component versus gradually increasing migration for the cemented component). Conclusion. The tibial components of PA-coated TKAs showed more overall migration compared with the tibial components of cemented TKAs. However, post hoc analysis showed that this difference was caused by higher migration of PA-coated components in the first three months, after which a stable migration pattern was observed. Clinically, there was no significant difference in outcome between the groups. Cite this article: Bone Joint J 2017;99-B:1467–76

The vertical migration of four configurations of a proximal femoral prosthesis, followed for up to nine years, was measured on standard radiographs. The same implant was used without cement (group 1) and with cement (group 2). The migration of both groups was linear from six months onwards. The mean migration rate and the incidence of late aseptic loosening were both greater in group 1. Survival analysis of the two groups, however, showed no statistically significant difference. In both groups, hips later destined for revision migrated more rapidly from the initial postoperative period onwards, than did the remainder. A threshold migration of 1.2 mm/year during the first two years after implantation detected hips likely to fail with a specificity of 86% and a sensitivity of 78%. This 'migration test' was applied to the results in two further groups of patients in which a modified femoral prosthesis had been implanted without hydroxyapatite coating (group 3) and with hydroxyapatite coating (group 4). The test distinguished between the four groups and suggested that at least two fixation procedures should be abandoned. We conclude that vertical migration measured on standard radiographs in the first two years after implantation can be used to predict late aseptic loosening. New prosthetic configurations should be evaluated by migration measurements before their general release. Our observations support the view that one cause of late aseptic loosening is imperfect initial fixation

In this study we present our experience with four generations of uncemented total knee arthroplasty (TKA) from Smith & Nephew: Tricon M, Tricon LS, Tricon II and Profix, focusing on the failure rates correlating with each design change. Beginning in 1984, 380 Tricon M, 435 Tricon LS, 305 Tricon 2 and 588 Profix were implanted by the senior author. The rate of revision for loosening was 1.1% for the Tricon M, 1.1% for the Tricon LS, 0.5% for the Tricon 2 with a HA coated tibial component, and 1.3% for the Profix TKA. No loosening of the femoral component was seen with the Tricon M, Tricon LS or Tricon 2, with no loosening seen of the tibial component with the Profix TKA. Regarding revision for wear, the incidence was 13.1% for the Tricon M, 6.6% for the Tricon LS, 2.3% for the Tricon 2, and 0% for the Profix. These results demonstrate that improvements in the design of uncemented components, including increased polyethylene thickness, improved polyethylene quality, and the introduction of hydroxyapatite coating, has improved the outcomes of uncemented TKA over time

Aims. The aim of this study was to conduct the largest low contact stress (LCS) retrieval study to elucidate the failure mechanisms of the Porocoat and Duofix femoral component. The latter design was voluntarily recalled by the manufacturer. Materials and Methods. Uncemented LCS explants were divided into three groups: Duofix, Porocoat, and mixed. Demographics, polyethylene wear, tissue ingrowth, and metallurgical analyses were performed. Results. In 104 implants, a decrease in the odds of loosening and an increase in metallosis and tissue staining in the Duofix group relative to Porocoat group was detected (p = 0.028). There was an increased presence of embedded metallic debris in the Duofix group (p < 0.001). Decreased tissue ingrowth was associated with the Duofix surface (p < 0.001). The attached beads had reduced microhardness, indicative of adverse thermal processing, which resulted in bead shedding, particulate debris, and metallosis. Conclusion. Hydroxyapatite coating of the LCS femoral component produced unexpected results and led to its recall. The root cause was likely a combination of retained alumina grit and a reduction in bead microhardness (mechanical strength) resulting in increased particle debris, metallosis, and early revision. The Duofix LCS femoral component was not equivalent to the Porocoat version despite its approval through the Food and Drug Administration (FDA) 510(k) equivalance approval process. Regulation of the introduction of modified existing devices needs to be improved and the Duofix LCS should have been considered to be a new device for which equivalence had not been demonstrated at the point of introduction. Cite this article: Bone Joint J 2019;101-B:1248–1255

Aims. Hydroxyapatite coatings for uncemented fixation in total knee arthroplasty can theoretically provide a long-lasting biological interface with the host bone. The objective of this study was to test this hypothesis with propriety hydroxyapatite, peri-apatite, coated tibial components using component migration measured with radiostereometric analysis over two years as an indicator of long-term fixation. Patients and Methods. A total of 29 patients at two centres received uncemented PA-coated tibial components and were followed for two years with radiostereometric analysis exams to quantify the migration of the component. Results. While there was significant variation in individual migration patterns, the overall migration of the tibial component in the study group demonstrated a pattern of initial migration followed by stabilisation after one year, with mean maximum total point motion (MTPM) of 0.02 mm (standard deviation (. sd. ) 0.20) between one and two years post-operatively. The direction of greatest motion was subsidence, which stabilised at three months post-operatively (mean translation of 0.21 mm, . sd. 0.40). Conclusion. The tibial component migration pattern of stabilisation in the second post-operative year is indicative of successful long-term fixation for this PA-coated tibial component. Cite this article: Bone Joint J 2017;99-B:1596–1602

Aims

The aim of this study was to evaluate the survival of a collarless, straight, hydroxyapatite-coated femoral stem in total hip arthroplasty (THA) at a minimum follow-up of 20 years.

Aims. The purpose of this study was to evaluate the biological fixation of a 3D printed porous implant, with and without different hydroxyapatite (HA) coatings, in a canine model. Materials and Methods. A canine transcortical model was used to evaluate the characteristics of bone ingrowth of Ti6Al4V cylindrical implants fabricated using laser rapid manufacturing (LRM). At four and 12 weeks post-implantation, we performed histological analysis and mechanical push-out testing on three groups of implants: a HA-free control (LRM), LRM with precipitated HA (LRM-PA), and LRM with plasma-sprayed HA (LRM-PSHA). Results. Substantial bone ingrowth was observed in all LRM implants, with and without HA, at both time periods. Bone ingrowth increased from 42% to 52% at four weeks, to 60% to 65% at 12 weeks. Mechanical tests indicated a minimum shear fixation strength of 20 MPa to 24 MPa at four weeks, and 34 MPa to 40 MPa at 12 weeks. There was no significant difference in the amount of bone ingrowth or in the shear strength between the three implant types at either time period. Conclusion. At four and 12 weeks, the 3D printed porous implants exhibited consistent bone ingrowth and high mechanical shear strength. Based on the results of this study, we confirmed the suitability of this novel new additive manufacturing porous material for biological fixation by bone ingrowth. Cite this article: Bone Joint J 2019;101-B(6 Supple B):62–67

We examined specimens of hydroxyapatite-coated femoral prostheses from four patients who had died within nine months of implantation for fractured neck of femur. Histology showed newly formed immature bone overlying the hydroxyapatite coating with new trabeculae bridging to the endosteal bone layer. In the diaphysis, where there had been contact between the hydroxyapatite and the cortex, there was dense, firmly anchored bone with an haversian architecture. In other places the newly formed bone had a trabecular structure, containing bone marrow tissue with normal cellularity. It appeared that biological osseointegration had taken place

We describe the clinical and radiological outcome of 100 consecutive total hip replacements in 86 patients using the JRI Furlong hydroxyapatite-coated femoral component. The follow-up was 100% at a mean of ten years (9.0 to 12.0). All 54 living patients (62 hips) were examined annually. Their mean Merle d’Aubigné score was 5.8/5.6/4.6. A total of 32 patients had died. Their notes at the last annual assessment recorded a similar outcome to that of the living patients. Radiographs showed no radiolucent lines around any femoral component and there were no signs of impending failure. One patient required excision arthroplasty, but the femoral component had been bonded satisfactorily. There have been no other revisions of femoral components. Our findings suggest that the hydroxyapatite coating gives a satisfactory prosthesis-bone interface which is preferable to any other system

Aims

The benefit of a dual-mobility acetabular component (DMC) for primary total hip arthroplasties (THAs) is controversial. This study aimed to compare the dislocation and complication rates when using a DMC compared to single-mobility (SM) acetabular component in primary elective THA using data collected at a single centre, and compare the revision rates and survival outcomes in these two groups.

Aims

The use of cementless total knee arthroplasty (TKA) components has increased during the past decade. The initial design of cementless metal-backed patellar components had shown high failure rates due to many factors. The aim of this study was to evaluate the clinical results of a second-generation cementless, metal-backed patellar component of a modern design.

Aims

Femoral component anteversion is an important factor in the success of total hip arthroplasty (THA). This retrospective study aimed to investigate the accuracy of femoral component anteversion with the Mako THA system and software using the Exeter cemented femoral component, compared to the Accolade II cementless femoral component.

Aims

Instability is a common cause of failure after total hip arthroplasty. A novel reverse total hip has been developed, with a femoral cup and acetabular ball, creating enhanced mechanical stability. The purpose of this study was to assess the implant fixation using radiostereometric analysis (RSA), and the clinical safety and efficacy of this novel design.

Aims

The primary aim of this study is to assess the survival of the uncemented hydroxyapatite (HA) coated Trident II acetabular component as part of a hybrid total hip arthroplasty (THA) using a cemented Exeter stem. The secondary aims are to assess the complications, joint-specific function, health-related quality of life, and radiological signs of loosening of the acetabular component.