The clinical use of hydroxyapatite (HA) coating is controversial especially in regard to the long-term performance of the coating and the effects of resorption. In each of 15 consenting patients we inserted two implants, coated with either HA or fluorapatite (FA) into the iliac crest. They were harvested at a mean of 13.6 ± 0.6 months after surgery.

Histological examination showed that bone ongrowth on the HA-coated implants was significantly greater (29%) than that on the FA-coated implants. When bone was present on the coating surface the HA coating was significantly thicker than the FA coating. When bone marrow was present, the HA coating was significantly thinner than the FA coating. The reduction in coating thickness when covered by bone or bone marrow was 23.1 ± 9.7 μm for HA and 5.1 ± 1.7 μm for FA (p < 0.01) suggesting that FA is more stable than HA against resorption by bone marrow.

The findings suggest that in man the osteoconductive properties of HA coating are superior to those of FA. Resorption rates for both coatings were approximately 20% of the coating thickness per year. Bone ongrowth appears to protect against resorption whereas bone marrow seems to accelerate resorption. No adverse reaction was seen in the surrounding bone.

Bone growth into cementless prosthetic components is compromised by osteoporosis, by any gap between the implant and the bone, by micromotion, and after the revision of failed prostheses. Recombinant human transforming growth factor-β1 (rhTGF-β1) has recently been shown to be a potent stimulator of bone healing and bone formation in various models in vivo.

We have investigated the potential of rhTGF-β1, adsorbed on to weight-loaded tricalcium phosphate (TCP) coated implants, to enhance bone ongrowth and mechanical fixation. We inserted cylindrical grit-blasted titanium alloy implants bilaterally into the weight-bearing part of the medial femoral condyles of ten skeletally mature dogs. The implants were mounted on special devices which ensured stable weight-loading during each gait cycle. All implants were initially surrounded by a 0.75 mm gap and were coated with TCP ceramic.

Each animal received two implants, one with 0.3 μg rhTGF-β1 adsorbed on the ceramic surface and the other without growth factor. Histological analysis showed that bone ongrowth was significantly increased from 22 ± 5.6% bone-implant contact in the control group to 36 ± 2.9% in the rhTGF-β stimulated group, an increase of 59%. The volume of bone in the gap was increased by 16% in rhTGF-β1-stimulated TCP-coated implants, but this difference was not significant. Mechanical push-out tests showed no difference in fixation of the implant between the two groups. Our study suggests that rhTGF-β1 adsorbed on TCP-ceramic-coated implants can enhance bone ongrowth.

We recorded inter- and intra-observer variations in the classification of ankle fractures by the Lauge Hansen and Weber systems. Radiographs of 94 patients were classified independently by four observers. The observer variation was calculated by kappa statistics, which corrects the obtained values for the agreement expected by chance. There was an acceptable level of agreement for the overall classification into both systems. For the staging of supination-adduction and supination-eversion fractures in the Lauge Hansen system the agreement was poor. The results indicate that future classification systems should be subject to reliability analysis before they are accepted.