The creep and wear behaviour of highly cross-linked polyethylene and standard polyethylene liners were examined in a prospective, double-blind randomised, controlled trial using radiostereometric analysis.

We randomised 54 patients to receive hip replacements with either highly cross-linked polyethylene or standard liners and determined the three-dimensional penetration of the liners over three years.

After three years the mean total penetration was 0.35 mm (SD 0.14) for the highly cross-linked polyethylene group and 0.45 mm (SD 0.19) for the standard group. The difference was statistically significant (p = 0.0184). From the pattern of penetration it was possible to discriminate creep from wear. Most (95%) of the creep occurred within six months of implantation and nearly all within the first year. There was no difference in the mean degree of creep between the two types of polyethylene (highly cross-linked polyethylene 0.26 mm, SD 0.17; standard 0.27 mm, SD 0.2; p = 0.83). There was, however, a significant difference (p = 0.012) in the mean wear rate (highly cross-linked polyethylene 0.03 mm/yr, SD 0.06; standard 0.07 mm/yr, SD 0.05). Creep and wear occurred in significantly different directions (p = 0.01); creep was predominantly proximal whereas wear was anterior, proximal and medial.

We conclude that penetration in the first six months is creep-dominated, but after one year virtually all penetration is due to wear. Highly cross-linked polyethylene has a 60% lower rate of wear than standard polyethylene and therefore will probably perform better in the long term.

We have reviewed the rate of revision of fully cemented, hybrid and uncemented primary total hip replacements (THRs) registered in the New Zealand Joint Registry between 1999 and December 2006 to determine whether there was any statistically significant difference in the early survival and reason for revision in these different types of fixation. The percentage rate of revision was calculated per 100 component years and compared with the reason for revision, the type of fixation and the age of the patients.

Of the 42 665 primary THRs registered, 920 (2.16%) underwent revision requiring change of at least one component. Fully-cemented THRs had a lower rate of revision when considering all causes for failure (p < 0.001), but below the age of 65 years uncemented THRs had a lower rate (p < 0.01). The rate of revision of the acetabular component for aseptic loosening was less in the uncemented and hybrid groups compared with that in the fully cemented group (p < 0.001), and the rate of revision of cemented and uncemented femoral components was similar, except in patients over 75 years of age in whom revision of cemented femoral components was significantly less frequent (p < 0.02). Revision for infection was more common in patients aged below 65 years and in cemented and hybrid THRs compared with cementless THRs (p < 0.001). Dislocation was the most common cause of revision for all types of fixation and was more frequent in both uncemented acetabular groups (p < 0.001). The experience of the surgeon did not affect the findings.

Although cemented THR had the lowest rate of revision for all causes in the short term (90 days), uncemented THR had the lowest rate of aseptic loosening in patients under 65 years of age and had rates comparable with international rates of aseptic loosening in those over 65 years.

A 34-year-old woman with a benign form of osteopetrosis developed osteoarthritis of the hip. In order to avoid the difficulties associated with inserting the femoral component of a conventional total hip arthroplasty, a hybrid metal-on-metal resurfacing was performed. There were several technical challenges associated with the procedure, including the sizing of the component, press-fit fixation of the acetabular component and femoral head preparation, as well as trying to avoid a fracture. No surgical complication occurred. After more than a year following surgery, the patient showed excellent clinical function and remained satisfied with the outcome. We conclude that the hybrid metal-on-metal resurfacing arthroplasty represents a valuable option for the treatment of patients with osteopetrosis and secondary hip osteoarthritis.

We reviewed the initial post-operative radiographs of the Trident acetabulum and identified a problem with seating of the metal-backed ceramic liner. We identified 117 hips in 113 patients who had undergone primary total hip replacement using the Trident shell with a metal-backed alumina liner. Of these, 19 (16.4%) were noted to have incomplete seating of the liner, as judged by plain anteroposterior and lateral radiographs. One case of complete liner dissociation necessitating early revision was not included in the prevalence figures. One mis-seated liner was revised in the early post-operative period and two that were initially incompletely seated were found on follow-up radiographs to have become correctly seated. There may be technical issues with regard to the implanting of this prosthesis of which surgeons should be aware. However, there is the distinct possibility that the Trident shell deforms upon implantation, thereby preventing complete seating of the liner.

We evaluated the long-term fixation of 64 press-fit cemented stems of constrained total knee prostheses in 32 young patients with primary malignant bone tumours. Initial stable fixation, especially in rotation, was achieved by precise fit of the stem into the reamed endosteum, before cementation. Complementary fixation, especially in migration and rotation, was obtained by pressurised antibiotic-loaded cement. The mean age at operation was 33 years (13 to 61). No patient was lost to follow-up; 13 patients died and the 19 survivors were examined at a mean follow-up of 12.5 years (4 to 21). Standard revision press-fit cemented stems were used on the side of the joint which was not involved with tumour (26 tibial and six femoral), on this side there was no loosening or osteolysis and stem survival was 100%. On the reconstruction side, custom-made press-fit stems were used and the survival rate, with any cause for revision as an end point, was 88%, but 97% for loosening or osteolysis. This longevity is similar to that achieved at 20 years with the Charnley-Kerboull primary total hip replacement with press-fit cemented femoral components.

We recommend this type of fixation when extensive reconstruction of the knee is required. It may also be suitable for older patients requiring revision of a total knee replacement or in difficult situations such as severe deformity and complex articular fractures.

It has been suggested that the wear of ultra-high molecular weight polyethylene (UHMWPE) in total hip replacement is substantially reduced when the femoral head is ceramic rather than metal. However, studies of alumina and zirconia ceramic femoral heads on the penetration of an UHMWPE liner in vivo have given conflicting results.

The purpose of this study was to examine the surface characteristics of 30 alumina and 24 zirconia ceramic femoral heads and to identify any phase transformation in the zirconia heads. We also studied the penetration rate of alumina and zirconia heads into contemporary UHMWPE liners. The alumina heads had been implanted for a mean of 11.3 years (8.1 to 16.2) and zirconia heads for a mean of 9.8 years (7.5 to 15).

The mean surface roughness values of the explanted alumina heads (Ra 40.12 nm and Rpm 578.34 nm) were similar to those for the explanted zirconia heads (Ra 36.21 nm and Rpm 607.34 nm). The mean value of the monoclinic phase of two control zirconia heads was 1% (0.8% to 1.5%) and 1.2% (0.9% to 1.3%), respectively. The mean value of the monoclinic phase of 24 explanted zirconia heads was 7.3% (1% to 26%).

In the alumina group, the mean linear penetration rate of the UMWPE liner was 0.10 mm/yr (0.09 to 0.12) in hips with low Ra and Rpm values (13.22 nm and 85.91 nm, respectively). The mean linear penetration rate of the UHMWPE liner was 0.13 mm/yr (0.07 to 0.23) in hips with high Ra and Rpm values (198.72 nm and 1329 nm, respectively). This difference was significant (p = 0.041).

In the zirconia head group, the mean linear penetration rate of the UHMWPE liner was 0.09 mm/yr (0.07 to 0.14) in hips with low Ra and Rpm values (12.78 nm and 92.99 nm, respectively). The mean linear penetration rate of the UHMWPE liner was 0.12 mm/yr (0.08 to 0.22) in hips with high Ra and Rpm values (199.21 nm and 1381 nm, respectively). This difference was significant (p = 0.039).

The explanted zirconia heads which had a minimal phase transformation had similar surface roughness and a similar penetration rate of UHMWPE liner as the explanted alumina head.

We investigated whether improvements in design have altered the outcome for patients undergoing endoprosthetic replacement of the distal femur after resection of a tumour. Survival of the implant and ‘servicing’ procedures have been documented using a prospective database, review of the design of the implant and case records. In total, 335 patients underwent a distal femoral replacement, 162 having a fixed-hinge design and 173 a rotating-hinge. The median age of the patients was 24 years (interquartile range 17 to 48).

A total of 192 patients remained alive with a mean follow-up of 12 years (5 to 30). The risk of revision for any reason was 17% at five years, 33% at ten years and 58% at 20 years. Aseptic loosening was the main reason for revision of the fixed-hinge knees while infection and fracture of the stem were the most common for the rotating-hinge implant. The risk of revision for aseptic loosening was 35% at ten years with the fixed-hinge knee, which has, however, been replaced by the rotating-hinge knee with a hydroxyapatite collar. The overall risk of revision for any reason fell by 52% when the rotating-hinge implant was used.

Improvements in the design of distal femoral endoprostheses have significantly decreased the need for revision operations, but infection remains a serious problem. We believe that a cemented, rotating-hinge prosthesis with a hydroxyapatite collar offers the best chance of long-term survival of the prosthesis.

Because the femoral head/neck junction is preserved in hip resurfacing, patients may be at greater risk of impingement, leading to abnormal wear patterns and pain. We assessed femoral head/neck offset in 63 hips undergoing metal-on-metal hip resurfacing and in 56 hips presenting with non-arthritic pain secondary to femoroacetabular impingement. Most hips undergoing resurfacing (57%; 36) had an offset ratio ≤ 0.15 pre-operatively and required greater correction of offset at operation than the rest of the group. In the non-arthritic hips the mean offset ratio was 0.137 (0.04 to 0.23), with the offset ratio correlating negatively to an increasing α angle. An offset ratio ≤ 0.15 had a 9.5-fold increased relative risk of having an α angle ≥ 50.5°. Most hips undergoing resurfacing have an abnormal femoral head/neck offset, which is best assessed in the sagittal plane.

During hip resurfacing arthroplasty, excessive valgus positioning or surgical technique can result in notching of the femoral neck. Although mechanical weakening and subsequent fracture of the femoral neck are well described, the potential damage to the retinacular vessels leading to an ischaemic event is relatively unknown. Using laser Doppler flowmetry, we measured the blood flow in 14 osteoarthritic femoral heads during routine total hip replacement surgery, before and after notching of the femoral neck. In ten hips there was a reduction in blood flow of more than 50% from the baseline value after simulated notching of the femoral neck. Our results suggest that femoral head vascularity in the osteoarthritic state is similar to the non-arthritic state, where damage to the extraosseous vessels can predispose to avascular necrosis. Surgeons who perform resurfacing arthroplasty of the hip should pay careful attention to these vessels by avoiding excessive dissection around the femoral neck and/or notching.

We studied prospectively the long-term results of the Charnley Elite-Plus femoral stem in 184 consecutive young patients (194 hips). There were 130 men and 54 women with a mean age of 49.1 years (21 to 60). The predominant diagnosis was osteonecrosis of the femoral head (63.6%, 117 patients). Clinical and radiological evaluation was undertaken at each follow-up. The mean follow-up was 11.2 years (10 to 12).

The mean pre-operative Harris hip score was 43.4 (12 to 49) which improved to 91 (59 to 100) at the final follow-up. The survival of the femoral stem at 12 years was 99% with revision as the end-point. The mean annual linear wear of the polyethylene liner was 0.17 mm (0.13 to 0.22). The prevalence of acetabular osteolysis was 10.8% (21 hips) and osteolysis of the calcar femorale 12.9% (25 hips).

A third-generation cementing technique, accurate alignment of the stem and the use of a 22 mm zirconia head were important factors in the prevention of aseptic loosening of the Elite Plus femoral stem in these high-risk young patients.

Our aim in this prospective study was to compare the bone mineral density (BMD) around cementless acetabular and femoral components which were identical in geometry and had the same alumina modular femoral head, but differed in regard to the material of the acetabular liners (alumina ceramic or polyethylene) in 50 patients (100 hips) who had undergone bilateral simultaneous primary total hip replacement. Dual energy X-ray absorptiometry scans of the pelvis and proximal femur were obtained at one week, at one year, and annually thereafter during the five-year period of the study.

At the final follow-up, the mean BMD had increased significantly in each group in acetabular zone I of DeLee and Charnley (20% (15% to 26%), p = 0.003), but had decreased in acetabular zone II (24% (18% to 36%) in the alumina group and 25% (17% to 31%) in the polyethylene group, p = 0.001). There was an increase in the mean BMD in zone III of 2% (0.8% to 3.2%) in the alumina group and 1% (0.6% to 2.2%) in the polyethylene group (p = 0.315). There was a decrease in the mean BMD in the calcar region (femoral zone 7) of 15% (8% to 24%) in the alumina group and 14% (6% to 23%) in the polyethylene group (p < 0.001). The mean bone loss in femoral zone 1 of Gruen et al was 2% (1.1% to 3.1%) in the alumina group and 3% (1.3% to 4.3%) in the polyethylene group (p = 0.03), and in femoral zone 6, the mean bone loss was 15% (9% to 27%) in the alumina group and 14% (11% to 29%) in the polyethylene group compared with baseline values. There was an increase in the mean BMD on the final scans in femoral zones 2 (p = 0.04), 3 (p = 0.04), 4 (p = 0.12) and 5 (p = 0.049) in both groups.

There was thus no significant difference in the bone remodelling of the acetabulum and femur five years after total hip replacement in those two groups where the only difference was in the acetabular liner.

A modular layered acetabular component (metal-polyethylene-ceramic) was developed in Japan for use in alumina ceramic-on-ceramic total hip replacement. Between May 1999 and July 2000, we performed 35 alumina ceramic-on-ceramic total hip replacements in 30 consecutive patients, using this layered component and evaluated the clinical and radiological results over a mean follow-up of 5.8 years (5 to 6.5). A total of six hips underwent revision, one for infection, two for dislocation with loosening of the acetabular component, two for alumina liner fractures and one for component dissociation with pelvic osteolysis. There were no fractures of the ceramic heads, and no loosening of the femoral or acetabular component in the unrevised hips was seen at final follow-up. Osteolysis was not observed in any of the unrevised hips. The survivorship analysis at six years after surgery was 83%. The layered acetabular component in our experience, has poor durability because of unexpected mechanical failures including alumina liner fracture and component dissociation.

We present a retrospective series of 170 cemented titanium straight-stem femoral components combined with two types of femoral head: cobalt-chromium (CoCr) alloy (114 heads) and alumina ceramic (50 heads). Of the study group, 55 patients (55 stems) had died and six (six stems) were lost to follow-up. At a mean of 13.1 years (3 to 15.3) 26 stems had been revised for aseptic loosening. The mean follow-up time for stable stems was 15.1 years (12.1 to 16.6).

Survival of the stem at 15 years was 75.4% (95% confidence interval (CI) 67.3 to 83.5) with aseptic failure (including radiological failure) as the end-point, irrespective of the nature of the head and the quality of the cement mantle. Survival of the stem at 15 years was 79.1% (95% CI 69.8 to 88.4) and 67.1% (95% CI 51.3 to 82.9) with the CoCr alloy and ceramic heads, respectively. The quality of the cement mantle was graded as a function of stem coverage: stems with complete tip coverage (type 1) had an 84.9% (95% CI 77.6 to 92.2) survival at 15 years, compared with those with a poor tip coverage (type 2) which had a survival of only 22.4% (95% CI 2.4 to 42.4). The poor quality of the cement mantle and the implantation of an alumina head substantially lowered the survival of the stem.

In our opinion, further use of the cemented titanium alloy straight-stem femoral components used in our series is undesirable.

Polyethylene particulate wear debris continues to be implicated in the aetiology of aseptic loosening following knee arthroplasty. The Oxford unicompartmental knee arthroplasty employs a spherical femoral component and a fully congruous meniscal bearing to increase contact area and theoretically reduce the potential for polyethylene wear. This study measures the in vivo ten-year linear wear of the device, using a roentgenstereophotogrammetric technique.

In this in vivo study, seven medial Oxford unicompartmental prostheses, which had been implanted ten years previously were studied. Stereo pairs of radiographs were acquired for each patient and the films were analysed using a roentgen stereophotogrammetric analysis calibration and a computer-aided design model silhouette-fitting technique. Penetration of the femoral component into the original volume of the bearing was our estimate of linear wear. In addition, eight control patients were examined less than three weeks post-insertion of an Oxford prosthesis, where no wear would be expected. The control group showed no measured wear and suggested a system accuracy of 0.1 mm. At ten years, the mean linear wear rate was 0.02 mm/year.

The results from this in vivo study confirm that the device has low ten-year linear wear in clinical practice. This may offer the device a survival advantage in the long term.

Primary uncemented femoral stems reported to the Norwegian arthroplasty register between 1987 and 2005 were included in this prospective observational study. There were 11 516 hips (9679 patients) and 14 different designs of stem. Kaplan-Meier survival probabilities and Cox regression were used to analyse the data.

With aseptic loosening as the end-point, all currently used designs performed excellently with survival of 96% to 100% at ten years. With the end-point as stem revision for any cause, the long-term results of the different designs varied from poor to excellent, with survival at 15 years ranging between 29% and 97%. Follow-up for longer than seven years was needed to identify some of the poorly-performing designs. There were differences between the stems; the Corail, used in 5456 hips, was the most frequently used stem with a survival of 97% at 15 years. Male gender was associated with an increased risk of revision of × 1.3 (95% confidence interval 1.05 to 1.52), but age and diagnosis had no influence on the results. Overall, modern uncemented femoral stems performed well.

Moderate differences in survival between well-performing stems should be interpreted with caution since the differences may be caused by factors other than the stem itself.

Between January 1984 and January 1986, 131 porous-coated anatomic total hip replacements were performed in 119 consecutive patients. Of these, 100 patients (110 hips) who were alive at a minimum of 18 years after replacement were included in the study. The mean age of the patients at surgery was 48.4 years and that of surviving patients at the latest follow-up was 67.8 years. The mean duration of the clinical and radiological follow-up was 19.4 years (18 to 20).

The mean Harris hip score initially improved from 55 points before to 95 points at two years after operation, but subsequently decreased to 91 points after six years, 87 points after 11.2 years, and 85 points after 19.4 years. At the final follow-up, 23 hips (18%) of the entire cohort and 21% of survivors had undergone revision because of loosening or osteolysis of the acetabular component and eight hips (6%) of the entire cohort and 7% of survivors for loosening or osteolysis of the femoral component. Only four femoral components (4%) were revised for isolated aseptic loosening without osteolysis and two (2%) for recurrent dislocation. On the basis of these long-term results, the porous-coated anatomic femoral component survived for a minimum of 18 years after operation while the acetabular component was less durable. The findings identify the principles of uncemented joint replacement which can be applied to current practice.

We have undertaken a prospective, randomised study to compare conservation of acetabular bone after total hip replacement and resurfacing arthroplasty of the hip. We randomly assigned 210 hips to one of the two treatment groups. Uncemented, press-fit acetabular components were used for both.

No significant difference was found in the mean diameter of acetabular implant inserted in the groups (54.74 mm for total hip replacement and 54.90 mm for resurfacing arthroplasty). In seven resurfacing procedures (6.8%), the surgeon used a larger size of component in order to match the corresponding diameter of the femoral component.

With resurfacing arthroplasty, conservation of bone is clearly advantageous on the femoral side. Our study has shown that, with a specific design of acetabular implant and by following a careful surgical technique, removal of bone on the acetabular side is comparable with that of total hip replacement.

We describe the experience with the first consecutive 230 Birmingham hip resurfacings at our centre. At a mean follow-up of three years (25 to 52 months) survivorship was 99.14% with revision in one patient for a loose acetabular component and one death from unrelated causes. One patient developed a fracture of the femoral neck at six weeks which united unremarkably after a period of non-weight-bearing. The Harris hip score improved from a mean of 62.54 (8 to 92) to 97.74 (61 to 100). The mean flexion improved from 91.52° (25 to 140) to 110.41° (80 to 145).

Most patients (97%) considered the outcome to be good or excellent. Our preliminary experience with this implant is encouraging and the results are superior to the earlier generation of resurfacings for the same length of follow-up.

Between January 1998 and December 1998, 82 consecutive patients (86 hips) underwent total hip arthroplasty using a trabecular metal monoblock acetabular component. All patients had a clinical and radiological follow-up evaluation at six, 12 and 24 weeks, 12 months, and then annually thereafter. On the initial post-operative radiograph 25 hips had a gap between the outer surface of the component and the acetabular host bed which ranged from 1 to 5 mm. All patients were followed up clinically and radiologically for a mean of 7.3 years (7 to 7.5). The 25 hips with the 1 to 5 mm gaps were studied for component migration at two years using the Einzel-Bild-Roentgen-Analyse (EBRA) digital measurement method. At 24 weeks all the post-operative gaps were filled with bone and no acetabular component had migrated. The radiographic outcome of all 86 components showed no radiolucent lines and no evidence of lysis. No acetabular implant was revised. There were no dislocations or other complications. The bridging of the interface gaps (up to 5 mm) by the trabecular metal monoblock acetabular component indicates the strong osteoconductive, and possibly osteoinductive, properties of trabecular metal.

We have compared the biomechanical nature of the reconstruction of the hip in conventional total hip arthroplasty (THA) and surface replacement arthroplasty (SRA) in a randomised study involving 120 patients undergoing unilateral primary hip replacement. The contralateral hip was used as a control.

Post-operatively, the femoral offset was significantly increased with THA (mean 5.1 mm; −2.8 to 11.6) and decreased with SRA (mean −3.3 mm; −8.9 to 8.2). Femoral offset was restored within sd 4 mm in 14 (25%) of those with THA and in 28 (57%) of the patients receiving SRA (p < 0.001). In the THA group, the leg was lengthened by a mean of 2.6 mm (−6.04 to +12.9), whereas it was shortened by a mean of 1.9 mm (−7.1 to +2.05) in the SRA group, compared with the contralateral side. Leg-length inequality was restored within sd 4 mm in 42 (86%) of the SRA and 33 (60%) of the THA patients. The radiological parameters of acetabular reconstruction were similar in both groups.

Restoration of the normal proximal femoral anatomy was more precise with SRA. The enhanced stability afforded by the use of a large-diameter femoral head avoided over-lengthening of the limb or increased offset to improve soft-tissue tension as occurs sometimes in THA. In a subgroup of patients with significant pre-operative deformity, restoration of the normal hip anatomy with lower pre-operative femoral offset or significant shortening of the leg was still possible with SRA.