We have studied the beneficial effects of a hydroxyapatite (HA) coating on the prevention of the migration of wear debris along the implant-bone interface. We implanted a loaded HA-coated implant and a non-coated grit-blasted titanium alloy (Ti) implant in each distal femoral condyle of eight Labrador dogs. The test implant was surrounded by a gap communicating with the joint space and allowing access of joint fluid to the implant-bone interface. We injected polyethylene (PE) particles into the right knee three weeks after surgery and repeated this weekly for the following five weeks. The left knee received sham injections. The animals were killed eight weeks after surgery. Specimens from the implant-bone interface were examined under plain and polarised light. Only a few particles were found around HA-coated implants, but around Ti implants there was a large amount of particles. HA-coated implants had approximately 35% bone ingrowth, whereas Ti implants had virtually no bone ingrowth and were surrounded by a fibrous membrane. Our findings suggest that HA coating of implants is able to inhibit peri-implant migration of PE particles by creating a seal of tightly-bonded bone on the surface of the implant

In a single-blind, randomised series of knee replacements in 116 patients, we used radiostereometric analysis (RSA) to measure micromotion in three types of tibial implant fixation for two years after knee replacement. We compared hydroxyapatite-augmented porous coating, porous coating, and cemented fixation of the same design of tibial component. At one to two years, porous-coated implants migrated at a statistically significantly higher rate than hydroxyapatite-augmented or cemented implants. There was no significant difference between hydroxyapatite-coated and cemented implants. We conclude that hydroxyapatite augmentation may offer a clinically relevant advantage over a simple porous coating for tibial component fixation, but is no better than cemented fixation

We treated 75 patients with benign bone tumours by curettage and filling the defect with calcium hydroxyapatite (HA). There were 28 women and 47 men with a mean age of 27.7 years (3 to 80). The mean follow-up was for 41.3 months. Postoperative radiological assessment revealed that the implanted HA was well incorporated into the surrounding host bone in all patients. Two patients suffered fractures in the postoperative period. Two patients complained of pain associated with HA in the soft tissues, but this diminished within six months. No patient had local pain at the final follow-up. Recurrence of the tumour was seen in three cases. Histopathological study of the implanted area showed removal of the HA by histiocytes and multinucleated giant cells, and the formation of much appositional bone. We conclude that HA is an excellent bone-graft substitute in surgery for benign bone tumours

Hydroxyapatite (HA) granules of 100 to 300 μm, 0.9 to 1.2 mm and 3.0 to 5.0 mm were mixed in a ratio of 10:45:45 and packed into massive bone deficiencies in revision operations for total hip arthroplasty. We did not use additional graft or cup support for deficiencies of the lateral and medial wall. The procedure was carried out in 40 hips between 1986 and 1992. The radiographic spaces seen at the interface between HA and bone immediately after surgery disappeared within three months. Some spaces appeared between HA granules near the bone in the lateral part of two joints, and three sockets migrated in patients with severe segmental and cavitary deficiencies. Direct bonding of HA to bone was observed radiologically without morphological changes, except in the three joints with migration. All patients could walk without pain but the three with definite loosening needed crutches

A clay containing hydroxyapatite (HA) was developed for use as a filling material between an uncemented implant and bone. It consists of 55% HA granules greater than 0.1 mm in size with a homogeneous pore distribution and a porosity of 35% to 48% in a saline solution of sodium alginate (6%). Ti-6A1-4V alloy rods with smooth surfaces were implanted into the distal medullary canal of one osteotomised tibia of 32 Japanese white rabbits. Sixteen rods were inserted with HA clay and 16 without the clay to act as a control group. Six of each group were killed at one week and ten at 12 weeks postoperatively. The pull-out strength of the implants with HA clay was significantly greater at 12 weeks (p < 0.05), as was the percentage of the area of the new bone (p < 0.05). The study suggests that HA clay has an osteoconductive property, allowing adequate bone fixation across a gap at an early stage. The use of HA clay to enhance the early stability of uncemented components may help to improve the functional outcome of total joint arthroplasty

We allocated randomly 27 patients undergoing 28 primary uncemented total hip replacements (THR) to receive prosthetic components of similar design with either plasma-sprayed titanium alloy (Ti) coating (n = 13) or hydroxyapatite (HA) coating (n = 15). After some exclusions, 15 of the patients (15 THR; 7 with HA- and 8 with Ti-coating) were followed by roentgen stereophotogrammetric analysis at 3, 6 and 12 months to measure migration of the femoral component. Twenty-six of the patients (26 THR) were followed clinically and by conventional radiography. All the femoral components had migrated at 3 months. From 3 to 12 months, the migration of Ti-coated components continued whereas the HA-coated components had stabilised. At 12 months there was significantly less migration of the HA-coated components (p < 0.05). The maximum subsidence was 0.2 mm in both groups. The Harris hip score was equal in the two groups preoperatively but at follow-up it was better in the HA-coated group (p < 0.05) and visual analogue scale scores showed that they had less pain (p < 0.05)

We have studied in vitro the effect of a hydroxyapatite (HA) tricalcium phosphate material coated with hepatocyte growth factor (HA-HGF) on cell growth, collagen synthesis and secretion of metalloproteinases (MMPs) by human osteoblasts. Cell proliferation was stimulated when osteoblasts were incubated with untreated HA and was further increased after exposure to HA-HGF. The uptake of [. 3. H]-proline was increased after treatment with HA. When osteoblasts were exposed to HA-HGF, collagen synthesis was increased with respect to HA. The secretion of MMPs in control cells was undetectable, but in HA and HA-HGF cells MMP 2 and MMP 9 were clearly synthesised. Our results suggest that HA can promote osteoblast activity and that HGF can further increase its bioactivity

In previous studies, we have demonstrated a fibrocartilaginous membrane around hydroxyapatite-coated implants subjected to micromovement in contrast to the fibrous connective tissue which predominates around similarly loaded titanium alloy implants. In the present study, in mature dogs, we investigated the effect of immobilising titanium (Ti)- or hydroxyapatite (HA)-coated implants already surrounded by a movement-induced fibrous membrane and compared the results with those of similar implants in which continuous micromovement was allowed to continue. The implants were inserted in the medial femoral condyles of 14 dogs and subjected to 150 microns movements during each gait cycle. After four weeks (when a fibrous membrane had developed), half the implants were immobilised to prevent further micromovement. The dogs were killed at 16 weeks and the results were evaluated by push-out tests and histological analysis. The continuously loaded Ti-coated implants were surrounded by a fibrous membrane, whereas bridges of new bone anchored the HA-coated implants. The immobilised implants were surrounded by bone irrespective of the type of coating. Push-out tests of the continuously loaded implants showed better fixation of those with HA coating (p < 0.001). The immobilised Ti-coated implants had four times stronger fixation than did continuously loaded Ti-coated implants (p < 0.01) but there was no equivalent difference between the two groups of HA-coated implants. The amount of bone ingrowth was greater into immobilised HA-coated implants than into immobilised Ti-coated implants (p < 0.01). Two-thirds of the HA coating had been resorbed after 16 weeks of implantation, but 25% of this resorbed HA had been replaced by bone.(ABSTRACT TRUNCATED AT 250 WORDS)

We have studied the effect of hydroxyapatite (HA) coating in 15 ovariectomised and 15 normal rats which had had a sham procedure. Twenty-four weeks after operation, HA-coated implants were inserted into the intramedullary canal of the right femur and uncoated implants into the left femur. The prostheses were removed four weeks after implantation. Twelve specimens in each group had mechanical push-out tests. Sagittal sections of the other three were evaluated by SEM. The bone mineral density (BMD) of the dissected left tibia was measured by dual-energy x-ray absorptiometry. The difference in BMD between the control and ovariectomised tibiae was 35.01 mg/cm. 2. (95% CI, 26.60 to 43.42). The push-out strength of the HA-coated implants was higher than that of the uncoated implants in both groups (p < 0.0001), but the HA-coated implants of the ovariectomised group had a reduction in push-out strength of 40.3% compared with the control group (p < 0.0001). Our findings suggest that HA-coated implants may improve the fixation of a cementless total hip prosthesis but that the presence of osteoporosis may limit the magnitude of this benefit

Objectives

An experimental rabbit model was used to test the null hypothesis, that there is no difference in new bone formation around uncoated titanium discs compared with coated titanium discs when implanted into the muscles of rabbits.

Aims

The Intraosseous Transcutaneous Amputation Prosthesis (ITAP) may improve quality of life for amputees by avoiding soft-tissue complications associated with socket prostheses and by improving sensory feedback and function. It relies on the formation of a seal between the soft tissues and the implant and currently has a flange with drilled holes to promote dermal attachment. Despite this, infection remains a significant risk. This study explored alternative strategies to enhance soft-tissue integration.

Aims

To compare the structural durability of hydroxyapatite-tricalcium phosphate (HATCP) to autologous iliac crest bone graft in calcaneal lengthening osteotomy (CLO) for pes planovalgus in childhood.

We have carried out a radiostereometric study of 50 patients (54 knees) with osteoarthritis of the knee who were randomly allocated to receive a cemented or a hydroxyapatite-coated femoral component for total knee replacement. The patients were also stratified to receive one of three types of articulating surface (standard, rotating platform, Freeman-Samuelson (FS)1000) all based on the Freeman-Samuelson design. The tibial components were cemented in all cases. Radiostereometry was performed post-operatively and at 3, 12 and 24 months. The analysis was restricted to rotation of the femoral component over time.

After two years, rotation of the femoral components in the transverse, longitudinal and sagittal planes did not differ between the cemented and the hydroxyapatite-coated implants (p = 0.2 to 0.9).

In total knee replacements with a rotating platform, the femoral component tended to tilt more posteriorly than in the other two designs, regardless of the choice of fixation (cemented or hydroxyapatite-coated, p = 0.04). The standard version of the femoral component, whether cemented or hydroxyapatite-coated, rotated more into valgus than was observed with the rotating-platform and FS1000 designs (p = 0.005). The increased constraint provided by the FS1000 component did not appear to have any adverse effect on fixation of the femoral component.