Hydroxyapatite-coated standard anatomical and customised femoral stems are designed to transmit load to the metaphyseal part of the proximal femur in order to avoid stress shielding and to reduce resorption of bone. In a randomised in vitro study, we compared the changes in the pattern of cortical strain after the insertion of hydroxyapatite-coated standard anatomical and customised stems in 12 pairs of human cadaver femora. A hip simulator reproduced the physiological loads on the proximal femur in single-leg stance and stair-climbing. The cortical strains were measured before and after the insertion of the stems.

Significantly higher strain shielding was seen in Gruen zones 7, 6, 5, 3 and 2 after the insertion of the anatomical stem compared with the customised stem. For the anatomical stem, the hoop strains on the femur also indicated that the load was transferred to the cortical bone at the lower metaphyseal or upper diaphyseal part of the proximal femur.

The customised stem induced a strain pattern more similar to that of the intact femur than the standard, anatomical stem.

Since the Oxford knee was first used unicompartmentally in 1982, a small number of bearings have fractured. Of 14 retrieved bearings, we examined ten samples with known durations in situ (four Phase 1, four Phase 2 and two Phase 3). Evidence of impingement and associated abnormally high wear (> 0.05 mm per year) as well as oxidation was observed in all bearings. In four samples the fracture was associated with the posterior radio-opaque wire. Fracture surfaces indicated fatigue failure, and scanning electron microscopy suggested that the crack initiated in the thinnest region. The estimated incidence of fracture was 3.20% for Phase 1, 0.74% for Phase 2, 0.35% for Phase 3, and 0% for Phase 3 without the posterior marker wire. The important aetiological factors for bearing fracture are impingement leading to high wear, oxidation, and the posterior marker wire. With improved surgical technique, impingement and high wear should be prevented and modern polyethylene may reduce the oxidation risk. A posterior marker wire is no longer used in the polyethylene meniscus. Therefore, the rate of fracture, which is now very low, should be reduced to a negligible level.

This systematic review of the literature summarises the clinical experience with ceramic-on-ceramic hip bearings over the past 40 years and discusses the concerns that exist in relation to the bearing combination. Loosening, fracture, liner chipping on insertion, liner canting and dissociation, edge-loading and squeaking have all been reported, and the relationship between these issues and implant design and surgical technique is investigated. New design concepts are introduced and analysed with respect to previous clinical experience.

Objectives

The objective of this study is to determine an optimal antibiotic-loaded bone cement (ALBC) for infection prophylaxis in total joint arthroplasty (TJA).

The June 2013 Research Roundup³⁶⁰ looks at: a contact patch to rim distance and metal ions; the matrix of hypoxic cartilage; CT assessment of early fracture healing; Hawthornes and radiographs; cardiovascular mortality and fragility fractures; and muscle strength decline preceding OA changes.

Bioengineering reasons for increased wear and failure of metal-on-metal (MoM) bearings in hip prostheses have been described. Low wear occurs in MoM hips when the centre of the femoral head is concentric with the centre of the acetabular component and the implants are correctly positioned. Translational or rotational malpositioning of the components can lead to the contact-patch of the femoral component being displaced to the rim of the acetabular component, resulting in a ten- to 100-fold increase in wear and metal ion levels. This may cause adverse tissue reactions, loosening of components and failure of the prosthesis.

The treatment of osteochondral lesions and osteoarthritis remains an ongoing clinical challenge in orthopaedics. This review examines the current research in the fields of cartilage regeneration, osteochondral defect treatment, and biological joint resurfacing, and reports on the results of clinical and pre-clinical studies. We also report on novel treatment strategies and discuss their potential promise or pitfalls. Current focus involves the use of a scaffold providing mechanical support with the addition of chondrocytes or mesenchymal stem cells (MSCs), or the use of cell homing to differentiate the organism’s own endogenous cell sources into cartilage. This method is usually performed with scaffolds that have been coated with a chemotactic agent or with structures that support the sustained release of growth factors or other chondroinductive agents. We also discuss unique methods and designs for cell homing and scaffold production, and improvements in biological joint resurfacing. There have been a number of exciting new studies and techniques developed that aim to repair or restore osteochondral lesions and to treat larger defects or the entire articular surface. The concept of a biological total joint replacement appears to have much potential.

Cite this article: Bone Joint Res 2013;2:193–9.

Polyethylene wear of acetabular components is a key factor in the development of periprosthetic osteolysis and wear at the articular surface has been well documented and quantified, but fewer data are available about changes which occur at the backside of the liner.

At revision surgery for loosening of the femoral component we retrieved 35 conventional modular acetabular liners of the same design. Linear and volumetric articular wear, backside volumetric change and the volume of the screw-head indentations were quantified. These volumes, clinical data and the results from radiological Ein Bild Röntgen Analyse migration analysis were used to identify potential factors influencing the volumetric articular wear and backside volumetric change.

The rate of backside volumetric change was found to be 2.8% of the rate of volumetric articular wear and decreased with increasing liner size. Migrated acetabular components showed significantly higher rates of backside volumetric change plus screw-head indentations than those without migration.

The backside volumetric change was at least ten times larger than finite-element simulation had suggested. In a stable acetabular component with well-anchored screws, the amount of backside wear should not cause clinical problems. Impingement of the screw-heads could produce more wear particles than those generated at the liner-shell interface. Because the rate of backside volumetric change is only 2.8% of the rate of volumetric articular wear and since creep is likely to contribute a significant portion to this, the debris generated by wear at the backside of the liner may not be sufficient to create a strong osteolytic response.

This study investigated the anatomical relationship between the clavicle and its adjacent vascular structures, in order to define safe zones, in terms of distance and direction, for drilling of the clavicle during osteosynthesis using a plate and screws following a fracture. We used reconstructed three-dimensional CT arteriograms of the head, neck and shoulder region. The results have enabled us to divide the clavicle into three zones based on the proximity and relationship of the vascular structures adjacent to it. The results show that at the medial end of the clavicle the subclavian vessels are situated behind it, with the vein intimately related to it. In some scans the vein was opposed to the posterior cortex of the clavicle. At the middle one-third of the clavicle the artery and vein are a mean of 17.02 mm (5.4 to 26.8) and 12.45 mm (5 to 26.1) from the clavicle, respectively, and at a mean angle of 50° (12 to 80) and 70° (38 to 100), respectively, to the horizontal. At the lateral end of the clavicle the artery and vein are at mean distances of 63.4 mm (46.8 to 96.5) and 75.67 mm (50 to 109), respectively.

An appreciation of the information gathered from this study will help minimise the risk of inadvertent iatrogenic vascular injury during plating of the clavicle.

A retrospective study was conducted to investigate the changes in metal ion levels in a consecutive series of Birmingham Hip Resurfacings (BHRs) at a minimum ten-year follow-up. We reviewed 250 BHRs implanted in 232 patients between 1998 and 2001. Implant survival, clinical outcome (Harris hip score), radiographs and serum chromium (Cr) and cobalt (Co) ion levels were assessed.

Of 232 patients, 18 were dead (five bilateral BHRs), 15 lost to follow-up and ten had been revised. The remaining 202 BHRs in 190 patients (136 men and 54 women; mean age at surgery 50.5 years (17 to 76)) were evaluated at a minimum follow-up of ten years (mean 10.8 years (10 to 13.6)). The overall implant survival at 13.2 years was 92.4% (95% confidence interval 90.8 to 94.0). The mean Harris hip score was 97.7 (median 100; 65 to 100). Median and mean ion levels were low for unilateral resurfacings (Cr: median 1.3 µg/l, mean 1.95 µg/l (< 0.5 to 16.2); Co: median 1.0 µg/l, mean 1.62 µg/l (< 0.5 to 17.3)) and bilateral resurfacings (Cr: median 3.2 µg/l, mean 3.46 µg/l (< 0.5 to 10.0); Co: median 2.3 µg/l, mean 2.66 µg/l (< 0.5 to 9.5)). In 80 unilateral BHRs with sequential ion measurements, Cr and Co levels were found to decrease significantly (p < 0.001) from the initial assessment at a median of six years (4 to 8) to the last assessment at a median of 11 years (9 to 13), with a mean reduction of 1.24 µg/l for Cr and 0.88 µg/l for Co. Three female patients had a > 2.5 µg/l increase of Co ions, associated with head sizes ≤ 50 mm, clinical symptoms and osteolysis. Overall, there was no significant difference in change of ion levels between genders (Cr, p = 0.845; Co, p = 0.310) or component sizes (Cr, p = 0.505; Co, p = 0.370). Higher acetabular component inclination angles correlated with greater change in ion levels (Cr, p = 0.013; Co, p = 0.002). Patients with increased ion levels had lower Harris hip scores (p = 0.038).

In conclusion, in well-functioning BHRs the metal ion levels decreased significantly at ten years. An increase > 2.5 µg/l was associated with poor function.

Cite this article: Bone Joint J 2013;95-B:1332–8.

We have studied the effects of bupivacaine on human and bovine articular chondrocytes in vitro. Time-lapse confocal microscopy of human articular chondrocytes showed > 95% cellular death after exposure to 0.5% bupivacaine for 30 minutes. Human and bovine chondrocytes exposed to 0.25% bupivacaine had a time-dependent reduction in viability, with longer exposure times resulting in higher cytotoxicity. Cellular death continued even after removal of 0.25% bupivacaine. After exposure to 0.25% bupivacaine for 15 minutes, flow cytometry showed bovine chondrocyte viability to be 41% of saline control after seven days. After exposure to 0.125% bupivacaine for up to 60 minutes, the viability of both bovine and human chondrocytes was similar to that of control groups.

These data show that prolonged exposure 0.5% and 0.25% bupivacaine solutions are potentially chondrotoxic.

The efficacy of β-tricalcium phosphate (β-TCP) loaded with bone morphogenetic protein-2 (BMP-2)-gene-modified bone-marrow mesenchymal stem cells (BMSCs) was evaluated for the repair of experimentally-induced osteonecrosis of the femoral head in goats.

Bilateral early-stage osteonecrosis was induced in adult goats three weeks after ligation of the lateral and medial circumflex arteries and delivery of liquid nitrogen into the femoral head. After core decompression, porous β-TCP loaded with BMP-2 gene- or β-galactosidase (gal)-gene-transduced BMSCs was implanted into the left and right femoral heads, respectively. At 16 weeks after implantation, there was collapse of the femoral head in the untreated group but not in the BMP-2 or β-gal groups. The femoral heads in the BMP-2 group had a normal density and surface, while those in the β-gal group presented with a low density and an irregular surface. Histologically, new bone and fibrous tissue were formed in the macropores of the β-TCP. Sixteen weeks after implantation, lamellar bone had formed in the BMP-2 group, but there were some empty cavities and residual fibrous tissue in the β-gal group. The new bone volume in the BMP-2 group was significantly higher than that in the β-gal group. The maximum compressive strength and Young’s modulus of the repaired tissue in the BMP-2 group were similar to those of normal bone and significantly higher than those in the β-gal group.

Our findings indicate that porous β-TCP loaded with BMP-2-gene-transduced BMSCs are capable of repairing early-stage, experimentally-induced osteonecrosis of the femoral head and of restoring its mechanical function.

The aim of this study was to evaluate whether coating titanium discs with selenium in the form of sodium selenite decreased bacterial adhesion of Staphylococcus aureus and Staph. epidermidis and impeded osteoblastic cell growth.

In order to evaluate bacterial adhesion, sterile titanium discs were coated with increasing concentrations of selenium and incubated with bacterial solutions of Staph. aureus (ATCC 29213) and Staph. epidermidis (DSM 3269) and stained with Safranin-O. The effect of selenium on osteoblastic cell growth was also observed. The adherence of MG-63 cells on the coated discs was detected by staining with Safranin-O. The proportion of covered area was calculated with imaging software.

The tested Staph. aureus strain showed a significantly reduced attachment on titanium discs with 0.5% (p = 0.011) and 0.2% (p = 0.02) selenium coating. Our test strain from Staph. epidermidis showed a highly significant reduction in bacterial adherence on discs coated with 0.5% (p = 0.0099) and 0.2% (p = 0.002) selenium solution. There was no inhibitory effect of the selenium coating on the osteoblastic cell growth.

Selenium coating is a promising method to reduce bacterial attachment on prosthetic material.

Cite this article: Bone Joint J 2013;95-B:678–82.

This paper outlines the recent development of an exchange Travelling Fellowship scheme between the British and American Orthopaedic Research Societies.

Objectives

To quantify and compare peri-acetabular bone mineral density (BMD) between a monoblock acetabular component using a metal-on-metal (MoM) bearing and a modular titanium shell with a polyethylene (PE) insert. The secondary outcome was to measure patient-reported clinical function.

There is currently no consensus about the mean volume of blood lost during spinal tumour surgery and surgery for metastatic spinal disease. We conducted a systematic review of papers published in the English language between 31 January 1992 and 31 January 2012. Only papers that clearly presented blood loss data in spinal surgery for metastatic disease were included. The random effects model was used to obtain the pooled estimate of mean blood loss.

We selected 18 papers, including six case series, ten retrospective reviews and two prospective studies. Altogether, there were 760 patients who had undergone spinal tumour surgery and surgery for metastatic spinal disease. The pooled estimate of peri-operative blood loss was 2180 ml (95% confidence interval 1805 to 2554) with catastrophic blood loss as high as 5000 ml, which is rare. Aside from two studies that reported large amounts of mean blood loss (> 5500 ml), the resulting funnel plot suggested an absence of publication bias. This was confirmed by Egger’s test, which did not show any small-study effects (p = 0.119). However, there was strong evidence of heterogeneity between studies (I² = 90%; p < 0.001).

Spinal surgery for metastatic disease is associated with significant blood loss and the possibility of catastrophic blood loss. There is a need to establish standardised methods of calculating and reporting this blood loss. Analysis should include assessment by area of the spine, primary pathology and nature of surgery so that the amount of blood loss can be predicted. Consideration should be given to autotransfusion in these patients.

Cite this article: Bone Joint J 2013;95-B:683–8.

We used a biodegradable mesh to convert an acetabular defect into a contained defect in six patients at total hip replacement. Their mean age was 61 years (46 to 69). The mean follow-up was 32 months (19 to 50). Before clinical use, the strength retention and hydrolytic in vitro degradation properties of the implants were studied in the laboratory over a two-year period. A successful clinical outcome was determined by the radiological findings and the Harris hip score.

All the patients had a satisfactory outcome and no mechanical failures or other complications were observed. No protrusion of any of the impacted grafts was observed beyond the mesh. According to our preliminary laboratory and clinical results the biodegradable mesh is suitable for augmenting uncontained acetabular defects in which the primary stability of the implanted acetabular component is provided by the host bone. In the case of defects of the acetabular floor this new application provides a safe method of preventing graft material from protruding excessively into the pelvis and the mesh seems to tolerate bone-impaction grafting in selected patients with primary and revision total hip replacement.

The April 2013 Research Roundup³⁶⁰ looks at: when the ‘residency cake’ is done; steroids, stem cells and tendons; what exactly is osteoarthritis; platelet-rich plasma; CRPS; d-Dimer for DVT; reducing bacterial adhesion; and fin or limb?

We examined cultured osteoblasts derived from paired samples from the greater tuberosity and acromion from eight patients with large chronic tears of the rotator cuff.

We found that osteoblasts from the tuberosity had no apparent response to mechanical stimulation, whereas those derived from the acromion showed an increase in alkaline phosphatase activity and nitric oxide release which is normally a response of bone cells to mechanical strain. By contrast, we found that cells from both regions were able to respond to dexamethasone, a well-established promoter of osteoblastic differentiation, with the expected increase in alkaline phosphatase activity.

Our findings indicate that the failure of repair of the rotator cuff may be due, at least in part, to a compromised capacity for mechanoadaptation within the greater tuberosity. It remains to be seen whether this apparent decrease in the sensitivity of bone cells to mechanical stimulation is the specific consequence of the reduced load-bearing history of the greater tuberosity in these patients.

This study reports the application of a novel method for quantitatively determining differences in the mechanical properties of healthy and torn rotator cuff tissues. In order to overcome problems of stress risers at the grip-tendon interface that can obscure mechanical measurements of small tendons, we conducted our investigation using dynamic shear analysis.

Rotator cuff tendon specimens were obtained from 100 patients during shoulder surgery. They included 82 differently sized tears and 18 matched controls. We subjected biopsy samples of 3 mm in diameter to oscillatory deformation under compression using dynamic shear analysis. The storage modulus (G’) was calculated as an indicator of mechanical integrity.

Normal tendons had a significantly higher storage modulus than torn tendons, indicating that torn tendons are mechanically weaker than normal tendons (p = 0.003). Normal tendons had a significantly higher mean shear modulus than tendons with massive tears (p < 0.01).

Dynamic shear analysis allows the determination of shear mechanical properties of small tissue specimens obtained intra-operatively that could not be studied by conventional methods of tensile testing. These methods could be employed to investigate other musculoskeletal tissues. This pilot study provides some insight into mechanisms that might contribute to the failure of repair surgery, and with future application could help direct the most appropriate treatment for specific rotator cuff tears.