The leading indication for revision total hip arthroplasty (THA) remains aseptic loosening owing to wear. The younger, more active patients currently undergoing THA present unprecedented demands on the bearings. Ceramic-on-ceramic (CoC) bearings have consistently shown the lowest rates of wear. The recent advances, especially involving alumina/zirconia composite ceramic, have led to substantial improvements and good results in vitro.

Alumina/zirconia composite ceramics are extremely hard, scratch resistant and biocompatible. They offer a low co-efficient of friction and superior lubrication and lower rates of wear compared with other bearings. The major disadvantage is the risk of fracture of the ceramic. The new composite ceramic has reduced the risk of fracture of the femoral head to 0.002%. The risk of fracture of the liner is slightly higher (0.02%).

Assuming that the components are introduced without impingement, CoC bearings have major advantages over other bearings. Owing to the superior hardness, they produce less third body wear and are less vulnerable to intra-operative damage.

The improved tribology means that CoC bearings are an excellent choice for young, active patients requiring THA.

Cite this article: Bone Joint J 2016;98-B(1 Suppl A):14–17.

Dual mobility cups have two points of articulation, one between the shell and the polyethylene (external bearing) and one between the polyethylene and the femoral head (internal bearing). Movement occurs at the inner bearing; the outer bearing only moves at extremes of movement.

Dislocation after total hip arthroplasty (THA) is a cause of much morbidity and its treatment has significant cost implications. Dual mobility cups provide an increased range of movement and a may reduce the risk of dislocation.

This paper reviews the use of these cups in THA, particularly where stability is an issue. Dual mobility cups may be of benefit in primary THA in patients at a high risk of dislocation, such as those who are older with increased comorbidities and a higher American Association of Anesthesiology grade and those with a neuromuscular disease. They may be used at revision surgery where the risk of dislocation is high, such as in patients with many prior dislocations, or those with abductor deficiency. They may also be used in THA for displaced fractures of the femoral neck, which has a notoriously high rate of dislocation.

Cite this article: Bone Joint J 2016;98-B(1 Suppl A):60–3.

A pelvic discontinuity occurs when the superior and inferior parts of the hemi-pelvis are no longer connected, which is difficult to manage when associated with a failed total hip replacement. Chronic pelvic discontinuity is found in 0.9% to 2.1% of hip revision cases with risk factors including severe pelvic bone loss, female gender, prior pelvic radiation and rheumatoid arthritis. Common treatment options include: pelvic plating with allograft, cage reconstruction, custom triflange implants, and porous tantalum implants with modular augments. The optimal technique is dependent upon the degree of the discontinuity, the amount of available bone stock and the likelihood of achieving stable healing between the two segments. A method of treating pelvic discontinuity using porous tantalum components with a distraction technique that achieves both initial stability and subsequent long-term biological fixation is described.

Cite this article: Bone Joint J 2014;96-B(11 Suppl A):73–7.

Metal-on-metal resurfacing of the hip (MoMHR) has enjoyed a resurgence in the last decade, but is now again in question as a routine option for osteoarthritis of the hip. Proponents of hip resurfacing suggest that its survival is superior to that of conventional hip replacement (THR), and that hip resurfacing is less invasive, is easier to revise than THR, and provides superior functional outcomes. Our argument serves to illustrate that none of these proposed advantages have been realised and new and unanticipated serious complications, such as pseudotumors, have been associated with the procedure. As such, we feel that the routine use of MoMHR is not justified.

Cite this article: Bone Joint J 2014;96-B(11 Suppl A):17–21.

In a time of limited resources, the debate continues over which types of hip prosthesis are clinically superior and more cost-effective. Orthopaedic surgeons increasingly need robust economic evidence to understand the full value of the operation, and to aid decision making on the ‘package’ of procedures that are available and to justify their practice beyond traditional clinical preference.

In this paper we explore the current economic debate about the merits of cemented and cementless total hip replacement, an issue that continues to divide the orthopaedic community.

Cite this article: Bone Joint J 2013;95-B:874–6.

Persistent groin pain after seemingly successful total hip replacement (THR) appears to have become more common. Recent studies have indicated a high incidence after metal-on-polyethylene and metal-on-metal conventional THR and it has been documented in up to 18% of patients after metal-on-metal resurfacing. There are many causes, including acetabular loosening, stress fracture, and iliopsoas tendonitis and impingement. The evaluation of this problem requires a careful history and examination, plain radiographs and an algorithmic approach to special diagnostic imaging and tests. Non-operative treatment is not usually successful. Specific operative treatment depending on the cause of the pain usually involves revision of the acetabular component, iliopsoas tenotomy or other procedures, and is usually successful. Here, an appropriate algorithm is described.

We present our experience with a double-mobility acetabular component in 155 consecutive revision total hip replacements in 149 patients undertaken between 2005 and 2009, with particular emphasis on the incidence of further dislocation. The mean age of the patients was 77 years (42 to 89) with 59 males and 90 females. In all, five patients died and seven were lost to follow-up. Indications for revision were aseptic loosening in 113 hips, recurrent instability in 29, peri-prosthetic fracture in 11 and sepsis in two. The mean follow-up was 42 months (18 to 68). Three hips (2%) in three patients dislocated within six weeks of surgery; one of these dislocated again after one year. All three were managed successfully with closed reduction. Two of the three dislocations occurred in patients who had undergone revision for recurrent dislocation. All three were found at revision to have abductor deficiency. There were no dislocations in those revised for either aseptic loosening or sepsis.

These results demonstrate a good mid-term outcome for this component. In the 29 patients revised for instability, only two had a further dislocation, both of which were managed by closed reduction.

This review summarises the evidence for the treatment of displaced fractures of the femoral neck in elderly patients. Results from randomised clinical trials and national register studies are presented when available.

The advantages of arthroplasty compared with internal fixation are supported by several studies. A number of studies contribute to the discussions of total hip arthroplasty (THA) versus hemiarthroplasty and unipolar versus bipolar hemiarthroplasty, but no clear-cut evidence-based recommendation can be made. THA may be particularly advantageous for active, lucid patients with a relatively long life expectancy. For patients who are physiologically older, hemiarthoplasty is probably satisfactory, and for the oldest patients with more comorbidities, unipolar implants are considered to be sufficient. If the hospital can support emergency THA surgery in sufficient numbers and quality, there may be few patients who warrant bipolar hemiarthroplasty.

The direct lateral approach reduces the risk of dislocation compared with the posterior approach. Cemented implants lower the risk of periprosthetic fracture and its subsequent morbidity and mortality. As the risk of peri-operative death related to bone cement can be reduced by adequate measures, cemented implants are recommended in fracture cases.

Take home message: There remains a great variation in the surgical management of patients with a hip fracture, and an evidence-based approach should improve the outcomes for this vulnerable patient group.

Cite this article: Bone Joint J 2016;98-B:291–7.

The common recommended treatment for infected total hip replacement is two-staged exchange including removal of all components. However, removal of well-fixed femoral stems can result in structural bone damage. We recently reported on an alternative treatment of partial two-stage exchange used in selected cases, in which a well-fixed femoral stem was left and only the acetabular component removed, the joint space was debrided thoroughly, an antibiotic-laden polymethylmethacrylate spacer was moulded using a bulb-type syringe and placed in the acetabulum, intravenous antibiotics were administered during the interval, and delayed re-implantation was performed. In 19 patients treated with this technique from January 2000 to January 2011, 89% were free of infection at a mean follow-up of four years (2 to 11). Since then, disposable silicone moulds have become available to fabricate spacers in separate femoral and head units. The head spacer mould, which incorporates various neck taper adapter options, greatly facilitates the technique of partial two-stage exchange. We report our early experience using disposable silicone head spacer moulds for partial two-stage exchange in seven patients with infected primary hip replacements.

Cite this article: Bone Joint J 2014;96-B(11 Suppl A):66–9

Hip resurfacing has been proposed as an alternative to traditional total hip arthroplasty in young, active patients. Much has been learned following the introduction of metal-on-metal resurfacing devices in the 1990s. The triad of a well-designed device, implanted accurately, in the correct patient has never been more critical than with these implants.

Following Food and Drug Administration approval in 2006, we studied the safety and effectiveness of one hip resurfacing device (Birmingham Hip Resurfacing) at our hospital in a large, single-surgeon series. We report our early to mid–term results in 1333 cases followed for a mean of 4.3 years (2 to 5.7) using a prospective, observational registry. The mean patient age was 53.1 years (12 to 84); 70% were male and 91% had osteoarthritis. Complications were few, including no dislocations, no femoral component loosening, two femoral neck fractures (0.15%), one socket loosening (0.08%), three deep infections (0.23%), and three cases of metallosis (0.23%). There were no destructive pseudotumours.

Overall survivorship at up to 5.7 years was 99.2%. Aseptic survivorship in males under the age of 50 was 100%. We believe this is the largest United States series of a single surgeon using a single resurfacing system.

Cite this article: Bone Joint J 2016;98-B (1 Suppl A):10–13.

There is widespread concern regarding the incidence of adverse soft-tissue reactions after metal-on-metal (MoM) hip replacement. Recent National Joint Registry data have shown clear differences in the rates of failure of different designs of hip resurfacing. Our aim was to update the failure rates related to metal debris for the Articular Surface Replacement (ASR). A total of 505 of these were implanted.

Kaplan-Meier analysis showed a failure rate of 25% at six years for the ASR resurfacing and of 48.8% for the ASR total hip replacement (THR). Of 257 patients with a minimum follow-up of two years, 67 (26.1%) had a serum cobalt concentration which was greater than 7 μg/l. Co-ordinate measuring machine analysis of revised components showed that all patients suffering adverse tissue reactions in the resurfacing group had abnormal wear of the bearing surfaces. Six THR patients had relatively low rates of articular wear, but were found to have considerable damage at the trunion-taper interface. Our results suggest that wear at the modular junction is an important factor in the development of adverse tissue reactions after implantation of a large-diameter MoM THR.

Aims

The long-term functional outcome of total hip arthroplasty (THA) performed by trainees is not known. A multicentre retrospective study of 879 THAs was undertaken to investigate any differences in outcome between those performed by trainee surgeons and consultants.

We compared the clinical and radiological outcomes of two cementless femoral stems in the treatment of patients with a Garden III or IV fracture of the femoral neck. A total of 70 patients (70 hips) in each group were enrolled into a prospective randomised study. One group received a short anatomical cementless stem and the other received a conventional cementless stem. Their mean age was 74.9 years (50 to 94) and 76.0 years (55 to 96), respectively (p = 0.328). The mean follow-up was 4.1 years (2 to 5) and 4.8 years (2 to 6), respectively. Perfusion lung scans and high resolution chest CTs were performed to detect pulmonary microemboli.

At final follow-up there were no statistically significant differences between the short anatomical and the conventional stems with regard to the mean Harris hip score (85.7 (66 to 100) versus 86.5 (55 to 100); p = 0.791), the mean Western Ontario and McMaster Universities Osteoarthritis Index (17 (6 to 34) versus 16 (5 to 35); p = 0.13) or the mean University of California, Los Angeles activity score (5 (3 to 6) versus 4 (3 to 6); p = 0.032). No patient with a short stem had thigh pain, but 11 patients (16%) with a conventional stem had thigh pain. No patients with a short stem had symptomatic pulmonary microemboli, but 11 patients with a conventional stem had pulmonary microemboli (symptomatic in three patients and asymptomatic in eight patients). One hip (1.4%) in the short stem group and eight (11.4%) in the conventional group had an intra-operative undisplaced fracture of the calcar. No component was revised for aseptic loosening in either group. One acetabular component in the short stem group and two acetabular components in the conventional stem group were revised for recurrent dislocation.

Our study demonstrated that despite the poor bone quality in these elderly patients with a fracture of the femoral neck, osseo-integration was obtained in all hips in both groups. However, the incidence of thigh pain, pulmonary microemboli and peri-prosthetic fracture was significantly higher in the conventional stem group than in the short stem group.

We sought to establish the incidence of joint failure secondary to adverse reaction to metal debris (ARMD) following metal-on-metal hip resurfacing in a large, three surgeon, multicentre study involving 4226 hips with a follow-up of 10 to 142 months. Three implants were studied: the Articular Surface Replacement; the Birmingham Hip Resurfacing; and the Conserve Plus. Retrieved implants underwent analysis using a co-ordinate measuring machine to determine volumetric wear. There were 58 failures associated with ARMD. The median chromium and cobalt concentrations in the failed group were significantly higher than in the control group (p < 0.001). Survival analysis showed a failure rate in the patients with Articular Surface Replacement of 9.8% at five years, compared with < 1% at five years for the Conserve Plus and 1.5% at ten years for the Birmingham Hip Resurfacing. Two ARMD patients had relatively low wear of the retrieved components. Increased wear from the metal-on-metal bearing surface was associated with an increased rate of failure secondary to ARMD. However, the extent of tissue destruction at revision surgery did not appear to be dose-related to the volumetric wear.

Eighteen hip fusions were converted to total hip replacements. A constrained acetabular liner was used in three hips. Mean follow up was five years (two to 15). Two (11%) hips failed, requiring revision surgery and two patients (11%) had injury to the peroneal nerve. Heterotopic ossification developed in seven (39%) hips, in one case resulting in joint ankylosis. No hips dislocated.

Conversion of hip fusion to hip replacement carries an increased risk of heterotopic ossification and neurological injury. We advise prophylaxis against heterotropic ossification. When there is concern about hip stability we suggest that the use of a constrained acetabular liner is considered. Despite the potential for complications, this procedure had a high success rate and was effective in restoring hip function.

Aims

The optimal management of intracapsular fractures of the femoral neck in independently mobile patients remains open to debate. Successful fixation obviates the limitations of arthroplasty for this group of patients. However, with fixation failure rates as high as 30%, the outcome of revision surgery to salvage total hip arthroplasty (THA) must be considered. We carried out a systematic review to compare the outcomes of salvage THA and primary THA for intracapsular fractures of the femoral neck.

This multicentre study analysed 12 alumina ceramic-on-ceramic components retrieved from squeaking total hip replacements after a mean of 23 months in situ (11 to 61). The rates and patterns of wear seen in these squeaking hips were compared with those seen in matched controls using retrieval data from 33 ‘silent’ hip replacements with similar ceramic bearings. All 12 bearings showed evidence characteristic of edge-loading wear. The median rate of volumetric wear was 3.4 mm³/year for the acetabular component, 2.9 mm³/year on the femoral heads and 6.3 mm³/year for head and insert combined. This was up to 45 times greater than that of previously reported silent ceramic-on-ceramic retrievals. The rate of wear seen in ceramic components revised for squeaking hips appears to be much greater than in that seen in retrievals from ‘silent’ hips.

Aims

The purpose of this study was to validate the diagnosis of periprosthetic joint infection (PJI) in the Danish Hip Arthroplasty Register (DHR).

The term developmental dysplasia of the hip (DDH) describes a spectrum of disorders that results in abnormal development of the hip joint. If not treated successfully in childhood, these patients may go on to develop hip symptoms and/or secondary osteoarthritis in adulthood. In this review we describe the altered anatomy encountered in adults with DDH along with the management options, and the challenges associated with hip arthroscopy, osteotomies and arthroplasty for the treatment of DDH in young adults.

Cite this article: Bone Joint J 2013;95-B:732–7.

Surface hip replacement (SHR) is generally used in younger, active patients as an alternative conventional total hip replacement in part because of the ability to preserve femoral bone. This major benefit of surface replacement will only hold true if revision procedures of SHRs are found to provide good clinical results.

A retrospective review of SHR revisions between 2007 and 2012 was presented, and the type of revision and aetiologies were recorded. There were 55 SHR revisions, of which 27 were in women. At a mean follow-up of 2.3 years (0.72 to 6.4), the mean post-operative Harris hip score (HHS) was 94.8 (66 to 100). Overall 23 were revised for mechanical reasons, nine for impingement, 13 for metallosis, nine for unexplained pain and one for sepsis. Of the type of revision surgery performed, 14 were femoral-only revisions; four were acetabular-only revisions, and 37 were complete revisions.

We did not find that clinical scores were significantly different between gender or different types of revisions. However, the mean post-operative HHS was significantly lower in patients revised for unexplained pain compared with patients revised for mechanical reasons (86.9 (66 to 100) versus 99 (96 to 100); p = 0.029). There were two re-revisions for infection in the entire cohort.

Based on the overall clinical results, we believe that revision of SHR can have good or excellent results and warrants a continued use of the procedure in selected patients. Close monitoring of these patients facilitates early intervention, as we believe that tissue damage may be related to the duration of an ongoing problem. There should be a low threshold to revise a surface replacement if there is component malposition, rising metal ion levels, or evidence of soft-tissue abnormalities.

Cite this article: Bone Joint J 2013;95-B, Supple A:88–91.