Aims

Acetabular edge-loading was a cause of increased wear rates in metal-on-metal hip arthroplasties, ultimately contributing to their failure. Although such wear patterns have been regularly reported in retrieval analyses, this study aimed to determine their in vivo location and investigate their relationship with acetabular component positioning.

Aims

Hip resurfacing arthroplasty (HRA) is typically indicated for young and active patients. Due to the longevity of arthroplasty, these patients are likely to undergo revision surgery during their lifetime. There is a paucity of information on the long-term outcome of revision surgeries performed after failed HRA. The aim of our study was to provide survivorship data as well as clinical scores after HRA revisions.

Tapered, fluted, modular, titanium stems have a long history in Europe and are increasing in popularity in North America. We have reviewed the results at our institution looking at stem survival and clinical outcomes. Radiological outcomes and quality of life assessments have been performed and compared to cylindrical non-modular cobalt chromium stems. Survival at five years was 94%. This fell to 85% at ten years due to stem breakage with older designs. Review of radiology showed maintenance or improvement of bone stock in 87% of cases. Outcome scores were superior in tapered stems despite worse pre-operative femoral deficiency. Tapered stems have proved to be a useful alternative in revision total hip arthroplasty across the spectrum of femoral bone deficiency

Aims

The optimum clearance between the bearing surfaces of hip arthroplasties is unknown. Theoretically, to minimize wear, it is understood that clearances must be low enough to maintain optimal contact pressure and fluid film lubrication, while being large enough to allow lubricant recovery and reduce contact patch size. This study aimed to identify the relationship between diametrical clearance and volumetric wear, through the analysis of retrieved components.

Aims

The Exeter V40 cemented polished tapered stem system has demonstrated excellent long-term outcomes. This paper presents a systematic review of the existing literature and reports on a large case series comparing implant fractures between the Exeter V40 series; 125 mm and conventional length stem systems.

Aims

Unicompartmental knee arthroplasty (UKA) has become a popular method of treating knee localized osteoarthritis (OA). Additionally, the posterior cruciate ligament (PCL) is essential to maintaining the physiological kinematics and functions of the knee joint. Considering these factors, the purpose of this study was to investigate the biomechanical effects on PCL-deficient knees in medial UKA.

Aims

We present the clinical and radiological results at a minimum follow-up of 20 years using a second-generation uncemented total hip arthroplasty (THA). These results are compared to our previously published results using a first-generation hip arthroplasty followed for 20 years.

Aims

This study aimed to determine if macrophages can attach and directly affect the oxide layers of 316L stainless steel, titanium alloy (Ti6Al4V), and cobalt-chromium-molybdenum alloy (CoCrMo) by releasing components of these alloys.

Aims

For many designs of total knee arthroplasty (TKA) it remains unclear whether cemented or uncemented fixation provides optimal long-term survival. The main limitation in most studies is a retrospective or non-comparative study design. The same is true for comparative trials looking only at the survival rate as extensive sample sizes are needed to detect true differences in fixation and durability. Studies using radiostereometric analysis (RSA) techniques have shown to be highly predictive in detecting late occurring aseptic loosening at an early stage. To investigate the difference in predicted long-term survival between cemented, uncemented, and hybrid fixation of TKA, we performed a randomized controlled trial using RSA.

Tissue reaction to wear particles from metal implants may play a major role in the aseptic loosening of implants. We used electron microprobe elemental analysis to determine the chemical composition of wear particles embedded in the soft tissues around hip and knee implants from 11 patients at revision surgery for aseptic loosening. The implants were made of cobalt-chromium-molybdenum alloy or titanium-aluminium-vanadium alloy. Histological examination showed a widespread giant-cell reaction to the particles. Elemental analysis showed that the chemical composition of the particles was different from that of the implanted alloys: cobalt and titanium were reduced, often down to zero, whereas chromium and aluminium persisted. Our findings indicate that corrosion is continually changing the shape, size and chemical composition of the implanted alloy. This may alter the biochemical environment of the tissue surrounding an implant to favour bone resorption

This is part of a larger study designed to investigate the action of particulate metals of orthopaedic interest on tissues. Damaging effects were determined by cytological examination and the assay of two enzymes. Lactic dehydrogenase (LDH) if released into the supernatant indicates a damaged cell membrane; decreased intracellular levels of glucose-6-phosphate dehydrogenase (G6PD) indicates a lowered phagocytic capacity of the cells. Soluble and wear products around implanted prostheses could facilitate late infections by impairing local reactions to bacteria. Particulate cobalt, nickel and cobalt-chromium alloy were found to damage the cells and to cause LDH release. G6PD was found to have a lower activity in the cells exposed to these materials. In contrast, titanium, chromium and molybdenum were well tolerated by macrophages and had no effect on the distribution and activity of either enzyme. The solubility of these metals in the culture medium was also measured

Wear debris was extracted from 21 worn hip and knee replacements. Its mutagenic effects were tested on human cells in tissue culture using the micronucleus assay and fluorescent in situ hybridisation. The extracted wear debris increased the level of micronuclei in a linear dose-dependent manner but with a tenfold difference between samples. The concentration of titanium +/− vanadium and aluminium within the wear debris was linearly related both to the level of centromere-positive micronuclei in tissue culture, indicating an aneuploid event, and to the level of aneuploidy in vivo in peripheral blood lymphocytes. The concentration of cobalt and chromium +/− nickel and molybdenum in the wear debris correlated with the total index of micronuclei in tissue culture, both centromere-positive and centromere-negative i.e. both chromosomal breakage and aneuploidy events. The results show that wear debris can damage chromosomes in a dose-dependent manner which is specific to the type of metal. The results from studies in vitro correlate with those in vivo and suggest that the wear debris from a worn implant is at least partly responsible for the chromosomal damage which is seen in vivo

We aimed to assess whether the immunological abnormalities which have been observed in patients with loose total hip replacements (THRs) are present in patients with a well-fixed prosthesis. We examined blood samples from 39 healthy donors, 22 patients before THR and 41 with well-fixed THRs of different types (15 metal-on-metal, 13 metal-on-polyethylene, 13 ceramic-on-ceramic). Before THR, the patients showed a decrease in leukocytes and myeloid cells in comparison with healthy donors, and a prevalence of type-1 T lymphocytes, which was confirmed by the increase in ratio of interferon-γ to interleukin 4. Moreover, patients with metal-on-metal or metal-on-polyethylene implants showed a significant decrease in the number of T lymphocytes and a significant increase in the serum level of chromium and cobalt, although no significant correlation was observed with the immunological changes. In the ceramic-on-ceramic group, leukocytes and lymphocyte subsets were not significantly changed, but a significant increase in type-2 cytokines restored the ratio of interferon-γ to interleukin 4 to normal values. We conclude that abnormalities of the cell-mediated immune response may be present in patients with a well-fixed THR, and that the immunological changes are more evident in those who have at least one metal component in the articular coupling

Aims

To compare the in vivo long-term fixation achieved by two acetabular components with different porous ingrowth surfaces using radiostereometric analysis (RSA).

Aims

Modular dual mobility (DM) prostheses in which a cobalt-chromium liner is inserted into a titanium acetabular shell (vs a monoblock acetabular component) have the advantage of allowing supplementary screw fixation, but the potential for corrosion between the liner and acetabulum has raised concerns. While DM prostheses have shown improved stability in patients deemed ‘high-risk’ for dislocation undergoing total hip arthroplasty (THA), their performance in young, active patients has not been reported. This study’s purpose was to assess clinical outcomes, metal ion levels, and periprosthetic femoral bone mineral density (BMD) in young, active patients receiving a modular DM acetabulum and recently introduced titanium, proximally coated, tapered femoral stem design.