To assess the effect of improved methods of femoral cementing on the loosening rates in young patients, we reviewed 50 'second-generation' cemented hip arthroplasties in 44 patients aged 50 years or less. The femoral stems were all collared and rectangular in cross-section with rounded corners. The cement was delivered by a gun into a medullary canal occluded distally with a cement plug. A clinical and radiographic review was undertaken at an average of 12 years (10 to 14.8) and no patient was lost to follow-up. No
There is increasing global awareness of adverse
reactions to metal debris and elevated serum metal ion concentrations
following the use of second generation metal-on-metal total hip
arthroplasties. The high incidence of these complications can be
largely attributed to corrosion at the head-neck interface. Severe
corrosion of the taper is identified most commonly in association
with larger diameter femoral heads. However, there is emerging evidence
of varying levels of corrosion observed in retrieved components
with smaller diameter femoral heads. This same mechanism of galvanic
and mechanically-assisted crevice corrosion has been observed in
metal-on-polyethylene and ceramic components, suggesting an inherent
biomechanical problem with current designs of the head-neck interface. We provide a review of the fundamental questions and answers
clinicians and researchers must understand regarding corrosion of
the taper, and its relevance to current orthopaedic practice. Cite this article:
After cemented total hip arthroplasty (THA) there may be failure at either the cement-stem or the cement-bone interface. This results from the occurrence of abnormally high shear and compressive stresses within the cement and excessive relative micromovement. We therefore evaluated micromovement and stress at the cement-bone and cement-stem interfaces for a titanium and a chromium-cobalt stem. The behaviour of both implants was similar and no substantial differences were found in the size and distribution of micromovement on either interface with respect to the stiffness of the stem. Micromovement was minimal with a cement mantle 3 to 4 mm thick but then increased with greater thickness of the cement. Abnormally high micromovement occurred when the cement was thinner than 2 mm and the stem was made of titanium. The relative decrease in surface roughness augmented slipping but decreased debonding at the cement-bone interface. Shear stress at this site did not vary significantly for the different coefficients of cement-bone friction while compressive and hoop stresses within the cement increased slightly.
We studied prospectively the long-term results of the Charnley Elite-Plus femoral stem in 184 consecutive young patients (194 hips). There were 130 men and 54 women with a mean age of 49.1 years (21 to 60). The predominant diagnosis was osteonecrosis of the femoral head (63.6%, 117 patients). Clinical and radiological evaluation was undertaken at each follow-up. The mean follow-up was 11.2 years (10 to 12). The mean pre-operative Harris hip score was 43.4 (12 to 49) which improved to 91 (59 to 100) at the final follow-up. The survival of the femoral stem at 12 years was 99% with revision as the end-point. The mean annual linear wear of the polyethylene liner was 0.17 mm (0.13 to 0.22). The prevalence of acetabular osteolysis was 10.8% (21 hips) and osteolysis of the calcar femorale 12.9% (25 hips). A third-generation cementing technique, accurate alignment of the stem and the use of a 22 mm zirconia head were important factors in the prevention of aseptic loosening of the Elite Plus femoral stem in these high-risk young patients.
We retrieved 159 femoral heads at revision surgery to determine changes in surface configuration. Macroscopic wear of the head was observed in three bipolar hip prostheses as a result of three-body wear. There was a considerable change in surface roughness in the internal articulation of bipolar hip prostheses. Roughness in alumina heads was almost the same as that in new cobalt-chromium heads. The annual linear wear rate of polyethylene cups with alumina heads was less than that of cups with cobalt-chromium alloy heads. Polyethylene wear was increased in the prostheses which had increased roughness of the head.
The outcome of 219 revision total hip arthroplasties
(THAs) in 98 male and 121 female patients, using 137 long length
and 82 standard length cemented collarless double-taper femoral
stems in 211 patients, with a mean age of 72 years (30 to 90) and
mean follow-up of six years (two to 18) have been described previously.
We have extended the follow-up to a mean of 13 years (8 to 20) in
this cohort of patients in which the pre-operative bone deficiency Paprosky
grading was IIIA or worse in 79% and 73% of femurs with long and
standard stems, respectively. For the long stem revision group, survival to re-revision for
aseptic loosening at 14 years was 97% (95% confidence interval (CI)
91 to 100) and in patients aged >
70 years, survival was 100%. Two
patients (two revisions) were lost to follow-up and 86 patients
with 88 revisions had died. Worst-case analysis for survival to
re-revision for aseptic loosening at 14 years was 95% (95% CI 89
to 100) and 99% (95% CI 96 to 100) for patients aged >
70 years. One
additional long stem was classified as loose radiographically but
not revised. For the standard stem revision group, survival to re-revision
for aseptic loosening at 14 years was 91% (95% CI 83 to 99). No
patients were lost to follow-up and 49 patients with 51 hips had
died. No additional stems were classified as loose radiographically. Femoral revision using a cemented collarless double-taper stem,
particularly with a long length stem, and in patients aged >
70
years, continues to yield excellent results up to 20 years post-operatively,
including in hips with considerable femoral metaphyseal bone loss. Cite this article:
We compared the clinical outcome with femoral subsidence and radiographic changes in 102 patients at 9 to 13 years after low friction arthroplasty. In 92 cases with a satisfactory outcome there was an average of 2.3 radiological signs and mean subsidence of less than 5 mm. An unsatisfactory outcome was associated with 3.4 signs per film and with subsidence of more than 5 mm. The radiological signs we describe are often the hallmark of successful load transmission, but if they increase with time or are associated with subsidence of over 5 mm, then clinical failure is likely. Fracture of the cement tip is associated with increased subsidence and adversely affects the long-term clinical outcome.
We assessed the outcome of patients with Vancouver type B2 and B3 periprosthetic fractures treated with femoral revision using an uncemented extensively porous-coated implant. A retrospective clinical and radiographic assessment of 22 patients with a mean follow-up of 33.7 months was performed. The mean time from the index procedure to fracture was 10.8 years. There were 17 patients with a satisfactory result. Complications in four patients included subsidence in two, deep sepsis in one, and delayed union in one. Concomitant acetabular revision was required in 19 patients. Uncemented extensively porous-coated femoral stems incorporate distally allowing stable fixation. We found good early survival rates and a low incidence of nonunion using this implant.
We have compared the survival and radiological outcome at ten years after total hip replacement using two techniques for preparing the femoral canal. The same prosthesis was used throughout and all operations were performed by the same surgical team. In technique 1 the canal was over-reamed by 2 mm and in technique 2 it was reamed to the same size as the prosthesis. Technique 1 was performed on 92 patients and technique 2 on 97 patients. The survival at ten years was 97.2% (90.6 to 99.2) for technique 1 and 98.8% (92.9 to 99.8) for technique 2. Vertical migration was greater in technique 1 (1.8 mm
We have investigated the role of the penetration of saline on the shear strength of the cement-stem interface for stems inserted at room temperature and those preheated to 37°C using a variety of commercial bone cements. Immersion in saline for two weeks at 37°C reduced interfacial strength by 56% to 88% after insertion at room temperature and by 28% to 49% after preheating of the stem. The reduction in porosity as a result of preheating ranged from 71% to 100%. Increased porosity correlated with a reduction in shear strength after immersion in saline (r = 0.839, p <
0.01) indicating that interfacial porosity may act as a fluid conduit.
We report a clinical and radiological survival analysis of 148 consecutive revisions of hip arthroplasties. All patients referred were offered revision if it was indicated and they were medically fit. About one-third (32%) had had at least one previous revision, and about one-third had an established deep infection. The revisions were performed in ultra-clean air with body-exhaust suits. The usual method of fixation was by contained and pressurised cement of standard viscosity, to which appropriate antibiotics had been added in infected cases. Some patients had cementless revision. Clinical failure meant that one or both of the implants had been removed; radiological failure was assessed from serial radiographs. The clinical survival at ten years was 95%. The Merle D'Aubigne and Postel rating for pain improved from a mean of 2.9 to 5.2; and in Charnley group A and B cases, walking ability improved from 2.3 to 4.3. In contrast to some reports we also found good radiological survival; this was 90.5% for cemented femoral stems. Isoelastic revision stems inserted without cement gave poor results.
Review of the radiographs of 882 consecutive metal-to-polyethylene hip replacements after a mean follow-up of 6.8 years showed 72 cases (8%) of aseptic femoral loosening, all of which showed a lucent zone or black line between metal and cement. In 97% of the series this appeared within two years of the arthroplasty. Progress of loosening was unpredictable and only 24% had significant symptoms. Improved technique with methylmethacrylate cement in Stanmore prostheses had reduced loosening after two years from 7.9% to 0.4%. Methods of detection of early loosening are discussed.