The outcome of total hip replacement (THR) is potentially affected by the body mass index (BMI) of the patient. We studied the outcome of 2026 consecutive primary cementless THRs performed for osteoarthritis. The mean follow-up was 6.3 years (0 to 11.71) and no patient was lost to follow-up for survival analysis. The patients were divided into two groups according to their BMI as follows: non-obese (BMI < 30 kg/m²) and obese (BMI ≥ 30 kg/m²).

The obese patient undergoing surgery was found to be significantly younger (p < 0.001). The log-rank test for equality of survival showed no difference in the mid-term survival (p = 0.552) with an estimated survival at 11 years of 95.2% (95% CI 92.5 to 98.0) in the non-obese and 96.7% (95% CI 94.9 to 98.5) in the obese groups. The clinical and radiological outcome was determined in a case-matched study performed on 134 obese individuals closely matched with 134 non-obese controls. The non-obese group was found to have a significantly higher post-operative Harris hip score (p < 0.001) and an increased range of movement, but overall satisfaction with surgery was comparable with that of the obese patients. Radiological analysis of the acetabular and femoral components showed no significant differences with regard to radiolucent lines, osteolysis, ingrowth of the femoral component, the acetabular inclination angle or alignment of the femoral component. Our results suggest that the survival of cementless THR is not adversely affected by obesity. Obese patients can therefore be counselled that despite a lower clinical score, they should expect to be satisfied with the result of their THR with a mid-term survival rate equivalent to that of non-obese patients.

We used demineralised bone matrix (DBM) to augment re-attachment of tendon to a metal prosthesis in an in vivo ovine model of reconstruction of the extensor mechanism at the knee. We hypothesised that augmentation of the tendon-implant interface with DBM would enhance the functional and histological outcomes as compared with previously reported control reconstructions without DBM. Function was assessed at six and 12 weeks postoperatively, and histological examination was undertaken at 12 weeks.

A significant increase of 23.5% was observed in functional weight-bearing at six weeks in the DBM-augmented group compared with non-augmented controls (p = 0.004). By 12 weeks augmentation with DBM resulted in regeneration of a more direct-type enthesis, with regions of fibrocartilage, mineralised fibrocartilage and bone. In the controls the interface was predominantly indirect, with the tendon attached to the bone graft-hydroxyapatite base plate by perforating collagen fibres.

Between 2002 and 2008, 130 consecutive ankles were replaced with an hydroxyapatite (HA) and titanium-HA-coated Ankle Evolutive System total ankle prosthesis. Plain radiographs were analysed by two independent observers. Osteolytic lesions were classified by their size and location, with cavities > 10 mm in diameter considered to be ‘marked’. CT scanning was undertaken in all patients with marked osteolysis seen on the plain radiographs.

Osteolytic lesions were seen on the plain films in 48 (37%) and marked lesions in 27 (21%) ankles. The risk for osteolysis was found to be 3.1 (95% confidence interval 1.6 to 5.9) times higher with implants with Ti-HA porous coating.

Care should be taken with ankle arthroplasty until more is known about the reasons for these severe osteolyses.

Second-generation metal-on-metal bearings were introduced as a response to the considerable incidence of wear-induced failures associated with conventional replacements, especially in young patients. We present the results at ten years of a consecutive series of patients treated using a metal-on-metal hip resurfacing. A distinct feature of the bearings used in our series was that they had been subjected to double-heat treatments during the post-casting phase of their manufacture. In the past these bearings had not been subjected to thermal treatments, making this a unique metal-on-metal bearing which had not been used before in clinical practice.

We report the outcome of 184 consecutive hips (160 patients) treated using a hybrid-fixed metal-on-metal hip resurfacing during 1996. Patients were invited for a clinicoradiological follow-up at a minimum of ten years. The Oxford hip score and anteroposterior and lateral radiographs were obtained. The mean age at operation was 54 years (21 to 75). A series of 107 consecutive hips (99 patients) who received the same prosthesis, but subjected to a single thermal treatment after being cast, between March 1994 and December 1995, were used as a control group for comparison.

In the 1994 to 1995 group seven patients (seven hips) died from unrelated causes and there were four revisions (4%) for osteolysis and aseptic loosening. In the 1996 group nine patients died at a mean of 6.9 years after operation because of unrelated causes. There were 30 revisions (16%) at a mean of 7.3 years (1.2 to 10.9), one for infection at 1.2 years and 29 for osteolysis and aseptic loosening. Furthermore, in the latter group there were radiological signs of failure in 27 (24%) of the 111 surviving hips.

The magnitude of the problem of osteolysis and aseptic loosening in the 1996 cohort did not become obvious until five years after the operation. Our results indicate that double-heat treatments of metal-on-metal bearings can lead to an increased incidence of wear-induced osteolysis.

We analysed the results of different strategies in the revision of primary uncemented acetabular components reported to the Norwegian Arthroplasty Register. The aim was to compare the risk of further acetabular revision after isolated liner exchange and complete component revision. The results of exchanging well-fixed components were also compared with those of exchanging loose acetabular components. The period studied was between September 1987 and April 2005. The following groups were compared: group 1, exchange of liner only in 318 hips; group 2, exchange of well-fixed components in 398; and group 3, exchange of loose components in 933. We found that the risk of a further cup revision was lower after revision of well-fixed components (relative risk from a Cox model (RR) = 0.56, 95% confidence interval 0.37% to 0.87%) and loose components (RR = 0.56, 95% confidence interval 0.39% to 0.80%), compared with exchange of the liner in isolation. The most frequent reason for a further acetabular revision was dislocation, accounting for 61 (28%) of the re-revisions. Other reasons for further revision included pain in 27 (12%), loosening in 24 (11%) and infection in 20 (9%). Re-revisions because of pain were less frequent when complete component (fixed or loose) revision was undertaken compared with isolated exchange of the liner (RR = 0.20 (95% confidence interval 0.06% to 0.65%) and RR = 0.10 (95% confidence interval 0.03% to 0.30%), respectively). The risk of further acetabular revision for infection, however, did not differ between the groups.

In this study, exchange of the liner only had a higher risk of further cup revision than revision of the complete acetabular component. Our results suggest that the threshold for revising well-fixed components in the case of liner wear and osteolysis should be lowered.

We report the clinical and radiographic outcome of a consecutive series of 138 hydroxyapatite-coated total knee replacements with a mean follow-up of 11 years (10 to 13). The patients were entered into a prospective study and all living patients (76 knees) were evaluated. The Hospital for Special Surgery knee score was obtained for comparison with the pre-operative situation. No patient was lost to follow-up. Radiographic assessment revealed no loosening. Seven prostheses have been revised, giving a cumulative survival rate of 93% at 13 years. We believe this to be the longest follow-up report available for an hydroxyapatite-coated knee replacement and the first for this design of Insall-Burstein II knee.

We describe the experience with the first consecutive 230 Birmingham hip resurfacings at our centre. At a mean follow-up of three years (25 to 52 months) survivorship was 99.14% with revision in one patient for a loose acetabular component and one death from unrelated causes. One patient developed a fracture of the femoral neck at six weeks which united unremarkably after a period of non-weight-bearing. The Harris hip score improved from a mean of 62.54 (8 to 92) to 97.74 (61 to 100). The mean flexion improved from 91.52° (25 to 140) to 110.41° (80 to 145).

Most patients (97%) considered the outcome to be good or excellent. Our preliminary experience with this implant is encouraging and the results are superior to the earlier generation of resurfacings for the same length of follow-up.

The Cambridge Cup has been designed to replace the horseshoe-shaped articular cartilage of the acetabulum and the underlying subchondral bone. It is intended to provide physiological loading with minimal resection of healthy bone.

The cup has been used in 50 women with displaced, subcapital fractures of the neck of the femur. In 24 cases, the cup was coated with hydroxyapatite. In 26, the coating was removed before implantation in order to simulate the effect of long-term resorption.

The mean Barthel index and the Charnley-modified Merle d’Aubigné scores recovered to their levels before fracture. We reviewed 30 women at two years, 21 were asymptomatic and nine reported minimal pain. The mean scores deteriorated slightly after five years reflecting the comorbidity of advancing age. Patients with the hydroxyapatite-coated components remained asymptomatic, with no wear or loosening. The uncoated components migrated after four years and three required revision. This trial shows good early results using a novel, hydroxyapatite-coated, physiological acetabular component.