We analysed revised Mathys isoelastic polyacetal femoral stems with stainless-steel heads and polyethylene acetabular cups from eight patients in order to differentiate various types of particle of wear debris. Loosening of isoelastic femoral stems is associated with the formation of polyacetal wear particles as well as those of polyethylene and metal. All three types of particle were isolated simultaneously by tissue digestion followed by sucrose gradient centrifugation. Polyacetal particles were either elongated, ranging from 10 to 150 μm in size, or shred-like and up to 100 μm in size. Polyethylene particles were elongated or granules, and were typically submicron or micronsized. Polyacetal and polyethylene polymer particles were differentiated by the presence of BaSO. 4. , which is added as a radiopaque agent to polyacetal but not to polyethylene. This was easily detectable by back-scattered SEM analysis and verified by energy dispersive x-ray analysis. Two types of foreign-body giant cell (FBGC) were recognised in the histological specimens. Extremely large FBGCs with irregular polygonal particles showing an uneven, spotty birefringence in polarised light were ascribed to polyacetal debris. Smaller FBGCs with slender elongated particles shining uniformly brightly in polarisation were related to polyethylene. Mononucleated histiocytes containing both types of particle were also present. Our findings offer a better understanding of the processes involved in the loosening of polyacetal stems and indicate why the idea of ‘isoelasticity’ proved to be unsuccessful in clinical practice

Our aim was to determine whether in vitro studies would detect differences in the cellular response to wear particles of two titanium alloys commonly used in the manufacture of joint replacement prostheses. Particles were of the order of 1 μm in diameter representative of those found adjacent to failed prostheses. Exposure of human monocytes to titanium 6-aluminium 4- vanadium (TiAlV) at concentrations of 4 x 10. 7. particles/ml produced a mean prostaglandin E. 2. release of 2627.6 pM; this was significantly higher than the 317.4 pM induced by titanium 6-aluminium 7-niobium alloy (TiAlNb) particles (p = 0.006). Commercially-pure titanium particles induced a release of 347.8 pM. In addition, TiAlV stimulated significantly more release of the other cell mediators, interleukin-1, tumour necrosis factor and interleukin-6. At lower concentrations of particles there was less mediator release and less obvious differences between materials. None of the materials caused significant toxicity. The levels of inflammatory mediators released by phagocytic cells in response to wear particles may influence the amount of periprosthetic bone loss. Our findings have shown that in vitro studies can detect differences in cellular response induced by particles of similar titanium alloys in common clinical use, although in vivo studies have shown little difference. While in vitro studies should not be used as the only form of assessment, they must be considered when assessing the relative biocompatibility of different implant materials

We studied wear in the ultra-high-molecular-weight polyethylene offset bore socket in 54 hips which had had Charnley low-friction arthroplasty. At an average follow-up of 8.1 years, the mean penetration rate was 0.04 mm per year. Correlation between the depth of socket penetration and the incidence of socket migration was confirmed, but socket migration occurred with lower penetration than had been previously reported

Twenty-two high-density polyethylene sockets from Charnley low-friction arthroplasties have been studied. Acrylic casts and shadowgraph techniques were used to measure both the real and radiographic rates of wear; these rates showed a significant correlation. In the sagittal plane, nine of the sockets had worn lateral to a line drawn vertically from the centre of curvature of the socket, 12 had worn medial to that line and only one was worn exactly in the line. In the coronal plane, nine sockets had worn in front of a similar vertical line, two behind that line and 11 had worn exactly in the line. Evidence of impingement of the neck of the stem onto the rim of the socket was found in 14 patients; this is considered to be one of the causes of socket loosening. The obvious solution is to reduce the diameter of the neck of the stem from 12.5 mm to 10 mm; provided that it is made of cold-formed, high nitrogen-content stainless steel, this narrower neck is strong enough not to fracture

We have updated our previous randomised controlled trial comparing release of chromium (Cr) and cobalt (Co) ions and included levels of titanium (Ti) ions. We have compared the findings from 28 mm metal-on-metal total hip replacement, performed using titanium CLS/Spotorno femoral components and titanium AlloFit acetabular components with Metasul bearings, with Durom hip resurfacing using a Metasul articulation or bearing and a titanium plasma-sprayed coating for fixation of the acetabular component. Although significantly higher blood ion levels of Cr and Co were observed at three months in the resurfaced group than in total hip replacement, no significant difference was found at two years post-operatively for Cr, 1.58 μg/L and 1.62 μg/L respectively (p = 0.819) and for Co, 0.67 μg/L and 0.94 μg/L respectively (p = 0.207). A steady state was reached at one year in the resurfaced group and after three months in the total hip replacement group. Interestingly, Ti, which is not part of the bearing surfaces with its release resulting from metal corrosion, had significantly elevated ion levels after implantation in both groups. The hip resurfacing group had significantly higher Ti levels than the total hip replacement group for all periods of follow-up. At two years the mean blood levels of Ti ions were 1.87 μg/L in hip resurfacing and and 1.30 μg/L in total hip replacement (p = 0.001). The study confirms even with different bearing diameters and clearances, hip replacement and 28 mm metal-on-metal total hip replacement produced similar Cr and Co metal ion levels in this randomised controlled trial study design, but apart from wear on bearing surfaces, passive corrosion of exposed metallic surfaces is a factor which influences ion concentrations. Ti plasma spray coating the acetabular components for hip resurfacing produces significantly higher release of Ti than Ti grit-blasted surfaces in total hip replacement

We have followed up for a period of seven to nine years 100 consecutive arthroplasties of the hip in which an entirely HA-coated implant had been used. The clinical results were excellent and bony incorporation was extensive in all components. No stem became loose or subsided but five cups were revised because of loosening after 3.8 to 5.5 years, having functioned painlessly and shown radiological ingrowth. Revision procedures because of excessive polyethylene wear have been performed on 18 hips and are planned for six more. Two eroded metal backings with worn-through polyethylene were exchanged; six hips showed metallosis without polyethylene wear-through. There were two cases of granulomatous cysts in the groin and 66 hips had osteolysis located periarticularly, in the greater trochanter or in the acetabulum

We studied cartilage degeneration in 45 canine acetabula after implantation of prostheses with articulating surfaces of low-temperature isotropic (LTI) pyrolytic carbon, cobalt-chromium-molybdenum alloy and titanium alloy for periods ranging from two weeks to 18 months. Gross specimens and histological sections were compared with the nonoperated (control) acetabulum of the same animal. Cartilage articulating with LTI pyrolytic carbon exhibited significantly lower levels of gross wear, fibrillation, eburnation, glycosaminoglycan loss, and subchondral bone change than with metallic surfaces. Survivorship analysis showed a 92% probability of survival for cartilage articulating with LTI pyrolytic carbon at 18 months, as compared to only a 20% probability of survival for cartilage articulating with either of the metallic alloys

It has been suggested that the wear of ultra-high molecular weight polyethylene (UHMWPE) in total hip replacement is substantially reduced when the femoral head is ceramic rather than metal. However, studies of alumina and zirconia ceramic femoral heads on the penetration of an UHMWPE liner in vivo have given conflicting results. The purpose of this study was to examine the surface characteristics of 30 alumina and 24 zirconia ceramic femoral heads and to identify any phase transformation in the zirconia heads. We also studied the penetration rate of alumina and zirconia heads into contemporary UHMWPE liners. The alumina heads had been implanted for a mean of 11.3 years (8.1 to 16.2) and zirconia heads for a mean of 9.8 years (7.5 to 15). The mean surface roughness values of the explanted alumina heads (Ra 40.12 nm and Rpm 578.34 nm) were similar to those for the explanted zirconia heads (Ra 36.21 nm and Rpm 607.34 nm). The mean value of the monoclinic phase of two control zirconia heads was 1% (0.8% to 1.5%) and 1.2% (0.9% to 1.3%), respectively. The mean value of the monoclinic phase of 24 explanted zirconia heads was 7.3% (1% to 26%). In the alumina group, the mean linear penetration rate of the UMWPE liner was 0.10 mm/yr (0.09 to 0.12) in hips with low Ra and Rpm values (13.22 nm and 85.91 nm, respectively). The mean linear penetration rate of the UHMWPE liner was 0.13 mm/yr (0.07 to 0.23) in hips with high Ra and Rpm values (198.72 nm and 1329 nm, respectively). This difference was significant (p = 0.041). In the zirconia head group, the mean linear penetration rate of the UHMWPE liner was 0.09 mm/yr (0.07 to 0.14) in hips with low Ra and Rpm values (12.78 nm and 92.99 nm, respectively). The mean linear penetration rate of the UHMWPE liner was 0.12 mm/yr (0.08 to 0.22) in hips with high Ra and Rpm values (199.21 nm and 1381 nm, respectively). This difference was significant (p = 0.039). The explanted zirconia heads which had a minimal phase transformation had similar surface roughness and a similar penetration rate of UHMWPE liner as the explanted alumina head

The aim of this study was to assess the effect of frictional torque and bending moment on fretting corrosion at the taper interface of a modular femoral component and to investigate whether different combinations of material also had an effect. The combinations we examined were 1) cobalt–chromium (CoCr) heads on CoCr stems 2) CoCr heads on titanium alloy (Ti) stems and 3) ceramic heads on CoCr stems.

In test 1 increasing torque was imposed by offsetting the stem in the anteroposterior plane in increments of 0 mm, 4 mm, 6 mm and 8 mm when the torque generated was equivalent to 0 Nm, 9 Nm, 14 Nm and 18 Nm.

In test 2 we investigated the effect of increasing the bending moment by offsetting the application of axial load from the midline in the mediolateral plane. Increments of offset equivalent to head + 0 mm, head + 7 mm and head + 14 mm were used.

Significantly higher currents and amplitudes were seen with increasing torque for all combinations of material. However, Ti stems showed the highest corrosion currents. Increased bending moments associated with using larger offset heads produced more corrosion: Ti stems generally performed worse than CoCr stems. Using ceramic heads did not prevent corrosion, but reduced it significantly in all loading configurations.

Cite this article: Bone Joint J 2015;97-B:463–72.

Between 1999 and 2001, 90 patients underwent total hip replacement using the same uncemented acetabular and femoral components with a 28 mm metallic femoral head but with prospective randomisation of the acetabular liner to either Durasul highly cross-linked polyethylene or nitrogen-sterilised Sulene polyethylene. We assessed 83 patients at a minimum follow-up of ten years. Linear penetration of the femoral head was estimated at six weeks, six and 12 months and annually thereafter, using the Dorr method, given the non-spherical shape of the acetabular component.

There was no loosening of any component; only one hip in the Sulene group showed proximal femoral osteolysis. The mean penetration of the femoral head at six weeks was 0.08 mm (0.02 to 0.15) for the Durasul group and 0.16 mm (0.05 to 0.28) for the Sulene group (p = 0.001). The mean yearly linear penetration was 64.8% lower for the Durasul group at 0.05 mm/year (sd 0.035) for the Sulene group and 0.02 mm/year (sd 0.016) for the Durasul (p < 0.001). Mean linear femoral head penetration at ten years was 61% less in the Durasul than Sulene group. Highly cross-linked polyethylene gives excellent results at ten years.

Cite this article: Bone Joint J 2013;95-B:326–32.

Pain in the distribution of the sciatic nerve is common in the elderly. In the presence of a long-standing joint replacement, consideration should be given as to whether compression might be due to an extraspinal cause. We present three women, in whom a mass of wear debris from a previous total hip replacement caused compression of the sciatic nerve posterior to the hip. The symptoms were relieved immediately following operation

We examined the cellular responses to various particles injected into the knees and the intramedullary femoral cavities of rats in the presence of polymethyl-methacrylate (PMMA) plugs. The intra-articular particles were mainly ingested by synovial fibroblasts. Increased numbers of macrophages were not detected and there was only a slight increase in synovial thickness. Cellular responses in the intramedullary space were similarly mild and bone resorption around the PMMA plug did not occur. Bone formation was inhibited only by polyethylene particles. In contrast to current views, our study shows that wear particles per se do not initiate bone resorption

We recovered 23 meniscal bearings from 18 failed bicompartmental Oxford knee prostheses. They had been implanted for one to nine years. The minimum thickness of the retrieved bearings was measured and compared with the thickness of 25 unused bearings. The mean penetration rate, calculated by two methods, was either 0.043 or 0.026 mm per annum. This compares with 0.19 mm per annum reported for the Charnley hip. The use of a fully congruous meniscal bearing prosthesis can reduce wear in knee arthroplasty to a very low rate

We report a case of a male patient presenting with bilateral painful but apparently well-positioned and -fixed large-diameter metal-on-metal hip replacements four years post-operatively. Multiple imaging modes revealed a thick-walled, cystic expansile mass in communication with the hip joint (a pseudotumour). Implant retrieval analysis and tissue culture eliminated high bearing wear or infection as causes for the soft-tissue reaction, but noted marked corrosion of the modular neck taper adaptor and corrosion products in the tissues. Therefore, we believe corrosion products from the taper caused by mismatch of the implant components led to pseudotumour formation requiring revision.

We revised seven alumina-blasted cementless hip prostheses (Ti-alloy stems, cp Ti threaded sockets) with low- or high-carbon Co-alloy bearings at a mean of 20.1 months after implantation because of pain and loosening. Histological examination of the retrieved periprosthetic tissues from two cases in which the implant was stable and three in which the socket was loose showed macrophages with basophilic granules containing metal and alumina wear particles and lymph-cell infiltrates. In one of the two cases of stem loosening the thickened neocapsule also contained definite lymphatic follicles and gross lymphocyte/plasma-cell infiltrates. Spectrometric determination of the concentration of elements in periprosthetic tissues from six cases was compared with that of joint capsules from five control patients undergoing primary hip surgery. In the revisions the mean concentration of implant-relevant elements was 693.85 μg/g dry tissue. In addition to Cr (15.2%), Co (4.3%), and Ti (10.3%), Al was predominant (68.1%) and all concentrations were significantly higher (p < 0.001) than those in the control tissues. The annual rates of linear wear were calculated for six implants. The mean value was 11.1 μm (heads 6.25 μm, inserts 4.82 μm). SEM/EDXA showed numerous fine scratches and deep furrows containing alumina particles in loosened sockets, and stems showed contamination with adhering or impacted alumina particles of between 2 and 50 μm in size

We have prospectively studied the wear of enhanced ultra-high molecular-weight polyethylene (Hylamer) in combination with a zirconia femoral head of 22.225 mm diameter on a cemented, triple-tapered, collarless, polished stem, the C Stem. The 71 patients who underwent total hip arthroplasty had a mean follow-up of six years (3 to 8). No patient died or was lost to follow-up. The clinical results were excellent with 96% of patients satisfied. There were no revisions. Two cups were considered to be loose radiologically. One was avulsed from the cement in a skiing accident, with a periprosthetic fracture of the femur, but has remained stable for more than seven years. One femur shows radiological appearances which are compatible with a healing infection. One femoral component is at risk of loosening. The mean rate of penetration of the cup was 0.22 mm/year (0.06 to 0.55). Our results appear to be within the guidelines set by the National Institute of Clinical Excellence. We have discontinued the use of Hylamer despite excellent clinical results and no revisions to date because the high initial rates of penetration did not settle to the expected low levels within the anticipated time